• Nanomaterials
• /
• 제12권20호
• /
• pp.3605-3620
• /
• 2022

Microtube-like porous carbon (MPC) and tube-like porous carbon-sulfur (MPC-S) composites were synthesized by carbonizing milkweed pappus with sulfur, and they were used as cathodes for lithium-sulfur batteries. The morphology and uniformity of these materials were characterized using X-ray powder diffraction, Raman spectroscopy, scanning electron microscopy, transmission electron microscopy with an energy-dispersive X-ray analyzer, thermogravimetric analysis, and X-ray photoelectron spectrometry. The electrochemical performance of the MPC-S cathodes was measured using the charge/discharge cycling performance, C rate, and AC impedance. The composite cathodes with 93.8 wt.% sulfur exhibited a stable specific capacity of 743 mAh g^-1 after 200 cycles at a 0.5 C.

• Bulletin of the Korean Chemical Society
• /
• 제35권2호
• /
• pp.377-382
• /
• 2014

Micro-/macroporous carbons (MMCs) were prepared using a hollow mesoporous silica capsule (HMSC) as a sacrificial hard template. The carbonization process after the infiltration of furfuryl alcohol into the template-free HMSC material afforded MMC materials in high yield. The hard template HMSC could be removed by HF etching without deteriorating the structure of MMC. The MMC materials were fully characterized by SEM, TEM, PXRD, XPS, and Raman spectroscopy. The replication processes were so successful that MMCs exhibited a hollow capsular structure with multimodal microporosity. Detailed textural properties of MMC materials were investigated by volumetric $N_2$ adsorption-desorption analysis at 77 K. To explore the gas sorption abilities of MMCs for other gases, $H_2$ and $CO_2$ sorption analyses were also performed at various temperatures. The multimodal MMC materials were found to be good sorbents for both $H_2$ and $CO_2$ at low pressure.

• Electronic Materials Letters
• /
• 제14권6호
• /
• pp.755-765
• /
• 2018

In situ nitrogen doped hard carbon nanotubes (NHCNT) were fabricated by pyrolyzing tubular nitrogen doped conjugated microporous polymer. KOH activated NHCNT (K-NHCNT) were also prepared to improve their porous structure. XRD, SEM, TEM, EDS, XPS, Raman spectra, $N_2$ adsorption-desorption, galvanostatic charging-discharge, cyclic voltammetry and EIS were used to characterize the structure and performance of NHCNT and K-NHCNT. XRD and Raman spectra reveal K-NHCNT own a more disorder carbon. SEM indicate that the diameters of K-NHCNT are smaller than that of NHCNT. TEM and EDS further indicate that K-NHCNT are hollow carbon nanotubes with nitrogen uniformly distributed. $N_2$ adsorption-desorption analysis reveals that K-NHCNT have an ultra high specific surface area of $1787.37m^2g^{-1}$, which is much larger than that of NHCNT ($531.98m^2g^{-1}$). K-NHCNT delivers a high reversible capacity of $918mAh\;g^{-1}$ at $0.6A\;g^{-1}$. Even after 350 times cycling, the capacity of K-NHCNT cycled after 350 cycles at $0.6A\;g^{-1}$ is still as high as $591.6mAh\;g^{-1}$. Such outstanding electrochemical performance of the K-NHCNT are clearly attributed by its superior characters, which have great advantages over those commercial available carbon nanotubes ($200-450mAh\;g^{-1}$) not only for its desired electrochemical performance but also for its easily and scaling-up preparation.