• Journal of Powder Materials
• /
• v.17 no.2
• /
• pp.113-122
• /
• 2010

Two kinds of oxide-dispersion-strengthened (ODS) 316L stainless steel were manufactured using a wet mixing process(wet) and a mechanical alloying method (MA). An MA 316L ODS was prepared by a mixing of metal powder and a mechanical alloying process. A wet 316L ODS was manufactured by a wet mixing with 316L stainless steel powder. A solution of yttrium nitrate was dried after being in the wet 316L ODS alloy. The results showed that carbon and oxygen were effectively reduced during the degassing process before the hydroisostatic process (HIP) in both alloys. It appeared that the effect of HIP treatment on increase in impact energy was pronounced in the MA 316L ODS alloy. The MA 316L ODS alloy showed a higher yield strength and a smaller elongation, when compared to the wet 316L ODS alloy. This seemed to be attributed to the enhancement of bonding between oxide and matrix particles from HIP and to the presence of a finer oxide of about 20 nm from the MA process in the MA 316L ODS alloy.

• Journal of Technologic Dentistry
• /
• v.37 no.1
• /
• pp.23-29
• /
• 2015

Purpose: The selective laser melting (SLM) process for dentistry, which is one of the additive manufacturing technologies (AM) allows for rapid production of a three-dimensional model with complex shape by directly melting metal powder. This process generates detailed items of a three-dimensional model shape through consolidation of a thin powder layer by utilizing both selective melting and laser beam simultaneously. In regard to SLM process, Fe-base powder, Ti-6AI-4V powder, AI-base powder, etc. have been researched. It is believed that the aforementioned technologies will be widely utilized in manufacturing metal parts using metal powder of raw material. This study chose Ni-Cr-Mo metal powder in order to manufacture metal powder materials that would be used in the selective laser melting for dentistry. Methods: This study manufactured metal powder using mechanical alloying technique (MA) among those metal powder manufacturing techniques. Moreover, this study aimed to utilize the metal powder manufactured after observing the characteristics of powder as preliminary data of Ni-Cr-Mo metal powder. This study could obtain the following conclusions within the experimental limitations. Results: As a result of mechanically alloying Ni-Cr-Mo powder over time, its mean particle size was $66.93{\mu}m$ $54.4{\mu}m$ and $45.39{\mu}m$ at 10h, 20h and 30h, respectively. The gtain form of metal powder by mechanical alloying technique was a sponge-like shape of irregular plate; however, the gtain form manufactured by high-pressure water aromization process had the following three types: globular type, chain type and oval type. Conclusion: This study found $37.65{\mu}m$ as the mean particle size of Ni-Cr-Mo metal powder, which was manufactured using water atomization technique under the following conditions: water atomization flux of 300 liter/min, hydraulic pressure of $400kgf/cm^2$ and injection angle of $45^{\circ}$. This study confirmed that the grain form of powder (solid particle form) would vary depending on the manufacturing process.

• Korean Journal of Materials Research
• /
• v.5 no.2
• /
• pp.223-231
• /
• 1995

Mechanical alloying behavior of the PbTe intermetallic compound, which is used for thermoelectric generation, has been investigated with milling time and ball-to-powder weight ratio. Formation of PbTe alloy was completed by mechanical alloying of the as-mixed Pb and Te powders for 2 minutes at ball-to-powder weight ratio of 2 : 1. In situ measurement of the abrupt temperature rise during the ball milling process indicated that the PbTe intermetallic compound was formed by a self-sustained reaction rather than diffusional reactions. Lattice constant of PbTe alloy fabricated by mechanical alloying, 0. 6462nm, was not varied with milling time and ball-to-powder weight ratio. This value of the lattice parameter is in excellent agreement with 0.6459nm, which was reported for PbTe powders processed by melting and grinding.

• Analytical Science and Technology
• /
• v.6 no.2
• /
• pp.197-205
• /
• 1993

Blends of elemental Ni and 20 weight % Cr powder were milled for different period in a laboratory attritor. Powder size distribution, microstructure and X-ray diffraction characteristics were investigated as a function of processing period. Saturated magnetization, Ms and coercive force, Hc we also measured and compared with plasma melted ingot to confirm the mechanically alloyed states. Mechanical alloying occurred as a consequence of the partition of powders and the increase of interfacial area driving diffusing of Cr into Ni. However, magnetic properties of chemically homogeneous solid solution like melted ingot has not been observed even though steady state of submicron grain size has been achieved after milling over 15 hrs. Further mechanical alloying period gave refinement of grain size, which resulted in the increase of alloyed layer. It is concluded that homogenization should be controlled by the increase of interfacial area between constitutive powders caused by plastic particle deformation and by the diffusion of Cr within the alloyed phase into Ni-rich phase through lattice defects.

• Journal of Powder Materials
• /
• v.12 no.5 s.52
• /
• pp.357-361
• /
• 2005

Fe-doped skutterudite $CoSb_3$ with a nominal composition of $Fe_{x}Co_{4-x}Sb_{12}(0\;{\le}\;x\;{\le}\;2.5)$ has been synthesized by mechanical alloying (MA) of elemental powders, followed by hot pressing. Phase transformations during mechanical alloying and hot pressing were systematically investigated using XRD. Single phase skutterudite was successfully produced by vacuum hot pressing using as-milled powders without subsequent annealing. However, second phase in the form of marcasite structure $FeSb_2$ was found to exist in case of $x\;{\ge}\;2$, suggesting the solubility limit of Fe with Co in this system. Thermoelectric properties as functions of temperature and Fe contents were evaluated for the hot pressed specimens. Fe substitution up to x=1.5 with Co in $Fe_{x}Co_{4-x}Sb_{12}$ appeared to increase thermoelectric figure of merit (ZT) and the maximum ZT was found to be 0.78 at 525K in this study.

• Nuclear Engineering and Technology
• /
• v.53 no.8
• /
• pp.2582-2590
• /
• 2021

The high-energy milling is one of the most extended techniques to produce Oxide dispersion strengthened (ODS) powder steels for nuclear applications. The consequences of the high energy mill process on the final powders can be measured by means of deformation level, size, morphology and alloying degree. In this work, an ODS ferritic steel, Fe-14Cr-5Al-3W-0.4Ti-0.25Y₂O₃-0.6Zr, was fabricated using two different mechanical alloying (MA) conditions (M_std and M_act) and subsequently consolidated by Spark Plasma Sintering (SPS). Milling conditions were set to evidence the effectivity of milling by changing the revolutions per minute (rpm) and dwell milling time. Differences on the particle size distribution as well as on the stored plastic deformation were observed, determining the consolidation ability of the material and the achieved microstructure. Since recrystallization depends on the plastic deformation degree, the composition of each particle and the promoted oxide dispersion, a dual grain size distribution was attained after SPS consolidation. M_act showed the highest areas of ultrafine regions when the material is consolidated at 1100 ℃. Microhardness and small punch tests were used to evaluate the material under room temperature and up to 500 ℃. The produced materials have attained remarkable mechanical properties under high temperature conditions.

• Journal of the Korean institute of surface engineering
• /
• v.49 no.4
• /
• pp.368-375
• /
• 2016

MoN-Cu thin films were prepared to achieve appropriate properties of high hardness and low friction coefficient, which could be applied to automobile engine parts for reducing energy consumption as well as solving wear problems. Composite thin films of MoN-Cu have been deposited by various processes using multiple targets such as Mo and Cu. However, those deposition with multiple targets revealed demerits such as difficulties in exact control of composition and homogeneous deposition. This study is aiming for suggesting an appropriate process to solve those problems. A single alloying target of Mo-Cu (10 at%) was prepared by powder metallurgy methods of mechanical alloying (MA) and spar plasma sintering (SPS). Thin film of MoN-Cu was then deposited by magnetron sputtering using the single alloying target of Mo-Cu (10 at%). Properties of the resulting MoN-Cu thin film were examined and compared to those of MoN-Cu thin films prepared with double targets of Mo and Cu.

• Journal of Powder Materials
• /
• v.13 no.3 s.56
• /
• pp.178-186
• /
• 2006

The effect of use of $H_2O$ as PCA(process control agent) to prevent the carbon contamination during mechanical alloying process and the precipitation behavior in Ni-20Cr-20Fe-5Nb bulk alloy after aging were investigated. NbC and $Cr_2O_3$ were formed during mechanical alloying and consolidation processes in the Ni-20Cr-20Fe-5Nb alloy in which methanol($CH_3OH$) was added as PCA. Formation of NbC in this alloy decreased the amount of Nb dissolved in the Ni matrix. The use of $H_2O$ as PCA in Ni-20Cr-20Fe-5Nb alloy prevented the formation of NbC and increased the hardness. The increase of hardness in this alloy was attributed to the increased amount of Nb dissolved in the Ni matrix. After aging treatment for 20 hours at $600^{\circ}C\;and\;720^{\circ}C$ of Ni-20Cr-20Fe-5Nb bulk alloy in which $H_2O$ added as PCA, ${\gamma}"$$(Ni_3Nb,\;tetragonal)\;and\;{\delta}\;(Ni_3Nb,\;orthorhombic)$ precipitates were formed, respectively. The precipitation temperatures of ${\gamma}"$ and ${\delta}$ in this bulk alloy were lower than those in commercial IN 718 alloy. It seemed that the lower precipitation temperatures for ${\gamma}"$ and ${\delta}$ in this bulk alloy than in commercial IN 718 alloy were due to severe plastic deformation during mechanical alloying.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.29 no.10
• /
• pp.665-670
• /
• 2016

Prevailing dissemination of machine tools and cutting technology have caused drastic developments of high speed dry machining with work materials of high hardness, and demands on the high-hardness-materials with high efficiency have become increasingly important in terms of productivity, cost reduction, as well as environment-friendly issue. Addition of Si to TiAlN has been known to form nano-composite coating with higher hardness of over 30 GPa and oxidation temperature over $1,000^{\circ}C$. However, it is not easy to add Si to TiAlN by using conventional PVD technologies. Therefore, Ti-Al-Si-N have been prepared by hybrid process of PVD with multiple target sources or PVD combined with PECVD of Si source gas. In this study, a single composite target of Ti-Al-Si was prepared by powder metallurgy of MA (mechanical alloying) and SPS (spark plasma sintering). Properties of he resulting alloying targets were examined. They revealed a microstructure with micro-sized grain of about $1{\sim}5{\mu}m$, and all the elements were distributed homogeneously in the alloying target. Hardness of the Ti-Al-Si-N target was about 1,127 Hv. Thin films of Ti-Al-Si-N were prepared by unbalanced magnetron sputtering method by using the home-made Ti-Al-Si alloying target. Composition of the resulting thin film of Ti-Al-Si-N was almost the same with that of the target. The thin film of Ti-Al-Si-N showed a hardness of 35 GPa and friction coefficient of 0.66.

• Electronic Materials Letters
• /
• v.14 no.6
• /
• pp.725-732
• /
• 2018

The thermoelectric and transport properties of Ti-doped FeVSb half-Heusler alloys were studied in this study. $FeV_{1-x}Ti_xSb$ (0.1 < x < 0.5) half-Heusler alloys were synthesized by mechanical alloying process and subsequent vacuum hot pressing. After vacuum hot pressing, a near singe phase with a small fraction of second phase was obtained in this experiment. Investigation of microstructure revealed that both grain and particle sizes were decreased on doping which would influence on thermal conductivity. No foreign elements pick up from the vial was seen during milling process. Thermoelectric properties were investigated as a function of temperature and doping level. The absolute value of Seebeck coefficient showed transition from negative to positive with increasing doping concentrations ($x{\geq}0.3$). Electrical conductivity, Seebeck coefficient and power factor increased with the increasing amount of Ti contents. The lattice thermal conductivity decreased considerably, possibly due to the mass disorder and grain boundary scattering. All of these turned out to increase in power factor significantly. As a result, the thermoelectric figure of merit increased comprehensively with Ti doping for this experiment, resulting in maximum thermoelectric figure of merit for $FeV_{0.7}Ti_{0.3}Sb$ at 658 K.