• Corrosion Science and Technology
• /
• v.14 no.5
• /
• pp.207-212
• /
• 2015

The purpose of this research was to synthesize fluorine modified waterborne polyurethane dispersion (F-WPU) by soap-free (internal emulsifier) emulsion polymerization techniques, to prepare coating solution based on fluorine modified waterborne polyurethane dispersion (F-WPU) and to compare the chemical and thermo-mechanical properties on the electrogalvanized steel sheet. Environmentally friendly F-WPU was prepared with a fluorinated polyol containing 60 wt% of fluorine. There are various ways of combining a wide variety of fluorinated polyols and diisocyanate to exhibit novel properties of waterborne polyurethane dispersion. Components of coating solution were largely divided into 4 kinds i.e., F-WPU, acrylic emulsion, silane coupling agent, and colloidal silicate. F-WPU coating solution on the electro-galvanized steel sheet showed excellent properties of corrosion resistance, alkali resistance and heat resistance, as compared to other coating solutions using a general waterborne resin. The F-WPU coating solution's reliable effects are possibly due to the fluorine atoms incorporated even in a small amount of F-WPU.

• Applied Chemistry for Engineering
• /
• v.10 no.6
• /
• pp.913-916
• /
• 1999

Fluorine modified diisocyanate(FMD) was synthesized from tris(6-isocyanatohexyl)isocyanurate(TIHI) and N-ethyl-N-2-hydroxyethyl-perfluorooctanesulfonamide(HFA). Fluorine modified polyurethane(FMPU) was also synthesized from FMD and poly(tetramethylene) glycol(PTMG). Modified polyurethanes were made by blending FMPU into the polyester type base polyurethane(BPU). Surface and thermal properties of the blended BPU film was measured by contact angle measurement and DSC. As the amounts of FMPU was increased from 0 wt % to 1 wt %, the surface energy was dramatically decreased from 47.82 dyne/cm to 17.64 dyne/cm. But we observed little change of the contact angle with further increase in the amount of the FMPU up to 10 wt %. The data meant that the surface of the blended polyurethanes was hydrophobic due to the surface arrangement of the fluorine containing moiety in FMPU. Phase separation was induced by the incompatibility of FMPU and BPU for the samples having over 5 wt % of FMPU. The thermal analysis data of these samples showed the thermal behavior of the FMPU itself.