• Journal of Welding and Joining
• /
• v.32 no.1
• /
• pp.66-70
• /
• 2014

In Ti active brazing of YSZ to STS 430 using Ag-Cu Filler Metal, the effect of Ti contents on the shear bonding strength were investigated together with the effect of brazing temperature and holding time. The addition of Ti in Ag-Cu Filler Metal increased the bonding strength up to 4.68% Ti, followed by the decrease with further addition. This seems to be caused by formation of TixOy at the reaction layer. Brazing temperature was optimized at $960^{\circ}C$ among a given temperature ranges. The addion of Sn to Ag-Cu filler metal brought the decrease of its melting temperature its melting temperature without a significant decrease of bonging strength.

• Korean Journal of Materials Research
• /
• v.25 no.6
• /
• pp.269-273
• /
• 2015

The effect of adding Ca on the microstructural and mechanical properties of as-cast Mg-11Li-3Zn-1Sn(wt%) alloys were investigated. Mg-11Li-3Zn-1Sn-0.4Mn with different Ca additions (0.4, 0.8, 1.2 wt%) were cast under an $SF_6$ and $Co_2$ atmosphere at $720^{\circ}C$. The cast billets were homogenized at $400^{\circ}C$ for 12h and extruded at $200^{\circ}C$. The microstructural and mechanical properties were analyzed by OM, XRD, SEM, and tensile tests. The addition of Ca to the Mg-11Li-3Zn-1Sn-0.4Mn alloy resulted in the formation of $Ca_2Mg_6Zn_3$, MgSnCa intermetallic compound. By increasing Ca addition, the volume fraction and size of $Ca_2Mg_6Zn_3$ with needle shape were increased. This $Ca_2Mg_6Zn_3$ intermetallic compound was elongated to the extrusion direction and refined to fine particles due to severe deformation during hot extrusion. The elongation of the 0.8 wt% Ca containing alloy improved remarkably without reduction strength due to the formation of fine grain and $Ca_2Mg_6Zn_3$ intermetallic compounds by Ca addition. It is probable that fine and homogeneous $Ca_2Mg_6Zn_3$ intermetallic compounds played a significant role in the increase of mechanical properties.

• Transactions of Materials Processing
• /
• v.30 no.1
• /
• pp.22-26
• /
• 2021

The present study demonstrated the effects of processing variable and alloying elements on the processing window of austempered cast iron, one of the heat-treatable cast irons, in order to elucidate the relation between heat treatment and microstructure in terms of time and temperature. Such microstructure is strongly affected by austenitizing conditions and alloying elements. The size of processing window tends to increase initially with increasing austenitizing temperature from 1123 to 1173 K, followed by a decline in the reverse direction between 1173 and 1223 K. Thus, the optimized processing window with large frame was found at an austenitizing temperature of 1173 K. To determine the effect of Sn addition, the processing window in the sample was created by the addition of 0.08 wt.% Sn, which appeared larger than that without Sn and with 0.06 wt.% Sn.

• Korean Journal of Materials Research
• /
• v.4 no.4
• /
• pp.428-438
• /
• 1994

In order to investigate the effect of $SnO_2$ on the growth of 123 phase in Y-Ba-Cu-0 system, O.1Sn-doped 123+Sn compact was coupled with Sn-free 123 compact by placing the former on the latter. In case of the coupled samples which were held at $1100^{\circ}C$ for 24hr and then at $970^{\circ}C$ for lhr, 123 phase grew from the surface of O.1Sn-doped 123+Sn compact toward the inner of Sn-free 123 compact. In case of the coupled samples which were held at $1100^{\circ}C$ for 48hr and then at $970^{\circ}C$ for lhr, it was not the 123 phase but Ba-Y-Sn grains that were observed. Ba-Y-Sn grains with a shape of bar was composed of Ba : Y : Sn=5 : 3 : 2, approximately.

• Journal of the Korean Society for Heat Treatment
• /
• v.28 no.5
• /
• pp.229-238
• /
• 2015

The effects of Sn addition and solution treatment on corrosion behavior were studied in AZ91 magnesium casting alloy. The addition of 5%Sn contributed to the introduction of $Mg_2Sn$ phase, to the reduction in dendritic cell size and to the increase in the amount of secondary phases. After the solution treatment, trace amount of $Al_8Mn_5$ particles were observed in the ${\alpha}$-(Mg) matrix for the AZ91 alloy, while $Mg_2Sn$ phase with high thermal stability was additionally found in the AZ91-5%Sn alloy. Before the solution treatment, the AZ91-5%Sn alloy had better corrosion resistance than the Sn-free alloy, which is caused by the enhanced barrier effect of the (${\beta}+Mg_2Sn$) phases formed more continuously along the dendritic cell boundaries. It is interesting to note that after the solution treatment, the corrosion rate of both alloys became increased, but the Sn-added alloy showed higher corrosion rate than the Sn-free alloy. The microstructural examination on the corroded surfaces revealed that the remaining $Mg_2Sn$ particles in the solution-treated AZ91-5%Sn alloy play a role in accelerating corrosion by galvanic coupling with the ${\alpha}$-(Mg) matrix.

• Journal of the Korean Chemical Society
• /
• v.24 no.3
• /
• pp.183-192
• /
• 1980

Oxidation reactions of carbon monoxide on $SnO_2$, Sb-doped $SnO_2$, and Pt catalyst were studied. The oxidation reaction was found to be first order with respect to both CO and O$_2$ on $SnO_2$ and Sb-doped $SnO_2$ catalysts, and to be of half order on Pt catalyst. A small addition of Sb to $SnO_2$ (depant composition: 0.05∼0.1 mol %) increased the rate of oxidation. On the contrary, a large addition decreased the rate. From the rate expression of oxidation on Pt catalyst, the inhibition effect of carbon monoxide on the rate of oxidation was deduced. The experimentally obtained activatio energies were 5.7 kcal for the Sb doped $SnO_2$ catalyst (dopant composion: 0.05 mole%), and 6.4 kcal for the Pt catalyst. A possible reaction mechanism was proposed from the experimentally obtained kinetic data.

• Korean Journal of Materials Research
• /
• v.19 no.2
• /
• pp.111-114
• /
• 2009

For the fabrication of core-shell structure bimetallic lead-free solder balls, both the critical temperature ($T_{cr}$) for the phase separation of two immiscible liquid phases and the temperature coefficient of the interfacial tension between the two separated liquid phases are required. In order to obtain this information, the temperature dependence of the surface tension of 60%Bi-24%Cu-16%Sn(-REM) alloys was measured using the constrained drop method. The slope of the temperature dependence of the surface tension changed clearly at a critical temperature for the separation of two immiscible liquid phases. The critical temperature of the 60%Bi-24%Cu-16%Sn alloy was estimated to be 1097K. An addition of 0.05% Ce decreased the critical temperature to 1085K, whereas that of 0.05% La increased it to 1117K. It was found that the surface tension and its temperature coefficient of the 60%Bi-24%Cu-16%Sn alloy were slightly increased by the addition of 0.05% Ce and 0.05% La. In addition, additions of Ce and La increased the temperature coefficient of the interfacial tension.

• Korean Journal of Materials Research
• /
• v.31 no.12
• /
• pp.690-696
• /
• 2021

The purpose of this study is to develop a zirconium-based alloy with low modulus and magnetic susceptibility to prevent the stress-shielding effect and the generation of artifacts. Zr-7Cu-xSn (x = 1, 5, 10, 15 mass%) alloys are prepared by an arc melting process. Microstructure characterization is performed by microscopy and X-ray diffraction. Mechanical properties are evaluated using micro Vickers hardness and compression test. The magnetic susceptibility is evaluated using a SQUID-VSM. The average magnetic susceptibility value of the Zr-7Cu-xSn alloy is 1.176 × 10^-8 cm³g^-1. Corrosion tests of zirconium-based alloys are conducted through polarization test. The average Icorr value of the Zr-7Cu-xSn alloy is 0.1912 ㎂/cm². The elastic modulus value of 14 ~ 18 GPa of the zirconium-based alloy is very similar to the elastic modulus value of 15 ~ 30 GPa of the human bone. Consequently, the Sn added zirconium alloy, Zr-7Cu-xSn, is very interesting and attractive as a biomaterial that reduces the stress-shielding effect caused by differences of elastic modulus between human bone and metallic implants. In addition, this material has the potential to be used in metallic dental implants to effectively eliminate artifacts in MRI images due to low magnetic susceptibility.

• Journal of the Microelectronics and Packaging Society
• /
• v.28 no.1
• /
• pp.61-66
• /
• 2021

SnO2 has the wide bandgap which allows it to be used as the photocatalyst. There are many studies to enhance the photocatalytic properties of SnO2. In this study, 3-dimensional SnO2 aerogel was synthesized using epoxide-initiated sol-gel method for the optimal specific surface area. Also, graphene oxide (GO) was added before the gelation process of the aerogel to maximize the specific surface area. Addition of 0.5 wt% of GO would possibly enhance the specific surface area by 1.7 times compared with the bare tin oxide aerogel. Furthermore, enhanced specific surface area could degrade 67.3% of initial Rhodamine B in 120 minutes. To compare with the bare SnO2 aerogel, 0.5 wt% GO addition to SnO2 could double the reaction rate of the photocatalytic degradation.

• Journal of the Microelectronics and Packaging Society
• /
• v.8 no.1
• /
• pp.27-32
• /
• 2001

The effect of $V_2O_5$, a donor-type dopant on the degradation of quality factor of ($Zr_{0.8}, Sn_{0.2})TiO_4$was compared with Ta$_2$O$_{5}$ doped ($Zr_{0.8}, Sn_{0.2})TiO_4$ in terms of microstructure, electrical conductivity, and oxidation state of the dopant. It is well known that the addition of the donor type species such as $Ta_2O_5,Nb_2O_5, Sb_2O_5, WO_{3}$, increases the quality factor of ($Zr_{0.8}, Sn_{0.2})TiO_4$due to decrease the oxygen vacancy concentration. Unlike other dopants, however, the addition of $V_2O_5$ decreased the quality factor. The degradation of quality factor of ($Zr_{0.8}, Sn_{0.2})TiO_4$was resulted from the formation of grain boundary phase and $V_2O_5$rich fiber shaped secondary phase, and the increasing the oxygen vacancy concentration due to unstability of oxidation state of vanadium ions in ($Zr_{0.8}, Sn_{0.2})TiO_4$ceramic.c.