• Journal of the Korean Wood Science and Technology
• /
• 제23권4호
• /
• pp.74-84
• /
• 1995

Eight types of thin composite panels were manufactured by press-lam and mat-forming process applied to optimum manufacturing condition, studied in former first research by author (1995). They were tested and compared with control boards on dimensional stability, internal bond strength, tensile strength, Screw withdrawal strength, and bending properties. These thin composite panels manufactured by mat-forming process were generally superior to those by press-lam in dimensional stability and mechanical properties. In the dimensional stability and mechanical properties of thin composite panels manufactured by mat-forming process, the thin composite panels (A and E type) composed of particle or sawdust core and veneer face with polyethylene film, were as good as those of common plywood (control board). Internal bond strength showed highest value in the thin composite panel(D type) which composed of particle core and polypropylene screen face with polyethylene film. The thin composite panels(G and H type) composed of sawdust or particle core and polypropylene screen face with polyethylene film by press-lam and mat-forming process, showed most highest value in dimensional stability and water absorption.

• 한국진공학회:학술대회논문집
• /
• 한국진공학회 2014년도 제46회 동계 정기학술대회 초록집
• /
• pp.272-272
• /
• 2014

SnO thin films, 100 nm in thickness, were deposited on glass substrates by RF magnetron sputtering. A stack structure of $SnO_2/SnO$, where few nanometers of $SnO_2$ were determined on the SnO thin film by X-ray photoelectron spectroscopy. In addition, XPS depth profile analysis of the pristine and heat treated thin films were introduced. The electrical behavior of the as-sputtered films during the annealing was recorded to investigate the working conditions for the SnO sensor. Subsequently, The NH3 sensing properties of the SnO sensor at operating temperature of $50-200^{\circ}C$ were examined, in which the p-type semiconducting sensing properties of the thin film were noted. The sensor shows good sensitivity and repeatability to $NH_3$ vapor. The sensor properties toward several gases like $H_2S$, $CH_4$ and $C_3H_8$ were also introduced. Finally, a sensing mechanism was proposed and discussed.

• 한국전기전자재료학회논문지
• /
• 제15권12호
• /
• pp.1060-1064
• /
• 2002

We have studied the effect of crystallization temperature, composition and film thickness, which are the fundamental processing parameters of lead zirconate titanate(PZT) thin film fabrication, in the respect of the piezoelectric properties by our pneumatic loading method(PLM). A great deal of research has been done in the field of characterization for piezoelectric thin films after the first report on the measurement for the piezoelectric coefficient of thin films in 1990. Even though the piezoelectric properties of thin films are very critical factors in the micro-electro mechanical system(MEMS) and thin film sensor devices, a few reports for the piezoelectric characterization are provided for the last decade unlikely the bulk piezoelectric devices. We have found that the piezoelectric properties of thin films are improved as the increase of crystallization temperature up to 750$\^{C}$ and this behavior can be also explained by the analysis of dielectric polarization hysteresis loop, X-ray diffraction and scanning electron microscopy. The effect of Zr/Ti composition has been also studied. This gives us the fact that the maximum piezoelectricity is found near Morphotropic Phase Boundary(MPB) as bulk PZT system does.

• 한국전기전자재료학회논문지
• /
• 제29권8호
• /
• pp.476-482
• /
• 2016

Convectional PZT based piezoelectric ceramics have to sinter at high temperature about $1,200^{\circ}C$ for their suitable electrical properties. However, some issues: low temperature sintering piezoelectric ceramic composition and reliable internal electrode, have recently attracted a great deal of interest as a highly efficient multi-layered piezoelectric ceramics. In order to optimize low temperature sintering conditions of thick-film PMN-PZ-PT ceramic, it was investigated sintering and piezoelectric properties according to the change of $LiBiO_2$ contents. Thus, the superior piezoelectric properties were found at the pallet type PMN-PZ-PT optimized with low sintering processing at $925^{\circ}C$ including 7 wt% $LiBiO_2$ sintering aid. Consequentially, we successfully manufactured thick-film PMN-PZ-PT ceramics, which had superior piezoelectric and dielectric properties, with 5 wt% of $LiBiO_2$ sintering aid at temperature of $900^{\circ}C$.

• 폴리머
• /
• 제25권2호
• /
• pp.208-217
• /
• 2001

테레프탈산 (terephthalic acid), 비스페놀에이 (bisphenol-A)와 에틸렌글리콜 (ethyleneglycol)로 제조된 PET/BPA 공중합체를 용융 압축시켜 필름을 만들어 얼음물에 급냉시켰다. 이 공중합체 필름을 모세관 레오메타로 고상 압출시켜 연신 필름을 만들었다. 이 연신된 필름의 수축율, 결정성, 형태학, 열적, 동역학적 및 기계적 특성을 조사하였다. 공중합체 필름의 융점은 순수 폴리에틸렌테레프탈레이트(PET)보다 낮게 나타났다. 또한 결정화도와 밀도는 연신비와 연신속도의 증가와 더불어 증가하였으나, 연신온도 증가와 더불어 감소하였다. 공중합체 필름의 인장강도와 인장탄성률은 연신비 증가와 더불어 증가하였고, 연신온도 증가에 따라 감소하였다. 연신된 공중합체 필름의 수축율은 연신비와 연신속도가 증가할수록 감소하였다.

• Bulletin of the Korean Chemical Society
• /
• 제24권7호
• /
• pp.975-980
• /
• 2003

The electrochemical properties and the mechanism of formation of anodic oxide films on Mg alloys containing 0-15 mass% Al, when anodized in NaOH solution, were investigated by focusing on the effects of anodizing potential, Al content, and anodizing time. The intensity ratio of Mg(OH)₂ in the XRD analysis decreased with increasing applied potential, while that of MgO increased. Mg(OH)₂ was barely detected at 80 V, while MgO was readily detected. The anti-corrosion properties of anodized specimens at each constant potential were better than those of non-anodized specimens. The specimen anodized at an applied potential of 3 V had the best anti-corrosion property. The intensity ratio of the β phase increased with aluminum content in Mg-Al alloys. During anodizing, the active dissolution reaction occurred preferentially in β phase until about 4 min, and then the current density increased gradually until 7 min. The dissolution reaction progressed in α phase, which had a lower Al content. In the anodic polarization test in 0.017 mol·$dm^{-3}$ NaCl and 0.1 mol·$dm^{-3}$ Na₂SO₄ at 298 K, the current density of Mg-15 mass% Al alloy anodized for 10 min increased, since the anodic film that forms on the α phase is a non-compacted film. The anodic film on the α phase at 30 min was a compact film as compared with that at 10 min.

• International Journal of Ocean System Engineering
• /
• 제3권2호
• /
• pp.102-110
• /
• 2013

The purpose of this study was to improve the properties of epoxy resin using titanium oxide nanoparticles. The effects of particle weight fraction, dispersion agent, and curing agents with different molecular weights on the thermal and mechanical properties of titanium-oxide-reinforced epoxy resin were investigated. In addition, the effect of the particle dispersion condition on the mechanical properties of nanocomposites was studied. As a result, it was found that the glass transition temperature of film-shaped nanocomposites decreased with an in-crease in the nanoparticle content. Because nanoparticles interrupted the cross linkage between the epoxy resin and the amine curing agent, the cross-link density of the epoxy became lower and led to a decrease in $T_g$ in the nanocompo-sites. The tensile strength and modulus in film-shaped nanocomposites also increased with the particles content. But in the case of dog-bone-shaped nanocomposites, the values were not similar to the trend for the film-shaped nanocompo-sites. This was probably a result of the different nanoparticles dispersions in the epoxy resins resulting from the respective-thicknesses of the film and dog-bone-shaped samples.

• Transactions on Electrical and Electronic Materials
• /
• 제7권5호
• /
• pp.267-270
• /
• 2006

The Indium tin oxide (ITO) films were deposited on CR39 substrate using DC magnetron sputtering. ITO thin films deposited at room temperature because CR39 substrates its glass-transition temperature of is $130^{\circ}C$. ITO thin films used bottom and top electrode and for organic thin film transparent transistor.(OTFT) ITO thin film electrodes electrical properties and optical transparency properties in the visible wavelength range (300 - 800 nm) strongly dependent on volume of oxygen percent. For the optimum resistivity and transparency of ITO thin film electrode achieved with a 75 W plasma power, 10 % volume of oxygen and a 27 nm/min deposition rate. Above 85 % transparency in the visible wavelength range (300 - 800 nm) measured without post annealing process and $9.83{times}10{-4}{\Omega}cm$ a low resistivity was measured thickness of 300 nm.

• Fibers and Polymers
• /
• 제6권3호
• /
• pp.200-205
• /
• 2005

Celite powder surface-modified with cationic surfactant was used to make polyethylene (PE) specialty film that can be contrasted with ordinary film in having high odor storing capacity and long odor lasting period. Mechanical properties of the films were sacrificed as more celite particles were included, whether celite surface was modified or not. The film with CTAS-modified celite showed the best odor storing and lasting properties for five different flavors of odor, three artificial and two natural ones, among the kinds of films developed. Comparisons among the different films are made, together with brief discussion about the reason for differences in odor lasting period and possible application to packaging industry.

• Journal of Electrical Engineering and Technology
• /
• 제6권6호
• /
• pp.836-841
• /
• 2011

Plasma polymerized methyl methacrylate (ppMMA) thin films were deposited by plasma polymerization technique with different plasma powers and subsequently thermally treated at temperatures of 60 to $150^{\circ}C$. To find a better ppMMA preparation technique for application to organic thin film transistor (OTFT) as dielectric layer, the chemical composition, surface morphology, and electrical properties of ppMMA were investigated. The effect of ppMMA thin-film preparation conditions on the resulting thin film properties were discussed, specifically O-H site content in the pMMA, dielectric constant, leakage current density, and hysteresis.