• 한국전기전자재료학회논문지
• /
• 제19권1호
• /
• pp.58-63
• /
• 2006

In this Paper, ZnO films mixed with iron oxide were prepared by an ultrasonic spray pyrolysis method. The chemical composition and structural properties as a function of the Fe atomic ratio in the deposition solution were studied. Zinc acetate and ferrous chloride were used as precursors of Zn and Fe, respectively. Fe atomic ratio to Zn varied from 0.15 to 10.0. Substrate temperature was fixed at $250^{\circ}C$. The crystallographic properties and surface morphologies of the films were studied by X-ray diffraction (XRD) and scanning electron microscopy (SEM), respectively. Electron probe X-ray microanalysis (EPMA) and X-ray photoelectron spectroscopy (XPS) were carried out to analyse the chemical composition and state of Zn and Fe atoms.

• 한국표면공학회지
• /
• 제32권6호
• /
• pp.686-694
• /
• 1999

Insoluble anodes of the Ta/Ir mixed metal oxide for electrodeposition of Ni-W alloy in ammoniacal citrate bath were prepared by thermal decomposition method. Ti plate was etched in boiling oxalic acid solution and coated with ethanol solution of $TaCl_{5}$ and $IrCl_4$ mixed in a fixed ratio, followed by drying and treating at various temperatures. The coating layer of these insoluble anode was characterized by SEM, EDX, XRD and DSC. The decomposition rate of citric acid in plating bath was determined by measuring the $CO_2$ gas evolved at the anodes with Gas Chromatography. Evolution of $CO_2$ gas from Ta/Ir oxide anodes decreased about 5% compared with that of Pt. The $CO_2$ gas evolution was increased with the amount of Ir-oxide in the coatings. The coatings which have more than 40% ratio of Ta content and heat-treated at the temperature higher than $400^{\circ}C$ showed better efficiency

• Journal of Industrial and Engineering Chemistry
• /
• 제68권
• /
• pp.311-324
• /
• 2018

Herein,the Neodymium ion ($Nd^{3+}$) doped CoAl-LDH have been successfully prepared via co-precipitation method and was used as a precursor of Nd-doped CoAl-mixed metal oxides (MMO). The photocatalytic activity of doped LDH and MMO was investigated in the degradation of an azo dye, C.I. Acid Red 14, under visible light irradiation. DRS and PL analysis demonstrated decreasing in the band gap energy and recombination of photo-induced charge carriers of Nd-doped LDH and MMO compared with the pristine CoAL-LDH. Due to significant difference in photocatalytic performance. A power law empirical kinetic model was obtained for predicting the photocatalytic degradation efficiency.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2002년도 하계학술대회 논문집 Vol.3 No.2
• /
• pp.549-552
• /
• 2002

$(SrBi_2Nb_2O_9)_{0.5}-(Bi_3TiNbO_9)_{0.5}$ ceramics were fabricated by the mixed-oxide method, and the structural and electrical properties with variation of ball-milling time were investigated. All SBN-BTN specimens showed the typical polycrystalline X-ray diffraction patterns without the presence of the second phase. The SBN-BTN specimen sintered at $1200^{\circ}C$ and ball-milled for 168h showed the average grain size of $16{\mu}m$. The dielectric constant and dielectric loss of the SBN-BTN specimen sintered at $1150^{\circ}C$ and ball-mill for 72h were 225, 0.4% at 1KHz, respectively.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2001년도 춘계학술대회 논문집 유기절연재료 전자세라믹 방전플라즈마 연구회
• /
• pp.114-117
• /
• 2001

$(Ba_{0.6-x}Sr_{0.4}Ca_x)TiO_3$(x=0.10, 0.15, 0.20) ceramics were fabricated by the mixed-oxide method and their structural and dielectric properties were investigated with variation of composition ratio and sintering temperature. As a result of the differential thermal analysis(DTA), exothermic peak was observed at around $1020^{\circ}C$ due to the formation of the polycrystalline perovskite phase. BSCT(50/40/10) specimen sintered at $1500^{\circ}C$ showed the highest average grain size(18.25$[{\mu}m]$). Curie temperature and dielectric constant at room temperature decreased with increasing amount of Ca. BSCT(50/40/10) specimen sintered at $1450^{\circ}C$ showed a good dielectric constant, K, (=4324) and dielectric loss, $tan{\delta}$, (=0.972%) properties at 1[KHz].

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 1988년도 추계학술대회 논문집
• /
• pp.50-53
• /
• 1988

Lead titanate powders were prepared by mixed-oxide and sol-gel method. O-3 composites were prepared with these powders using Eccogel polymer. According to the volume percent of the PbTiO$_3$ powders, dielectric, piezoelectric properties and poling conditions were investigated. Relative dielectric constants were exponentially increased with volume percent of PbTiO$_3$. Piezoelectric strain coefficients (d$_{33}$ ) were increased with volume percent of PbTiO$_3$. Figure of merit (d$_{h}$.g$_{h}$) for the O-3 composites prepared by the mixed-oxide and sol-gel method were 2728(x10$^{-15}$ $m^2$/N) and 3100(x10$^{-15}$ $m^2$/N) at 70 volume percent of PbTiO$_3$, respectively.ely.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2008년도 추계학술대회 논문집 Vol.21
• /
• pp.189-189
• /
• 2008

Due to the environmental issue vast research is going on to replace the widely used lead contented piezoelectric materials. Bismuth sodium titanate (abbreviated as BNT) based bismuth sodium titanate-barium titanate (abbreviated as BNBT) ceramic was prepared by using modified method rather than conventional mixed oxide method. This modification was made to improve the properties of BNT based ceramic. In this procedure $BaTiO_3$ (abbreviated as BT) was prepared using conventional mixed oxide method. Analytical grade raw materials of $BaCO_3$ and $TiO_2$ were weighted and ball milled using ethanol medium. The mixed slurry was dried and sieved under 80 mesh. Then the powder was calcined at $1100^{\circ}C$ for 2 hours. This calcined BT powder was used in the preparation of BNBT. Stoichiometric amount of $Bi_2O_3$, $Na_2CO_3$, $TiO_2$ and BT were weighted and mixed by using ball mill. The used calcination temperature was $850^{\circ}C$ for 2 hours. Calcined powder was taken for another milling step. BNBT disks were pressed to 15 mm of diameter and then cold isostatical press (CIP) was used. Pressed samples were sintered at $1150^{\circ}C$ for 2 hours. The SEM microstructure analysis revealed that the grain shape of the sintered ceramic was polyhedral and grain boundary was well matched where as the sample prepared by conventional method showed irregular arrangement and grain boundary not well matched. And sintered density was better (5.78 g/cc) for the modified method. It was strongly observed that the properties of BNBT ceramic near MPB composition was found to be improved by the modified method compare to the conventional mixed oxide method. The piezoelectric constant dB of 177.33 pC/N, electromechanical coupling factor $k_p$ of 33.4%, dielectric constant $K_{33}^T$ of 688.237 and mechanical quality factor $Q_m$ of 109.37 was found.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 1994년도 추계학술대회 논문집
• /
• pp.8-12
• /
• 1994

Solid solutions $Sr_2$($Ta_{1-x}$$Nb_{x}$)$_2$$O_{7}$ (x = 0.0 - 1.0) composed of strontium-tantalate (low Curie temperature) and strontium-niobate (high Curie temperature) were prepared by the conventional mixed oxide method and the molten salt synthesis method (flux method). Phase relation, sintering temperature, grain-orientation and dielectric properties were investigated for sintered ceramic samples with different compositions. Both Curie temperature and dielectric constant at Curie temperature were increased, and sintering behavior and the degree of grain-orientation were improved with the increase of Nb content. Single phase $Sr_2$$Nb_2$$O_{7}$ powder was synthesized by using flux method at lower temperatures, and sintering temperature was also reduced by using flux method derived powder than using mixed-oxide derived powder. Sintering characteristics and dielectric properties of specimens prepared by flux method were better than those derived through the conventional method.

• 대한치과의사협회지
• /
• 제9권4호
• /
• pp.157-160
• /
• 1971

To compare the effects of various pulp capping agents that are usually applied to human pulp tissue, adult dogs were bred for a certain period and each capping agent was applied experimentally to pulp tissue after vital pulpotomy. Histological observations are as follows. 1) In comparison between methods of vital pulpotomy, one and two appointment method, different courses of healing were observed. In one appointment method, the granulation tissue formation at the amputation sur face of pulp tissue had a tendency to be transformed to scar tissue formation. In two appointment method, more transformation than that of one appointment method from scar tissue to dentin matrix formation were observed. 2) Histologic changes that have appeared in pulp tissue are a) fixation at outer layer b) degeneration at middle layer c) hyperemia and round cell infiltration at inner layer 3) With use of formocresol mixed zinc oxide powder in two appointment method complete formation of dentin matrix were observed. 4) Among the methods and aagents described above formocresol mixed zinc oxide powder in two appointment method appeared to be relatively effective.

• Journal of Electrochemical Science and Technology
• /
• 제9권2호
• /
• pp.93-98
• /
• 2018

$MnO_2$, a metal oxide used as an electrode material in electrochemical capacitors (EDLCs), has been applied in binary oxide and conducting polymer hybrid electrodes to increase their stability and capacitance. We developed a method for electrodepositing Mn-Ni oxide/PANI, Mn-Ni oxide/PEDOT, and Mn-Ni-Ru oxide/PEDOT films on carbon paper in a single step using a mixed bath. Mn-Ni oxide/PEDOT and Mn-Ni-Ru oxide/PEDOT electrodes used in an electro-osmotic pump (EOP) have shown better efficiency compared to Mn-Ni oxide and Mn-Ni oxide/PANI electrodes through testing in water as a pumping solution. EOP using a Mn-Ni-Ru oxide/PEDOT electrode was also tested in a 0.5 mM $Li_2SO_4$ solution as a pumping solution to confirm the effect of the $Li^+$ insertion/de-insertion reaction of Ruthenium oxide on the EOP. Experimental results show that the flow rate increases with the increase in current in a 0.5 mM $Li_2SO_4$ solution compared to that obtained when water was used as a pumping solution.