• Structural Engineering and Mechanics
• /
• 제67권6호
• /
• pp.579-585
• /
• 2018

Masonry walls are of a complex (anisotropic) structure in terms of their mechanical properties. The mechanical properties of the walls are affected by the properties of the materials used in wall construction, joint thickness and the type of masonry bond. The carried-out studies, particularly in the seismic zones, have revealed that the most of the conventional masonry walls were constructed without considering any engineering approach. Along with that, large-scale damages were detected on such structural elements after major earthquake(s), and such damages were commonly occurred at the brick-joint interfaces. The aim of this study was to investigate the effect of joint thickness and also type of mortar on the mechanical behavior of the masonry walls. For this aim, the brick masonry walls were constructed through examination of both the literature and the conventional masonry walls. In the construction process, a single-type of brick was combined with two different types of mortar: cement mortar and hydraulic lime mortar. Three different joint thicknesses were used for each mortar type; thus, a total of six masonry walls were constructed in the laboratory. The mechanical properties of brick and mortars, and also of the constructed walls were determined. As a conclusion, it can be stated that the failure mechanism of the brick masonry walls differed due to the mechanical properties of the mortars. The use of bed joint thickness not less than 20 mm is recommended in construction of conventional masonry walls in order to maintain the act of brick in conjunction with mortar under load.

• 콘크리트학회논문집
• /
• 제25권3호
• /
• pp.305-312
• /
• 2013

이 연구는 물-결합재(W/B) 비에 따른 실리카 퓸이 알칼리 활성화 슬래그 시멘트(AASC)에 미치는 유동성과 강도 특성에 대한 연구이다. W/B비는 0.50에서 0.60까지 0.05 단위로 일정하게 변화시켰다. 실리카 퓸은 고로슬래그 중량의 0%에서 50%까지 치환시켰다. 활성화제는 수산화나트륨(NaOH)를 사용하였고, 농도는 3M로 하였다. W/B 비에 따른 강도는 1, 3, 7 그리고 28일을 측정하였다. 유동성 측정 결과는 실리카 퓸의 치환율이 증가할수록 감소하였다. 압축강도는 실리카 퓸의 치환율이 증가할수록 증가하였다. 또한 W/B 비가 증가할수록 모든 재령에서 강도는 감소하였다. 실리카 퓸은 W/B 비와 실리카 퓸의 치환율에 따라서 활성화 반응을 증대시켜 강도를 증가시키는 것을 알 수 있었다.

• 지구물리와물리탐사
• /
• 제12권2호
• /
• pp.215-220
• /
• 2009

시멘트 모르타르는 고속도로 건설 및 댐 사이트의 연약지반 보강과 석회암 공동의 지반보강에 널리 사용되고 있다. 모르타르의 물리적 성질은 많은 연구 결과로부터 잘 알려져 있지만, 연약지반의 개량 정도를 평가하기 위해서 알아야 할 가장 중요한 물성 중의 하나인 전기비저항에 대해서는 극히 일부의 연구만 수행되어 있다. 이 연구에서는 물과 포틀랜드 시멘트의 배합비(0.35, 0.45, 0.50, 0.65)를 달리하여 원통형의 모르타르 시료를 제작하여, 웨너 배열 방식으로 전기비저항을 측정하였다. 그 결과 모르타르 시료의 전기비저항은 경과시간에 따라 증가하였으며, 함수비와 물/시멘트의 배합비가 증가할수록 감소하였다. 이 결과로부터 모르타르의 전기비저항과 압축강도는 밀접한 관계를 가지고 있음을 알 수 있었다.

• Computers and Concrete
• /
• 제19권4호
• /
• pp.429-434
• /
• 2017

Failure of basic structures material is usually accompanied by expansion of interior cracks due to stress concentration at the cracks tip. This phenomenon shows the importance of examination of the failure behavior of concrete structures. To this end, 4 types of mortar samples with different amounts of nano-silica (0%, 0.5%, 1%, and 1.5%) were made to prepare twelve $50{\times}50{\times}50mm$ cubic samples. The goal of this study was to describe the failure and micro-crack growth behavior of the cement mortars in presence of nano-silica particles and control mortars during different curing days. Failure of mortar samples under compressive strength were sensed with acoustic emission technique (AET) at different curing days. It was concluded that the addition of nano-silica particles could modify failure and micro-crack growth behavior of mortar samples. Also, monitoring of acoustic emission parameters exposed differences in failure behavior due to the addition of the nanoparticles. Mortar samples of nano-silica particles revealed stronger shear mode characteristics than those without nanoparticles, which revealed high acoustic activity due to heterogeneous matrix. It is worth mentioning that the highest compressive strength for 3 and 7 test ages obtained from samples with the addition of 1.5% nano-silica particles. On the other hand maximum compressive strength of 28 curing days obtained from samples with 1% combination of nano-silica particles.

• 한국농공학회논문집
• /
• 제48권1호
• /
• pp.51-60
• /
• 2006

This study was conducted to investigate experimentally the drying shrinkage and the strength properties of redispersible SBR and PAE powder-modified mortars. Polymer-cement ratio, content of shrinkage-reducing agent and antifoamer content were manipulated as the experimental variables. The peculiarity of this study is to obtain a high early-age strength by using the portland cement and alumina cement with the ratio of 8 : 2. Until 7 days of age, the drying shrinkage remarkably increased up to $1\~2\times10^{-4}$, while it tended to decrease as the ratio of polymer to cement ratio and the content of shrinkage-reducing agent increased. Polymer-cement ratio was effective in improving the flexural, tensile and adhesive strengths: As the ratio increased, the strengths correspondingly increased. The flexural strength was in the range of $7\~11$ MPa, the tensile strength was $3.5\~5$ MPa and the adhesive strength was $1.2\~3.9$ MPa. On the other hand, the compressive strength tended to decrease as the polymer-cement ratio increased, and it was in the range of $23\~39$ MPa. All strengths, flexural, tensile, adhesive and compressive strengths, decreased as the content of powder shrinkage-reducing agent increased. It turned out that the polymer-cement ratio influenced more on the behavior of drying shrinkage and the properties of strength than the powder shrinkage-reducing agent did.

• 콘크리트학회논문집
• /
• 제24권3호
• /
• pp.241-248
• /
• 2012

이 연구에서는, 철근콘크리트 기둥 실험체를 대상으로 기둥의 휨 위험 단면부에 국부적으로 강섬유 시멘트모르타르를 적용함으로서 기존 철근콘크리트 기둥에 비해 내진성능이 우수한 강섬유 모르타르 적용 철근콘크리트 복합기둥공법에 관해 제시하였다. 제시된 적용공법의 성능검증을 위하여 기존 철근콘크리트 기둥 1개 및 소성힌지구간에 국부적으로 강섬유 모르타르를 적용한 복합기둥 실험체 2개를 제작하여 일정 축하중 하에서 횡방향 반복하중을 받는 재하시험을 수행하였다. 콘크리트 및 강섬유 모르타르는 모두 현장타설되었다. 재하시험 결과 기존 철근콘크리트 기둥 실험체와 비교하여 강섬유 모르타르 적용 철근콘크리트 복합기둥 실험체의 경우 휨 및 전단 균열의 제어에 우수할 뿐만 아니라 기둥의 횡하중 내력 및 횡방향 변형 능력 향상에서도 우수한 것으로 평가되었다.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2008년도 춘계 학술발표회 제20권1호
• /
• pp.893-896
• /
• 2008

본 연구는 황산염 환경하에서 메타카올린을 사용하여 제작된 시멘트 모르타르의 기초물성을 평가하기 위한 연구이다. 최근 열악한 환경에 노출되는 콘크리트 구조물이 증가함에 따라 콘크리트의 내구성에 대한 관심이 늘어나고 있다. 광물성 혼화재료를 첨가할 경우 콘크리트 내부의 조직을 치밀하게 하여 내구성을 좋게하는 방안이 있으며 현재에도 실리카흄, 플라이애쉬, 슬래그와 같은 기존의 광물질 혼화재료 이외에 새로운 혼화재료에 대한 연구가 활발히 진행되고 있는 실정이다. 따라서 본 연구에서는 열악한 환경에 노출된 콘크리트 열화에 대하여 아직 그 연구가 미비한 광물질 혼화재료인 메타카올린을 5%, 10%, 15%로 치환하여 시멘트 모르타르로 시편을 제작하였고, 이를 28일 표준양생을 시켜 담수, 해수, 10% 황산나트륨용액, 10% 황산마그네슘 용액에서 28일, 60일, 90일, 180일, 270일, 365일 동안 촉진양생 시켜 다양한 시편의 기초물성에 대한 실험을 수행하였다. 또한 현재 널리 쓰이고 있는 광물질 혼화재료인 실리카흄과 플라이애쉬를 가지고 같은 방법으로 실험을 한 후 메타카올린을 치환한 시편과의 비교 분석을 통하여 메타카올린의 내구적 성능을 평가하고자 한다.

• 콘크리트학회논문집
• /
• 제13권2호
• /
• pp.175-183
• /
• 2001

국내에서 생산되는 5종류 시멘트로 제조한 시멘트 경화체의 해수침식에 대한 저항성을 알아보기 위한 목적으로 2배농도 인공 해수에 각각 400일 및 800일동안 침지시켜 모르타르의 압축강도 및 길이변화를 측정한 결과, 혼합시멘트계 모르타르가 광물질혼 화재의 영향으로 포틀랜드시멘트계 모르타르와 비교하여 좋은 결과를 나타내었다. 또한 시멘트 페이스트의 XRD분석에 의한 수 화 및 반응생성물의 피크강도비를 살펴보면, 포틀랜드시멘트계 페이스트 중 저열포틀랜드시멘트의 피크강도비가 가장 작았으며, 혼합시멘트계 페이스트의 경우 portlandite 및 brucite의 피크강도비가 포틀랜드시멘트계 페이스트보다 작았다. 인공해수 침식으 로 인한 시멘트 페이스트의 공극량을 수은압입법으로 측정한 결과에 의하면 보통포틀랜드시멘트 페이스트의 총공극량이 가장 크게 나타났으나, 포틀랜드시멘트에 고로슬래그미분말 및 플라이애시를 혼합한 혼합시멘트계 페이스트의 경우 총공극량이 각각 약 56% 및 약 32 % 정도 저감되는 효과가 있었다.

• 한국건설순환자원학회논문집
• /
• 제7권4호
• /
• pp.395-404
• /
• 2019

외단열 마감 공법에서 사용되는 바탕조정재는 화재가 발생하는 경우 얇은 마감과 폴리머의 연소로 인해 표면부가 급속하게 붕괴되어 화재에 취약한 소재이다. 본 연구에서는 열적 성능이 우수한 팽창 흑연을 사용할 경우 바탕조정재의 성능을 개선할 수 있을 것으로 기대하였다. 실험결과, 팽창흑연을 사용한 바탕조정재는 부착강도 저하 및 물흡수계수 등의 감소가 발생하는 문제점이 있으나 플라이애시와 실리카흄을 사용하여 물리적 성능이 향상되는 것으로 나타났다. 팽창흑연을 사용한 바탕조정재는 복합 단열 시험체 표면의 페놀폼은 화염에 의한 표면 뚫림이 나타나지 않아 열원의 투과를 감소시킬 수 있을 것으로 나타났다.

• Computers and Concrete
• /
• 제27권3호
• /
• pp.241-252
• /
• 2021

An experimental program was conducted to investigate the fresh properties, mechanical properties and durability characteristics of the self-compacting mortars (SCM) produced with pumice powder and Artificial Lightweight Fine Aggregate (aLWFA). aLWFA was produced by using fly ash. A total of 16 different mixtures were designed with a constant water-binder ratio of 0.37, in which natural sands were partially replaced with aLWFA and pumice powder at different volume fractions of 5%, 10% and 15%. The artificial lightweight aggregates used in this study were manufactured through cold bonding pelletisation of 90% of class-F fly ash and 10% of Portland cement in a tilted pan with an ambient temperature and moisture content. Flowability tests were conducted on the fresh mortar mixtures beforehand, to determine the self-compacting characteristics on the basis of EFNARC. To determine the conformity of the fresh mortar characteristics with the standards, mini-slump and mini-V-funnel tests were carried out. Hardened state tests were conducted after 7, 28 and 56 days to determine the flexural strength and axial compressive strength respectively. Durability, sorptivity, permeability and density tests were conducted at the end of 28 days of curing time. The test results showed that the pumice powder replacement improved both the fresh state and the hardened state characteristics of the mortar and the optimum mixture ratio was determined as 15%, considering other studies in the literature. In the aLWFA mixtures used, the mechanical and durability characteristics of the modified compositions were very close to the control mixture. It is concluded in this study that mixtures with pumice powder replacement eliminated the negative effects of the aLWFA in the mortars and made a positive contribution.