• Journal of the Korean Ceramic Society
• /
• v.42 no.1
• /
• pp.37-42
• /
• 2005

Lightweight aggregate was made using glass abrasive sludge and graphite in this study. This study tried to draw the correlation between lightweight aggregate's properties and internal pore. The precursor was made by added different graphite contents and was burned for 20 min. at $700^{circ}C$ and $800^{circ}C$. The volume change of aggregate was checked at before and after homing, and confirmed that the homing temperature effected more than expanding agent on volume change. The size and area of pore in aggregate increased according to the amount of expanding agent and homing temperature but it didn't bring about big effect above $1\%$ of expanding agent. The absorbtion ratio, thermal conductivity and porosity have a high correlation, so each coefficient of correlation showed above $0.8\pm$.

• Restorative Dentistry and Endodontics
• /
• v.35 no.5
• /
• pp.344-352
• /
• 2010

Objectives: The purpose of this study was to determine the setting time, compressive strength, solubility, and pH of mineral trioxide aggregate (MTA) mixed with glass ionomer cement (GIC) and to compare these properties with those of MTA, GIC, IRM, and SuperEBA. Materials and Methods: Setting time, compressive strength, and solubility were determined according to the ISO 9917 or 6876 method. The pH of the test materials was determined using a pH meter with specified electrode for solid specimen. Results: The setting time of MTA mixed with GIC was significantly shorter than that of MTA. Compressive strength of MTA mixed with GIC was significantly lower than that of other materials at all time points for 7 days. Solubility of 1 : 1 and 2 : 1 specimen from MTA mixed with GIC was significantly higher than that of other materials. Solubility of 1 : 2 specimen was similar to that of MTA. The pH of MTA mixed with GIC was 2-4 immediately after mixing and increased to 5-7 after 1 day. Conclusions: The setting time of MTA mixed with GIC was improved compared with MTA. However, other properties such as compressive strength and pH proved to be inferior to those of MTA. To be clinically feasible, further investigation is necessary to find the proper mixing ratio in order to improve the drawbacks of MTA without impairing the pre-existing advantages and to assess the biocompatibility.

• Restorative Dentistry and Endodontics
• /
• v.35 no.5
• /
• pp.359-367
• /
• 2010

Objectives: The purpose of the present in vitro study was to evaluate the biocompatibility of mineral trioxide aggregate (MTA) mixed with glass ionomer cement (GIC), and to compare it with that of MTA, GIC, IRM and SuperEBA. Materials and Methods: Experimental groups were divided into 3 groups such as 1 : 1, 2 : 1, and 1 : 2 groups depending on the mixing ratios of MTA powder and GIC powder. Instead of distilled water, GIC liquid was mixed with the powder. This study was carried out using MG-63 cells derived from human osteosarcoma. They were incubated for 1 day on the surfaces of disc samples and examined by scanning electron microscopy. To evaluate the cytotoxicity of test materials quantitatively, XTT assay was used. The cells were exposed to the extracts and incubated. Cell viability was recorded by measuring the optical density of each test well in reference to controls. Results: The SEM revealed that elongated, dense, and almost confluent cells were observed in the cultures of MTA mixed with GIC, MTA and GIC. On the contrary, cells on the surface of IRM or SuperEBA were round in shape. In XTT assay, cell viability of MTA mixed with GIC group was similar to that of MTA or GIC at all time points. IRM and SuperEBA showed significantly lower cell viability than other groups at all time points (p < 0.05). Conclusions: In this research MTA mixed with GIC showed similar cellular responses as MTA and GIC. It suggests that MTA mixed with GIC has good biocompatibility like MTA and GIC.

• Journal of Power System Engineering
• /
• v.17 no.2
• /
• pp.108-113
• /
• 2013

In this study, lightweight aggregate was made from basalt stone powder sludge. Clay and glass powder were respectively added from 0 to 20 wt% and from 0 to 100 wt%. The glass powder helped to form glassy phase which trapped generating gas in the materials. $CaCO_3$ helping bloating process was added from 0 to 10 wt%. It was possible to produce lightweight aggregate at range from $1150^{\circ}C$ to $1200^{\circ}C$. The specimen was heated in furnace at 1100, 1150 and $1200^{\circ}C$ for 15 min, respectively, to sinter aggregates. Chemical composition of materials were determined, and characteristics were analyzed, including specific gravity, water absorption. Lightweight aggregate which was heated at $1200^{\circ}C$ had specific gravity of $0.53g/cm^3$, water absorption of 3.08%, and this value satisfied KS L 8551 standard.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.23 no.2
• /
• pp.20-27
• /
• 2019

Compared to the development and manufacturing technology of electronic goods, the development of waste glass recycling technology is relatively insufficient, leading to the acceleration of waste of resources and environmental pollution. Although waste glass recycling technology is being actively developed overseas, waste glass recycling technology is insufficient in Korea, leading to the illegal dumping or burial of waste glass. Waste glass has been confirmed to have pozzolan reaction potential when having hydration reaction with cement. Waste glass is also reported to be effective in reducing bleeding and inhibiting the development of hydration heat by improving the physical properties of concrete and the rheology properties of fresh concrete. Therefore, this paper analyzed the strength characteristics and the effect of alkalic-silica reaction on the expansion of shielding concrete that used waste glass as fine aggregate. Where, suitable admixture materials were used as a measure to suppress the expansion.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.23 no.1
• /
• pp.163-170
• /
• 2019

In recent years, various types of industrial wastes are rapidly increasing with the development of high-tech industries. Specially, high-density waste glass of CRT TV containing heavy metals are buried or disposed of due to reprocessing costs and environmental pollution problems. Thus, more basic research is needed to recycle waste such as CRT waste glass such. In this study, the fundamental properties and radiation shielding performance of mortar specimens substituted CRT waste glass as a fine aggregate were analyzed and their application to shielding materials was evaluated. According to the results, the bulk density of mortar specimen replaced with CRT waste glass was increased and the compressive strength and flexural strength were decreased. Meanwhile, the CRT waste glass substitute specimen containing a large amount of lead component showed a higher shielding performance than the general mortar specimen. Especially, the linear attenuation coefficient of CRT waste glass in $122KeV{\cdot}^{57}Co$ of the low energy field was 2.5 times higher than that of normal specimen.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2000.10a
• /
• pp.138-143
• /
• 2000

In this paper, we carried out experiment to use crushed waste glass as a fine aggregate. This study delt with the comparative analysis on the construction works and engineering properties of concrete containing crushed waste glass through physical experiment. The experimental variables are crushed waste glass substitution ratio and W/C(38, 53%). When the W/C was 38%, we could know that concrete containing crushed waste glass was good as general concrete on the construction works and engineering properties but the concrete containing crushed waste glass applied W/C 53% was not good as general concrete on those. Therefore, concrete containing crushed waste glass applied W/C 53% should use admixture on the site.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.10 no.1
• /
• pp.74-79
• /
• 2022

In this study, the effect of a sudden decrease in internal humidity and a decrease in hydration level due to the tight internal structure of high-strength concrete and cement composites was investigated. To verify the change in the internal Si hydration, waste glass foam beads were used as a lightweight aggregate, and the internal unreacted hydrate reduction and hydrate formation tendency were identified over the mid- to long-term. Waste glass foam beads were mixed with 5, 10, and 20 %, and were used by pre-wetting. As the mixing rate of the waste glass foamed beads increased, the strength showed a tendency to decrease. In addition, when the mixing amount of pre-wetted waste glass foam beads increases inside through XRD analysis, TGA analysis, and Si NMR analysis, it is judged that the hydration degree of internal Si is different because moisture is supplied to the paste.

• Magazine of the Korean Society of Agricultural Engineers
• /
• v.41 no.6
• /
• pp.90-96
• /
• 1999

Over 4.1 billion metric tons of non-hazardous solid wstes are generated in the United States annually. Therefore, there is a need to reuse or reprocess as many products or by-products as possible. In this report, theaggregates produced from Naval Shipyard and Charleston area dredge spoils are designated as GP-21-23 and GP 4-5, repectively. The major objective of this study is to determine the feasiblity of the use of these aggregates in concrete. The followings are some of the conclusions, observations and recommendations regarding this portion of the research project. In most cases, the unit weight of concrete containing GP 21-23 and GP 4-5 (vitrified galss) lower than the control concrete, and the concrete containing vitrified glass produced lower compressive and bending strength compared to the control. However the concrete containing virtrified glass could be used in the field based on the minimum criterial set for the mix design. The use of vitrified glass in concrete is recommended in several applications except parking lots, side walks and main roads, because abrasion resistace is not high.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2015.05a
• /
• pp.160-161
• /
• 2015

Borosilicate glass can be used for improving neutron shielding of concrete. The well known expansion of borosilicate glass caused by expansion of mortar bar was can cause serious damage to the concrete. In this research, borosilicate glass was powdered to reduce the particle size similar to that of cement, and 20% cement replacement set was reduced expansion rate about 30%. But aggregate replacement set was damaged because of Alkali-Silica Reaction expansion.