• Journal of Powder Materials
• /
• v.28 no.2
• /
• pp.110-119
• /
• 2021

In this study, the high-temperature oxidation properties of austenitic 316L stainless steel manufactured by laser powder bed fusion (LPBF) is investigated and compared with conventional 316L manufactured by hot rolling (HR). The initial microstructure of LPBF-SS316L exhibits a molten pool ~100 ㎛ in size and grains grown along the building direction. Isotropic grains (~35 ㎛) are detected in the HR-SS316L. In high-temperature oxidation tests performed at 700℃ and 900℃, LPBF-SS316L demonstrates slightly superior high-temperature oxidation resistance compared to HR-SS316L. After the initial oxidation at 700℃, shown as an increase in weight, almost no further oxidation is observed for both materials. At 900℃, the oxidation weight displays a parabolic trend and both materials exhibit similar behavior. However, at 1100℃, LPBF-SS316L oxidizes in a parabolic manner, but HR-SS316L shows a breakaway oxidation behavior. The oxide layers of LPBF-SS316L and HR-SS316L are mainly composed of Cr₂O₃, Fe-based oxides, and spinel phases. In LPBF-SS316L, a uniform Cr depletion region is observed, whereas a Cr depletion region appears at the grain boundary in HR-SS316L. It is evident from the results that the microstructure and the high-temperature oxidation characteristics and behavior are related.

• Journal of Power System Engineering
• /
• v.11 no.2
• /
• pp.44-50
• /
• 2007

The oxidation behavior of commercial pure titanium is investigated in the temperature range of $727^{\circ}C{\sim}950^{\circ}C$ in mixed gases. The weight change is measured by TGA during oxidation in mixed gases. The oxidation behavior indicated by weight gain or the growth of oxide layer is based on the linear rate law at high temperatures. The structure of the oxide scale formed during oxidation is analysed by optical microscopy, electron probe microanalyzer, scanning electron microscope and x-ray diffraction. Oxide scales have a $TiO_2$ structure, and are constituted with multi-layered or two layered porous external one and a dense internal one. Ti-O solid solution region is formed at the interface of metal and scale layer. The formation of oxide scale is influenced by the oxidation temperature, time, crystal structure and the condition of atmosphere.

• Nuclear Engineering and Technology
• /
• v.55 no.10
• /
• pp.3659-3664
• /
• 2023

The electrochemical behavior of dissolved hydrogen (H₂) was investigated at a Pt electrode in a high temperature LiOH-H₃BO₃ solution. The diffusion current of the H₂ oxidation was proportional to the concentration of the dissolved H₂ as well as the reciprocal of the temperature. In the polarization curve, a potential region in which the oxidation current decreases despite an increase in the applied potential between the H₂ oxidation and the water oxidation regions was observed. This potential region was interpreted as being caused by the formation of a Pt oxide layer. Using the properties of the Cl^- ion that reduces the growth rate of the Pt oxide layer, it was confirmed that there is a correlation between the Cl^- ion concentration and the transient current of the H₂ oxidation.

• Journal of the Korean Society for Heat Treatment
• /
• v.13 no.3
• /
• pp.158-162
• /
• 2000

The high temperature oxidation behavior and the surface defect in Fe-25Mn-1.5A1-0.5C steel was investigated by XRD (X-ray Diffractin) and electron microscopy. The intra- and inter-granular oxides were formed by the selective oxidation of manganese and aluminum, which were identified to MnAl2O4 phase. Aluminum nitride (AlN) was formed in front of these oxides. The ${\gamma}$-matrix was transformed to ${\alpha}$- and ${\varepsilon}$- phases by the selective oxidation of manganese. The surface defect, micro-scab was induced by the difference of the high temperature ductility between the matrix and the inter-granular oxide.

• Journal of Power System Engineering
• /
• v.10 no.3
• /
• pp.51-57
• /
• 2006

The effect of grain size on corrosion resistance and high temperature oxidation behavior was studied in 22Cr-15Ni-5W super austenitic stainless steels for desulfurization equipment as a heat power station. In the high temperature oxidation test, oxidation rate was increased as the temperature increased from $600^{\circ}C\;to\;800^{\circ}C$. In vapor, oxidation rate was faster than that in air. Because the vapor was inhibited nucleation of $Cr_2O_3$ film. And the high temperature oxidation resistance at $600^{\circ}C{\sim}800^{\circ}C$ was excellent from all specimens and specimen of the smallest grain size was the most excellent. Because increasing of diffusion course through the grain-boundary was promoted nucleation and growth of $Cr_2O_3$ film. In the test temperature at $600^{\circ}C{\sim}800^{\circ}C$, Cr rich round particle oxide was formed in air, whereas Fe rich needle type oxide was developed in vapor.

• Journal of the Korean Ceramic Society
• /
• v.31 no.7
• /
• pp.777-783
• /
• 1994

Oxidation behavior of hot-pressed silicon nitride ceramics with various sintering additives has been investigated. The weight gain of each specimens has shown in the range of 0.11 mg/$\textrm{cm}^2$ ~3.4 mg/$\textrm{cm}^2$ at 140$0^{\circ}C$ for 192 h and eleven compositions have shown good oxidation resistance with the weight gain below 0.5 mg/$\textrm{cm}^2$. The oxidation rate has been shown to obey the parabolic rate law and the oxidized surface has consisted of $\alpha$-cristobalite and M2Si2O7 or MSiO3 (M=rare earth or transition metals) phase. The oxidation rate of each specimens has related to the eutectic temperature between additive oxide and SiO2, and ionic radius of additive oxides, respectively. From the above results, it could be concluded that the oxidation behavior of hot pressed silicon nitride is dominated by the high temperature properties of grain boundary glassy phase and the high temperature properties of grain boundary glassy phase are affected by the ionic radius of additive oxides.

• Journal of the Korean institute of surface engineering
• /
• v.26 no.5
• /
• pp.235-244
• /
• 1993

The oxidation behavior of a two-phase(Ti3Al+TiAl) intermetallic compound, Ti-33.8wt%Al, has been in-vestigated in air at 800, 900 and $^1000{\circ}C$. Though the isothermal oxidation behavior followed a parabolic law up to 100$0^{\circ}C$ indicating that protective oxide scales were formed, the cyclic oxidation behavior followed a lin-ear law in the entire temperature range tested because flaky or stratified scales were usually spalled from the surface during cooling. During oxidation at 80$0^{\circ}C$, the alloy showed excellent oxidation resistance because continuous protective Al2O3 films were formed on the outermost surface of the alloy. However, above $900^{\circ}C$, the oxidation resistance of the alloy was decreased gradually because relatively non-protective TiO2 scales as well as some of Al2O3 scales were formed on the outer oxide scale. The oxidation mechanism of the alloy at different temperature was proposed.

• Journal of the Korean institute of surface engineering
• /
• v.44 no.1
• /
• pp.13-20
• /
• 2011

This study investigated the high temperature oxidation behavior of Fe-22%Cr-5.8%Al alloy and the oxidation kinetics of the alloy were discussed. Bulk samples were prepared by VAM (vacuum arc melting) and hot forging. High temperature oxidation testes were isothermally conducted up to 100 hours in 79%$N_2$+21%$O_2$ environment at three different temperatures ($900^{\circ}C$, $1000^{\circ}C$, $1100^{\circ}C$). The weight gain was measured after oxidation according to oxidation time (2, 4, 6, 8, 10, 15, 20, 25, 30, 60, 80, 100 hours). The weight gain significantly increased with increasing oxidation temperature. As the temperature increased, the oxidized samples showed sequential formation of $Al_2O_3$, Cr-rich oxide, Fe-rich oxide. The activation energy of high temperature oxidation was obtained as 306.63 KJ/mol. $Al_2O_3$ were developed on the surface in the early stage of oxidation, representing protective role of oxidation. However, Fe-based and Cr-based oxides leaded to breakaway of oxide layer, thus resulted in the significant increase of additional oxidation.

• Journal of Korea Foundry Society
• /
• v.22 no.6
• /
• pp.293-298
• /
• 2002

The effects of alloying elements added on the microstructure and high temperature oxidation behavior of the electro-slag remelted Fe-22Cr-5Al alloy were investigated. The amount of casting defect was makedly reduced by the electro-slag remelting. The electro-slag remelted ingot had a directionally solidified structure and cleaner surface than that of air-melted one. The high temperature oxidation reststance was greatly improved by the addition of Be and Zr.

• Korean Journal of Materials Research
• /
• v.6 no.1
• /
• pp.57-66
• /
• 1996

MoSi2 heating elements were fabricated by sintering of MoSi2 powders which were synthesized through SHS(Self-propagating high-temperature synthesis). Their high-temperature oxidation behavior in air through SHS(Self-propagating high-temperature synthesis). Their high-temperature oxidation behavior on air at 1000-1600$^{\circ}C$ was investigated through a high-temperature X-ray diffractomer and isothermal heating in a muffle furnace. The thermal expansion of MoSi2 and SiO2 was studied by measuring their lattice parameters on heating. The linear expansion coeffcient of MoSi2 along c-axis was about 1.5 times larger than that along a-axis showing a strong thermal anisotropy. Few $\mu\textrm{m}$-thick Mo5Si3 layer was found beneath SiO2 layer suggesting that The major reaction products would be SiO2 and Mo5Si3. The Si-rich bentonite resulted in the faster growth of MoSi2 grains probably by enhancing the mass transport when they are melted during high-temperature oxidation.