The Characteristics of Strength of Development and Hydration Heat on High Volume Fly-Ash Concrete

플라이애쉬 치환율이 높은 콘크리트의 강도 발현 및 수화열 특성

In this study, the characteristics of strength development and hydration heat on high volume fly ash concrete(HVFAC) was experimentally investigated. Two levels of W/B were selected. Seven levels of fly ash replacement ratios and two levels of silica fume replacement ratios were adopted. In the concrete mix, the water content of $125kg/m^3$ was used, which is less than that of usual water content. As a result, it appeared that the compressive strength gradually decreased with increasing fly ash replacement ratio at the early age, but the difference of strength up to replacement ratio of 50% was little at the age of 91 days because of the pozzolanic reaction of fly ash. The effect of hydration heat reduction on the concrete was affected by the fly ash replacement ratio. When the replacement ratio was over 30%, the reduction efficiency of hydration heat was large.

본 연구에서는 플라이애쉬가 다량 치환된 콘크리트 강도 발현과 수화열 특성에 대하여 연구를 수행하였다. 2수준의 W/B와 7수준의 플라이애쉬 치환률 및 2수준의 실리카흄 치환율을 실험 변수로 선택하였다. 콘크리트 배합에서 단위수량은 $125kg/m^3$으로 고정하였다. 결과로서 초기 재령에서는 플라이애쉬 치환율이 증가하면서 압축강도가 점진적으로 감소하는 경향을 나타내었다. 그러나 재령 91일에서는 50%의 플라이애쉬 치환률까지 압축강도가 큰 차이가 없는 것으로 나타났다. 그리고 수화열 저감 효과는 플라이애쉬 치환율에 영향을 받는 것으로 나타났다. 플라이애쉬 치환율이 30% 이상일 때 수화열 저감 효율이 더 좋은 것으로 나타났다.