• Steel and Composite Structures
• /
• v.53 no.4
• /
• pp.481-490
• /
• 2024

In the modern era, the world is grappling with unprecedented challenges posed by environmental pollution. International agencies are urging scientists and material engineers to seek out green materials and structures as solutions to this problem. Composites derived from renewable sources, such as plant-based and vegetable fibres, are increasingly being utilized in the interior composite components of automobiles, aircraft, and building construction. This work introduces an improved Single Fibre Tensile Test (SFTT) for natural fibres, which are often irregular in shape and non-uniform along their length. Conventional methods, which determine the fibre cross-section by measuring the diameter using optical microscopy, yield inaccurate properties with large standard deviations (SD). The proposed new SFTT method, based on standards set by the American Society of Textile Manufacturing, provides a more accurate assessment of the mechanical performance of fibres. Using this approach, the tensile strength of various single fibres, yarns, and fabrics was measured with an SD of less than 8%.

• The Korean Fashion and Textile Research Journal
• /
• v.17 no.3
• /
• pp.462-475
• /
• 2015

This paper investigated the characteristics of the physical properties of woven fabrics according to the yarn structure and fibre property. It was found that wicking property of woven fabrics made of sheath/core hybrid yarn were better than those of siro spun and siro-fil hybrid yarns, which was caused by platform for transport of moisture vapor by filaments on the core part of sheath core hybrid yarns. In drying property, the fabric specimen woven by PP/Tencel sheath core hybrid yarns as a warp and Coolmax/Tencel spun yarn as a weft showed quick drying property, which was caused by the sheath core hybrid yarn structure as drainage of water moisture and coolmax fibre characteristics as quick dry material. Concerning to breathability and thermal conductivity as heat transport phenomena, it was observed that breathability of fabrics woven with hybrid yarns such as sheath core and siro-fil in the warp and hi-multi filaments in the weft showed the lowest water vapor resistance, which was explained as due to for air gap in the fibres of the spun yarns to restrict the wet heat transport from perspiration vapor. Thermal conductivities of the fabrics woven with PET/Tencel siro-fil yarns in the weft and hybrid yarns such as sheath core and siro-fil in the warp revealed the highest values, which was observed as due to higher thermal conductivity of PET than PP and more contact point between fibres in the siro-fil and sheath core hybrid yarns.

• Fibers and Polymers
• /
• v.7 no.3
• /
• pp.310-316
• /
• 2006

In this article, an attempt has been made to explain the failure mechanism of spun yams. The mechanism includes the aspects of generation and distribution of forces on a fibre under the tensile loading of a yam, the free body diagram of forces, the conditions for gripping and slipping of a fibre, and the initiation, propagation, and ultimate yam rupture in its weakest link. A simple mathematical model for the tenacity of spun yams has been proposed. The model is based on the translation of fibre bundle tenacity into the yam tenacity.

• The Korean Fashion and Textile Research Journal
• /
• v.18 no.1
• /
• pp.113-119
• /
• 2016

The evolution of spinning technology was focused on improving productivity with good quality of yarns. More detail spinning technology according to mixing of various kinds of fibre materials on the air vortex spinning system is required for obtaining good quality yarns. This paper investigated the physical properties of air vortex yarns compared with ring and compact yarns using PTT/tencel/cotton fibres. It was observed that unevenness of air vortex yarns was higher than those of ring and compact yarns, which resulted in low tenacity and breaking strain of air vortex yarns. Initial modulus of air vortex yarns was higher than those of ring and compact yarns. Yarn imperfections of air vortex yarns such as thin, thick and nep were much more than those of ring and compact yarns. These poor yarn qualities of air vortex yarn were attributed to the fasciated yarn structure with parallel fibres in the core part of the air vortex yarn. However, yarn hairiness of air vortex yarns was less and shorter than those of ring and compact yarns. Thermal shrinkage of air vortex yarns were higher than that of ring yarns, which was caused by sensible thermal shrinkage of PTT fibres on the bulky yarn surface and core part of air vortex yarns.

• The Korean Fashion and Textile Research Journal
• /
• v.17 no.6
• /
• pp.1020-1029
• /
• 2015

This paper investigated the wearing performance of knitted fabrics made of air vortex yarns using PTT/tencel/cotton fibres in comparison with ring and compact yarns for emotional garment. Wicking property of knitted fabric made of MVS yarns was worse than those by ring and compact yarns, however, drying property of knitted fabric made of MVS yarns was better than those by ring and compact yarns, which was explained as more water vapor transport due to larger openness between fibres in the MVS yarns than those in the ring and compact yarns. Thermal conductivity of knitted fabric made of MVS was lower than those of ring and compact yarns and maximum heat flow(Q_max) at the transient state of MVS knitted fabric was lower than those of ring and compact yarns, which may be attributed to MVS yarn structure that has parallel fibres in the core part of the yarn and fasciated fibre bundles on the sheath part with roughness on the yarn surface. However, pilling of MVS knitted fabric was better than those by ring and compact yarns, which was caused by less and shorter hairy fibres protruded from MVS yarn surface than those of ring and compact yarns. It was observed that tactile hand of MVS yarn knitted fabrics was stiffer than those of ring and compact yarns knitted fabrics. It was explained by low extensibility and compressibility and high bending and shear rigidities of the MVS yarn knitted fabrics, which resulted in bad wearing performance of MVS knitted fabric.

• Science of Emotion and Sensibility
• /
• v.10 no.4
• /
• pp.623-629
• /
• 2007

Recently, the $"Optim"^{(R)}$ which is the wool fibre with high lustre developed by CSIRO in Australia is imported and commercialized as a high sensible fabrics for garment. But the price of this $"Optim"^{(R)}$ fibre is very high so material demand and supply is not smooth. This study is aiming to develop the drawing technology of the worsted yarn with washable function, lustre and low production cost. For this purpose, drawing yarns are made using developed drawing machine and high sensible fabrics are woven using this yarns, and various physical properties of the fabric specimen are measured and analysed with garment characteristics such as sewability and formability. The final objective of this study is seemed to be achieved by making the high sensible fabrics using drawing worsted yarns with high lustre such as $"Optim"^{(R)}$ fibre.

• Proceedings of the Korean Fiber Society Conference
• /
• 1990.06b
• /
• pp.58-59
• /
• 1990

• Fibers and Polymers
• /
• v.6 no.3
• /
• pp.250-258
• /
• 2005

The present paper is concerned with the influence of opening roller speed, drum speed difference and suction air pressure on properties of polyester and acrylic open-end friction spun yams. The results shows that the opening roller speed and the suction air pressure have considerable influence on the characteristics of polyester and acrylic open-end friction spun yams. In case of polyester yams the unevenness, imperfection and hairiness decreases and the yam tenacity increases with the increase in opening roller speed and suction air pressure. However for acrylic yams the unevenness and imperfections decreases and tenacity increases with the increase in opening roller speed and suction air pressure.

• Proceedings of the Korean Fiber Society Conference
• /
• 2003.10a
• /
• pp.83-84
• /
• 2003

The microstructure and tensile properties of ramie treated with NaOH and crosslinked with 1, 2, 3, 4-butanetetracarboxylic acid were characterised. X-ray diffraction and FTIR were used to study the crystalline structure o f the resultant ramie yarns. Results showed that the maximum change in the structure of the modified ramie took place at 16% NaOH, which would completely transform Cellulose I to Cellulose II. Also, the crystallinity index and fibre orientation decreased to the minimum value while the absorption properties were enhanced. The average degree of polymerization of the treated ramie yams slightly decreased after NaOH treatment.

• Elastomers and Composites
• /
• v.37 no.3
• /
• pp.192-194
• /
• 2002

Polyester cord yarns have been treated in an atmospheric-pressure nitrogen plasma reactor in order to enhance their adhesion to rubber. A thin layer or the plasma was generated in the close vicinity of the yam surface using various types or surface discharge. To assess the effect of the plasma treatment on fiber surface properties, the cord thread/rubber matrix adhesion values measured using the untreated and threads cord threads were compared. The static and dynamic adhesion of the cord thread to rubber was characterized by using the standard Henley test. The dynamic adhesion values for the reference and plasma treated fiber were $7,3{\pm}1,2\;N$ and $83,5{\pm}3,5\;N$. The surface properties were investigated by scanning electron microscopy, infrared spectroscopy and electron spin resonance spectroscopy. It is concluded that both polar group interactions and increased surface area of the fibers are responsible for the improved adhesive strength.