• Proceedings of the KIEE Conference
• /
• 1990.11a
• /
• pp.143-149
• /
• 1990

A sol-gel processing of $YBa_2Cu_3O_{7-x}$ superconductor using metal nitrate salts and sodium hydroxide as the starting materials has been investigated because of the need to produce pure, hompgeneous superconducting materials. Since the precipitation of barium hydroxides can be obtained only at high basicities, the process has to be carried out Ca. pH 13 to get the simultaneous coprecipitation with the other metal hydroxides. The involved reaction mechanisms were investigated and intermediate and final products were characterized by means of thermogravimetric analysis(TGA), infra-red(IR) spectroscopy, X-ray diffraction(XRD) analysis, scanning electron microscopy(SEM), thermal mechanical analysis(TMA) and electrical measurement.

• Korean Journal of Materials Research
• /
• v.6 no.5
• /
• pp.449-456
• /
• 1996

BaO, SrCI2.6H2O 그리고 Ti(OPri)4를 출발 원료로 사용하여 균일한 BaxSr1-xTiO3(BST) 솔을 합성하였고, BST 박막을 회전 코팅 법으로 Si 및 Pt/Ti/SiO2/Si 기판위에 제조하였다. 적외선 및 NMR 스펙트럼 분석으로 킬레이션 조제로 사용한 acetylacetone(AcAc)이 엔올 형태로 Ti-알콕사이드와 결합하여 솔 안정화에 기여함을 확인하였다. Xedrogel에 대한 DT/TGA 및 적외선 스펙트럼 결과로부터 페로브스카이트 상생성이 $600^{\circ}C$ 이상에서 이루어짐을 관찰하였다. $700^{\circ}C$에서 열처리한 박마은 -300(10 KHz)의 상대유전율을 나타내었고, 결정립의 저항 및 입계의 병렬 RC 성분으로 등가회로를 구성할 수 있었다.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2003.03a
• /
• pp.178-178
• /
• 2003

II-Ⅵ족 반도체 중에서 넓은 밴드갭을 가지는 ZnO에 Mn 이온을 doping할 경우 Tc가 상온보다 높을 것이라는 이론적 계산이 2000년 Science에 발표되었다. 이후 ZnO에 전이금속 이온을 doping하여 상온에서도 강자성을 나타내는 자성 반도체 (DMS)를 만들기 위한 연구가 활발히 진행되고 있다. Co-doped ZnO 박막은 PLD로 증착하였을 경우 Tc가 상온보다 높으나 재현성이 낮은 것으로 알려져 있었다. 그러나 최근 sol-gel 방법을 이용하여 Co-doped ZnO 박막을 제조하면 강자기 특성의 재현성을 높일 수 있다는 결과가 보고되었다. 이에 본 연구에서는 sol-gel 방법을 사용하여 여러 조성의 Co-doped ZnO 박막을 합성한 후 이들의 자성 특성을 검토하였다. 이러한 결과를 바탕으로 Co-doped ZnO 박막에서 강자성 발현의 근원을 규명하고자 (ⅰ) 조성에 따른 Co-doped ZnO의 Raman peak과 EXAFS peak의 변화를 측정하여 구조적 특성과 ZnO 내에서의 Co 이온의 상태를 분석하였으며, (ⅱ) Hall 효과 실험으로 carrier density를 측정함으로써 Fermi 준위에서의 파수 벡터의 크기를 산출하고자 하였다.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.07a
• /
• pp.753-756
• /
• 2001

This research made a study of MnO$_2$electrode for supercapacitor with a diffuser (Polyvinyl alcohol). Manganese dioxide was used as active material. We tried to increase specific surface area by adding PVA. Manganese dioxide was synthesized by a sol-gel method using fumaric acid and oxalic acid in low temperature with high yield. Therefore, We prepared Manganese dioxide powder. This powder was used by active materials. The electrode was made by a mixture of active material, ketjen-black which is a large specific surface area, and PVdF-co-HFP as binder agent with using Nickel mesh as current collector. Here we reported on the synthesis and electrochemical performance of a enhanced material. All active materials have been submitted to X-ray diffraction and Scanning electron microscopy.

• Journal of the Korean Ceramic Society
• /
• v.55 no.2
• /
• pp.174-177
• /
• 2018

ZnO/Ag/ZnO multilayers were fabricated and their optical properties were investigated in terms of the micro-cavity effect in electroluminescent devices based on colloidal quantum dots. The top and bottom ZnO layers were formed by a sol-gel method while the middle Ag layer was deposited by thermal evaporation. After the fabrication of the ZnO/Ag/ZnO structure, the transmittance increased to 74%. When the oxide/metal/oxide multilayers were applied to quantum dot light-emitting diodes, the color purity was enhanced due to the narrower full width at half maximum.

• Transactions on Electrical and Electronic Materials
• /
• v.11 no.5
• /
• pp.212-215
• /
• 2010

$BiFeO_3/Pb(Zr_{0.95}Ti_{0.05})O_3$ (BFO/PZT) heterolayered thin films were fabricated by the spin coating method on a Pt/Ti/$SiO_2$/Si substrate using metal alkoxide solutions. The coating and heating procedure was repeated 6 times to form the heterolayered films. The thickness of the BFO/PZT films after one cycle of drying/sintering is about 30-40 nm. All BFO/PZT films show a void free uniform grain structure without the presence of rosette structures. It can be assumed that the crystal growth of the upper BFO layers can be influenced by the lower PZT layers. As the number of coatings increased, the dielectric constant increased, so that the value for the 6-layer film was 1360 at 1 KHz.

• Journal of Surface Science and Engineering
• /
• v.41 no.4
• /
• pp.169-173
• /
• 2008

The objective of this study is to coat the $SiO_2$ layer uniformly on the ZnS:Cu phosphors by using Sol-Gel method. From results of SEM micrographs observation, XRD and XPS analysis, it could be confirmed that $SiO_2$ layer was relatively well coated on ZnS:Cu particles. $Ag_2S$ was used as a decoding chemical to analyze the dense and uniform coating performance of $SiO_2$ layer on phosphor particles. It could be concluded that phosphors synthesized from our two step replacement method showed strong blue peak comparing to other method and rather weak green peak also. Obtained particle size of phosphors were about 20m diameter. Luminescence properties of the phosphors were examined by photoluminescence spectra at the excitation wavelength of 270 nm.

• Textile Coloration and Finishing
• /
• v.19 no.2
• /
• pp.7-13
• /
• 2007

Photopolymerization of 2-hydroxyethyl methacrylate(HEMA), in the presence of ethyleneglycol dimethacrylate(EGDMA) and 1-Hydroxycyclohexyl phenyl ketone as crosslinker and photoinitiator, respectively, produced crosslinked poly-HEMA hydrogels. The hydrogels were colored by the exhaustion of vinylsul-phone-type reactive dyes. Good colorfastness to laundering was achieved when colored with C.I. Reactive Black 5. We investigated that the effect of coloration on the hydrophilicity and swelling properties of the films. More hydrophilic gel-surfaces were generated with in increase in coloration and crosslinking. Higher surface energy was observed with higher crosslinking level. The more rapid and higher water swellability of poly-HEMA gels after coloration may be resulted from a more opened gel structure by the easier hydration of the hydrophilic sulphonic acid groups of the reacted dyes in water.

• Proceedings of the Korean Society Of Semiconductor Equipment Technology
• /
• 2006.05a
• /
• pp.194-197
• /
• 2006

Lead-free bismuth-layered perovskite ferroelectric europium-substituted $Bi_{4}Ti_{3}O_{12}(BTO)$ thin films have been successfully deposited on Pt/Ti/$SiO_2$/Si substrate by a sol-gel spin-coating process. $Bi(TMHD)_3,\;Eu(THMD)_3,\;Ti(OiPr)_4$ were used as the precursors, which were dissolved in 2-methoxyethanol. The thin films were annealed at various temperatures from $600^{\circ}\;to\;720^{\circ}C$ in oxygen ambient for 1 hr, which was followed by post-annealed for 1 hr after depositing a Pt electrode to enhance the electrical properties. X-ray diffraction (XRD) and scanning electron microscopy (SEM) were used to analyze the crystallinity and surface morphology of layered perovskite phase, respectively. The remanent polarization value of the BET thin films annealed at $720^{\circ}C\;was\;25.95{\mu}C/cm^2$ at an applied voltage of 5 V.

• Korean Journal of Materials Research
• /
• v.9 no.11
• /
• pp.1069-1074
• /
• 1999

본 연구에서는 PbZr(sub)0.53Ti(sub)0.47O$_3$(PZT) 박막을 복수 도포함에 따른 박막내의 응력을 온도의 함수로 실시간(in situ) 측정하였으며, 응력발생의 원인에 박막의 건조, 열분해(pyrolysis), 치밀화 및 결정화 현상과 연관시켜 설명하였다. 도포직후 단층박막에 생성된 55MPa의 인장응력은 가열됨에 따라$ 300^{\circ}C$-$350^{\circ}C$에서 최대 145MPa로 증가하였으며, 박막내의 응력은 모든 온도구간에서 항상 인장응력을 나타내었더. 다층도포시 $650^{\circ}C$까지 열처리 주기를 완료한 층이 두꺼워질수록 새로 도포한 층의 영향은 점차 감소하였으며, 9층박막에 이르러서는 가열과 냉각에 따라 응력이 동일하게 변화하였다. 응력측정 결과 다층박막의 치밀화는 $350^{\circ}C$에서 시작되어 $520^{\circ}C$-$550^{\circ}C$ 부근에서 완료되는 것으로 나타났으며 치밀화가 시작하는 온도는 미세경도 측정결과와 일치하였다. $PbTiO_3$(PT)와 달리 PZT 다층박막은 Si 기판 위에서 perovskite로의 결정화가 일어나지 않았다.