• Journal of the Microelectronics and Packaging Society
• /
• v.10 no.4
• /
• pp.61-64
• /
• 2003

The fractography was used to observe the stress profile on a single ion-exchanged glass. In the processing, the temperature was varied during the ion exchange, and then the stress profile on the single ion-exchanged glass was shifted from glass surface to slightly below the glass surface. The hackle mark and mirror surface were varied according to process conditions, and the glass strength was increased with increasing the number of hackle markers. In case of breaking the stress profile by using indenter, the breaking property was similar to the annealed glass.

• Journal of Dental Rehabilitation and Applied Science
• /
• v.38 no.3
• /
• pp.138-149
• /
• 2022

The clinical applicability of ceramics can be increased by analyzing the causes of fractures after fracture testing of dental ceramics. Fractography to analyze the cause of fracture of dental ceramics is being widely applied with the development of imaging technologies such as scanning electron microscopy. Setting the experimental conditions is important for accurate interpretation. The fractured specimens should be stored and cleaned to avoid contamination, and metal pretreatment is required for better observation. Depending on the type of fracture, there are dimple rupture, cleavage, and decohesive rupture mainly observed in metals, and fatigue fractures and conchoidal fractures observed in ceramics. In order to reproduce fatigue fracture in the laboratory, which is the main cause of fracture of ceramics, a dynamic loading for observing slow crack growth is essential, and the load conditions and number of loads must be appropriately set. A typical characteristic of a fracture surface of ceramic is a hackle, and the causes of fracture vary depending on the shape of hackle. Fractography is a useful method for in-depth understanding of fractures of dental ceramics, so it is necessary to follow the exact experimental procedure and interpret the results with caution.

• Composites Research
• /
• v.26 no.2
• /
• pp.141-145
• /
• 2013

The mode II interlaminar fracture toughness was evaluated for CFRP laminates with different types of nonwoven tissues and the source of increased mode II interlaminar fracture toughness was examined by SEM analysis in this paper. The interlaminar fracture toughness in mode II is obtained by an end notched flexure test. The experiment is performed using three types of non-woven tissues: 8 $g/m^2$ of carbon tissue, 10 $g/m^2$ of glass tissue, and 8 $g/m^2$ of polyester tissue. On the basis of the specimen with no non-woven tissue, interlaminar fracture toughness on mode II at specimens inserted with non-woven carbon and glass tissues and polyester tissues increases as much as 166.5% and 137.1% and 157.4% respectively. The results show that mode II interlaminar fracture toughness of CFRP laminates inserted with nonwoven tissues increased due to the fiber bridging, fiber breakage, and hackle etc. by SEM analysis.

• Journal of the Korean Ceramic Society
• /
• v.26 no.5
• /
• pp.645-654
• /
• 1989

Specimens of WC-Co were indented to measure the resulting crack size and unindented samples were fractured in 3-point flexure to obtain the strength and to measure characteristic features on the fracture surface. Fracture toughness was determined using fractography and compared to those determined using identation techniques. We show that principles of fracture mechanics can be applied WC-Co composites and can be used to analyze the fracture process. The fracture surfaces were examined by scanning electron microscopy and optical microscopy. Characteristic feature observed in glasses, single crystals and polycrystalline materials known as mirror, mist, hackle, and crack branching were identified for these composites. We discuss the importance of fracture surface analysis in determining the failure-initiating sources and the failure behaviorof WC-Co composites.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.20 no.11
• /
• pp.3433-3440
• /
• 1996

This paper was investigation of the stres corrosion cracking(SCC) mechanism and the properties of corrosion fracture surface of glass fiber reinforced plastics(GFRP) produced by hand lay up(HLU) method in synthetic sea water. Test material is GFRP, that was used vinylester type epoxy acrylate resin and an unsaturated polyester as the matrix and the chopped strand mat(CSM) type E-glss fiber as the reinforcement. The slow strain rate test(SSRT) was performed on dry, wet and saturated wet specimens in sea water. Here the pH concentration of synthetic sea water was 8.2 and the strain rate is 1 x $10^{-6}$($sec^{-1}$) and test temperature ranges varied from $-60^{\circ}C$ to $80^{\circ}C$. It could be confirmed the fact that wet specimens tested at a particular test temperature ranges were appeared the eviences of SCC such as con-planar, mirror and hackle zone. Moreover, SCC of GFRP in sea water was characterised by falt fracture surfaces with only small amounts of fiber pull-out, in partial.

• Korean Journal of Veterinary Research
• /
• v.48 no.2
• /
• pp.161-165
• /
• 2008

Many neurotoxigenic clostridia are found in soil. Among animals, birds are especially susceptible to botulism, perhaps because they feed on insects, invertebrate carcasses, and decayed feeds contaminated with spores of Clostridium (C.) botulinum. C. botulinum type C is mainly involved in avian botulism. In the summer of 2005, death of a mute swan (cygnus olor) living in the pond of large bird cage was found in Seoul Grand Park Zoo. The birds presented presumptive clinical signs of botulism, such as ruffled hackle feathers, abnormal posture of the head, weakness, and flaccid paralysis. At that time, pond water in the breeding facilities was drained for 7 days, but there were still remained water containing sediment of feed and feces. Therefore, botulism was suspected and an experimentation were made to detect C. botulinum in the dead mute swan. Gross post-mortem findings of a mute swan showed jelly-like hemorrhagic contents in the intestine, sands and vegetations in the stomach. C. botulinum was isolated from the liver, small intestine and large intestine samples. Botulism was also confirmed by mouse inoculation test with the organ samples. With PCR, a gene encoding C. botulinum type C toxin was detected for the several organs of the mute swan died. These results suggested that death of mute swan was caused by C. botulinum type C.

• Korean Journal of Materials Research
• /
• v.14 no.5
• /
• pp.322-327
• /
• 2004

Copper-based leadframe sheets were oxidized in two kinds of hot alkaline solutions to form brown-oxide or black-oxide layer on the surface. The oxide coated leadframe sheets were molded with epoxy molding compound (EMC). After post mold curing, the oxide-coated EMC-leadframe joints were machined to form sandwiched Brazil-nut (SBN) specimens. The SBN specimens were used to measure the fracture toughness of the EMC/leadframe interfaces under mixed-mode (mode I + mode II) loading conditions. Fracture surfaces were analyzed by various equipment to investigate failure path. The results revealed that the failure paths were strongly dependent on the oxide type. In case of brown oxide, hackle-type failure was observed and failure path lay near the EMC/CuO interface with a little inclining to CuO at all case. On the other hand, in case of black oxide, quite different failure path was observed with respect to the distance from the tip of pre-crack and phase angle. Different failures occurred with oxide type is presumed to be due to the difference in microstructure of the oxides.

• Journal of Biomedical Engineering Research
• /
• v.19 no.5
• /
• pp.433-441
• /
• 1998

This study was performed to evaluate the effects of surface flaw on the fracture of all-ceramic materials. A feldspathic porce lain of VMK68, a cashable ceramic of IPS-Empress, and an alumina-glass composite of In-Ceram were used. Specimens were prepared as 12$\times$3$\times$1mm in dimensions, and a Vickers-produced indentation crack was made at the center of the tensile surface. Test specimens were immersed in dlstilled water and In oil, which were broken under a crosshead speed of 0.05 mm/min by 3-point bend test at 37$^{\circ}C$. The characteristic patterns of Vickers indentation and fracture surfaces were examined by an optical microscope and a scanning electron microscope. The fracture surfaces of the VMK68 and the IPS-Empress showed a median crack pattern at the fracture origin and indicated a tendency to cleavage hackle. The fracture surface of the alumina-glass composite, In-Ceram, showed a Palmqvist crack pattern at the fracture origin and indicated a tendency of toughening by the frictional Interlocking between the microstructurally rough fracture surfaces.