• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.15 no.12
• /
• pp.1033-1038
• /
• 2002

In this study, urethane acrylate macromer was synthesized and it was used in a gel polymer electrolyte (GPE), and then its electrochemical performances were evaluated. LiCoO$_2$/GPE/graphite cells were Prepared and their performances depending on discharge currents and temperatures were evaluated. The precursor consisting of urethane acrylate (UA), hexanediol dimethacrylate (HDDA) and benzoyl peroxide (BPO) had a low viscosity relatively ionic conductivity of the gel polymer electrolyte with UA at room temperature and -20$\^{C}$ was ca. 4.5 $\times$ 10$\^$-3/S$.$cm$\^$-1/ and 1.7 x 10$\^$-3/ S$.$cm$\^$-1/, respectively GPR was stable electrochemically up to potential of 4.i V vs. Li/Li$\^$+/. LiCoO$_2$/GPE/graphite cells showed good a high-rate and a low-temperature performance.

• Journal of the Korean Electrochemical Society
• /
• v.5 no.4
• /
• pp.197-201
• /
• 2002

In this study, a gel polymer electrolyte was prepared from urethane acrylate and its electrochemical performances were evaluated. And, $LiCoO_2/GPE/graphite$ cells were prepared and their performances depending on discharge currents and temperatures were evaluated. The precursor containing $5 vol\%$ curable mixture had a low viscosity relatively. Ionic conductivity of the gel polymer electrolyte at room temperature and $-20^{\circ}C$ was ca. $5.9\times10^{-3}S{\cdot}cm^{-1}\;and\;1.7\times10^{-3}S{\cdot}cm^{-1}$, respectively. GPE showed electrochemical stability up to potential of 4.5V vs. $Li/Li^+.LiCoO_2/GPE/graphite$ cell showed a good high-rate and a low-temperature performance.

• Journal of the Korean Electrochemical Society
• /
• v.12 no.3
• /
• pp.251-257
• /
• 2009

In this study, we fabricated nickel oxide thin film for lithium based electrolyte using sol-gel method. This film was deposited by dip-coating method with mixed solvent of DameH (N,N-dimethylaminoethanol) and DI water. As changing the ratio between DmaeH and DI water, nickel oxide thin film was presented in different charge density and optical transmittance because they were shown various thickness. It was accounted for changing viscosity and density by the ratio of DmaeH and DI water. The thin film synthesized with 1 : 1 ratio of DmaeH and DI water was expressed best electrochromic performance in lithium based electrolyte, because of thick thickness but porous structures.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.16 no.11
• /
• pp.994-1000
• /
• 2003

In this study, gel polymer electrolytes (GPE) with semi-interpenerating network of poly (methyl methacrylate) and hexanediol dimethacrylate were synthesized and their electrochemical performances were evaluated. LiCoO$_2$/GPE/graphite cells were prepared and their performances depending on discharge currents and temperatures were evaluated. The precursor containing 5 vol% curable mixture had a low viscosity relatively. GPE showed good electrochemical stability up to potential of 4.8 V vs. Li/Li$\^$+/. Ionic conductivity of the gel polymer electrolyte at room temperature and -20$^{\circ}C$ was ca. 5.9 and 1.4${\times}$10$\^$-3/ Scm$\^$-1/, respectively. LiCoO$_2$/GPE/graphite cells showed good rate capability, low-temperature performance and cycleability.

• Bulletin of the Korean Chemical Society
• /
• v.30 no.2
• /
• pp.319-322
• /
• 2009

Gel polymer electrolytes were prepared by immersing a porous poly(vinylidene fluoride-co-hexafluoropropylene) membrane in an electrolyte solution containing small amounts of polymerizable additive (3,4-ethylenedioxythiophene, thiophene, biphenyl). The organic additives were electrochemically oxidized to form conductive polymer films on the electrode at high potential. With the gel polymer electrolytes containing different organic additive, lithium-ion polymer cells composed of carbon anode and LiCo$O_2$ cathode were assembled and their cycling performances were evaluated. Adding small amounts of thiophene or 3,4-ethylenedioxythiophene to the gel polymer electrolyte was found to reduce the charge transfer resistance in the cell and it thus exhibited less capacity fading and better high rate performance.

• Journal of the Korean Electrochemical Society
• /
• v.6 no.2
• /
• pp.98-102
• /
• 2003

Urethane acrylate oligomer was synthesized and used in a gel polymer electrolyte (GPE) and then its electrochemical performances were evaluated. $LiCoO_2/GPE/graphite$ cells were prepared and their performances depending on discharge currents and temperatures were evaluated. The precursor containing $5 vol\%$ curable mixture had a low viscosity relatively. ionic conductivity of the gel polymer electrolyte at room temperature and $-20^{\circ}C$ was ca. $5.9\times10^{-3}S{\cdot}cm^{-1}\;and\;1.4times10^{-3}S{\cdot}cm^{-1}$, respectively. GPE showed good electrochemical stability up to potential of 4.5V vs. RLi/Li^+.\;LiCoO_2/GPE/graphite$ cell showed a good high-rate and low-temperature performance.

• Journal of Electrochemical Science and Technology
• /
• v.8 no.3
• /
• pp.257-264
• /
• 2017

A polymeric ionic liquid, poly(1-methyl 3-(2-acryloyloxypropyl) imidazolium iodide) (PMAPII), was synthesized as a single-iodide-ion-conducting polymer and employed in a gel polymer electrolyte. Gel polymer electrolytes prepared from iodine, 4-tert-butylpyridine, ${\gamma}$-butyrolactone, and PMAPII were applied in quasi-solid-state dye-sensitized solar cells (DSSCs). The addition of 16 wt.% PMAPII provided the most favorable environment, striking a compromise between the iodide ion concentration and the ionic mobility, which resulted in the highest conversion efficiency of the resulting DSSCs. The quasi-solid-state DSSC assembled with the optimized gel polymer electrolyte exhibited a relatively high conversion efficiency of 7.67% under AM 1.5 illumination at $100mA\;cm^{-2}$ and better stability than that of the DSSC with a liquid electrolyte.

• Polymer(Korea)
• /
• v.33 no.6
• /
• pp.544-550
• /
• 2009

In this study, we have designed [Epoxy/PEG] polymer gel electrolyte systems by thermal curing the mixtures of epoxy, PEG, imidazole catalyst, and a plasticizer of 1:1 ethylene carbonate and propylene carbonate in the presence of $LiPF_6$ salt. In order to enhance the poor mechanical property of the Corresponding [Epoxy/PEG] gel electrolyte PVdF-HFP was incorporated into the system. The ionic conductivities of the polymer gel electrolytes were related to the amount of PVdF-HFP in blends as well as the amount of liquid electrolyte. The optimized gel system showed room-temperature conductivities of $2.56\times10^{-3}S/cm$.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.18 no.1
• /
• pp.68-74
• /
• 2005

In this work, polymerization conditions of the gel polymer electrolyte (GPE) were studied to obtain better electrochemical performances in a lithium-ion polymer battery. When the polymerization temperature and time of the GPE were 70$^{\circ}C$ and 70 min, respectively, the lithium polymer battery showed excellent a rate capability and cycleability. The TMPETA (trimethylolpropane ethoxylate triacrylate)/TEGDMA (triethylene glycol dimethacrylate)-based cells prepared under optimized polymerization conditions showed excellent rate capability and low-temperature performances: The discharge capacity of cells at 2 Crate showed 92.1 % against 0.2C rate. The cell at -20 $^{\circ}C$ also delivered 82.4 % of the discharge capacity at room temperature.

• Macromolecular Research
• /
• v.16 no.2
• /
• pp.134-138
• /
• 2008

A novel acrylol borate was designed and synthesized by reacting acrylate monomer and boric acid. The obtained acrylol borate was used as both gelator and anion receptor for the liquid electrolyte in a lithium secondary battery. It was found that the ionic conductivity of the gel polymer electrolyte (GPE) was as high as that of the liquid electrolyte, and the thermal stability of GPE was increased when only 2 wt% acrylol borate was incorporated into the liquid electrolyte. These results suggest that acrylol borate can be used as an effective additive to enhance the thermal stability of the electrolyte without adversely affecting its conductivity. It is believed that the strong complex formation between boron in the gelator and the anion of the salt is responsible for the enhanced thermal stability of the electrolyte solution and the increased ionic conductivity.