• Polymer(Korea)
• /
• v.29 no.3
• /
• pp.248-252
• /
• 2005

PP/MMT nanocomposites having a various compositions were prepared by melt blending with a twin screw extruder. In this study, maleic anhydride-grafted PP (MAH-g-PP) was used as a compatibilizer in order to assist the exfoliation or hen in the pp matrix. from the results or x-ray diffraction (XRD) and transmission electron microscope (TEM) measurements for the nanocomposites, we confirmed that MMT was exfoliated. PPM nanocomposites have shown good flame retardancy by synergistic effect between MMT and flame retardant. The mechanical and thermal properties of the nanocomposites showed significant enhancement compared with those of neat PP, The excellent flame retardancy of the PP/MMT nanocomposites, UL94 V-0 value, was successfully obtained with reduced amount of the flame retardant.

• Polymer(Korea)
• /
• v.34 no.4
• /
• pp.294-299
• /
• 2010

Clay-loaded polypropylene (PP) nanocomposites were fabricated via melt-compounding of two molecular weight ($M_w$) PPs (140 and 410 kg/mol) and octadecylammine-treated clay (C18MMT), with the assistance of maleic anhydride-grafted PP(PP-MAH), respectively, at $170^{\circ}C$ and $190^{\circ}C$. At both melt-compounding temperatures, the low-$M_w$ PP tends to easily diffuse into silicate layers, especially in the presence of the mobile PP-MAH, resulting in a marked increase in silicate layer spacing (above 58 $\AA$), when compared to 27 $\AA$ in the high-$M_w$ PP-based system. Due to relatively lower melt-viscosity of the low-$M_w$ PP-based system, however, there existed quasi-stacked clay aggregates with a thickness of 60~80 nm, while the high-$M_w$ PP-based nanocomposites showed relatively homogeneous dispersion of clays. The different morphologies are mainly related to changes in the viscoelastic properties of PPs, dependent on the processing temperature and their $M_{w}s$. The slight differences in nanocomposites induce discernible crystallization and mechanical behaviors. High-$M_w$ PP-based nanocomposites containing 1~3 wt% C18MMT showed improvement in both tensile strength and modulus, while maintaining the inherent ductility of pure PP.

• Elastomers and Composites
• /
• v.35 no.1
• /
• pp.46-52
• /
• 2000

Miscibility improvement between polypropylene(PP) and ethylene-propylene-diene-terpolymer (EPDM) was studied by introducing specific interaction into both polymers. PP was modified by grafting maleic anhydride(MAH) onto backbone, leading to MAH-grafted PP(PP-g-MAH). Sulfonated EPDM ionomer neutralized with bivalent zinc cation(ZnSEPDM) was used as one component. The blends of PP-g-MAH and ZnSEPDM were prepared at $200^{\circ}C$ in Brabender Roller Mixer. Fourier transform-infrared(FT-IR) spectroscopic and dynamic mechanical studies have been performed to investigate the miscibility. FT-IR spectral peak corresponding to carbonyl group in PP-g-MAH and that to sulfonate group in ZnSEPDM were shifted to lower and higher frequency with increasing ZnSEPDM content, respectively, in the blends. Glass transition temperature of ZnSEPDM was increased up to 70wt.% of ZnSEPDM, and again decreased above 70wt.%. It can be concluded from the shift of FT-IR characteristic peaks and the changes of glass transition temperatures that the miscibility between PP and EPDM was improved via introducing specific interaction, i.e., dipole-ion interaction.

• Elastomers and Composites
• /
• v.46 no.3
• /
• pp.211-217
• /
• 2011

Wood Polymer Composite (WPC) has attracted a great deal of attention in environmental industries due to renewable resources, processability, excellent physical properties and logging regulations for application to housing units and engineering construction materials. In this study, commercial WPCs were prepared by using a modular intermeshing co-rotating twin screw extruder. The effect of three main factors such as wood flour contents, coupling agent concentrations and pre-treatment of wood flour on the properties of WPCs was extensively investigated. It was found that tensile strength and thermal stability were decreased with increasing wood flour contents whereas the water absorption was increased. Addition of maleic anhydride grafted polypropylene (PP-g-MA) into WPC exhibited better physical properties. On the contrary, the water absorption was slightly decreased with PP-g-MA. Finally the sample, which was prepared with pre-treated wood flour, represented the highest tensile strength. However, the water absorption of the sample was increased due to the transition of crystalline structure of cellulose.