The flow accelerated galvanic corrosion characteristics of a carbon steel coupled to stainless steel were investigated in deaerated alkaline-chloride solutions as a function of flow velocities(0, 0.2, 0.4 and 0.6 m/s), pH(8, 9, and 10) and temperature(25, 50 and $75^{\circ}C$). The electrochemical properties of specimens were investigated by potentiodynamic test and galvanic corrosion test using RCE(Rotating Cylinder Electrode). Carbon steel did not show passive behavior in the alkaline-chloride solution. The galvanic current density increases with increasing flow velocity and temperature, but decreased with increasing pH. Flow velocity had a small effect on the galvanic current density at $25^{\circ}C$, whereas the flow velocity increased galvanic current density significantly at $50^{\circ}C$ and $75^{\circ}C$. This might be due to the increased solubility of magnetite at the higher temperature.

• Journal of Advanced Marine Engineering and Technology
• /
• v.26 no.1
• /
• pp.99-107
• /
• 2002

Recently all kinds of structural materials are subjected to the severe corrosive environment. Especially corrosion problems of heat exchanger such as galvanic corrosion, erosion and cavitation raised by both contaminated solution and high velocity of fluid to increase cooling effect of heat exchanger have been frequently reported in these days. In this study two kinds of sheet materials and five kinds of tube materials are used for galvanic corrosion characteristics and their corrosion current density calculation. The tube materials having the most galvanic corrosion resistance between tube and sheet of heat exchanger were Al Brass(68700) and Al Brass(C6872TS) and although Ti tube predominantly indicated the highest individual corrosion resistance among those five tube materials. it appeared that Ti tube can be allowed as sheet materials to get galvanic corrosion easily. However it is considered that Cu-Ni tube materials is not only easy to produce galvanic corrosion significantly between tube and sheet regardless of kinds of sheet materials but also is appeared considerably its own high corrosion current density

• Corrosion Science and Technology
• /
• v.8 no.1
• /
• pp.27-39
• /
• 2009

Non metallic composite materials, for example, GECM(graphite epoxy composite material) show high specific strength because of low density. These kinds of non metallic composite materials improved the structural effectiveness and operation economics. However, if these materials contacted several metals, corrosion can be arisen since non metallic composite materials have electrical conductivity. This paper dealt with galvanic corrosion between graphite epoxy composite material and several metals. Base on the electrochemical galvanic corrosion test between GECM and metals, corrosion current of carbon steel and aluminium increased with time but corrosion current of stainless steels and titanium decreased and galvanic potential increased. This behavior shows the galvanic corrosion depends upon the presence of passive film. Also, galvanic effect of GECM coupled with ferrous alloys and non-ferrous alloys was lower than that of 100% graphite, which is attributed to lower exposed area of graphite fiber in the GECM than apparent area of the GECM specimen used for the calculation of galvanic current in this work.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2012.05a
• /
• pp.280-280
• /
• 2012

Mg의 첨가한 Zn-Mg-Al 합금도금강판에 형성된 $Zn-MgZn_2$ 공정조직의 부식거동을 이해하고자 진공 고주파 용해로 $MgZn_2$ 제작한 후 Zn와 galvanic coupling하여 $MgZn_2$합금과 Zn간의 galvanic corrosion 거동을 알아보았다. $MgZn_2-Zn$ galvanic coupling의 SVET 결과에서 $MgZn_2$가 anode, Zn가 cathode가 됨을 확인되었다. $MgZn_2$의 Zn와의 galvanic corrosion 평가에서 galvanic current는 Zn 보다 낮은 potential에서 anodic current density를 나타내었으며, galvanic potential은 $MgZn_2$전위로부터 두 합금의 혼합전위를 향해 증가함을 알 수 있었다. Zn-Mg-Al 합금도금강판의 염수분무 평가에서도 초기 $Zn-MgZn_2$ 공정조직에서 $MgZn_2$가 용출되는 것이 관찰되었다.

• Corrosion Science and Technology
• /
• v.16 no.3
• /
• pp.128-140
• /
• 2017

Aluminum alloy matrix may be used for manufacturing lighter automobiles. However, galvanic corrosion may occur between the rivet joint combining aluminum alloy matrix and a CFRP (carbon fiber reinforced plastic) laminate. The possibility of galvanic corrosion may be investigated by measuring galvanic couple currents. Two types of galvanic current measuring methods were used. One method is to use potentiodynamic polarization curves and the other is the ZRA (zero resistance ammeter) method. For galvanic corrosion experiments graphite, a major component of CFRP, was used with carbon steel (rivets) and 6061 aluminum alloys. Regardless of carbon steel, Ni deposited carbon steel, and 316L stainless steels we also investigated the possibility of reduction in galvanic corrosion. Results revealed that even though Ni deposited carbon steel or 316L stainless rivet may slightly increase galvanic current density between those and Al matrix, substitute rivets for carbon steel may be considerably useful for reducing overall galvanic corrosion.

• Corrosion Science and Technology
• /
• v.7 no.2
• /
• pp.134-137
• /
• 2008

Cold arc welding of cast iron has been widely used with repair welding of metal structures. However its welding is often resulted in the galvanic corrosion between weld metal zone and heat affected zone(HAZ) due to increasing of hardness. In this study, corrosion properties such as hardness, corrosion potential, surface microstructures, and variation of corrosion current density of welding zone with parameters of used electrodes for cast iron welding were investigated with an electrochemical evaluation. Hardness of HAZ showed the highest value compared to other welding zone regardless of kinds of used electrodes for cast iron welding. And its corrosion potential was also shifted to more negative direction than other welding zone. In addition, corrosion current density of WM in polarization curves was qualitatively smaller than that of HAZ. Therefore galvanic corrosion may be apparently observed at HAZ. However galvanic corrosion may be somewhat controlled by using an optimum welding electrode.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2017.05a
• /
• pp.151.1-151.1
• /
• 2017

This work studied the corrosion behavior of AZ31 Mg alloy galvanically coupled with Cu during immersion in 0.1 and 0.5 M NaCl solutions by in-situ observation and galvanic corrosion current measurement using a zero resistance ammeter. The corrosion behavior of AZ31 Mg alloy was also studied by salt spray test. The average galvanic corrosion density during 2 h immersion in 0.1 NaCl solution was found to decrease as an exponential function with increasing the surface area ratios between AZ31:Cu or with increasing the distance between AZ31 and Cu. The corrosion of electrodeposited Cu on AZ31 Mg alloy was concentrated at the area next to Cu (about 5 mm for immersion test and 2 mm for salt spray test) and pitting corrosion was accelerated at the area beyond the severely corroded area by the galvanic coupling effect.

• Corrosion Science and Technology
• /
• v.22 no.5
• /
• pp.322-329
• /
• 2023

There are a variety of heat exchangers used in automobiles, such as shell and tube heat exchangers, double tube heat exchangers, and plate heat exchangers. Most of them are water-cooled to prevent engine overheating. There have been reports of corrosion damage to these heat exchangers due to continuous wetting caused by external temperature differences, road pollutants, and snow removal. In addition, galvanic corrosion, which occurs when two dissimilar materials come into contact, has been identified as a major cause. In this study, corrosion characteristics and galvanic corrosion behavior of Al alloy (AA3003, AA4045 and AA7072) used in automobile heat exchangers were analyzed. Effective clad materials for heat exchanger tubes and fins were also evaluated. It was found that AA7072 should be applied as the cladding material for fin AA3003 and that AA4045 was suitable as a cladding material for tube AA3003 because this clad materials application was the most effective clad design to delay the occurrence of pinhole in the tube. Main factors influencing galvanic corrosion dissolution were found to be galvanic corrosion potential difference and galvanic corrosion current density.

• Proceedings of the Korean Society of Marine Engineers Conference
• /
• 2001.05a
• /
• pp.152-157
• /
• 2001

This paper was studied on the characteristics of crevice corrosion prevention of SS 400 in marine environment. In NaCl solution, polarization behavior under the crevice corrosion was investigated. And Weight loss rate of SS 400 applied cathodic protection and non cathodic protection was measured according to the NaCl concentration. The main results obtained are as follows : The weight loss rate of Al-alloy galvanic anode was increased as the concentration of NaCl solution increased by 3.5% but the concentration increased over 3.5%, that of Al-alloy galvanic anode become decreased. The protective potential of SS 400 used Al-alloy galvanic anode becomes more cathodic polarization with increasing concentration of NaCl solution. Effects of oxygen on the weight loss rate of Al-alloy sacrificial anode for cathodic protection as the concentration of 3.5% NaCl solution become sensitive than that of 0% NaCl solution.

• The Journal of Korean Academy of Prosthodontics
• /
• v.31 no.3
• /
• pp.423-446
• /
• 1993

Titanium and its alloys are finding increasing use in medical devices and dental implants. The strong selling point of titanium is its resistance to the highly corrosive body fluids in which an implant must survive. This corrosion resistance is due to a tenacious passive oxide or film which exists on the metal's surface and renders it passive. Potentiodynamic polarization measurement is one of the most commonly used electro-chemical methods that have been applied to measure corrosion rates. And the potentiodynamic polarization test supplies detailed information such as open circuit, rupture, and passivation potential. Furthermore, it indicates the passive range and sensitivity to pitting corrosion. This study was designed to compare the corrosion resistance of the commonly used dental implant materials such as CP Ti, Ti-6A1-4V, Co-Cr-Mo alloy, and 316L stainless steel. And the effects of galvanic couples between titanium and the dental alloys were assessed for their useful-ness-as. materials for superstructure. The working electrode is the specimen , the reference electrode is a saturated calomel electrode (SCE), and the counter electrode is made of carbon. In $N_2-saturated$ 0.9% NaCl solutions, the potential scanning was performed starting from -800mV (SCE) and the scan rate was 1 mV/sec. At least three different polarization measurements were carried out for each material on separate specimen. The galvanic corrosion measurements were conducted in the zero-shunt ammeter with an implant supraconstruction surface ratio of 1:1. The contact current density was recorded over a 24-hour period. The results were as follows : 1. In potential-time curve, all specimens became increasingly more noble after immersion in the test solution and reached between -70mV and 50mV (SCE) respectively after 12 hours. 2. The Ti and Ti alloy in the saline solution were most resistant to corrosion. They showed the typical passive behavior which was exhibited over the entire experimental range. Therefore no breakdown potentials were observed. 3. Comparing the rupture potentials, Ti and Ti alloy had the high(:st value (because their break-down potentials were not observed in this study potential range ) followed by Co-Cr-Mo alloy and stainless steel (316L). So , the corrosion resistance of titanium was cecellent, Co-Cr-Mo alloy slightly inferior and stainless steel (316L) much less. 4. The contact current density sinks faster than any other galvanic couple in the case of Ti/gold alloy. 5. Ag-Pd alloy coupled with Ti yielded high current density in the early stage. Furthermore, Ti became anodic. 6. Ti/Ni-Cr alloy showed a relatively high galvanic current and a tendency to increase.