• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 1995년도 봄 학술발표회 논문집
• /
• pp.84-87
• /
• 1995

Production of high strength concrete requires a low water-cement ratio and this leads to the high cement content. Mineral admixture like fly ash(FA) is often cheaper than ordinary portland cement(OPC) and this factor in combination with possible improvement in workability and moderation of the heat evolution of the cement-rich mixes tends to encourage its use. The other mineral admisture that its use has been widly advocated is silica fume that increases compressive strength due to its pozzolanic reaction. The objective of this study is to assess the contribution of mineral admixtures(FA, SF) to the workability and the strength of concrete with low water-binder ratios. In this experimental study that investigates and analyzes the properties of fresh concrete. it is presented that using admixtures like flyash and silica fume as binding material increases properties of high strength flowing concrete having very low water cementitious ratios of 0.25 and 0.30.

• 한국건설순환자원학회논문집
• /
• 제5권1호
• /
• pp.131-138
• /
• 2010

본 연구에서는 보통포틀랜드 시멘트(이하 OPC)제조과정의 분쇄공정 중 밀출구에서 배출되는 비교적 가격이 저렴하면서, 수화열면으로도 효과일 것으로 예상되는 입자분포를 갖는 시멘트(이하 CC)를 대상으로 플라이애시(이하 FA)와 고로슬래그 미분말(이하 BS)를 복합치환하는 3성분계 저발열 시멘트로의 개발 가능성을 검토하기 위하여 유동성, 강도, 간이단열온도 상승량 등 기초적인 특성에 대하여 분석하고자 한다. 실험결과로 유동성은 CC의 치환율이 증가함에 따라 저하하는 경향을 보였고, FA+BS의 치환율이 늘어남에 따라 증가하는 경향을 나타냈다. 공기량은 CC의 치환율이 증가함에 따라 미소하게 감소하는 경향을 나타냈고, FA+BS의 치환율이 증가함에 따라 감소하였다. 응결특성으로 CC 및 FA+BS의 치환율이 증가 할수록 응결 시간은 지연되었다. 간이 단열에 의한 온도 상승량은 전반적으로 CC 치환율이 증가할수록, FA+BS의 치환율이 증가할수록 피크온도는 감소하였고, 이후 온도저하가 완만해 지는 경향을 나타냈다. 압축강도는 CC 및 FA+BS 치환율이 증가할수록 저하하였는데, 재령이 경과함에 따라 장기강도는 Plain과 동등하거나 동등 이상의 강도를 발현 하였다. 종합적으로 CC에 FA+BS를 치환하였을 때 유동성 및 공기량은 저하하는 경향을 나타냈으나, 수화열 면에서 양호한 저감효과를 보여 3성분계 저발열 시멘트로의 개발이 가능성할 것으로 사료된다.

• 한국건축시공학회지
• /
• 제15권4호
• /
• pp.367-373
• /
• 2015

본 연구에서는 저온환경에 고분말도 시멘트를 적용하기 위하여 기초 특성을 검토하고자 하였다. 실험 결과 일반 시멘트에서 입도 분급된 고분말도 시멘트는 초기 수화에 큰 영향을 미치는 $10{\mu}m$이하의 입자가 다수 분포하였으며 분말도가 매우 높은 것으로 나타났다. 또한 분급된 미세한 시멘트 입자는 초기 수화반응이 매우 빠르고 이것은 시멘트의 수화 반응을 상승시킨다. 또한 고분말도 시멘트는 응결시간이 단축되고 모든 재령에서 압축강도가 높게 나타났다. 특히 저온환경에서는 초기 3일 압축강도 발현속도가 OPC 보다 2배 이상 발현하는 것을 확인할 수 있었으며 미소수화열 분석을 통해 수화반응 속도가 빠르고 수화열 또한 높은 것을 확인하였다. 또한 단열온도 상승 실험을 통해 초기 수화발열 상승온도 및 최고 상승온도가 높은 것으로 나타났다. 따라서 본 연구범위 내에서 저온환경 콘크리트에 우수한 시멘트 원료는 고분말시멘트로 판단된다.

• 콘크리트학회지
• /
• 제9권3호
• /
• pp.48-56
• /
• 1997

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2021년도 봄 학술논문 발표대회
• /
• pp.129-130
• /
• 2021

In order to solve the problem of low early-age compressive strength of high volume fly ash concrete. This paper studies the effect of 2% sodium sulfate (Na₂SO₄) as a chemical activator on the paste with 40% fly ash content and a water-binder ratio of 0.30. The results indicate that the addition of Na₂SO₄ can effectively improve the early-age compressive strength of the fly ash-cement system, and the strength improvement rate on the first day reached nearly 70%. In addition, calorimetric analysis reveals that the incorporation of Na₂SO₄ promotes the early hydration of cement and fly ash, increases the cumulative hydration heat and delays the heat peak of the aluminum phase.

• 한국구조물진단유지관리공학회 논문집
• /
• 제23권7호
• /
• pp.113-119
• /
• 2019

해안매립지에 건설되는 구조물은 해수로부터 유입되는 염소 및 황산염 이온 등의 화학적 침식에 의한 영향을 복합적으로 받는다. 염해는 콘크리트 내부의 철근을 부식시켜 구조물의 성능을 저하시킨다. 또한, 하수처리시설에서는 내부에서 발생되는 황산염에 의해 콘크리트가 열화되는 문제점을 가진다. 따라서 본 연구에서는 해안매립지에 건설되는 하수처리구조물에 적용할 수 있는 혼합형 저발열시멘트의 특성 및 내화학성을 평가하였다. 실험결과, 모든 배합조건에서 목표슬럼프 및 공기량을 모두 만족하였다. 동일 배합조건에서 LHC사용시 OPC 보다 슬럼프는 증가되고, 공기량은 감소하는 경향을 나타내었다. 압축강도 시험결과, 초기재령에서는 OPC의 강도발현이 빨랐으며, 28일 이후 LHC가 OPC보다 높은 강도를 나타내었다. 염소이온침투저항성 평가결과, LHC-B의 경우 56일 재령에서, "매우낮음" 단계의 염소이온침투저항성을 나타내 LHC의 내염해성을 확인하였다. 내화학성 평가 결과, 에폭시 처리 하지 않은 경우 LHC를 적용한 경우, OPC보다 약 18%정도 내화학성이 개선되는 것으로 나타났으며, 콘크리트 표면에 에폭시 공법 적용시 강도보존율이 95% 이상 확보 가능한 것으로 확인되었다.

• Computers and Concrete
• /
• 제17권2호
• /
• pp.271-280
• /
• 2016

This study examined the mechanical properties and adiabatic temperature rise of low-heat concrete developed based on ternary blended cement using ASTM type IV (LHC) cement, ground fly ash (GFA) and limestone powder (LSP). To enhance reactivity of fly ash, especially at an early age, the grassy membrane was scratched through the additional vibrator milling process. The targeted 28-day strength of concrete was selected to be 42 MPa for application to high-strength mass concrete including nuclear plant structures. The concrete mixes prepared were cured under the isothermal conditions of $5^{\circ}C$, $20^{\circ}C$, and $40^{\circ}C$. Most concrete specimens gained a relatively high strength exceeding 10 MPa at an early age, achieving the targeted 28-day strength. All concrete specimens had higher moduli of elasticity and rupture than the predictions using ACI 318-11 equations, regardless of the curing temperature. The peak temperature rise and the ascending rate of the adiabatic temperature curve measured from the prepared concrete mixes were lower by 12% and 32%, respectively, in average than those of the control specimen made using 80% ordinary Portland cement and 20% conventional fly ash.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2022년도 봄 학술논문 발표대회
• /
• pp.158-159
• /
• 2022

This study analyzed the temperature stress through mixtures mass concrete hydration heat analysis according to the replacement rates of FAC and CGS. As a result of the analysis, it was possible to confirm the effect of reducing hydration heat when CGS is substituted for the low heat mixture of mass concrete. However, the stress of the FAC+CGS combination exceeded the tensile stress. It is believed that it is necessary to apply the insulating sheet of the surface part and reduce the unit weight of cement.

• 한국조경학회지
• /
• 제32권6호
• /
• pp.82-94
• /
• 2005

This study was undertaken to measure and analyze the thermal environment characteristics of the grey permeable cement concrete pavement(GPCCP), the permeable cement concrete brick pavement(PCCBP) compared with impermeable cement concrete pavement(ICCP) and bare soil(BS) under the summer outdoor environment. Following is a summary of major results. 1) The peak surface temperature was greatest in the GPCCP$(54.2^{\circ}C)$ followed by ICCP$(47.2^{\circ}C)$ rut August 2, 2002, the hottest day$(35.3^{\circ}C\;of\;highest\;temperature)$ during the experiment; peak temperature in the ICCP and BS were $45.5^{\circ}C)$ and $45.3^{\circ}C)$ respectively. 2) Analysis of heat budget of the pavements has revealed that the heat environment was worse in the GPCCP than that in the ICCP and that this was mainly due to a low albedo in the former(0.2) relative to that of the latter(0.4). 3) Analysis of heat budget of the pavements has revealed that the heat environment was worse in the GPCCP than that in the PCCBP, BS and that this was mainly due to a decreased latent heat resulting from a time dependent decreasing impact of rainfall. 4) It is necessary to make cool pavements to further studies on light-colored surface materials for attaining high albdo and construction methods which can enhance the latent heat through the continuous evaporation from pavements surface. 5) Vertical arrangement of pavement layers has not been considered in the present study, which has been focuses on the heat characteristics of the surface layer materials. Accordingly, future studies will have to be empasized on pavement methods including the vertical arrangement of the pavement layers.

• 콘크리트학회논문집
• /
• 제21권4호
• /
• pp.441-447
• /
• 2009

황산염침식을 방지하기 위하여 포틀랜드시멘트 중의 황산염침식 저항성이 우수한 시멘트를 선정하기 위한 연구의 일환으로 황산나트륨 용액에 360일간 침지한 후 모르타르의 역학적 특성 및 기기분석을 통하여 침식 특성을 평 가한 결과, 외관조사, 강도감소 및 길이변화에 따른 성능저하 순서는 보통 포틀랜드시멘트 >내황산염 포틀랜드시멘트 > 저열 포틀랜드시멘트 순으로 나타났다. 포틀랜드시멘트의 주요 반응생성물은 Calcite 피크 이외에도 황산염과의 반응으 로 인한 Gypsum, 에트린자이트 및 Thaumasite로 확인되었다. 포틀랜드시멘트의 경우 시멘트의 조성광물 비에 따라 성 능저하 형태가 상이하게 나타났다. 특히, C3A량과 칼슘실리케이트비가 가장 적은 저열 포틀랜드시멘트가 황산염침식 저 항성에 매우 우수한 것으로 확인되었다.