• Journal of Korea Foundry Society
• /
• v.14 no.3
• /
• pp.258-266
• /
• 1994

AC4A $Al/Al_2O_3+SiC_p$ hybrid composites were fabricated by the squeeze infiltration technique. Effect of applied pressure, volume fraction of reinforcement($Al_2O_3$ and SiC) and SiC particle size($4.5{\mu}m$, $6.5{\mu}m$ and $9.3{\mu}m$) on the solidification microstructure of the hybrid composites were examined. Mechanical properties were estimated preliminarly by fractographic observation, hardness measurement and wear test. Results show that the microstructure of the hybrid composites were quite satisfactory, namely revealing relatively uniform distribution of reinforcements and refined matrix. Some aggregation of SiC particle caused by particle pushing was observed especially in the hybrid composites containg in fine particle($4.5{\mu}m$). Refined matrix was attributed to applied pressure and increased nucleation sites with addition of reinforcements. Fractured facet also revealed finer for the hybrid composites possibly due to refined matrix. Hardness and wear resistance increased with volume fraction of reinforcements. For hybrid composites with $9.3{\mu}m$ SiC, hardness was somewhat lower and wear resistance higher than other composites.

• Journal of the Korean Ceramic Society
• /
• v.32 no.6
• /
• pp.726-734
• /
• 1995

Pb(Zr0.53Ti0.47)O3 (PZT) ceramics having different microstructures were fabricated at low temperatures using calcined PZT powders with addition of excess PbO powder and/or ball milling. The effects of excess PbO and ball milling time on the microstructure, the sintering characteristic, and the mechanical properties of these ceramics were studied. Fine powders with average particle size of 0.38㎛ could be obtained by ball milling with 2.5 mm Ф zirconia balls for 120 hours. By the addition of 2mol% of excess PbO to these powders, it was possible to obtain well-densitified PZT ceramics at low sintering temperature of 980℃. Densification behavior of PZT was affected by the addition of excess PbO powder, while, grain growth was hardly affected by PbO addition. It was observed that Vicker's hardness decreased and fracture toughness increased with the increasing amount of PbO. At 1mol% excess PbO, it was shown that the minimum values of hardness and maximum fracture toughness were achieved. In addition, with increasing sintering time, the fracture toughness decreased and the hardness increased.

• Journal of Korea Foundry Society
• /
• v.27 no.3
• /
• pp.120-125
• /
• 2007

The microstructure, mechanical properties and melting range of Ni-Cr-Mo based alloys were investigated to develop Be-free Ni-Cr-Mo base dental alloys for Porcelain-Fused-to-Metal Firing(PFM). All as-cast alloys showed dendritic structure. Rockwell hardness of 20Cr7Mo was increased with addition of Si and Ti. On the contrary, it was decreased with addition of Co. The duplex alloying elemental addition such as 3Co + xTi, 2Si + xCo and 2Si + xTi to 20Cr7Mo resulted in much increase of hardness. Rockwell hardness and compressive strength for 20Cr3CoSiTi or 17Cr6CoSiTi alloy that add Si-Ti had similar values compared to the commercial alloys. Melting range for 20Cr3CoSiTi and 17Cr6CoSiTi alloy that add Si-Ti showed similar or lower than commercial alloys. In conclusion, 20Cr3CoSiTi and 17Cr6CoSiTi alloys can be applied for commercial use.

• International Journal of Advanced Culture Technology
• /
• v.3 no.1
• /
• pp.169-178
• /
• 2015

This research aims to study the effects of various welding parameters in gas metal arc welding (GMAW) process on welding penetration, microstructure and hardness of AS3578-A350 high strength steel with the thickness of 10 mm. The welding process parameters were a welding current of 100-200A, an arc voltage of 20-30V, a welding speed of 20-60 cm/min and a gas shielding type of Ar and $Ar+CO_2$. The summarized experimental results are as follows. An increase of the welding current and voltage affected to increase the penetration depth of the joint. However, when the welding speed was decreased, it increased the penetration depth of the joint. Using the Ar gas for shielding the weld area, produced the higher penetration depth and the less narrow weld bead than the joint that was shielded by the mix gas of $Ar+CO_2$. The variation of the welding process parameters affected to produce the various microstructures of weld metal and heat affected zone and also showed the various kind of hardness along the weld joint.

• Journal of the Korean Society of Manufacturing Process Engineers
• /
• v.7 no.1
• /
• pp.9-16
• /
• 2008

It is important not only to reduce the casting defects of piston but also to improvement in the mechanical properties(hardness) of piston for the air compressor. The blow hole is typical casting defects in the conventional cast of aluminium alloy(AC8A-T6) piston. Because of the heat treatment method, mechanical properties of the aluminium alloy for piston was decided on the heat treatment method and cycle. Therefore, we tested on the development of mechanical properties and on the casting defects of piston for the air compressor in accordance with the heat treatment and casting condition. After the heat treatment and casting was carried out as several times, and was compared with the imported piston. As a result of several investigations; microstructure, hardness and casting defects of piston was changed under the influence of the heat treatment and casting method. When the cooling rate was controlled and the uni-cast method used, it bas the same mechanical properties and microstructure.

• Korean Journal of Materials Research
• /
• v.28 no.5
• /
• pp.295-300
• /
• 2018

Effects of annealing temperature on the microstructure and mechanical properties through thickness of a Cu-3.0Ni-0.7Si alloy processed by differential speed rolling are investigated in detail. The copper alloy with a thickness of 3 mm is rolled to a 50 % reduction at ambient temperature without lubricant and subsequently annealed for 0.5 h at $200-900^{\circ}C$. The microstructure of the copper alloy after annealing is different in the thickness direction depending on the amount of the shear and compressive strain introduced by the rolling; the recrystallization occurs first in the upper roll side and center regions which are largely shear-deformed. The complete recrystallization occurs at an annealing temperature of $800^{\circ}C$. The grain size after the complete recrystallization is finer than that of the conventional rolling. The hardness distribution of the specimens annealed at $500-700^{\circ}C$ is not uniform in the thickness direction due to partial recrystallization. This ununiformity of hardness corresponds well to the amount of shear strain in the thickness direction. The average hardness and ultimate tensile strength has the maximum values of 250 Hv and 450 Mpa, respectively, in the specimen annealed at $400^{\circ}C$. It is considered that the complex mode of strain introduced by rolling directly affects the microstructure and the mechanical properties of the annealed specimens.

• Journal of the Korean Society for Heat Treatment
• /
• v.34 no.6
• /
• pp.287-293
• /
• 2021

This study was intended to investigate the influence of Al content on hardness and microstructural characteristics of discontinuous precipitates (DPs) formed by isothermal aging in Mg-8.7%Al and Mg-10%Al alloys. In order to obtain large amount of DPs in the microstructure, the alloy specimens were solution-treated at 688K for 24 h followed by water quenching, and then aged at 418K for 48h. The Mg-Al alloy with higher Al content was characterized by higher volume fraction of DPs at the same aging condition, lower interlamellar spacing of the DPs, thinner β phase layer and higher β phase content in the DPs. This is closely related to the higher velocity of discontinuous precipitation process resulting from the higher Al supersaturation in the α-(Mg) matrix. The Mg-10%Al alloy showed higher hardness of the DPs and greater difference in hardness between as-cast state and DPs than the Mg-8.7%Al alloy.

• Journal of Power System Engineering
• /
• v.13 no.3
• /
• pp.47-52
• /
• 2009

The effect of forging start temperature, forging ratio on the microstructure and mechanical properties of B7B4 steel ware investigated. Microstructure of centrifugal casted B7B4 steel consisted of martensite and ferrite phase. The volume fraction of ferrite increased with increase of forging start temperature and decreased with increase of forging ratio. Tensile strength and hardness decreased with higher of forging start temperature, while impact value and elongation increased with higher of forging start temperature. With increase of forging ratio, tensile strength rapidly increased up to the forging ratio of 30%, and then slowly increased, but elongation was decreased. Hardness and impact value rapidly increased with increase of forging ratio.

• Journal of the Korean Society for Precision Engineering
• /
• v.18 no.9
• /
• pp.82-88
• /
• 2001

In order to fulfil the requirements of the various performance profiles of ceramic cutting tools, six different SiC-based ceramics have been fabricated by hot-pressing (SiC--${Si}_3 {N}_4$composites) or by hot-pressing and subsequent annealing (monolithic SiC and SiC-TiC composites). Correlation between the annealing time and the corresponding microstructure and the mechanical properties of resulting ceramics have been investigated. The grain size of both ${Si}_3 {N}_4$and SiC in SiC-${Si}_3 {N}_4$composites increased with the annealing time. Monolithic SiC has the highest hardness, SiC-TiC composite the highest toughness, and the SiC-${Si}_3 {N}_4$composite the highest strength among the ceramics investigated. The hardness of SiC-${Si}_3 {N}_4$composites was relatively independent of the grain size, but dependent on the sintered density. The cutting performance of the newly developed SiC-based ceramic cutting tools will be described in Part 2 of this paper.

• Journal of the Korean Society for Heat Treatment
• /
• v.20 no.2
• /
• pp.78-83
• /
• 2007

CrN coatings were deposited by cathodic arc ion plating method on the SKD11 steel substrates. Atmosphere temperature of $350^{\circ}C$, arc current of 90 A, nitrogen partial pressure of 1.0-5.3 Pa, and negative bias voltage of 30-135 V were selected. The characteristics of microstructure were investigated with XRD. Hardness, adhesion and friction coefficient measured by microhardness tester, scratch tester, and ball on disk tribometer. Microstructures depended on nitrogen partial pressure and bias voltage. The preferred orientation of the films was changed from (200) to (111) with decreasing pressure and increasing bias voltage. Adhesion properties related with microstructure, but microstructure changes slightly influenced on hardness and friction properties. The critical load.($Lc_1$) and hardness of CrN films deposited at 5.3 Pa, -30 V condition were 55 N(HF1), $2157{\pm}47\;Hk_{0.025}$. The friction coefficient were about 0.5 under dry condition.