• Applied Chemistry for Engineering
• /
• v.27 no.2
• /
• pp.179-184
• /
• 2016

In this work, the influence of milled carbon fiber direction on mechanical properties of milled carbon fibers/carbon blacks/natural rubber compounds was investigated. The compounds were prepared by adding the 6 phr milled carbon fibers (MCFs) and 40 phr carbon blacks (CBs) into the natural rubber. The MCFs were aligned in a parallel and orthogonal direction in the compounds using two-roll-mill machine. Mechanical properties of compounds were studied by tensile characteristics and tearing strength. As a result, the compounds showed higher tensile strength, 100%~300% modulus, and tearing strength than those of using any other compounds due to the aligning MCFs in parallel. Mechanical properties of the compounds reinforced with non-aligned MCFs were inferior to those of others. Consequently, the parallel aligned MCFs in the compounds led to an increase of tensile properties and improvement of tearing strength, resulted from MCFs with the high elastic modulus.

• Composites Research
• /
• v.29 no.5
• /
• pp.262-268
• /
• 2016

In this work, the pitch-based carbon paper (P-CP) was prepared by re-impregnating of binder pitches and PAN-based milled carbon fibers (MCF) at low temperature carbonization process. The influence of MCF content on physicochemical properties of MCF/P-CP was investigated. As a result, the tensile strength of MCF/P-CP was increased sharply from 10 wt.% to 20 wt.% of MCF. Also, the increase of MCF content led to the decrease of interfacial contact resistivity and the improvement of electrical and thermal conductivity of MCF/P-CP. These results were probably due to the increase of density of MCF/P-CP, resulting in the formation of electrically and thermally conductive paths of the carbon paper.

• Journal of the Korean Ceramic Society
• /
• v.32 no.9
• /
• pp.989-994
• /
• 1995

Rigid porous carbon fiber composites with the uniform pore size distribution were prepared by vacuum forming from water slurries containing carbonized PAN fibers, a phenolic resin and ceramic binders. The composites were designed to use for highly efficient carbon fiber filters for particulate filtration and gas adsorption. As the as-received carbon fibers of 1mm in length were milled to an approximate average length of 300${\mu}{\textrm}{m}$, modulus of rupture (MOR) of the composite filter was increased from 1MPa to the value larger than 5 MPa. Modulus of rupture (MOR) for the composite filter fabricated using the milled carbon fiber was increased from 5 MPa to 10 MPa as the carbonization temperature of the PAN fiber was raised from 90$0^{\circ}C$ to 140$0^{\circ}C$. The air permeability and an average pore size of the composite filter were increased from 40 to 270cc/min.$\textrm{cm}^2$ and from 35 to 80${\mu}{\textrm}{m}$, respectively, as the apparent porosity increased from 80 to 95%. It was shown that the MOR of the carbon fiber composite filter was dependent primarily on the average length of carbon fiber, carbonization temperature and the type of bonding materials.