• 폴리머
• /
• 제27권6호
• /
• pp.521-527
• /
• 2003

신디오택틱 폴리프로필렌 (sPP)과 아이소택틱 폴리프로필렌 (iPP)은 용융과정에서 결정의 재배열이 나타나며 이와 같은 재결정 현상을 해석하기 위하여 결정화도와 결정구조의 변화, 동역학적 물성을 고찰하였고 DSC, FT-IR, SAXS, DMA를 이용하였다. 본 연구에서 실험된 조건에서는 sPP의 재결정화 현상을 확인할 수 없었으며, iPP는 용융으로부터 냉각되는 속도가 빠르게 될 수록 재가열시 재결정화 현상이 두드러졌다. iPP의 재결정화가 진행되는 동안 tan $\delta$가 0.119에서 0.101로 감소하여 탄성율이 증가한 결과를 보이나 결정화도는 거의 일정하게 유지되었다. 더욱이 재결정 현상이 진행되는 동안 SAXS 산란피크의 반가폭이 약 30% 감소하여 라멜라의 질서가 증가하는 거동을 보였다.

• 열처리공학회지
• /
• 제18권1호
• /
• pp.18-23
• /
• 2005

Effect of cold rolling on microstructural changes has been investigated for a Zn-15%Al alloy to elucidate the reason for its work softening behavior. Fully annealed microstructure of the Zn-15%Al alloy is characterized by ${\eta}$ grains and (${\eta}+{\alpha}$) lamellar colonies, where ${\eta}$ and ${\alpha}$ are Zn-rich HCP and Al-rich FCC phases, respectively. The hardness decreases continuously with increasing cold rolling degree, exhibiting work softening behavior. It is revealed that during the cold rolling, (${\eta}+{\alpha}$) lamellar colonies gradually change into equiaxed ${\eta}$ and ${\alpha}$ grains due to dynamic recrystallization at room temperature, while pre-existing ${\eta}$ grains are only deformed without recrystallization. Furthermore, cold rolling causes the precipitation of dissolved Al solutes in ${\eta}$ grains. In view of these results, change of (${\eta}+{\alpha}$) phases from lamellar to equiaxed morphology, which results in structural softness and increase in equiaxed ${\eta}/{\alpha}$ grain boundaries with higher mobility, and deterioration of solution hardening by precipitation of Al solutes from ${\eta}$ grains, are thought to contribute to the work softening of Zn-15%Al alloy.

• 한국소성가공학회:학술대회논문집
• /
• 한국소성가공학회 2002년도 춘계학술대회 논문집
• /
• pp.169-172
• /
• 2002

Recently, the application of 3-roll mill is increasing, because of its flexibility in spread control and stand arrangements due to its compact size. But deformation characteristics and microstructural change in the process is not well known. In this study, austenite grain size (AGS) predictions were made by isothermal FE analyses and a microstructure model available in the literature. From this study, the effect of draught on the AGS characteristics was analyzed based on the divided zones of two major recrystallization behaviors.

• 분석과학
• /
• 제9권2호
• /
• pp.179-191
• /
• 1996

초내열 718 합금의 고온 변형 거동을 이해하기 위하여 rotating grade의 718 합금을 이용하여 온도 $927{\sim}1066^{\circ}C$, 변형속도 $5{\times}10^{-4}{\sim}5{\times}10^0sec^{-1}$ 범위에서 진변형량 0.7까지 압축실험을 수행하였다. 최대 유동 응력은 변형 속도가 증가하고 시험 온도가 감소함에 따라 증가하였다. 변형 속도 $5{\times}10^{-1}sec^{-1}$을 제외한 대부분의 설험 조건에서 가공 연화현상이 관찰되었다. 가공 연화는 저온, 고변형 속도에서는 주로 동적 회복 및 변형 쌍정에 의해 일어나는 반면 고온, 저변형 속도 조건에서는 동적 재결정에 의해 발생하였으며 $5{\times}10^{-1}sec^{-1}$의 변형 속도 조건에서는 동적 재결정된 결정 입자들의 재가공 경화에 의해 가동 경화현상이 나타났다. 변형 속도 감도(m)는 변형 속도가 낮은 경우에는 0.3 정도로서 주로 동적 재결정에 의해 변형 거동이 나타남을 반영하였으며 고변형 속도에서는 0.1 정도로서 동적 회복과 변형 쌍정의 발생으로 718 합금의 변형이 이루어짐을 알 수 있었다.

• 한국주조공학회지
• /
• 제30권6호
• /
• pp.210-216
• /
• 2010

The aim of this study is to characterize a thixoextruded 7075 Al wrought alloy bar in terms of its isotropic behavior through the optical microscope, mechanical test and electron back scattered diffraction. It is also discussed of the extrudability improvement for 7075 Al wrought alloy by thixoextrusion, with emphasis on controlling thixoextrusion parameters. Hot extrusion shows that the maximum extrusion pressure depends on their characteristics in terms of flow stress and hot workability. In the contrary, thixoextrusion demonstrates that the maximum extrusion pressure is almost uniform regardless of the experimental parameters, such as initial ram speed, die bearing length and thixoextrusion temperature. The hot extruded microstructures become elongated to extrusion direction, while the thixoextruded microstructures are isotropic and homogeneously distributed due to the existence of liquid phase between solid grains during the process. The grain refinement due to dynamic recrystallization during thixoextrusion has been also occurred. Subsequent recrystallization would lead to the strengthening of mechanical properties, as observed in the study. The important point is that the values of tensile, yield strength and elongation of the thixoextruded bar without plastic deformation are similar to those of the hot extruded bar with severe plastic deformation.

• 열처리공학회지
• /
• 제32권1호
• /
• pp.1-11
• /
• 2019

In this study, microstructure evolution and crystallographic orientation are investigated under various deformation conditions in M1 magnesium alloy. M1 magnesium ingot was rolled at 673 K with the rolling reduction of 30%. The compression test specimens were machined out from rolled plate, and then the specimens were annealed at 823 K for 1h. Uniaxial compression tests were conducted at 723 K and under the strain rate ranging from $5.0{\times}10^{-4}s^{-1}$ to $5.0{\times}10^{-2}s^{-1}$ up to a true strain of -1.0. For observation of crystal orientation distribution, EBSD measurement was performed. Occurrence of the dynamic recrystallization and grain boundary migration were confirmed in all case of the specimens. The distribution of the grains is not uniformed in the experimental conditions.

• 한국주조공학회지
• /
• 제22권1호
• /
• pp.11-16
• /
• 2002

Hot deformation behavior of GCD-50 cast iron has been investigated by employing the compressive test. Phenomenological deformation behaviors, which were modeled based on the dynamic materials model and the kinetic model, have been correlated with the microstructural change taken place during compression. Microstructural investigation revealed that the adiabatic shear band caused by the locallized deformation was taken place in low temperature and high strain rate. On the other hand, the wavy and curved grain boundaries, which repersent the occurrence of dynamic microstructure change such as dynamic recovery and dynamic recrystallization, were observed in high temperature and low strain rate. Deformation model based on hyperbolic sine law has also been suggested.

• 소성∙가공
• /
• 제3권4호
• /
• pp.427-439
• /
• 1994

The high temperature deformation behavior of $SiC_p/Al-Si$ composites and Al-Si matrix was studied by hot torsion test in a range of temperature from $270^{\circ}C$ to $520^{\circ}C$ and at strain rate range of $1.2{\times}10_{-3}~2.16{\times}10_{-1}/sec$. The hot restoration mechanisms for both matrix and composites were found to be dynamic recrystallization(DRX) from the investigation of flow curves and microstructural evolutions. The Si precipitates and SiC particles promoted DRX, and the peak strain$({\varepsilon}_p)$ of the composites was smaller than that of the matrix. Flow stresses of $SiC_p/Al-Si$ composites were found to be generally higher than the matrix, but the difference was quite small at higher temperature due to the decrease of capability of load transfer by SiC particles. With increasing temperature, failure strain of matrix and composites are inclined to increase, the increasing value of failure strain for the $SiC_p/Al-Si$ composites was small compared to that of matrix. The stress dependence of both materials on strain rate() and temperature(T) was examined by hyperbolic sine law, $\.{\varepsilon}=A_1[sinh({\alpha}{\cdot}{\sigma})]_n$exp(-Q/RT)

• 한국재료학회지
• /
• 제22권1호
• /
• pp.42-45
• /
• 2012

The mechanical behavior and microstructural evolution during high temperature tensile deformation of recrystallized Ni3Al polycrystals doped with boron were investigated as functions of initial grain size, tensile strain rate and temperature. In order to obtain more precise information on the deformation mechanism, tensile specimens were rapidly quenched immediately after deformation at a cooling rate of more than $2000Ks^{-1}$, and were then observed by transmission electron microscopy (TEM). Mechanical tests in the range of 923 K to 1012 K were carried out in a vacuum of less than $3{\times}10^{-4}$ Pa using an Instron-type machine with various but constant cross head speeds corresponding to the initial strain rates from $1.0{\times}10^{-4}$ to $3.1{\times}10^{-5}s^{-1}$. After heating to deformation temperature, the specimen was kept for more than 1.8 ks before testing. The following results were obtained: (1) Flow behavior was affected by initial strain size; with decreasing initial grain size, the level of a stress peak in the true stress-true strain curve decreased, the steady state region was enlarged and elongation increased. (2) On the basis of TEM observation of rapidly quenched specimens, it was confirmed that dynamic recrystallization certainly occurred on deformation of fine-grained ($3.3{\mu}m$) and intermediate-grained ($5.0{\mu}m$) specimens at an initial strain rate of $3.1{\times}10^{-5}s^{-1}$ and at 973 K. (3) There were some dislocation-free grains among the new recrystallized grains. The obtained results suggest that both dynamic recrystallization and grain boundary sliding are operative during high temperature deformation.

• 한국소성가공학회:학술대회논문집
• /
• 한국소성가공학회 2000년도 춘계학술대회논문집
• /
• pp.183-186
• /
• 2000

The high temperature deformation behavior of spray-formed Al-19wt%Si-1.87wt%Mg-0.085wt.%Fe alloy was studied by torsion testing in the strain rate range of 0.001-1 sec-1 and in the temperature range of 300-500 $^{\circ}C$. The relationship between stress temperature and strain rate is expressed using the Power law. the behavior of dynamic recrystallization is showed in 300-35$0^{\circ}C$, 1-0.1sec-1 and the behavior of dynamic recovery is showed in 450-50$0^{\circ}C$, 0.01-0.001sec-1 The size of Si particles is mall when the temperature is low and the strain rate is high. The strain rate sensitivity(m) and the apparent activation energy(Q) indicate the dependence on strain rate and temperature for flow stress respectively. The hot ductility is high when m is high and Q is low. The maps of strain rate sensitivity and apparent activation energy suggest the optimum processing conditions.