• Proceedings of the Korean Society of Tribologists and Lubrication Engineers Conference
• /
• 1996.10a
• /
• pp.163-167
• /
• 1996

The life of rolling elements depends on various factors such as operating conditions and material properties. In this work, the effect of microstructure on the rolling behavior is investigated. Specially, the deformations in the substrate regions before and after rolling are compared. It is found that rolling action causes severe flow of material in the direction opposite to the rolling direction in the case of dry rolling direction. With lubrication, the deformation is more severe at the subsurface region rather than at the surface.

• Journal of Powder Materials
• /
• v.10 no.5
• /
• pp.310-317
• /
• 2003

Two-component ceramic (alumina-zirconia) composites were fabricated by a soft-solution process in which polyethylene glycol (PEG) was used as a polymeric carrier. Metal salts and PEG were dissolved in ethyl alcohol without any precipitation in 1:1 volume ratio of alumina and zirconia. In the non-aqueous system, the flammable solvent made explosive, exothermic reaction during drying process. The reaction resulted in formation of volume expanded, porous precursor powders by a vigorous decomposition of organic components in the precursor sol. The PEG content affected the grain size of sintered composites as well as the morphology of precursor powders. The difference of microstructure in sintered composite was attribute to the solubility and homogeneity of metal cations in precursor sol. At the optimum amount of the PEG polymer, the metal ions were dispersed effectively in solution and a homogeneous polymeric network was formed. It made less agglomerated particles in the precursor sol and affected on uniform grain size in sintered composite.

• Journal of Powder Materials
• /
• v.19 no.5
• /
• pp.343-347
• /
• 2012

In this study, an oxygen plasma treatment was used as a low temperature debinding method to form a conductive copper feature on a flexible substrate using a direct printing process. To demonstrate this concept, conductive copper patterns were formed on polyimide films using a copper nanoparticle-based paste with polymeric binders and dispersing agents and a screen printing method. Thermal and oxygen plasma treatments were utilized to remove the polymeric vehicle before a sintering of copper nanoparticles. The effect of the debinding methods on the phase, microstructure and electrical conductivity of the screen-printed patterns was systematically investigated by FE-SEM, TGA, XRD and four-point probe analysis. The patterns formed using oxygen plasma debinding showed the well-developed microstructure and the superior electrical conductivity compared with those of using thermal debinding.

• Journal of Powder Materials
• /
• v.11 no.1
• /
• pp.16-21
• /
• 2004

The nano-sized Co particles were successfully synthesized by chemical vapor condensation (CVC) process using the precursor of cobalt carbonyl ($Co_2(CO)_8$). The influence of carrier gases on the microstructure and magnetic properties of nanoparticles was investigated by means of XRD, TEM, XPS and VSM. The Co nano-particles with different phases and shapes were synthesized with a change of carrier gas : long string morphologies with coexistence of fcc and hcp structure in Ar carrier gas condition; finer Co core in a mass of cobalt oxide with only fcc structure in He; rod type cobalt oxide phase in Ar＋6vol％$O_2$. The saturation magnetization and coercivity was lower in Co nanoparticles synthesized in He carrier gas, due to their finer size.

• Journal of Powder Materials
• /
• v.8 no.2
• /
• pp.117-123
• /
• 2001

Formation of pores in melt-processed $YBa_2Cu_3O_{7-x}$ (123) oxides and its effect on the microstructure were studied. Spherical pores with a size of a few tens of microns were formed due to the evolution of oxygen gas during melting of a 123 oxide. Some of pores were converted into liquid pockets by liquid filling, but others remained unfilled. The liquid pockets were converted into spherical 123 regions with a lower $Y_2BaCuO_5$ (211)density through the peritectic reaction during subsequent cooling, while the pores were entrapped into the periteictically grown 123 grains. The spherical 123 regions often consists of a residual melt due to the unbalanced peritectically reaction.

• Journal of Powder Materials
• /
• v.11 no.4
• /
• pp.328-332
• /
• 2004

Fe nanopowders were successfully synthesized by plasma arc discharge (PAD) process using Fe rod. The influence of chamber pressure on the microstructure was investigated by means of X-ray Diffraction (XRD), Field Emission Scanning Electron Microscope (FE-SEM), Transmission Electron Microscopy (TEM) and X-ray Photoelectron Spectroscopy (XPS). The prepared particles had nearly spherical shapes and consisted of metallic cores (a-Fe) and oxide shells (Fe$_{3}$O$_{4}$), The powder size increased with increasing chamber pressure due to the higher dissolution and ejection rate of H$_2$ and gas density in the molten metal.

• Journal of Powder Materials
• /
• v.18 no.6
• /
• pp.502-509
• /
• 2011

In this study, a novel-processing route for fabricating microcellular zirconia ceramics has been developed. The proposed strategy for making the microcellula zirconia ceramics involved hollow microspheres as pore former. Compared to conventional dense microspheres pore former, well-defined pore structured zirconia ceramics were successfully fabricated. Effects of hollow microsphere content and sintering temperature on microstructure, porosity, pore distribution, and strength were investigated in the processing of microcellular zirconia ceramics.

• Proceedings of the KWS Conference
• /
• 2002.10a
• /
• pp.469-474
• /
• 2002

Laser and hot air reflow soldering of PBGA solder ball was investigated. Experimental results showed that surface quality and shear strength of solder bumps reflowed by laser was superior than the solder bumps reflowed by hot air, and the microstructure inside the solder bumps reflowed by laser was much finer. Analysis on interfacial reaction showed that eutectic solder reacted with Au/Ni/Cu pad shortly after the solder was melted. Interface of solder bump reflowed by laser consists of a continuous AuSn$_4$ layer and remnant Au element. Needle-like AuSn$_4$ grew sidewise from interface, and then spread out to the entire interface region. A thin layer of Ni$_3$Sn$_4$ intermetallic compound was found at the interface of solder bump reflowed by hot air, AuSn$_4$ particles distributed inside the whole solder bump randomly. It is the combination effect of the continuous AuSn$_4$ layer and finer eutectic microstructure inside the solder bump reflowed by laser that resulted in higher shear strength.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2003.10b
• /
• pp.40-42
• /
• 2003

The aim of this paper is to illustrate which factors influence the martensite grain fineness made by subsequently surface carburizing of extruded component. The effects of surface decarburizing by annealing, residual stress, initial microstructure and crystal oriental made by forward extrusion were taken into account. The available evidence suggests that the residual stress inside crystal or the crystal orientation is the main factor that results coarse martensite while cold extruded component was treated by carburizing.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2006.05a
• /
• pp.222-225
• /
• 2006

The effect of lubrication on the development of textures and Microstructure was studied by different lubricating condition during hot rolling of AA1050 aluminum alloy. Hot rolling without lubrication led to the evolution of the pronounced through-thickness texture gradients, whereas hot rolling with lubrication gave rise to the formation of uniform rolling texture in the whole thickness layer. The variation of texture and microstructure according to hot rolling condition are investigated by X-ray diffractometer (XRD) and Electron Back-Scattered Diffraction (EBSD). The experimental results were discussed base on the finite element method (FEM) simulation. FEM calculation reveals that a larger friction between roll and sheet causes the deviated strain state from a plane strain leading to the formation of shear textures in the thickness layers close to the surface.