• Journal of the Korean Magnetics Society
• /
• v.19 no.1
• /
• pp.12-16
• /
• 2009

Z-type barium ferrite [($Ba_{3}Co_{0.8}Zn_{1.2}Fe_{24}O_{41}$, $Ba_{3+{\delta}}Co_{0.8}Zn_{1.2}Fe_{24}O_{41}$ ${\delta}$ = 3, 5, 7, 13 wt%. $Ba_{3}Co_{0.8}Zn_{1.2}Fe_{24+{\delta}}O_{41}$ ${\delta}$ = 5, 7, 10 wt% )] were synthesized using co-precipitation method. The microstructure and magnetic properties of synthesized particles were investigated. In all prepared particles M-type Ba ferrite is identified with Z-type Ba ferrite together. It is found that particles having 7 wt% for Ba and 5 wt% for Fe excess addition revealed high saturation magnetization, respectively. All synthesized particles showed relatively high coercivity for device application. This result may be attributed to the contribution of M-type Ba ferrite. Ba and Fe excess addition was not affected to the structural change of CoZnZ Ba ferrite. The certain amount of excess additions of Ba and Fe and the 2 step heat-treatment may be beneficial to the improvement of soft magnetic properties of Z-type barium hexa-ferrite

• Journal of Sericultural and Entomological Science
• /
• v.43 no.2
• /
• pp.77-82
• /
• 2001

This study was investigated to know the effects of diflubenzuron(DFB) on the larval silkgland development of the silk-worm, Bombyx mori (L.). It has been known as a prohibitor of chitin synthesis mostly on the species of the Order Lepidoptera. In this work, the effects of the DFB concentrations (2.5$\times$10$\^$-1/,2.5$\times$10$\^$-2/, and 2.5$\times$10$\^$-3/$\mu\textrm{g}$/$\mu$l on the various larval stages, were investigated in terms on the silkgland. The macro- and microstructure of cell membrane of silkgland, and the differences of silkgland weight and water contents treated by DFB are also surveyed. As the tesults, the silkgland weight depended sensitively on not the DFB concentration but the DFB treatment period. The longer DFB treatment period, the lighter dried silkgland weight and the heavier water content of the silkgland. White opaque(WO) emerged in the middle silkgland of DFB treated larva. From the scanning election microscope observation, the cell membrane of silkgland of DFB treated larva was distinctly more compact compared to that of control. The WO was evidently resulted from the obstacles of normal transformation of silk protein through the cell membrane of middle silkgland.

• Korean Journal of Materials Research
• /
• v.28 no.11
• /
• pp.663-670
• /
• 2018

H13 tool steels are widely used as metallic mold materials due to their high hardness and thermal stability. Recently, many studies are undertaken to satisfy the demands for manufacturing the complex shape of the mold using a 3D printing technique. It is reported that the mechanical properties of 3D printed materials are lower than those of commercial forged alloys owing to micropores. In this study, we investigate the effect of microstructures and defects on mechanical properties in the 3D printed H13 tool steels. H13 tool steel is fabricated using a selective laser melting(SLM) process with a scan speed of 200 mm/s and a layer thickness of $25{\mu}m$. Microstructures are observed and porosities are measured by optical and scanning electron microscopy in the X-, Y-, and Z-directions with various the build heights. Tiny keyhole type pores are observed with a porosity of 0.4 %, which shows the lowest porosity in the center region. The measured Vickers hardness is around 550 HV and the yield and tensile strength are 1400 and 1700 MPa, respectively. The tensile properties are predicted using two empirical equations through the measured values of the Vickers hardness. The prediction of tensile strength has high accuracy with the experimental data of the 3D printed H13 tool steel. The effects of porosities and unmelted powders on mechanical properties are also elucidated by the metallic fractography analysis to understand tensile and fracture behavior.

• Asian-Australasian Journal of Animal Sciences
• /
• v.32 no.1
• /
• pp.63-71
• /
• 2019

Objective: The aim of the study was to investigate the effect of zinc-bearing palygorskite (Zn-Pal) on rumen fermentation by in vitro gas-production system. Methods: In trial, 90 incubators were evenly divided into five groups: control (0% Zn-Pal), treatment I (0.2% Zn-Pal), treatment II (0.4% Zn-Pal), treatment III (0.6% Zn-Pal), and treatment IV (0.8% Zn-Pal). The contents of zinc for treatments were 0, 49, 98, 147, 196 mg/kg, respectively. The main chemical composition and microstructure of Zn-Pal was investigated by X-ray diffraction. The physicochemical features were evaluated by Zeta potential analysis, cation-exchange capacity, ethylene blue absorption and specific surface area (the Brunauer-Emmett-Teller method). In vitro gas production (GP) was recorded at 3, 6, 9, 12, 18, 24, 36, 48, 60, and 72 h incubation. Incubation was stopped at 0, 6, 12, 24, 48, and 72 h and the inoculants were tested for pH, microbial protein yield (MCP), $NH_3-N$, volatile fatty acids (VFAs), lipopolysaccharide (LPS). Results: The results showed that the GP in the treatment groups was not significantly different from the control groups (p>0.05). Compared to the control group, pH was higher at 24 h, 48 h (p<0.05), and 72 h (p<0.01) (range 6 to 7). The concentration of $NH_3-N$ in the three treatment groups was higher than in the control group at 24 h (p<0.01), meanwhile, it was lower at 48 h and 72 h (p<0.01), except in the treatment IV. The concentration of MCP in treatment I group was higher than in the control at 48 h (p<0.01). Compared with control, the LPS concentration in treatment III became lower at 12 h (p<0.05). Total VFAs in treatments were higher than in the control at 24 h, 48 h (p<0.05). Conclusion: These results suggest that the addition of Zn-Pal can improve the rumen fermentation, especially when adding 0.2% Zn-Pal.

• Korean Journal of Metals and Materials
• /
• v.49 no.2
• /
• pp.167-173
• /
• 2011

Nickel cobalt ferrite($Ni_{0.5}Co_{0.5}Fe_2O_4$) powder was prepared through the ceramic route by the calcination of a stoichiometric mixture of NiO, CoO and $Fe_2O_3$ at $1100^{\circ}C$. The pressed pellets of $Ni_{0.5}Co_{0.5}Fe_2O_4$ were isothermally reduced in pure hydrogen at $800{\sim}1100^{\circ}C$. Based on the thermogravimetric analysis, the reduction behavior and the kinetic reaction mechanisms of the synthesized ferrite were studied. The initial ferrite powder and the various reduction products were characterized by X-ray diffraction, scanning electron microscopy, reflected light microscope and vibrating sample magnetometer to reveal the effect of hydrogen reduction on the composition, microstructure and magnetic properties of the produced Fe-Ni-Co alloy. The arrhenius equation with the approved mathematical formulations for the gas solid reaction was applied to calculate the activation energy($E_a$) and detect the controlling reaction mechanisms. In the initial stage of hydrogen reduction, the reduction rate was controlled by the gas diffusion and the interfacial chemical reaction. However, in later stages, the rate was controlled by the interfacial chemical reaction. The nature of the hydrogen reduction and the magnetic property changes for nickel cobalt ferrite were compared with the previous result for nickel ferrite. The microstructural development of the synthesized Fe-Ni-Co alloy with an increase in the reduction temperature improved its soft magnetic properties by increasing the saturation magnetization($M_s$) and by decreasing the coercivity($H_c$). The Fe-Ni-Co alloy showed higher saturation magnetization compared to Fe-Ni alloy.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.35 no.4
• /
• pp.398-406
• /
• 2022

In order to increase the electrochemical performance of thermal battery anode, LIFT anode having the same weight but a larger lithium content in electrodes was fabricated by mixing lithium, iron and titanium. By applying these electrodes, a single cell and a thermal battery were prepared, and the effect of LIFT anode on electrochemical performance was evaluated. The LIFT-applied single cell presented a better cell performance than LIFe-applied single cell at 500℃ and 550℃. The discharge performance of LIFT-applied single cell, which included the operating time (787s), specific capacity (1,683 Asg^-1), and electrode utilization (80.7%), was improved collectively compared to the LIFe applied single cell (736s, 1,245 As g^-1, and 74.6%) at 500℃. As the discharge progressed, the internal resistance of LIFT anode decreased, because the lithium migration path was formed due to the presence of large titanium particles among iron particles. These results were analyzed in terms of the microstructure of electrode using SEM. Energy density of LIFT-applied single cell also increased by 10% to 142.1 Wh kg^-1 compared to that of LIFe-applied single cell (127.4 Wh kg^-1). In addition, the LIFT-applied single cell presented a stable discharge performance for 6,500s without a short circuit which could occur by molten lithium under an open circuit voltage condition with a high pressure (4 kgf cm^-2). As observed in the high temperature thermal battery performance tests, the voltage and specific capacity of LIFT-applied thermal battery are superior to those of LIFe-applied thermal batteries, indicating that the energy density of LIFT-applied thermal batteries should remarkably increase.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.32 no.5
• /
• pp.175-182
• /
• 2022

Rare-earth elements were doped with Mg to enhance the temperature stability of dielectric properties of BaTiO₃ for its application to MLCC (Multi-Layer Ceramic Capacitor). The additives strongly affect both grain growth and densification behaviors during sintering, and hence dielectric properties. The additive effects therefore should be examined in each system with different additives. This study investigated the crystal structure, grain growth and densification behaviors and related variations in dielectric constant with respect to sintering temperature. Dielectric constant appears to be varied with grain size in a temperature range between 1200 and 1300℃, suggesting the importance of grain size control. The temperature dependence of grain size variation was well explained by an established theory correlating the grain growth behavior with grain boundary structure. This accordance provides a basis for sintering technique to control grain growth thus to improve dielectric constant in rare-earth doped BaTiO₃.

• Nuclear Engineering and Technology
• /
• v.54 no.9
• /
• pp.3250-3259
• /
• 2022

A new approach to the use of rice straw as a difficult-to-recycle agricultural waste was proposed. Potassium aluminosilicate was obtained by spark plasma sintering as an effective material for subsequent immobilization of ¹³⁷Cs into a solid-state matrix. The sorption properties of potassium aluminosilicate to ¹³⁷Cs from aqueous solutions were studied. The effect of the synthesis temperature on the phase composition, microstructure, and rate of cesium leaching from samples obtained at 800-1000 ℃ and a pressure of 25 MPa was investigated. It was shown that the positive dynamics of compaction was characteristic of glass ceramics throughout the sintering. Glass ceramics RS-(K,Cs)AlSi₃O₈ obtained by the SPS method at 1000 ℃ for 5 min was characterized by a high density of ~2.62 g/cm³, Vickers hardness ~ 2.1 GPa, compressive strength ~231.3 MPa and the rate of cesium ions leaching of ~1.37 × 10^-7 g cm^-2·day^-1. The proposed approach makes it possible to safe dispose of rice straw and reduce emissions into the atmosphere of microdisperse amorphous silica, which is formed during its combustion and causes respiratory diseases, including cancer. In addition, the obtained is perspective to solve the problem of recycling long-lived ¹³⁷Cs radionuclides formed during the operation of nuclear power plants into solid-state matrices.

• Journal of Korea Foundry Society
• /
• v.41 no.4
• /
• pp.349-356
• /
• 2021

Effects of cooling condition after solidification on the microstructure and the mechanical properties of 0.36Mn containing ductile cast iron have been studied based on the minimized addition of Cu and Sn for vehicle component applications with better quality and cost competitiveness. Cu and Sn were selected for additional elements judging from the well-known fact of strong tendency of pearlite promotion followed by the tensile property improvement. After pouring of the Mg treated cast iron melt with various chemical compositions into the block specimens, two ways of post solidification cooling conditions were applied for comparison; both cooling in the mold and cooling in the air after dismantle at 800℃. The pearlite fraction of the mold-cooled specimens was analyzed as 27-44%, with the tensile strength and elongation of 513-568N/mm² and 10.4-14.3%, respectively. Whilest, the air cooled specimens showed the pearlite fraction of 77~85%, with the tensile strength and elongation of 728~758N/mm² and 3.2~6.0%, respectively. It is worthwhile to note that the remarkable improvement of both tensile strength and elongation of the ductile iron was achieved by the present air cooling condition with the minimized combined addition of Cu and Sn to the 0.36Mn containing ductile iron.

• Journal of the Korean Institute of Gas
• /
• v.26 no.6
• /
• pp.16-23
• /
• 2022

In this study, characteristics of effect on hydrogen gas was investigated to hydrogen embrittlement by disk and tensile tests. The developed and commercial alloy was fabricated to a plate material made from an alloy ingot. The prepared materials were processed in the form of a disk to measure rupture pressure by hydrogen and helium gas at a rate of 0.1 to 1,000 bar/min. In the hydrogen pre-charged tensile test, a specimen was hydrogenated using an anode charging method, and the yield strength, ultimate tensile strength, elongation, and reduction in area rate were carried by a strain rate test. Also, the microstructure was observed to the fracture surface of the tensile test specimen. As a result, the developed materials satisfied endurable hydrogen embrittlement, and the fractured surface showed a brittleness fracture surface with a depth of several ㎛, but dimple due to ductile fracture could be observed.