• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2004년도 추계 학술발표회 제16권2호
• /
• pp.707-710
• /
• 2004

This paper reported the results of mock-up test on mass concrete for transfer girder using setting time difference of super retarding agent(SRA). According to test results, two mock-up structures were made. Plain concrete without placing layer reached maximum temperature after 24hours since placement and caused surface hydration cracks at top section. However, concrete with placing layer reached maximum temperature after 72hours and surface temperature was higher than center temperature, which did not cause surface crack. After form removing, no crack was observed at side surface of plain concrete, while concrete using SRA at mid section had surface scaling and settling crack. According to coring results, concrete with placing layer had a penetration crack from top section to bottom section. Therefore, the setting time difference method to reduce hydration heat will have difficulty in applying the mass concrete for transfer girder.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2008년도 춘계 학술발표회 제20권1호
• /
• pp.417-420
• /
• 2008

본 연구에서는 플라이애쉬가 다량 치환된 콘크리트 강도 발현과 수화열 특성에 대하여 연구를 수행하였다. 2수준의 W/B와 7수준의 플라이애쉬 치환률 및 2수준의 실리카흄 치환율을 실험 변수로 선택하였다. 콘크리트 배합에서 단위수량은 $125kg/m^3$으로 고정하였다. 결과로서 초기 재령에서는 플라이애쉬 치환율이 증가하면서 압축강도가 점진적으로 감소하는 경향을 나타내었다. 그러나 재령 91일에서는 50%의 플라이애쉬 치환률까지 압축강도가 큰 차이가 없는 것으로 나타났다. 그리고 수화열 저감 효과는 플라이애쉬 치환율에 영향을 받는 것으로 나타났다. 플라이애쉬 치환율이 30% 이상일 때 수화열 저감 효율이 더 좋은 것으로 나타났다.

• 콘크리트학회지
• /
• 제7권6호
• /
• pp.176-185
• /
• 1995

매스콘크리트 구조물에서 시멘트의 수화발열반응에 발생된 열은 약재령 콘크리트에서 내부온도의 증가와 체적변화를 일으키게 된다. 이와 같은 온도증가에 외부구속조건이 존재하게 되면, 구조물에는 인장응력이 발생하고 이는 구조물에 균열을 일으킬 수 있다. 따라서 매스콘크리트 구조물 건설시 수화열에 의한 온도증가를 제어하기 위해 다양한 시공기법을 이용하고 있으며, 이들 공법 중 하나가 관에 냉각수를 유입시켜 온도를 하강시키는 파이프쿨링 공법이다. 이 논문의 목적은 파이프쿨링을 실시할 때 수화열로 인한 온도이력을 모사할 수 있는 유한요소해석 프로그램을 개발하는 것이다. 이 연구에서 개발된 해석 프로그램의 결과와 실제 구조물의 기초부(11$\times$22cm)의 실측 결과가 잘 일치함을 보였다. 따라서 여기서 제시된 방법은 파이프쿨링으로 인한 콘크리트의 수화온도 예측에 유용하게 이용될 수 있을 것으로 판단된다.

• 콘크리트학회논문집
• /
• 제24권5호
• /
• pp.535-542
• /
• 2012

매스 콘크리트에서 발생하는 수화열을 예측하기 위한 단열온도상승시험은 시험 비용이 고가이고 시공간상 제약으로 인해 한계가 있는 실정이다. 이에 신속하고 경제적이며 간편한 간이 수화열 측정 장치의 개발이 필요한 실정이다. 이 연구에서는 간이 수화열 측정 장치를 완성하기 전 단열 성능이 뛰어난 보온병에 콘크리트를 타설하고 열손실량을 보정하여, 간이 수화열 측정 장치의 타당성을 입증하고자 하였다. 열손실량을 정확히 예측하기 위해서는 측정 장치의 정확한 열손실계수를 추정하는 것이 필수적인데, 열손실계수는 단열 장치 내부의 수온 변화를 이용하여 추정하였다. 시험 결과 장치 고유의 열손실계수는 외부 온도와 습도, 내부 온도 변화에 크게 변하지 않는 것으로 드러났다. 실제 단열온도상승시험과 열손실량이 보정된 보온병의 단열온도상승량과의 검증 시험을 통해 이 연구의 객관성과 타당성을 입증할 수 있었다.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2006년도 추계 학술발표회 논문집
• /
• pp.777-780
• /
• 2006

Recently, owing to the development of industry and the improvement of building techniques, the concrete structure is becoming larger and higher. In hardening these large concrete, the heat of hydration gives rise to considerable thermal stress depending on the size and environmental condition of concrete, which might cause thermal cracking. Especially, the crack may cause severe damage to the safety and the durability of concrete structure. This study is investigated the thermal properties of concrete according to several binder conditions, such as OPC, Belite Rich Cement(BRC), Low-Heat-Mixed Cement(LHC), Fly ash added cement. As a result of this study, the Flowability of concrete was beetter with BRC and LHC than FA(25) and OPC. On the other hand, LHC gets superior effect in the control of heat hydration, it's caused by the volume of OPC.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 1996년도 봄 학술발표회 논문집
• /
• pp.36-41
• /
• 1996

The selection of Cement types is greatly dependent on the structural requirement and consturction location associated with control of hydration heat, acquisition of early strength, existence of sulfate attacks and so on. Based on this, this study adresses the comparison of physical properties of concrete according to the use of different cement types. As a result of testing with OPC, blast furnace slag and low heat cement, it is found that concrete made with low heat cement is much better in term of hydration heat and permeability. It is also recommended to select a preper cement type depending on structural characteristics.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 1995년도 가을 학술발표회 논문집
• /
• pp.329-333
• /
• 1995

The usual methods for the temperature control of mass-concrete structures include the use of low-heat cement, pre-cooling, or pipe-cooling. In order to control the heat of hydration of mass-concrete structures such as massive pier or anchor block, and mat foundation, the pipe cooling method is widely acceptable for pratical use. In this paper, method of analysis using the Finite Element Method was applied to analyze the heat exchange on the field of three dimensional thermal conduction. The result of analysis Well agreed with experimentally measurement data by "KUMATANI". The method of this analysis will be used widely to control the heat of hydration by the pipe cooling in mass-concrete.-concrete.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2021년도 가을 학술논문 발표대회
• /
• pp.182-183
• /
• 2021

In this study, This is the result of thermal characteristics analysis to suggest an efficient method of using coal gasification slag(CGS) of byproduct from integrated gasification combined cycle(IGCC). In Specific Heat characteristics, CGS and CS showed similar values. Isothermal Conduction Calorimetry showed that the hydration reaction of cement was retarded when CGS was used. Therefore, it is expected that CGS will be used as an efficient alternative to reducing the hydration heat of mass concrete as a functional aggregate combination.

• Computers and Concrete
• /
• 제16권3호
• /
• pp.487-502
• /
• 2015

This study investigated particle expansion in basic oxygen furnace slag (BOF) and desulfurization slag (DSS) after heat curing by using the volume method. Concrete hydration was accelerated by heat curing. The compressive strength, ultrasonic pulse velocity, and resistivity of the concrete were analyzed. Maximum expansion occurred in the BOF and DSS samples containing 0.30-0.60 mm and 0.60-1.18 mm particles, respectively. Deterioration was more severe in the BOF samples. In the slag aggregates for the complete replacement of fine aggregate, severe fractures occurred in both the BOF and DSS samples. Scanning electron microscopy revealed excess CH after curing, which caused peripheral hydration products to become extruded, resulting in fracture.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2020년도 봄 학술논문 발표대회
• /
• pp.175-176
• /
• 2020

This study aims to develop the hydration heat reducing material (powder type) to lower the heat of hydration of mass members in the extremely hot weather condition. In this study, we applied the developed material to the concrete that used two kinds of binders with cement and evaluate the concrete properties with it.