• Bulletin of the Korean Chemical Society
• /
• v.34 no.7
• /
• pp.1995-2000
• /
• 2013

Layered $Li_{1.2}(Fe_{0.16}Mn_{0.32}Ni_{0.32})O_2$ was prepared by the mixed hydroxide method at various temperatures. Xray diffraction (XRD) pattern shows that this material has a ${\alpha}-NaFeO_2$ layered structure with $R{\bar{3}}m$ space group and that cation mixing is reduced with increasing synthesis temperature. Scanning electron microscopy (SEM) reveals that nano-sized $Li_{1.2}(Fe_{0.16}Mn_{0.32}Ni_{0.32})O_2$ powder has uniform particle size distribution. X-ray absorption near edge structure (XANES) analysis is used to study the local electronic structure changes around the Mn, Fe, and Ni atoms in this material. The sample prepared at $700^{\circ}C$ delivers the highest discharge capacity of 207 $mAhg^{-1}$ between 2-4.5 V at 0.1 $mAcm^{-2}$ with good capacity retention of 80% after 20 cycles.

• Journal of Adhesion and Interface
• /
• v.12 no.4
• /
• pp.133-137
• /
• 2011

Exfoliated graphite oxide (EGO) was prepared by graphite oxide in an aqueous solution of TMAOH. The hybrid graphene/Zn-Al LDH material was fabricated by the hydrothermal reduction of the solution of EGO, $Zn(NO_3)_2{\cdot}6H_2O$, $Al(NO_3)_3{\cdot}9H_2O$, urea, and trisodium citrate. That is, metal ions were absorbed on the surface of EGO, and Zn-Al LDH material was randomly dispersed on the surface of graphene along with a reduction process of EGO to graphene by hydrothermal treatment. The composition, morphology, and thermal property of the obtained graphene-based hybrid material were studied by FE-SEM, EDX, TEM, FT-IR, XRD, TGA, and DSC.

• Bulletin of the Korean Chemical Society
• /
• v.27 no.9
• /
• pp.1287-1288
• /
• 2006

• Proceedings of the Korean Magnestics Society Conference
• /
• 2016.11a
• /
• pp.107-107
• /
• 2016

• Journal of Electrochemical Science and Technology
• /
• v.2 no.3
• /
• pp.180-185
• /
• 2011

The layered lithium-manganese oxide ($Li_2MnO_3$) as a cathode material of lithium ion secondary batteries was prepared and characterized the physico-chemical and electrochemical properties. The morphological and structural changes of MnO(OH) and $Li_2MnO_3$ are closely connected to the changes of electrochemical properties. The crystallinity of $Li_2MnO_3$ is enhanced as the annealing temperature increase, but its capacity is reduced due to the easier structural changes of less crystalline $Li_2MnO_3$ than highly crystalline one. Moreover, the addition of buffer material such as MnO(OH) into cathode causes to reduce the morphological and structural changes of layered $Li_2MnO_3$ and increase the discharge capacity and cycleability.

• Bulletin of the Korean Chemical Society
• /
• v.28 no.6
• /
• pp.921-928
• /
• 2007

Three different phosphonated trisbipyridine ruthenium complexes, [(4-CH3-4'-CH2PO(OH)2-2,2'-bipyridine)- (bpy)2Ru]·(PF6)2 (Ru-P1), [(4-CH3-4'-CH2PO(OH)2-2,2'-bipyridine)3Ru]·(PF6)2 (Ru-P2), and [(4,4'-CH2PO- (OH)2-2,2'-bipyridine)3Ru]·(PF6)2 (Ru-P3) were synthesized and their photochemical and electrochemical properties were studied. These ruthenium complexes were strongly adsorbed on the surface of the layered metal oxide semiconductor K4Nb6O17 that was partially acid-exchanged and sensitized up to pH 10, while the carboxylated ruthenium complex, (4,4'-COOH-2,2'-bipyridine)3Ru·Cl2 (Ru-C) that was previously studied was sensitized only below pH 4. The visible light water reduction at K4Nb6O17 that was internally platinized and sensitized by these phosphonated Ru-complexes was comparatively studied using a reversible electron donor iodide.

• Corrosion Science and Technology
• /
• v.14 no.3
• /
• pp.113-119
• /
• 2015

Alloy 82/182 weld metals had been extensively used in joining the components of the PWR primary system. Unfortunately, there have been a number of incidents of cracking caused by PWSCC in Alloy 82/182 welds during the operation of PWR worldwide. To mitigate PWSCC, optimization of water-chemistry conditions, especially dissolved hydrogen (DH) and Zn contents, is considered as the most promising and effective remedial method. In this study, the PWSCC behaviours of Alloy 182 weld were investigated in simulated PWR environments with various DH content. Both in-situ and ex-situ oxide characterizations as well as PWSCC initiation tests were performed. The results showed that PWSCC crack initiation time was shortest in PWR water (DH: 30cc/kg). Also, high stress reduced crack initiation time. Oxide layer showed multi-layered structures consisted of the outer needle-like Ni-rich oxide layer, Fe-rich crystalline oxide, and inner Cr-rich inner oxide layers, which was not altered by the level of applied stress. To analyse the multi-layer structure of oxides, EIS measurement were fitted into an equivalent circuit model. Further analyses including TEM and EDS are underway to verify appropriateness of the equivalent circuit model.

• Environmental Engineering Research
• /
• v.15 no.3
• /
• pp.149-156
• /
• 2010

The objective of this study was to investigate microbial removal using layered double hydroxides (LDHs) and iron (hydr)oxides (IHs) immobilized onto granular media. Column experiments were performed using calcium alginate beads (CA beads), LDHs entrapped in CA beads (LDH beads), quartz sand (QS), iron hydroxide-coated sand (IHCS) and hematite-coated sand (HCS). Microbial breakthrough curves were obtained by monitoring the effluent, with the percentage of microbial removal and collector efficiency then quantified from these curves. The results showed that the LDH beads were ineffective for the removal of the negatively-charged microbes (27.7% at 1 mM solution), even though the positively-charged LDHs were contained on the beads. The above could be related to the immobilization method, where LDH powders were immobilized inside CA beads with nano-sized pores (about 10 nm); therefore, micro-sized microbes (E. coli = 1.21 ${\mu}m$) could not diffuse through the pores to come into contact with the LDHs in the beads, but adhere only to the exterior surface of the beads via polymeric interaction. IHCS was the most effective in the microbial removal (86.0% at 1 mM solution), which could be attributed to the iron hydroxide coated onto the exterior surface of QS had a positive surface charge and, therefore, effectively attracted the negatively-charged microbes via electrostatic interactions. Meanwhile, HCS was far less effective (35.6% at 1 mM solution) than IHCS because the hematite coated onto the external surface of QS is a crystallized iron oxide with a negative surface charge. This study has helped to improve our knowledge on the potential application of functional granular media for microbial removal.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.30 no.5
• /
• pp.194-199
• /
• 2020

By controlling the composition of the metal-oxide nanosheet having a two-dimensional layered crystal structure, material properties and application can be extended. In this study, the composition of the nanosheet could be expanded from pure composition to doping composition by successfully synthesizing the TiO₂ nanosheet doped with Nb. Specifically, the doping composition was designed when synthesizing the layered metal oxide as a starting material (K_0.8Ti_1.73-xNb_xLi_0.27O₄, x = 0, 0.03, 0.07) and chemical exfoliation was performed. By doing this, it was possible to obtain the Nb-doped TiO_y ultrathin nanosheet. The size of the nano sheet was 2 ㎛ or less based on the long length in the x-y direction, and the thickness was about 1 nm. Nb-doping was confirmed by XRD and SEM-EDS analysis.

• Journal of IKEEE
• /
• v.26 no.3
• /
• pp.500-505
• /
• 2022

In this study, we designed oxide thin-film transistors (TFTs) with dual gate and tri layered split channels, and investigated the structural effect of the TFTs on the electrical characteristics. The dual gates played a key role in increasing the driving current, and the channel structure of tri layers and split form contributed to the increase in the carrier mobility. The tri layered channels consisting of the a-ITGZO and two ITO layers inserted between the gate dielectric and a-ITGZO led to the increase in the on-current by using ITO layers with high conductivity, and the split channels lowered series resistance of the channels. Compared with the mobility (15 cm²/V·s) of the single gate a-ITGZO TFT, the mobility (134 cm²/V·s) of the dual gate tri-layer split channel TFT was remarkably enhanced by the structural effect.