• 한국복합재료학회:학술대회논문집
• /
• 한국복합재료학회 2003년도 춘계학술발표대회 논문집
• /
• pp.117-120
• /
• 2003

Electro-micromechanical techniques were applied using four-probe method for carbon nanotube (CNT) or nanofiber (CNF)/epoxy composites with their content. Carbon black (CB) was used to compare with CNT and CNF. The fracture of carbon fiber was detected by nondestructive acoustic emission (AE) relating to electrical resistivity for double-matrix composites test. Sensing for fiber tension was performed by electro-pullout test under uniform cyclic strain. The sensitivity for fiber damage such as fiber fracture and fiber tension was the highest for CNT/epoxy composites, and in CB case they were the lowest compared with CNT and CNF. Reinforcing effect of CNT obtained from apparent modulus measurement was the highest in the same content. The results obtained from sensing fiber damage were correlated with the morphological observation of nano-scale structure using FE-SEM. The information on fiber damage and matrix deformation and reinforcing effect of carbon nanocomposites could be obtained from electrical resistivity measurement as a new concept of nondestructive evaluation.

• 접착 및 계면
• /
• 제6권2호
• /
• pp.13-20
• /
• 2005

환경 친화적인 자연섬유 강화 고분자 복합재료의 계면 전단강도는 총체적인 기계적 물성을 조절하는데 매우 중요한 역할을 수행한다. Ramie와 Kenaf 섬유 강화 에폭시 복합재료의 계면 전단강도는 최종 물성을 위한 최적 조건을 찾아내기 위해 미세역학시험법과 비파괴 음향방출시험을 이용하여 평가했다. Ramie와 Kenaf 섬유의 동적 접촉각을 측정했고, 계면 접착에서 젖음성과 상호 관련시켜서 해석하였다. Ramie와 Kenaf 섬유의 기계적 물성은 단섬유 인장시험을 통해 조사했고, 통계학적으로 uni-와 bimodal Weibull 분포를 통해서 분석하였다. Ramie와 Kenaf 섬유에 대한 실제 신장율의 clamping 효과의 영향도 평가할 수 있었다. 두 가지의 다른 미세파괴 형상은 섬유다발과 단섬유 복합재료로부터 오는 축방향의 debonding과 섬유상의 fracture는 인장과 압축하중하에서 관찰할 수 있었다.

• 한국복합재료학회:학술대회논문집
• /
• 한국복합재료학회 2002년도 추계학술발표대회 논문집
• /
• pp.212-215
• /
• 2002

Interfacial evaluation and damage sensing of the carbon fiber/epoxy-amine terminated (AT)-polyetherimide (PEI) composites were performed using micromechanical test and electrical resistance measurement. As AT-PEI content increased, the fracture toughness of epoxy-AT-PEI matrix increased, and thus their interfacial shear strength (IFSS) was improved due to the improved toughness. After curing process, the changes in electrical resistance (ΔR) with increasing AT-PEI contents increased gradually because of the changes in thermal expansion coefficient (TEC) and thermal shrinkage of matrix. Matrix fracture toughness was correlated to the IFSS, residual stress and electrical resistance. The results obtained from the electrical resistance measurement during curing process, reversible stress/strain, and durability test were consistent with modified matrix toughness properties.

• Structural Engineering and Mechanics
• /
• 제42권2호
• /
• pp.153-174
• /
• 2012

Micromechanical facture models can be used to predict ductile fracture in steel structures. In order to calibrate the parameters in the micromechanical models for the largely used Q345 steel in China, uniaxial tensile tests, smooth notched tensile tests, cyclic notched bar tests, scanning electron microscope tests and finite element analyses were conducted in this paper. The test specimens were made from base metal, deposit metal and heat affected zone of Q345 steel to investigate crack initiation in welded steel connections. The calibrated parameters for the three different locations of Q345 steel were compared with that of the other seven varieties of structural steels. It indicates that the toughness index parameters in the stress modified critical strain (SMCS) model and the void growth model (VGM) are connected with ductility of the material but have no correlation with the yield strength, ultimate strength or the ratio of ultimate strength to yield strength. While the damage degraded parameters in the degraded significant plastic strain (DSPS) model and the cyclic void growth model (CVGM) and the characteristic length parameter are irrelevant with any properties of the material. The results of this paper can be applied to predict ductile fracture in welded steel connections.

• 한국복합재료학회:학술대회논문집
• /
• 한국복합재료학회 2002년도 춘계학술발표대회 논문집
• /
• pp.199-202
• /
• 2002

Interfacial properties and electrical sensing for fiber fracture in carbon and SiC fibers/epoxy composites were investigated by the electrical resistance measurement and fragmentation test. As fiber-embedded angle increased, interfacial shear strength (IFSS) of two-type fiber composites decreased, and the elapsed time was long to the infinity in electrical resistivity. The initial slope of electrical resistivity increased rapidly to the infinity at higher angle, whereas electrical resistivity increased gradually at small angle. Furthermore, both fiber composites with small embedded angle showed a fully-developed stress whitening pattern, whereas both composites with higher embedded angle exhibited a less developed stress whitening pattern. As embedded angle decreased, the gap between the fragments increased and the debonded length was wider for both fiber composites. Electro-micromechanical technique can be a feasible nondestructive evaluation to measure interfacial sensing properties depending on the fiber-embedded angle in conductive fiber reinforced composites.

• 폴리머
• /
• 제27권3호
• /
• pp.189-194
• /
• 2003

Electro-micromechanical 시험법을 이용하여 탄소 섬유 강화 열경화성 수지 복합재료의 경화 방법에 따른 계면 평가와 손상 감지능 및 경화 모니터링에 대해 고찰하였다. 경화 후 잔류 응력은 전기 저항 측정을 통해 모니터링 하였으며, 경화 방법에 따라 상호 비교하였다. 기지 재료의 인장 강도, 탄성률 및 계면 전단 강도는 열 경화의 경우가 자외선 경화보다 더 크게 나타났으며, 열 경화에서 경화 수축은 열팽창 계수 차이에 의한 잔류 응력 및 기지 재료의 수축에 의해 자외선 경화와 비교하여 더 크게 나타났다. 열 경화 시의 경화 중 전기 저항은 자외선 경화보다 더 큰 범위에서 변하였으며, 기지 재료의 기계적 물성과 계면 접착력에 의해 다르게 나타나는 겉보기 탄성률 또한 더 컸고, 같은 응력까지 더 빠르게 도달하였다.

• 한국복합재료학회:학술대회논문집
• /
• 한국복합재료학회 2005년도 추계학술발표대회 논문집
• /
• pp.141-144
• /
• 2005

Sensing and interfacial evaluation of Ni nanowire strands/polymer composites were investigated using Electro-micromechanical technique. Electro-micromechanical techniques can be used as sensing method for micro damage, loading, temperature of interfacial properties. Using Ni nanowire strands/silicone composites with different content, load sensing response of electrical contact resistivity was investigated under tensile and compression condition. The mechanical properties of Ni nanowire strands with different type/epoxy composites were measured using uniformed cyclic loading and tensile test. Ni nanowire strands/epoxy composites showed humidity and temperature sensing within limited ranges, 20 vol% reinforcement. Some new information on temperature and humidity sensing plus loading sensing of Ni nanowire strands/polymer composites could be obtained from the electrical resistance measurement as a new concept of the nondestructive interfacial evaluation.

• The Korean Journal of Ceramics
• /
• 제3권2호
• /
• pp.73-81
• /
• 1997

In this paper, it is intended to present more reproducible and quantitative method for adhesion assemssement. In scratch test, micromechanical analysis on the stress state beneath the indenter was carried out considering the additional blister field. The interface adhesion was quantified as work of adhesion through Griffith energy approach on the basis of the analyzed stress state. The work of adhesion for DLC film/WC-Co substrate calculated through the proposed analysis shows the identical value regardless of distinctly different critical loads measured with the change of film thickness and scratching speed. On the other hand, uniaxial loading was imposed on DCL film/Al substrate, developing the transverse film cracks perpendicular to loading direction. Since this film cracking behavior depends on the relative magnitude of adhesion strength to film fracture strength, the quantification of adhesion strength was given a trial through the micromechanical analysis of adhesion-dependence of film cracking patterns. The interface shear strength can be quantified from the measurement of strain $\varepsilon$s and crack spacing $\lambda$ at the cessation of film cracking.

• Composites Research
• /
• 제16권2호
• /
• pp.68-73
• /
• 2003

Fragmentation 시험법과 전기저항 측정을 통하여 탄소 및 SiC 섬유강화 에폭시 복합재료의 계면물성과 섬유파단에 대한 전기적 감지능을 연구하였다. 섬유 함침 각이 증가함에 따라서 계면전단강도는 감소하였고, 섬유파단에 의한 전기저항도 값이 무한대로 증가하는 시간은 길어졌다. 높은 함침 각에서 전기저항도의 초기 기울기는 급격히 증가한 반면. 낮은 각에서는 점차적으로 증가하였다. 또한 낮은 함침각의 두 섬유 모두에서 stress whitening pattern을 뚜렷하게 관찰할 수 있었지만, 높은 함침 각에서는 그렇지 못했다. 섬유 함침 각이 감소함에 따라서 섬유 파단 간격과 debonding된 길이는 두 섬유 모두에서 증가하였다. 본 연구에서 사용한 electro-micromechanical 시험법은 전도성 섬유강화 복합재료의 섬유 함침 각에 따른 계면 감지능 측정을 위해서 비파괴적 평가방법으로 실행 가능하였다.

• 접착 및 계면
• /
• 제23권3호
• /
• pp.59-69
• /
• 2022

섬유강화 복합재료에서 가장 중요한 부분은 섬유와 수지간의 계면 접착특성이다. 본 총설에서는, 섬유강화 복합재료의 계면특성을 평가하기 위해 사용되는 미세역학 시험법에 대해 역사적 초점을 두어 서술하고자 한다. 미세역학 시험법은 섬유 한 가닥과 기지재료 간의 계면 접착특성을 전단력평가로 관측하는 재료자체의 변수만이 고려되는 평가법으로써 계면에 대한 보다 정량적인 접착특성 및 감지능을 고찰할 수 있다. 미세역학시험법을 이용한 이전의 연구와 비교적 최근 연구동향을 본 총설에서 비교 논의하며, 미세역학 실험법에 대한 응용과 앞으로의 발전을 설명하고자 한다.