• Elastomers and Composites
• /
• 제32권3호
• /
• pp.157-165
• /
• 1997

The morphology of the thermoplastic vulcanizates prepared from ethylene-propylene-diene terpolymer, polypropylene and high density polyethylene(HDPE) or ethylene based ionomer were studied. Blends were prepared in a laboratory internal mixer where EPDM was cured in the presence of PP and HDPE or ionomer under shear with dicumyl peroxide(DCP). The effects of DCP concentration and rubber/plastics composition were studied. In the morphological analysis by scanning electron microscopy (SEM), a small amount of EPDM acted as a compatibilizer to HDPE and PP. It was also revealed that the dynamic vulcanization process could reduce the domain size of the crosslinked EPDM phase. When ionomer was added to EPDM/PP blend, the thermoplastic vulcanizate showed typical ductile fracture topology and the trend was more clearly observed when DCP contents and ionomer contents are higher.

• 한국산학기술학회논문지
• /
• 제14권6호
• /
• pp.3108-3113
• /
• 2013

이 연구에서는 옥텐의 함량이 다른 4가지 메탈로센 LLDPE (mLLDPE)를 각각 HDPE와 여러 조성에서 혼합한 후 시료들의 결정화 거동 및 기계적인 물성을 관찰하여 mLLDPE/HDPE의 혼화성에 관하여 연구하였다. 옥텐의 함량이 4.1, 6.8, 9.8 및 12.5 mol.% 인 네 종류의 mLLDPE에 HDPE를 100/0, 80/20, 60/40, 40/60/ 20/80 및 0/100의 비율로 용융 혼합하여 시료를 제조하였고, 이 시료의 결정화 온도, 용융온도를 DSC를 이용하여 측정하였다. 또한 각 시료의 기계적 물성을 인장 시험기를 이용하여 측정하였다. HDPE와 mLLDPE의 결정화 온도 및 용융온도는 상대편 고분자의 존재에 의하여 변하는 것으로 보아 용융상태에서 두 물질이 서로 같이 존재하는 구조, 즉 완전히 균일상이거나 최소한 부분적 상용성이 있음을 알 수 있었다. 용융온도가 낮은 mLLDPE의 용융피크는 HDPE를 첨가함에 따라증가하는 것으로 보아 mLLDPE의 결정상에는 HDPE가 같이 결정화가 되어 있는 것을 알 수 있었다. 그러나 HDPE결정에 mLLDPE가 같이 결정화 되어있는지는 확인할 수 없었다. 열분석과 기계적 물성을 측정한 결과 HDPE와 mLLDPE의 상용성은 mLLDPE에서 존재하는 옥텐의 함량이 낮을수록 증가하는 것을 알 수 있었다.

• 한국식품저장유통학회지
• /
• 제9권1호
• /
• pp.8-13
• /
• 2002

생홍고추 및 생홍피망의 장기저장 방법으로 HDPE 및 LDPE포장내에 시료와 함께 서로 다른 양의 NaCl을 삽입함으로써 MA저장 효과를 조사하였다. HDPE 및 LDPE 포장내의 NaCl 함량은 0 g, 15 g, 20 g, 25 g이었으며, 대조구로 무포장이 사용되었다. 홍고추 및 홍피망의 각각 50일 및 35일간 MA저장 동안 주기적으로 중량 변화와 곰팡이 발생율을 조사하였고, 저장 초기와 말기에는 색도와 경도를 측정·비교하였다. NaCl을 포함하지 않은 처리구에 있어 HDPE와 LDPE 포장 모두 홍고추 및 홍피망의 중량 감소율은 각각 4∼5% 및 3∼4%의 범위로 매우 낮았다. 그러나, 대조구인 무포장의 경우 중량 감소율이 저장 말기에 홍고추 및 홍피망 각각 45%와 22%로 높게 나타났다. 또한, 포장 내에 NaCl을 포함한 경우 홍고추 및 홍피망의 중량 감소율은 각각 19% 및 6% 이하로 무포장에 비해 매우 낮게 나타났다. 무포장인 홍고추 및 홍피망의 저장에 있어 곰팡이 발생율이 각파 5% 및 12.5%로 매우 낮았으나, NaCl을 포함하지 않는 HDPE 및 LDPE 저장에 있어서는 55∼65%로 매우 높게 나타났다. NaCl 함유량이 15 g, 20 g 및 25 g 일 때 HDPE 및 LDPE 포장에 저장된 홍고추 및 홍고추의 곰팡이 발생율은 20∼45%의 범위로 나타났다. NaCl을 포함하지 않는 HDPE와 LDPE 포장내에 저장된 홍고추 및 홍피망의 색도차는 각각 0.74와 1.50 이하로 매우 낮았다. 또한, 15∼25 g의 NaCl을 포함하는 MA 저장된 홍고추 및 홍피망의 색도차도 각각 0.85∼0.88 및 1.56∼1.61의 범위에 있었다. 그러나, 저장습도가 낮은 무포장의 경우 홍고추 및 홍피망의 색도차는 각각 1.15 및 1.78로 다른 처리구보다 매우 컸다. 무포장의 경도감소는 홍고추 및 홍피망이 각각 1.70 kg 및 0.71 kg으로 크게 나타났으나, 무포장에 비해 NaCl을 함유한 HDPE 및 LDPE 포장의 경우 홍고추 및 홍피망의 경도 감소는 각각 0.75∼1.02 kg 및 0.15∼0.49 kg의 범위로 낮게 나타났다.

• Nuclear Engineering and Technology
• /
• 제51권4호
• /
• pp.1142-1153
• /
• 2019

This paper presents the effect of fusion procedure on the fusion performance of the thermal butt fusion in the safety class III buried HDPE piping per various tests performed, including high speed tensile impact, free bend, blunt notched tensile, notched creep, and PENT tests. The suitability of fusion joints and qualification procedures was evaluated by comparing test results from the base material and buttfusion joints. From the notched tensile test result, it was found that the fused joints have much lower toughness than the base material. It was also identified that the notched tensile test is more desirable than the high speed tensile impact and free bend tests presented in the ASME Code Case N-755-3 as a fusion qualification test method. In addition, with regard to the single low-pressure fusion joint performances, the procedure given by the ISO 21307 was determined to be better that the one specified in the Code Case N-755-3.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2008년도 춘계학술대회 논문집 센서 박막재료연구회 및 광주 전남지부
• /
• pp.50-53
• /
• 2008

In this work, the $TiO_2$ pigment influence in HDPE dielectric strength was analyzed. Chemical and structural characterizations were made to identify changes during the processing and your influence in the electrical properties. Formulations containing 0, 0.5, 1, 2.5, 4 and 6 of titanium dioxide were processed by extrusion and injection molding with stabilization-antioxidants, ultraviolet stabilizers and plasticizers. The electrical strength tests were analyzed by the statistical distribution of Weibull, and the maximum likelihood method. The high concentrations present lower values to electrical strength. The $\beta$ parameter could be using to insulator particles dispersion. The $TiO_2$ concentration variation shows that these incorporations implicate strength values increase has a maximum (5,35MV/cm). High pigment concentration induces a little falls in property values. Observing the $\beta$ parameter, minimum experiment electric field (Ebmin) and electric strength value, found that the best electric perform formulation was the formulation with 2.5% $TiO_2$ weight.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2007년도 추계학술대회 논문집
• /
• pp.331-332
• /
• 2007

In this work, the TiO2 pigment influence in HDPE dielectric strength was analyzed. Chemical and structural characterizations were made to identify changes during the processing and your influence in the electrical properties, formulations containing 0, 0.5, 1, 2.5, 4 and 6 of titanium dioxide were processed by extrusion and injection molding with stabilization-antioxidants, ultraviolet stabilizers and plasticizers. The electrical strength tests were analyzed by the statistical distribution of Weibull, and the maximum likelihood method. The high concentrations present lower values to electrical strength. The parameter could be using to insulator panicles dispersion. The TiO2 concentration variation shows that these incorporations implicate strength values increase has a maximum (5,35MV/cm). High pigment concentration induces a little falls in property values. Observing the parameter, minimum experiment electric field (Ebmin) and electric strength value, found that the best electric perform formulation was the formulation with 2.5% TiO2 weight.

• 공업화학
• /
• 제10권6호
• /
• pp.944-948
• /
• 1999

메탈로센 촉매로 만든 폴리에틸렌(MCPE)과 Ziegler-Natta 촉매로 만들어진 4가지의 폴리올레핀으로 구성된 2원 블렌드의 상 형태학을 통하여 미세 분자 구조의 변화가 이들 블렌드의 상 형태학과 계면 거동에 미치는 영향을 연구하였다; 연구한 네 쌍의 블렌드는 고밀도 폴리에틸렌(HDPE)-MCPE, 폴리프로필렌(PP)-MCPE, poly(propylene-co-ethylene) (CoPP)-MCPE, poly(propylene-co-ethylene-co-1-buthylene) (TerPP)-MCPE이며 모두 상 분리된 시스템이다. HDPE-MCPE는 HDPE 성분이 증가할수록 HDPE 결정이 MCPE 연속상에서 고르게 성장하는 동질상(homogeneous phase)을 나타내는 반면에, 나머지 세 쌍의 블렌드는 복잡한 이종의 상(heterogeneous phase) 형태학을 보였다. PP-MCPE는 PP와 MCPE의 상과 계면이 완전히 분리된 상 형태학을 보였고, MCPE가 50% 함유된 조성에서 상전이가 일어났다. CoPP-MCPE와 TerPP-MCPE는 이들 코폴리머에 함유한 에틸렌기로 인해 두 계면 사이의 혼화성이 증가하는 현상을 보였으며 MCPE가 40%인 블렌드에서 상전이가 일어났다. 특히 TerPP-MCPE 블렌드는 TerPP의 코폴리머가 MCPE와 같은 화학구조를 보이는 1-부텐과 에틸렌기를 가지고 있어 다른 두 블렌드인 PP-MCPE, CoPP-MCPE 보다 두 상간의 계면이 서로 부분적으로 섞이는 양상을 보였다. 상 형태학에서 본 미세 분자구조에 의한 부분적 상용성은 기계적 특성이나 유변학적 성질과도 밀접한 관계를 나타냈다. 그러므로 본 연구에 사용한 네 가지 블렌드는 두 상이 완전히 분리되어 열역학적으로 비 혼화성을 나타내지만 다음과 같은 특성을 제시할 수 있다. 즉 계면의 세기는 HDPE-MCPE>TerPP-MCPE>CoPP-MCPE>PP-MCPE 순이며, 이는 미세 분자 구조측면에서 공통의 화학 구성물이 계면 접착력(interfacial adhesion)의 증가를 가져오는 중요한 요인으로 작용하기 때문으로 여겨진다.

• 콘크리트학회논문집
• /
• 제28권1호
• /
• pp.59-65
• /
• 2016

본 연구에서는 수소 함유량이 높아 중성자 차폐에 유리한 합성수지를 대상으로 중성자 차폐용 골재로서의 적용성 검토를 수행하였다. 사용된 합성수지는 고밀도 폴리에틸렌(HDPE), 폴리프로필렌(PP), 초고분자량 폴리에틸렌(UPE)으로 잔골재의 20%, 40%, 60%의 부피에 해당하는 양을 무게로 환산하여 배합하였다. 실험은 모르타르의 물리적 특성을 파악할 수 있는 플로우 테스트, 인장 및 압축강도 시험을 수행하였으며, 시험체 내부의 미세구조를 분석하기 위해 파단면의 이미지 분석, SEM 및 X-ray CT 촬영을 실시하였다. 합성수지를 혼입한 모르타르의 플로우의 값은 HDPE 및 PP는 증가하였지만 UPE의 경우 감소하였다. 반면 인장 및 압축강도의 경우 종류에 상관없이 전반적으로 강도가 감소하는 경향을 보였으며, 이미지 분석 결과, HDPE 및 PP를 혼입한 모르타르의 강도는 혼입량에 관계없이 파단면에서의 합성수지 비율에 영향을 받았으며, 모르타르 내의 시멘트 매트릭스와의 단락 및 재료의 불균등한 분포가 강도 저하에 영향을 미친 것으로 추정된다. 반면, 미분말 상태인 UPE는 혼입량이 증가함에 따라 내부 공극이 증가하였으며, 이러한 특징은 일정량 이하에서는 강도 저하가 미미하였으나 일정한 혼입률 이상, 특히 본 실험에서는 치환율이 60% 이상에서 급격한 강도 저하를 나타냈다.

• 한국식품저장유통학회:학술대회논문집
• /
• 한국식품저장유통학회 2003년도 제23차 추계총회 및 국제학술심포지움
• /
• pp.187-187
• /
• 2003

To examine the effect of packaging method on strawberry, tomato, and plum quality, the rate of weight loss, Hunter a value, decay rate, anthocyanin contents, and microbial (total bacterial counts, mold and yeast, and pseudomonas) changes were determined during storage. Strawberry was packaged with low density polyethylene (LDPE). Tomato and plum were packaged with high density polyethylene film (HDPE). Strawberries, tomatoes, and plums were then stored at 4$^{\circ}C$ and 20$^{\circ}C$, respectively. LDPE package was the most effective on the decrease of decay rate of strawberry and the rate of weight loss for packaged strawberry was lower than that of the non-packaged. HDPE package was the most effective on the rate of weight loss during storage of tomatoes and plums regardless of storage temperature. Hunter a value increased during storage. Anthocyanin contents of plums increased overall with increasing storage time, and plums stored without package were changed more than those with package. Microbial changes of strawberry, tomato, and plum stored at 4$^{\circ}C$ and 20$^{\circ}C$ were monitored during storage. Packaging method did not affect the microbial change, yet temperature did affect the microbial change significantly. These results indicate that storage of these commodities at 4$^{\circ}C$ should be recommended in terms ,of microbial safety as well as quality and shelf-life.

• 산업식품공학
• /
• 제15권3호
• /
• pp.257-261
• /
• 2011

본 연구에서는 자연분해재 펠릿과 polyethylene들을 이용해 LDPE와 신장율과 인장강도가 유사한 생붕괴성 플라스틱 필름들을 제조하였다. 식품 포장재로서의 안전성, 광분해성, 열분해성 및 곰팡이 생분해성을 평가한 결과 제작된 생붕괴성 플라스틱 필름들은 식품 포장재로 사용하기에 안전하고 LDPE 필름에 비해 상대적으로 우수한 분해 특성을 나타내어 환경친화적인 식품 포장 소재로 사용될 가능성을 보여주었다.