• 한국주조공학회지
• /
• 제11권3호
• /
• pp.236-244
• /
• 1991

This paper describes a study of the nucleation and growth of graphite crystal of levitation melted high purity Fe-C-Si alloys with emphasis on hypereutectic composition. Spherulitic graphite was observed to form at high purity alloy and converted to compacted by changing the starting iron from ultra-pure zone refined iron to 99.95 pct electrolitic iron. Residual C-C clusters might be acting as an effective nucleation site for graphite, and sulphur was the element to prevent graphite from nucleating. The graphite morphology changed from compacted to spherulitic as the sulphur content decreased.

• 한국주조공학회지
• /
• 제24권4호
• /
• pp.217-224
• /
• 2004

The effect of casting variable on the fluidity of high silicon, especially hypereutectic, heat-resistant ductile cast iron melt was investigated. When pouring temperature and silicon content were constant, that was increased with carbon content. When the pouring temperature and carbon content were constant, that also increased with the silicon content. Even though these results were thought to be caused by the high heat of fusion evolved during the crystallization of proeutectic graphite nodules, further research seemed to be needed. The fluidity for taller sprue was higher than that for smaller one.

• 한국재료학회지
• /
• 제5권4호
• /
• pp.412-419
• /
• 1995

과공정 Al-18wt%Si합금의 초정 Si입자의 미세화에 미치는 첨가원소의 영향에 관하여 조사하였다. 초정 Si입자의 크기는 P량이 증가함에 따라 미세해졌으며 적정 P량은 40ppm이었다. 최적주입온도는 AlCuP, CuP 경우 각각 75$0^{\circ}C$, 80$0^{\circ}C$이었으며 미세화 처리 후 10분 이상 경과되어도 초정 Si입자의 크기는 변화가 없었다. 또한 WDS분석 결과 초정 Si내에 AIP가 핵생성 site로 존재함을 알 수 있었다.

• 한국주조공학회지
• /
• 제16권2호
• /
• pp.116-123
• /
• 1996

The equipment for the horizontal continuous casting was built to produce hyper-eutectic Al-Si bars with a small cross-section of 25mm in diameter. The manufacturing processes including withdrawal cycle and secondary cooling methods were modified to refine the primary and the eutectic Si. The longitudinal casting speeds varied over the ranges of 670-1100mm/min for pure Al, and 200-350mm/min for Al-17wt%Si alloy. Due to the difference of cooling rate in the mould, microstructural asymmetry between the lower and the upper part of bar was observed. Thus, manufacturing processes such as cooling and withdrawal method were optimally combinated to get the homogeneous cast structure. With the increase of casting speed, the primary Si size was refined down to $30{\mu}m$ near the surface, and $80{\mu}m$ in the center of the bar.

• 한국주조공학회지
• /
• 제24권3호
• /
• pp.153-158
• /
• 2004

본 연구에서는 기존 고압주조법의 해결과제인 고속충진 시 혼입되는 금형 cavity 내부의 유해 gas에 의한 gas porosity를 제어하기 위한 고속 사출 전 진공시스템 설계와 응고과정에서 발생되는 응고수축에 의한 shrinkage를 효과적으로 제어하기 위한 국부가압 스퀴즈의 조합시스템의 설계로 최적의 기계적 성질을 갖는 부품을 제조할 수 있는 공법을 개발하였다. 또한 개발된 신공법으로 자동차용 고내마모성 요구부품인 Reaction Shaft Support에 기존의 주철제를 대체하는 Al-15wt.%Si 과공정합금을 적용하여 시제품을 제조하였으며, 기존의 공법과 비교한 결과, 내부 porosity가 없는 미세하고 균일한 공정 및 초정 Si의 미세조직을 얻을 수 있었고, 기계적 특성평가에서도 매우 우수한 결과를 얻을 수 있었다.

• 한국주조공학회지
• /
• 제4권4호
• /
• pp.14-19
• /
• 1984

In order to clarify the solidification mechanism of Al-Si alloy, Mushy Degree of Eutectic Solidification (MDE) and Centerline Feeding Resistance (CFR) were systematically studied by casting with various compositions of $Al-(6{\sim}18%)$ Si alloys into several kinds of molds having different cooling rates. The results are as follows: 1. CFR% increases slightly as solute concentration increases, but decreases remarkably as the cooling rate of the mold increases, that is, the composition dependence of the alloys has more effect on the change of CFR% than that of the mold cooling rate. 2. The composition dependence of MDE value has the same tendency as that of Degree of Eutectic Solidification (DES). MDE value within the range of hypereutectic composition is larger than that of hypoeutectic and it represents the maximum value at eutectic composition. The higher the cooling rate is, the less the MDE value is.

• 한국소성가공학회:학술대회논문집
• /
• 한국소성가공학회 1997년도 고액공존금속의 성형기술 심포지엄
• /
• pp.160-173
• /
• 1997

Microstructure of hypereutectic Al-17wt.% Si alloy, fabricated by mechanical stirring and by reheating at semi-solid state, was investigated by optical microscope. Flow behavior semi-solid metal also was investigated at diffentent mould temperatures 280$^{\circ}C$, 290$^{\circ}C$ and 300$^{\circ}C$. Size of silicon particles were increased over 100$\mu\textrm{m}$ during solidification as a result of stirring. It is considered as microstructural coarsening by bonding between neighbouring primary silion particles during stirring of slurry. In case of reheating at semi-solid state, however, primary silicon particle was not increased at size of 40$\mu\textrm{m}$ and nearly spherical aluminum solde particle also could be obtained uniformly in distribution. The fludity of Al-17wt.% Si alloys at semi-solid state was improved when solid fraction was 0.7 at mould temperature of 300$^{\circ}C$ than other conditions.

• Journal of Welding and Joining
• /
• 제16권2호
• /
• pp.64-72
• /
• 1998

This study aims a investigating the effect of volume fraction of chromium carbide phase(VFC) of hardfaced iron/chromium alloys on fracture toughness. The alloys were deposited twice on a mild steel plate using self-shielding flux cored arc welding process. In order to examine VFC effect, different VFC (0.28∼0.62) were employed by changing the Cr and C content, while the ratio of Cr/C was fixed in the range of 5.7∼6.6. Fracture toughness was constant as increasing VFC because fracture surface was developed in the eutectic phase which was growing parallel with introduced sharp notch in the hypoeutectic alloys, but fracture toughness did not decreased in spite of increasing volume fraction of coarse primary chromium carbide phase which was easily craced at the low stress because the growth direction of chromium carbide phase were more irregular as increasing VFC in the hypereutectic alloys.

• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 2004년도 International Symposium on Powder Materials and Processing
• /
• pp.46-47
• /
• 2004

The microstructure and mechanical properties of the hypereutectic prealloyed Al-Si powders prepared by the gas atomization process were described in this paper. With increasing the gas pressure of the atomization, the average powder size was decreased from about $145{\mu}m\;to\;80{\mu}m$. The primary eutectic Si particles were uniformly distributed in the Al matrix and their size varied in the range of $8-10{\mu}m$. The high densified specimens with above 96% of the theoretical density were fabricated the hot pressing process. The UTS mechanical properties of VN1 specimens were much higher than that of conventional hypoeutectic Al-Si alloys.

• 한국주조공학회지
• /
• 제15권3호
• /
• pp.262-271
• /
• 1995

It is well known what is impossible to refine primary and eutectic Si simultaneously by addition of both Cu-P and Sr(or Na). Because of the formation of compound $Sr_3P_2(or Na_3P)$ in the melt, in the result, both effects disappear. In this study Al-Cu-P alloy that comprises AlP compounds inside is added in the melt with Sr simultaneously. As AlP compounds that act on nucleation sites of primary Si are not formed but added directly an the melt, it is difficult to form $Sr_3P_2$ by reaction with Sr. Therefore it is possible to refine primary and eutectic Si simultaneously in the general casting process by use of Al-Cu-P alloy and Sr.