• Journal of Korea Foundry Society
• /
• v.33 no.6
• /
• pp.242-247
• /
• 2013

The most widely utilized commercial, aluminum-casting alloys are based on an aluminum-silicon system due to its excellent casting, and good mechanical, properties. Unfortunately, these Al-Si based alloys are inherently poor energy conductors; compared to pure aluminum, because of their high silicon content. This means that they are not suitable for applications demanding high eletrical or thermal conductivity. Therefore, efforts are currently being made to develop new, highly-conductive aluminum-casting alloys containing no silicon. In this research, a number of properties; including potential for castability, were investigated for a number of Al-Fe-Zn-Cu alloys with varying Cu content. As the copper content was increased, the tensile strength of Al-Fe-Zn-Cu alloy tended to increase gradually, while the electrical conductivity was slightly reduced. Fluidity was found to be lower in high-Cu alloys, and susceptibility to hot-cracking was generally high in all the alloys investigated.

• Journal of the Korean institute of surface engineering
• /
• v.55 no.3
• /
• pp.143-155
• /
• 2022

Ceramic oxide layers successfully were formed on the surface of cast Al alloys with high Si contents using plasma electrolytic oxidation (PEO) process in electrolytes containing Na₂SiO₃, NaOH, and additives. The microstructure of the oxide layers was systematically analyzed using scanning electron microscopy (SEM), cross-sectional transmission electron microscopy (TEM), X-ray diffraction patterns (XRD), and energy X-ray dispersive spectroscopy (EDS). XRD analysis indicated that the PEO untreated high-silicon Al alloys (i.e., 17.1 and 11.7 wt.% Si) consist of Al, Si and Al₂Cu phases whereas Al₂Cu phase selectively disappeared after PEO treatment. PEO process yielded an amorphous oxide layer with few second phases including γ-Al₂O₃ and Fe-rich phases. The corrosion behaviors of high-silicon Al alloys treated by PEO process were investigated using electrochemical impedance spectroscopy (EIS) and other electrochemical techniques (i.e., open circuit potential and polarization curve). Electroanalytical studies indicated that high-silicon Al alloys treated by PEO process have greater corrosion resistance than high-silicon alloys untreated by PEO process.

• Journal of Korea Foundry Society
• /
• v.33 no.1
• /
• pp.8-12
• /
• 2013

Although aluminum-silicon based commercial casting alloys have been used in applications that demand high electrical or thermal conductivity, new aluminum casting alloys that possess higher conductivities are currently required for advanced applications. Therefore, there is much research into the development of new high conductivity aluminum casting alloys that contain lower amounts of or no silicon. In this research, the properties and casting characteristics of Al-Zn-Fe-Si alloys with various Fe and Si contents were investigated. Two types of AlFeSi phases were formed depending on the Fe and Si contents. As the silicon content increased, the tensile strength of the Al-Zn-Fe-Si alloy increased slightly, while the electrical conductivity decreased slightly. It was also observed that both the fluidity and hot cracking susceptibility of the investigated alloys were closely related to the formation of the AlFeSi phases.

• Journal of the Korean Society of Manufacturing Process Engineers
• /
• v.21 no.2
• /
• pp.109-115
• /
• 2022

The demand for metal 3D printing technology is increasing in various industries. The materials commonly used for metal 3D printing include aluminum alloys, titanium alloys, and stainless steel. In particular, for applications in the aviation and defense industry, aluminum alloy 3D printing parts are being produced. To improve the corrosion resistance in the 3D printed aluminum alloy outputs, a post-treatment process, such as chromate coating, should be applied. However, powdered materials, such as AlSi7Mg and AlSi10Mg, used for 3D printing, have a high silicon content; therefore, a suitable pretreatment is required for chromate coating. In the desmut step of the pretreatment process, the chromate coating can be formed only when a smut composed of silicon compounds or oxides is effectively removed. In this study, suitable desmut solutions for 3D printed AlSi7Mg and AlSi10Mg materials with high silicon contents were presented, and the chromate coating properties were studied accordingly. The smut removal effect was confirmed using an aqueous desmut solution composed of sulfuric, nitric, and hydrofluoric acids. Thus, a chromate coating was successfully formed. The surfaces of the aluminum alloys after desmut and chromate coating were analyzed using SEM and EDS.

• Korean Journal of Metals and Materials
• /
• v.50 no.12
• /
• pp.907-911
• /
• 2012

High purity silicon can be obtained from Al-Si alloys by a combination of solvent refining and centrifugation. Silicon purification by crystallization of silicon from an Al-Si alloy melt was carried out using 2N and 4N purity aluminum and 2N purity silicon as raw materials. The effect of the purity of raw materials on the final silicon ingot purity by centrifugation was investigated for an Al-50 wt% Si alloy. Alloys were melted using an electrical resistance furnace, and then poured into a centrifuging apparatus. A silicon lump like foam was obtained after centrifugation and was leached by an acid in order to get pure silicon flakes. Then silicon flakes were melted to make a silicon ingot using an induction furnace. The purities of the silicon flakes and silicon ingot were enhanced significantly compared to those of the raw materials of silicon and aluminum. The silicon ingot made of 4N aluminum and 2N silicon showed the lowest impurities.

• Journal of the Microelectronics and Packaging Society
• /
• v.25 no.2
• /
• pp.9-17
• /
• 2018

Aluminum (Al) and its alloys have been used widely in a variety of industries such as structural, electronic, aerospace, and particularly automotive industries due to their lightweight characteristic, outstanding ductility, formability, high oxidation and corrosion resistance, and high thermal and electrical conductivity. Al have different kinds of alloys according to the various additional elements system and they should be selected properly depending on their effectiveness and suitability for their particular purpose. The major elements for Al alloys are silicon (Si), magnesium (Mg), manganese (Mn), copper (Cu), and zinc (Zn). In order for Al alloys to use for each industry, it is necessary to study of Al to Al joining and/or the Al to dissimilar materials joining to combine the individual parts into one. Many studies on joining technologies about Al to Al and Al to dissimilar materials have been performed such as press joining, bolted joint, welding, soldering, riveting, adhesive bonding, and brazing. This study reviews a variety of Al alloys and their joining method including its principles and properties with recent trends.

• Journal of Korea Foundry Society
• /
• v.32 no.2
• /
• pp.86-90
• /
• 2012

Aluminium-silicon based casting alloys have received an attention for high electrical and thermal conductivity applications, however relatively low conductivity of Al-Si alloys often limits the application. Efforts have been made to develop new high conductivity aluminium casting alloys containing no or less silicon. In this study Al-Zn-Fe based alloys were selected as the new alloys, and the effect of Mg additions on their properties and casting characteristics were investigated. As the magnesium content was increased, the tensile strength of Al-2Zn-0.2Fe based alloy was remarkably increased, while the electrical conductivity was deteriorated. It was observed that the fluidity of the alloys was generally inversely proportional to the Mg content but the hot cracking resistance was rather proportional to it. Cooling curve analyses were carried out to measure the actual solidification range and dendrite coherency temperature.

• Journal of the Korean institute of surface engineering
• /
• v.48 no.5
• /
• pp.227-232
• /
• 2015

Corrosion characteristic of the duplex Al-Mg-Si alloys with low, commercial and high solute contents were studied using an anodic polarization test in 1M NaCl solution at room temperature. Polarization range condition of the experiment were form .0.3V to .1.3V with a 0.2 mV scanning speed. The exchange current density means corrosion rate of the low solute alloy was low as about $16.29{\mu}A/cm^2$, and that of the high solute alloy was high as $84.92{\mu}A/cm^2$. The difference was mainly attributed to the inter-granular precipitates $Mg_2Si$ and Si which could make a galvanic corrosion on the aluminum base. The amount of precipitates was greater in high solute alloy at mainly in grain boundary. While, the extruded alloys had better corrosion resistance than the cast alloy because the silicon precipitates become coarse during the extrusion process.

• Journal of Korea Foundry Society
• /
• v.34 no.4
• /
• pp.130-135
• /
• 2014

Efforts have been made to develop new silicon-free aluminum casting alloys that possess high electrical and thermal conductivity. In this research Al-Fe-Cu-Mg alloys with various Cu and Mg contents were investigated for their various properties. As the Cu or Mg content was increased, the electrical conductivity gradually decreased, while the tensile strength of the Al-Fe-Cu-Mg alloy tended to be improved. It was found that fluidity was generally inversely proportional to the Cu content, but the alloys containing 1%Mg showed considerably low fluidity, regardless of the Cu content.

• Proceedings of the KWS Conference
• /
• 2006.05a
• /
• pp.68-70
• /
• 2006

For the aluminum material of the thick-thickness more than 100mm Penetration depth Electron beam welding is effectively applicable with a characteristic of high energy intensity. But Al 6061 alloy has high crack sensitivity due to minor alloys, which are silicon, magnesium, copper etc. With a sample block of 135mm thickness EBW test was performed in vertical position. As tensile strength has $210{\sim}220N/mm^2$ with weld area broken. Bend test shows low ductility with fracture of partly specimens. Chemical contents of alloys show no difference between weld and base metal. Defect in middle weld area figures out typical hot crack due to low melting materials. Micro structure of weld area has some difference compare to HAZ and base metal. As a result of EBW test for Al 6061 alloy, it shows that weld defect could be occurred even though establishing of optimum weld parameter condition.