• Elastomers and Composites
• /
• v.33 no.4
• /
• pp.267-273
• /
• 1998

Isocyante terminated urethane prepolymers were synthesized by the reaction of 4,4'-dimethyl phenyldiisocyanate(MDI) and ester type polyols such as ethylene glycol/ butanediol adipate(EBA), neopentylglycol/butanediol adipate (NBA) and hexanediol adipate (HA) . All of the NCO-terminated urethane prepolymers are solid at room temperature, but they become mobile enough to be disposed onto a substrate upon heating about $80^{\circ}C$. Subsequently, they are solidified and cured through the reaction with moisture. Tensile behavior of the ore-thane hotmelt exhibits characteristic features depending on the type of polyol. The adhesive strength determined by single lap shear joint is higher in order of HA, NBA and EBA based ore thane hotmelt, which can be correlated with the magnitude of breaking energy of the cured films. The failure mode are cohesive for all cases and the adhesive strength increases as the test is performed faster. This indicates that the strength of the adhesive joint is primarily dependent upon the bulk properties of the adhesives.

• 한국정보디스플레이학회:학술대회논문집
• /
• 2006.08a
• /
• pp.1779-1783
• /
• 2006

The hybrid thin-film (HTF) passivation layer composed of the UV curable acrylate layer and MS-31 (MgO:SiO2=3:1wt%) layer was adopted in organic light emitting diode (OLED) to protect organic light emitting materials from penetrations of oxygen and water vapors. The moisture resistance of the deposited HTF layer was measured by the water vapor transmission rate (WVTR). The results showed that the HTF layer possessed a very low WVTR value of lower than $0.007g/m^2$ per day at $37.8^{\circ}C$ and 100% RH. Therefore, the HTF on the OLED was found to be very effective in protect what from the penetrations of oxygen and moisture.

• Corrosion Science and Technology
• /
• v.4 no.5
• /
• pp.207-210
• /
• 2005

Coating performance of various coating systems including chlorinated rubber and epoxy/urethane used most for steel structures of highway in Korea, was evaluated by exposing test specimen to complex deterioration factors such as ultraviolet ray, moisture, freeze-thaw cycle and salt. Deteriorated specimens were evaluated by chalking and rust grades according to ASTM, and measurement of color differences and adhesion. In overall coating performances such as corrosion resistance, photochemical stability, and adhesion, ceramic/ urethane, moisture-curable urethane/ urethane, etc. were superior. As for other coating materials tested in this study, superior materials against certain deterioration factors may be inferior against other factors. Accordingly, in order to select suitable maintenance coating materials for the use, it is thought that investigation of suitability through experiment should precede selection of materials, especially for unusual coatings or paints.

• Textile Coloration and Finishing
• /
• v.22 no.3
• /
• pp.239-245
• /
• 2010

Breathable waterproof PET fabrics were prepared by the UV coating of UV-curable polyurethaneacrylate(PUA) formulation mixed with polyethyleneglycol(PEG) as a water soluble pore former. The dispersed PEG in the UV-cured coating was extracted by warm water, which can generate individual circular pores uniformly distributed all over the coating instead of pore channels. Accordingly the moisture permeability of the microporously coated fabrics increased substantially with increasing PEG addition without significant reduction of hydrostatic pressure. Also the silicone diacrylate addition in the formulation was beneficial in increasing the hydrostatic pressure. The UV-based microporous coating can be an alternative to conventional thermal curing of solventborne polyurethane coating owing to the enhanced environment friendliness and energy saving.

• Restorative Dentistry and Endodontics
• /
• v.20 no.2
• /
• pp.832-838
• /
• 1995

The purpose of this study was to evaluate the amount of marginal microleakage of 2 light curable GI cements(Fuji II LC & VariGlass), which contain some resin components. 4 volunteers kept on acrylic resin plates, which contained dentin disks with cavities filled with test materials for 2 weeks. The time when polishing was done(5 minutes and 24 hours after filling) and the use of protective agents were varied, so 8 groups with each 6 specimens were tested. After having specimens(disks with cavities filled with materials) penetrated with 1% Methylene Blue solution, specimens were stored in 40% nitric acid solution for 4 days to extract adsorbed dye material. Supernatants of centrifuged samples were diluted 5 times and Spectrophotometer was used to determine the degree of absorption. Dye concentration was calculated through the pre-obtained Linear Regression Curve. The results were as follows. 1. The best result was seen in groups (PF24, PV24) which were protected and polished 24 hours later and the opposite phenomenon was seen in groups(NF24, NV24) which were held without protection and polished 24 hours later. Groups polished S minutes later showed moderate leakage pattern. 2. Groups polished 5 minutes later showed similar leakage amount irrespective of using of protective agent. But statistically insignificant lower values were seen in VariGlass than in Fuji II LC groups, So It was considered that VariGlass may be more resistant to early moisture attack than Fuji II LC. 3. In groups polished 24 hours later, there was no significant difference between materials but was definitely significant difference according to the use of protective agent. If the cement in which polishing will be done 24 hours later, Protective agent should be used to cover the surface.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2006.04a
• /
• pp.78-80
• /
• 2006

The hybrid thin-film (HTF) passivation layer composed of the Ultra Violet (UV) curable acrylate layer and MS-31 (MgO:$SiO_2$=3:1wt%) layer was adopted in organic light emitting device (OLEO) to protect organic light emitting materials from penetrations of oxygen and water vapors. The results showed that the HTF layer possessed a very low WVTR value of lower than $0.007gm/m^{2+}day$ at $37.8^{\circ}C$ and 100% RH. This value was within the limited range of the sensitivity of WVTR measurements. And the lifetime of the HTF passivated device became almost three times longer than that of the bare device. The HTF on the OLEO was found to be very effective in protect what from the penetrations of oxygen and moisture.