• Fire Science and Engineering
• /
• v.3 no.2
• /
• pp.3-10
• /
• 1989

The results on high strength concrete by heating high are as follows: 1. High strength concrete appeared an estimated 5.5% higher than ordinary concrete in the central temperature of specimens by heating. 2. High strength concrete is higher than ordinary concrete in the decreased width of the ratio on the residual compressive strength by heating high. According to heating temperature and time, the inferred formula of compressive strength on high strength concrete showed: Fc=-0.53Te -2.4Ti +748.4

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2009.10a
• /
• pp.441-444
• /
• 2009

Weldlines are generated during the injection molding process when two or more melt flows are brought into contact. At the welded contact region, a 'V'-shaped notch is formed on the surface of the molded part. This 'V'-notch deteriorates not only surface appearance but also mechanical strength of the molded part. To eliminate or reduce weldlines so as to improve the weldline strength, the mold temperature at the corresponding weld locations should be maintained higher than the glass transition temperature of the resin material. The present study implements high-frequency induction heating in order to rapidly raise mold surface temperature without a significant increase in cycle time. This induction heating enables to local mold heating so as to eliminate or reduce weldlines in an injection-molded plastic part. The effect of induction heating conditions on the weldline strength and surface appearance of an injection-molded part is investigated.

• Journal of Industrial Technology
• /
• v.21 no.B
• /
• pp.213-222
• /
• 2001

In the study, the fatigue strength improvement and mechanism have been estimated by the Spot-Heating treatment on welded bead toes. For this, web-gusset specimens were made without residual stresses and the others with residual stresses imposed by Spot-Heating. The 4-point bending tests were performed in order to estimate the effect of spot-heating on fatigue strength and fatigue characteristics quantitatively for non load-carrying fillet welded joints subjected to pure bending. As a result of fatigue test, fatigue strength of As-Welded specimen for non load-carrying fillet welded joints subjected to pure bending has satisfied the grade of fatigue prescribed in specifications of korea, AASHTO and JSSC. As compare with As-Welded specimen and Spot-Heating specimen have increased about 20% for the fatigue strength at $7.7{\times}10^6$ cycles. The Spot-Heating by reformation of the residual stress on welded bead toes has greatly affected the fatigue crack propagation life, but has slightly affected the fatigue crack initiation life.

• Journal of the Korea Furniture Society
• /
• v.17 no.2
• /
• pp.25-34
• /
• 2006

This experiment was carried out to investigate the high-frequency gluing characteristics of poly vinyl acetate emulsion adhesive(PVAc) on MDF edge-glued boards. The edge-glued boards were glued lengthwise with butt, scarf, or finger joint. The wastes of MDF boards were reused as board materials. The obtained results are summarized as follows; the bending strength of edge-glued MDF increased slightly with the HF heating time, but the economically desirable heating time was 6 minutes. The bending and tensile strength of edge-glued MDF were high with scarf, finger and butt joint, in order. The strength of finger jointed MDF showed 80% of scarf jointed MDF. The effects of location of finger joints on the bending strength of edge-glued MDF were larger than those of the numbers of finger joints. The bending strength of edge-glued MDF with one joint on the middle position showed 40% decrease in comparison with non-jointed MDF.

• Journal of the Korean Society for Precision Engineering
• /
• v.27 no.1
• /
• pp.105-112
• /
• 2010

Weldlines are generated during the injection molding process when two or more melt flows are brought into contact. The weldlines are unavoidable in the cases of presence of holes or inserts, multi-gated delivery systems, significant thickness change, etc. At the welded contact region, a 'V'-shaped notch is formed on the surface of the molded part. This 'V'-notch deteriorates not only surface appearance but also mechanical strength of the molded part. To eliminate or reduce weldlines so as to improve the weldline strength, the mold temperature at the corresponding weld locations should be maintained higher than the glass transition temperature of the resin material. The present study implements high-frequency induction heating in order to rapidly raise mold surface temperature without a significant increase in cycle time. This induction heating enables to local mold heating so as to eliminate or reduce weldlines in an injection-molded plastic part. The effect of induction heating conditions on the weldline strength and surface appearance of an injection-molded part is investigated.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.13 no.3 s.55
• /
• pp.127-134
• /
• 2009

This study investigated their properties of spalling resistance and residual compressive strength after fire test corresponding to various ISO, RABT heating curves, and contents of hybrid organic fiber of high strength concrete. The results were summarized as following. As fundamental characters of concrete with hybrid organic fiber, the flowability was directly declined as the increase of fiber contents, and air contents were decreased or increased a little bit, but there was not big difference. The compressive strength was gradually declined sluggishly at 28 days. As properties of fire resistance, in case of RABT heating curves, compare with ISO heating curves a spalling aspect showed till range that has much contents of hybrid organic fiber, but they are mostly peeling spalling, which means spalling aspect didn't happen to inside. In conclusion, in case of W/B 25% high strength concrete, the spalling was prevented over 0.04% of contents of fiber at ISO heating curve and over 0.10% of contents of fiber at the RABT heating curve. In case of spalling was prevented, mass reduction rate according to the change of heating temperature curves showed around 7% at ISO heating curves and around 9% at RABT heating curves. The residual compressive strength rate corresponding to the change of heating temperature curves showed 50%~60% at ISO heating temperature curves and 30%~35% at RABT heating temperature curves in case of spalling was prevented.

• Advances in materials Research
• /
• v.4 no.1
• /
• pp.13-22
• /
• 2015

Concrete suffers strength loss when subjected to elevated temperatures during an accidental event such as fire. The loss in strength of concrete is mainly attributed to decomposition of C-S-H gel and release of chemically bound water, which begins when the temperature exceeds $500^{\circ}C$. But it is unclear about how much strength loss occurs in different stages of heating, retention and cooling regimes. This work is carried out to separate the total strength loss into losses during different stages of heating, retention and cooling. Tests were carried out on both Ordinary Portland Cement (OPC) based concrete and Ground Granulated Blast Furnace Slag (GGBFS) blended concrete for $200^{\circ}C$, $400^{\circ}C$, $600^{\circ}C$ and $800^{\circ}C$ with a retention period of 1 hour for each of these temperature levels. Furnace cooling was adopted throughout the experiment. This study reports strength loss contribution during heating, retention and cooling regimes for both OPC based and GGBFS based concretes.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2016.05a
• /
• pp.107-108
• /
• 2016

When the construction in a low temperature, the concrete performance is deteriorated by frost damage at early age. In this study, the form utilizing heating sheet and insulation is measured the performance to prevent frost damage at 10 below zero. It produced five types of the form and to measure the temperature history and compressive strength. At first, form attached heating sheet showed the highest temperature. But the form attached vacuum insulation showed the highest temperature ever since 12hours. In the case of compressive strength, the form attached heating sheet + isopink(polystyrene foam board) showed the highest compressive strength. It was followed by vacuum insulation. As a result, the form utilizing insulation and heating sheet helped to prevent frost damage.

• The Journal of Advanced Prosthodontics
• /
• v.11 no.4
• /
• pp.202-208
• /
• 2019

PURPOSE. Fabrication of zirconia restorations with ideal mechanical properties in a short period is a great challenge for clinicians. The purpose of the study was to investigate the effect of heating rate on the mechanical and microstructural properties of monolithic zirconia. MATERIALS AND METHODS. Forty monolithic zirconia specimens were prepared from presintered monolithic zirconia blanks. All specimens were then assigned to 4 groups according to heating rate as Control, Group $15^{\circ}C$, Group $20^{\circ}C$, and Group $40^{\circ}C$. All groups were sintered according to heating rates with the sintering temperature of $1500^{\circ}C$, a holding time of 90 minutes and natural cooling. The phase composition was examined by XRD analysis, three-point bending test was conducted to examine the flexural strength, and Weibull analysis was conducted to determine weibull modulus and characteristic strength. Average grain sizes were determined by SEM analysis. One-way ANOVA test was performed at a significance level of 0.05. RESULTS. Only tetragonal phase characteristic peaks were determined on the surface of analyzed specimens. Differences among the average grain sizes of the groups were not statistically significant. The results of the three-point bending test revealed no significant differences among the flexural strength of the groups (P>.05). Weibull modulus of groups was ranging from 3.50 to 4.74. The highest and the lowest characteristic strength values were obtained in Group $20^{\circ}C$ and Control Group, respectively. CONCLUSION. Heating rate has no significant effect on the flexural strength of monolithic zirconia. Monolithic zirconia restorations can be produced in shorter sintering periods without affecting the flexural strength by modifying the heating rate.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2007.04a
• /
• pp.9-12
• /
• 2007

Recently, research and development related to high strength concrete for the high rise and large scale reinforced concrete building has been actively promoted in worldwide by national and private research project. But, it is reported that violent explosive explosion would be happened when it was exposed in fire. In the existed study, a explosion in a reinforced concrete structure looses the organism by the different contraction and expansion of hardened cement paste and aggregate, and causes crack by thermal stress. In case of the Europe, Japan and America, they have studied the explosion for a long time. However it would hardly study the explosion in domestic, So it is needed base on mechanical properties of fire deterioration in high strength concrete. Therefore, this study is intend as an mechanical properties of specimen to high heating by heating and load test machine and $700^{\circ}C$. As a result, it is willing to propose fundamental data for quick and accurate diagnosis of deteriorated concrete structure by fire damage with experiment according to the design high strength concrete.