• 비파괴검사학회지
• /
• 제32권2호
• /
• pp.122-130
• /
• 2012

Adhesive bend and shear tests of micro-sized bonded component have been performed to clarify the relationship between effects of heat-treatment on the adhesive strength and the bonded specimen shape using Weibull analysis. Multiple micro-sized SU-8 columns with four different diameters were fabricated on a Si substrate under the same fabrication condition. Heat-treatment can improve both of the adhesive bend and shear strength. The improvement rate of the adhesive shear strength is much larger than that of the adhesive bend strength, because the residual stress, which must change by heat-treatment, should effect more strongly on the shear loading. In case of bend type test, the adhesive bend strength in the smaller diameters (50 and $75\;{\mu}m$) widely vary, because the critical size of the natural defect (micro-crack) should vary more widely in the smaller diameters. In contrast, in case of shear type test, the adhesive shear strengths in each diameter of the columns little vary. This suggests that the size of the natural defects may not strongly influence on the adhesive shear strength. All the result suggests that both of the adhesive bend and shear strengths should be complicatedly affected by heat-treatment and the bonded columnar diameter.

• Tribology and Lubricants
• /
• 제26권1호
• /
• pp.44-51
• /
• 2010

A miniature shear testing machine was designed and developed, adopting a piezoelectric actuator with mechanical advantage using 4 levers in order to investigate shear behavior of a small solder ball. The final output displacement was initially expected to be 2.88 mm without load resistance, considering the lever ratio of 24 and the piezo displacement of 0.12 mm with an exciting voltage of 10 V. However, the final plunger displacement ${\Delta}{\upsilon}$ can be expected as ${\Delta}{\upsilon}=2.88-3.04{\times}10^{-4}F$ as a function of piezoelectric force F due to the stiffness of various levers and connectors and piezo actuator. The shear behavior of lead-free solder ball in diameter of $760{\mu}m$ was successfully investigated in a speed range of 2 mm/s~0.0035 mm/s using this designed device.

• 대한치과보철학회지
• /
• 제42권6호
• /
• pp.654-663
• /
• 2004

Statement of problem. According to the fracture pattern in several reports, fractures most frequently occur in the interface between the ceromer and the substructure. Purpose. The aim of this in vitro study was to compare the macro shear bond strength and microshear bond strength of a ceromer bonded to a fiber reinforced composite (FRC) as well as metal alloys. Material and methods. Ten of the following substructures, type II gold alloy, Co-Cr alloy, Ni-Cr alloy, and FRC (Vectris) substructures with a 12 mm in diameter, were imbedded in acrylic resin and ground with 400, and 1, 000-grit sandpaper. The metal primer and wetting agent were applied to the sandblasted bonding area of the metal specimens and the FRC specimens, respectively. The ceromer was placed onto a 6 mm diameter and 3 mm height mold in the macro-shear test and 1 mm diameter and 2 mm height mold in the micro-shear test, and then polymerized. The macro- and micro-shear bond strength were measured using a universal testing machine and a micro-shear tester, respectively. The macro- and micro-shear strength were analyzed with ANOVA and a post-hoc Scheffe adjustment ($\alpha$ = .05). The fracture surfaces of the crowns were then examined by scanning electron microscopy to determine the mode of failure. Chi-square test was used to identify the differences in the failure mode. Results. The macro-shear strength and the micro-shear strength differed significantly with the types of substructure (P<.001). Although the ceromer/FRC group showed the highest macroand micro-shear strength, the micro-shear strength was not significantly different from that of the base metal alloy groups. The base metal alloy substructure groups showed the lowest mean macro-shear strength. However, the gold alloy substructure group exhibited the least micro-shear strength. The micro-shear strength was higher than the macro-shear strength excluding the gold alloy substructure group. Adhesive failure was most frequent type of fracture in the ceromer specimens bonded to the gold alloys. Cohesive failure at the ceromer layer was more common in the base metals and FRC substructures. Conclusion. The Vectris substructure had higher shear strength than the other substructures. Although the shear strength of the ceromer bonded to the base metals was lower than that of the gold alloy, the micro-shear strength of the base metals were superior to that of the gold alloy.

• Restorative Dentistry and Endodontics
• /
• 제40권1호
• /
• pp.30-36
• /
• 2015

Objectives: This study was performed to determine whether the combined use of one-bottle self-etch adhesives and composite resins from same manufacturers have better bond strengths than combinations of adhesive and resins from different manufacturers. Materials and Methods: 25 experimental micro-shear bond test groups were made from combinations of five dentin adhesives and five composite resins with extracted human molars stored in saline for 24 hr. Testing was performed using the wire-loop method and a universal testing machine. Bond strength data was statistically analyzed using two way analysis of variance (ANOVA) and Tukey's post hoc test. Results: Two way ANOVA revealed significant differences for the factors of dentin adhesives and composite resins, and significant interaction effect (p < 0.001). All combinations with Xeno V (Dentsply De Trey) and Clearfil $S^3$ Bond (Kuraray Dental) adhesives showed no significant differences in micro-shear bond strength, but other adhesives showed significant differences depending on the composite resin (p < 0.05). Contrary to the other adhesives, Xeno V and BondForce (Tokuyama Dental) had higher bond strengths with the same manufacturer's composite resin than other manufacturer's composite resin. Conclusions: Not all combinations of adhesive and composite resin by same manufacturers failed to show significantly higher bond strengths than mixed manufacturer combinations.

• 대한치과교정학회지
• /
• 제28권4호
• /
• pp.641-657
• /
• 1998

본 연구는 열을 이용한 금속 브라켓의 재생 처리시, 기저부 형태와 브라켓 재생 방법에 따른 전단접착강도 및 브라켓 탈락 양상을 비교하고자 시행되었다. 교정 치료를 위해 발거된 건전한 소구치 252개를 수집하고, Type I, Type II, Type III 스탠다드 브라켓을 각각 재생 방법에 따라 네 군으로 나누어 준비된 소구치에 접착하고, Instron Universal Testing Machine(Model 4466)으로 전단접착강도를 측정하였으며, 브라켓의 탈락 양상을 관찰하고 브라켓 기저부의 주사전자현미경 소견을 관찰하였다. SPSS 통계처 리 프로그램을 이용하여 일원분산분석(oneway ANOVA), Scheffe's multiple range test를 실시하여 다음과 같은 결론을 얻었다. 1. 브라켓 기저부 형태에 따른 전단접착강도는 유의차가 있었으며(p<0.001), 그 크기는 Type III(round indentation, micro-etched base), Typ I(foil-mesh base), Type II(grooved integral base, micro-etched)의 순이었다. 2. 생 방법에 따른 전단접착강도는, Type I, Tpe II 브라켓에서는 Big Jane에 1분간 처리시 우수한 결과를 보였고 (p<0.05), Type III 브라켓에서는 각 군간 유의한 차이를 보이지 않았다(p>0.05). 3. Type I, Type II 브라켓은 기저부-레진 계면에서 가장 높은 빈도로 탈락하였고, Type III 브라켓에서는 레진의 절반 가량이 치면에 잔존하는 탈락 양상이 가장 많았다. 4. 탈락 양상에 따라 탈락시의 전단접착강도가 유의성 있는 차이를 보였는데(p<0.05),브라켓 탈락시 접착제의 절반 가량이 치면에 잔존하는 경우 전단접착강도가 가장 큰 것으로 나타났다. 5. 브라켓 재생 후 기저부에 남아 있는 접착제는 전단접착강도의 감소에 영향을 미치지 않았다.

• 대한치과기공학회지
• /
• 제29권2호
• /
• pp.141-150
• /
• 2007

The purpose of this study was to ascertain the bonding durability of self-etching dentin bonding agents to dentin by means of shear bonding strength. Several acid-etching dentin bonding system (ESPE Z100) and self-etching dentin bonding systems (DEN-FIL, GRADIA DIRET) were used. The occlusion surface of human molars were ground flat to expose dentin and treated with the etch bonding system according to manufactures instruction and followed by composite resin application. After 24hours of storage at 37$^{\circ}C$, the shear bonding strength of the specimens was measured in a universal testing machine with a 1mm/min crosshead speed. An one-way analysis of variance and the scheffe test were performed to identify significant differences (p<0.05). The bonded interfacial surfaces and treated dentin surfaces were examined using a SEM. Through the analysis of shear bond strength data and micro-structures of dentin-resin interfaces, following results are obtained. In dentin group, the shear bond strength of DEN-FIL showed statistical superiority in comparison to the other groups and followed by ESPE Z100 and GRADIA DIRECT (p<0.05).

• Restorative Dentistry and Endodontics
• /
• 제28권3호
• /
• pp.209-221
• /
• 2003

The objectiveness of this study was to evaluate whether low-viscosity composite can bond effectively to dentin surface without bonding resin. The low-viscosity composites being 50wt% filler content were made by the inclusion of bonding resin of two self-etching systems(Cleafil SE Bond, Unifil Bond) varied with contents as 0, 10, 20, 30, 40, 50wt%. Exposed dentin surfaces of extracted 3rd molars are used. Dentin bond strengths were measured. The tests were carried out with a micro-shear device placed testing machine at a CHS of 1mm/min after a low-viscosity composite was filled into an iris cut from micro tygon tubing with internal diameter approximately 0.8mm and height of 1.0mm. 1 Flexural strength and modulus was increased with the addition of bonding resin. 2. Micro-shear bond strength to dentin was improved according to content of bonding resin irrespective of applying or not bonding resin in bonding procedure, and that of Clearfil SE Bond groups was higher than Unifil Bond. 3. There were no significant difference whether use of each bonding resin in bonding procedure for S-40, S-50, U-50(p＞0.05). 4. In SEM examination, resin was well infiltrated into dentin after primed with self-etching primer only for S-50 and U-50 in spite of the formation of thinner hybrid layer. Low viscosity composite including some functional monomer may be used as dentin bonding resin without an intermediary bonding agent. It makes a simplified bonding procedure and foresees the possibility of self-adhesive restorative material.

• Restorative Dentistry and Endodontics
• /
• 제22권2호
• /
• pp.680-692
• /
• 1997

New bonding agent systems have been supplied which operators can simply apply to conditioned tooth surfaces. The purpose of this study was to evaluate the shear bond strengths and the microleakages of three bonding agents and composite resins to dentin. Seventy-five extracted human maxillary and mandibular molar teeth were used in this study. For the shear bond strength test, the entire occlusal dentin surfaces of thirty teeth were exposed with Diamond Wheel Saw and smoothed with Lapping and Polishing Machine (South Bay Technology Co., U.S.A). For the microleakage test, Class V cavities were prepared in the buccal surfaces of fourtyfive teeth. They were randomly assigned into 3 groups according to dentin bonding agents ($Scotchbond^{TM}$ Multi-Purpose plus, ONE-$STEP^{TM}$ and Prime & $Bond^{TM}$)and composite resins (Z-100, $Aelitefil^{TM}$ and TPH $Spectrum^{TM}$) to be used. Bonding agents and composite resins were bonded to exposed dentin surfaces of the tooth crown and to Class V cavities on the buccal surfaces respectively according to manufacturer's directions. The shear bond strengths were measured by universal testing machine($U^{TM}$ AGS-100, Japan). In addition, the degree of micro leakage at the occlusal and gingival margin was examined by 2 % methylene blue and stereomicroscope(Olymous SZH 10, Japan). The results were as follows: 1. The shear bond strength to dentin was the highest value in SBMP-Plus group($16.68{\pm}7.38$ MPa) and the lowest value in Prime & Bond group($11.61{\pm}5.82$ MPa), but there was no significant difference of shear bond strength among three groups. 2. The degree of microleakage at both occlusal and gingival margin was showed the lowest in SBMP-Plus group and the highest in ONE-STEP group. 3. At both occlusal and gingival margin, there was significant difference of microleakage between SBMP-Plus and ONE-STEP/ Prime & Bond groups(p<0.05), but no significant difference of microleakage between ONE-STEP and Prime & Bond group(p>0.05).

• 대한치과교정학회지
• /
• 제29권5호
• /
• pp.599-611
• /
• 1999

금속 브라켓의 결합강도에 영향을 미치는 요소인 브라켓 기저부의 형태와 결합 부위에 적용되는 힘의 특성에 대해 알아보고자 연구를 시행하였다. 형태가 다른 5종의 금속브라켓의 기저부와 결합강도 측정후 접착파절양상을 stereoscope and scanning electron microscope를 통해 관찰하고 결합 부위에 적용되는 힘은 전단결합강도, 인장결합강도, 전단/인장복합결합강도로 구분하고 결합강도를 비교하여 다음과 같은 결론을 얻었다. 1. 브라켓 기저부 형태에 따른 모든 군에서 전단결합강토(SBS)가 제일 컸으며, 인장결합강도(TBS)는 SBS의 50%정도 수준이었고 전단/인장복합결합강도(S/TBS)는 전단결합강도(SBS)의 30%정도이었다. 2. 브라켓의 결합강도는 Micro-Loc base가 가장 크고($SBS:22.86{\pm}1.37kgf,\;TBS:11.37{\pm}1.43kgf,\;S/TBS:6.69{\pm}0.34kgf$), Integral base가 가장 작았다($SBS:10.52{\pm}1.27kgf,\;TBS:4.27{\pm}1.08kgf,\;S/TBS:2.94{\pm}0.58kgf). 3. 단위면적당 결합강도 비교시, Integral base가 가장 작았고(p<0.05), 전단결합강도와 인장결합강도에서는 Micro-Loc과 Chessboard base간의 차이가 없었으며 (p>0.05), Non-Etched Foil Mesh와 Micro-Etched Foil Mesh base간의 전단결합강도와 인장결합강도는 차이가 없었으나, 전단/인장복합결합강도에서는 Micro-Etched Foil Mesh base가 Non-Etched Foil Mesh base보다 더 크게 나타났다. 4. 전단, 인장, 전단/인장복합결합강도 측정후 접착파절은 브라켓/레진 계면에서 일어나 ARI score가 작게 나타났다.

• 대한치과기공학회지
• /
• 제32권3호
• /
• pp.195-207
• /
• 2010

Purpose: The purpose of this study was to observe the microstructural changes of surface in the specimens, performing the shear bond strength testing. The currently most used non-precious alloys are nickel-chromium based alloys with or without beryllium. However, their biocompatibility has been questioned concerning possible damages to the health of the patient and professionals involved in the fabrication of prosthesis caused by long exposure to Ni and Be. An option to nickel-chromium alloys is the cobalt-chromium alloy, an alternative that does not sacrifice the physical properties of the metal porcelain systems. Studies in the animals substantially show that the cobalt-chromium alloys are relatively well tolerated, being therefore more biocompatible than the nickel-chromium alloys. Methods: Non-addition Be to nickel-chromium based alloy(Bellabond plus) and cobalt-chromium alloy which has been widely used(Wirobond C) fused with ZEO light porcelain classified control group and cobalt-chromium alloy which is developing alloy of Alphadent company in Korea(Alphadent alloy) fused with ZEO light porcelain classified experimental group. The specimens of $4mm{\times}4mm{\times}0.5mm$ were prepared as-cast and as-opaque to cast body to analyze the mechanical characteristic change, the microstructure of alloy surface. The phase change was used to observe through XRD analysis and OM/SEM was used to observe the surface of specimens as-cast and as-opaque to cast body. Chemical formation of their elements was measured with EDS. Then hardness was measured with Micro Vicker's hardness tester. Shear bond strength test thirty specimens of $10mm{\times}10mm{\times}2mm$ was prepared, veneered, 3mm high and 3mm in diameter, over the alloy specimens. The shear bond strength test was performed in a universal testing machine(UTM) with a cross head speed of 0.5mm/min. Ultimate shear bond strength data were analyzed with one-way ANOVA and the Scheffe's test (P<0.05). Within the limits of this study, the following conclusions were drawn: The X-ray diffraction analysis results for the as-cast and as-opaque specimens showed that the major relative intensity of Bellabond plus alloy were changed smaller than Wirobond C and Alphadent Co-Cr based alloys. Results: Microstructural analysis results for the opaque specimens showed all the alloys increased carbides and precipitation(PPT). Alphadent Co-Cr based alloy showed the carbides of lamellar type. The Vickers hardness results for the opaque specimens showed Wirobond C and Alphadent Co-Cr based alloys were increaser than before ascast, but Bellabond plus alloy relatively decreased. The mean shear bond strengths (MPa) were: 33.11 for Wirobond C/ZEO light; 25.00 for Alphadent Co-Cr alloy/ZEO light; 18.02 for Bellabond plus/ZEO light. Conclusion: The mean shear bond strengths for Co-Cr and Ni-Cr based alloy were significantly different. But the all groups showed metal-metal oxide modes in shear bond strengths test at the interface.