• 한국염색가공학회지
• /
• 제33권4호
• /
• pp.327-337
• /
• 2021

The uniformly dispersed Aramid and Poly (phenylene benzobisoxazole) (PBO) in a variety of rubber was investigated. The mechanical properties of rubber were characterized by hardness, tensile strength, elongation at break, heat resistance, oil resistance, cold resistance, ozone resistance measurements. The 3mm Aramid chopped fiber better tensile strength than the other Chopped fiber. The Aramid of 3mm chopped fiber showed excellent reinforcing in rubber composite because of homogeneous dispersion. Consequently, the best 3mm Aramid chopped fiber and rubber improved the tensile strength and elongation at break of the composite. Also, 3mm Aramid chopped fiber improved the oil-resistant, ozone resistant and cold resistant.

• 한국염색가공학회지
• /
• 제28권3호
• /
• pp.183-188
• /
• 2016

The uniformly dispersed p-Aramid chopped fiber in a variety of rubber was investigated. The cross section and surface properties in a variety of rubber were characterized by scanning electron microscopy(SEM), weight, tensile strength, cold resistance measurements. The 1mm p-Aramid chopped fiber better uniformly dispersed than the other p-Aramid chopped fiber. The p-Aramid of lmm chopped fiber showed excellent adhesion in rubber composite because of homogeneous dispersion. Consequently, the best 1mm chopped fiber and rubber improved the strength of the composite.

• Elastomers and Composites
• /
• 제57권4호
• /
• pp.175-180
• /
• 2022

To produce a co-poly-para-aramid fiber (AF, Technora^®)-reinforced neoprene rubber composite, dispersion of AF in a neoprene matrix is investigated. The AF is then surface-modified by mercerization and acetone, plasma, and silane treatments to improve dispersibility. Finally, an internal mixer process is used to disperse the surface-modified fibers in the neoprene rubber matrix.

• 대한기계학회논문집A
• /
• 제30권12호
• /
• pp.1518-1525
• /
• 2006

Finite element analyses of structures made of the fiber reinforced composites require an adequate method to characterize the high anisotropic behavior induced by one or several layers of fiber cords with different spatial orientation embedded in a rubber matrix. This paper newly proposes a continuum based rebar element considering change of the orientation of the fiber during deformation of the composite. The mechanical behavior of the embedded fiber is modeled using two-node bar elements in order to consider the relative deformation and spatial orientation of the embedded fiber. For improvement of the analysis accuracy, the load-displacement curve of fiber is applied to the stiffness matrix of fiber. A finite element program is constructed based on the total Lagrangian formulation considering both geometric and material nonlinearity. Finite element analyses of the tensile test are carried out in order to evaluate the validity of the proposed method. Analysis results obtained with the proposed method provides realistic representation of the fiber reinforced rubber composite compared to results of other two models by the Halpin-Tsai equation and a rebar element in ABAQUS/Standard.

• 한국염색가공학회지
• /
• 제30권2호
• /
• pp.77-89
• /
• 2018

In the case of fiber/rubber composites for tire applications, the interfacial adhesion between fiber and rubber significantly affects the physical properties of the finished products. Generally, organic synthetic fibers used for tire cords are treated with resorcinol formaldehyde latex(RFL) primer on the surface of the fiber to improve the adhesion to rubber. Changes of adhesion between rubber and tire cords might weaken as temperature rises due to overheating of car engine and friction with road. In this study, the effects of temperature on the primer treated polyketone cord/rubber composites and the changes in interfacial adhesion were investigated. Polyketone cord/rubber composites were prepared after RFL solution treatment on the surface of polyketone fibers. After that, composites was thermally aged at different temperature conditions(60, 80, 100, $120^{\circ}C$) and times(1, 5, 10, 15days). The adhesion strength of polyketone cord/rubber composite treated with RFL primer was higher than untreated composite by more than 3 times. After heat aging, the adhesion strength of untreated polyketone cord/rubber composites increased while the RFL treated polyketone cord/rubber composites decreased somewhat.

• Composites Research
• /
• 제37권3호
• /
• pp.186-189
• /
• 2024

본 연구는 나노필러가 혼합된 열가소성 탄소섬유강화 복합재료(Carbon fiber reinforced thermoplastic polymer, CFRTP)의 물성을 비교 평가하였다. Polyamide 6 (PA6) 수지에 Multi-wall carbon nano tube (MWCNT), Silicon oxide, Core shell rubber, Aramid nano fiber 등의 다양한 나노필러를 혼합한 후, 이를 기지재(Matrix)로 탄소섬유강화복합 재료(CFRP)를 제조하여 그 물성을 측정하였다. 나노필러의 종류와 혼합비율에 따라, 인장강도, 층간계면결합력 (Inter-laminar shear strength), Izod 충격 강도 등이 측정되었다. 인장 강도와 충격 강도의 경우 Core shell rubber를 혼합한 경우 가장 높은 물성을 가졌으나, 계면결합력은 silicon oxide를 1 wt.% 이하 혼합하였을 때 최적값을 가졌다.

• 폴리머
• /
• 제25권1호
• /
• pp.122-132
• /
• 2001

본 연구에서는 온도의 상승에 의하여 팽창하는 열팽창 기능을 가지고 있으면서 부피의 감소에 의하여 발생하는 압력의 손실을 상쇄시킬 수 있는 고무 치공구를 열가소성 고분자의 필름 함침공정에 적용하였다. 일반적인 압축성형공정에서는 온도의 상승에 의하여 수지가 용융되고 이에 수지가 함침됨에 따라 압력이 감소하지만, 고무 치공구를 사용한 경우에는 수지의 함침을 보상한 고무 치공구가 팽창하여 감소된 압력을 보상하기 때문에 급격한 압력의 강하를 억제할 수 있었다. 이렇게 수지의 함침에 따른 고무 치공구의 부피 팽창 그리고 이에 따른 수지 함침속도의 변화를 고려하여 고무 치공구를 이용한 필름 함침공정 모델을 제안하였다. 또한 고무 치공구를 사용하지 않는 일반적인 압축공정에 있어서 수지의 함침에 따른 섬유층 탄성력의 변화를 실험적으로 측정하여 단계적인 압축공정에 있어서 수지의 함침속도를 예측할 수 있는 모델을 제안하였다.

• 한국농공학회논문집
• /
• 제53권5호
• /
• pp.17-23
• /
• 2011

Steel clapping plate is used to connecting rubber body in rubber dam. However, once the steel clapping plate corrodes, it may cause faults, such as the same problems experienced by typical reinforcing steel. This study evaluated the applicability of glass fiber reinforced polymer composite(GFRP) clapping plate as a substitute for steel clapping plate. Absorption and load test were conducted to evaluate the decrease in durability of GFRP clapping plate exposed to deterioration environments. In the durability test results, the absorption rate of GFRP clapping plate was appeared as 0.6~1.0% in 50 day of immersion time. Also, the fracture load decreased with accelerated degradation environment exposure. Moreover, the absorption rate in GFRP clapping plate increased as degradation progressed, reducing the fracture load.

• Composites Research
• /
• 제13권3호
• /
• pp.30-37
• /
• 2000

계면상 조건과 단섬유 함유량 증가에 따른 강화고무의 동적 특성에 대해 실험적 고찰을 하였다. 손실계수는 대체적으로 섬유 함유량 증가에 따라 감소하였고 계면상 조건에 따라 다른 경향을 보였다. 계면 조건이 우수할수록 손실탄성율, $E_2$ 는 낮게 나타났다. 또한 동배율은 섬유 함유량 증가에 따라 감소하였고, 계면상 조건이 우수할수록 크게 감소하였다. 따라서 단섬유 강화고무는 진동수비가 $\sqrt{2}$이상에서 더 큰 진동절연 효과가 있다고 할 수 있다. 손실계수와 동배률의 관계로부터, 자동차의 엔진과 차체의 진동을 절연하는 부품인 Engine Mount Rubber의 적용가능성을 검토하였다.

• Composites Research
• /
• 제13권5호
• /
• pp.10-17
• /
• 2000

계면상 조건과 단섬유 함유량 증가에 따른 강화고무의 피로특성에 대해 실험적 고찰을 하였다. 피로시험 후 기지고무의 스프링 상수는 약 21% 감소하였고, 강화고무는 반대로 증가하였다. 강화고무의 스프링 상수 변화율은 섬유함유량 증가에 따라 감소하였고, 계면상 조건이 우수할수록 변화율이 적었다. 피로시험 후 기지고무의 온도는 2.5배, 강화고무는 1.7∼2.0배 증가하였다. 강화고무의 온도 변화율은 섬유 함유량 증가에 따라 감소하였고, 동일한 섬유 함유량에서 계면상 조건이 우수할수록 변화율이 적었다. 이번 연구에서 접착제 402와 고무용액을 2번씩 도포한 경우가 가장 우수한 계면상 모델(C)이 되었다. 그리고 이러한 강화고무를 자동차의 Engine Mount Rubber, Bush 그리고 Stopper등의 적용을 검토하였다.