• Journal of the Microelectronics and Packaging Society
• /
• v.25 no.4
• /
• pp.143-148
• /
• 2018

Sodium silicate based silica aerogels are lower in cost than silica alkoxide based silica aerogels, but the demand is decreasing as their physical properties are lowered. In this research, acetonitrile as a drying control chemical additive (DCCA) is added in the sol state to improve the pore-structural properties of sodium silicate based silica aerogel by preventing the agglomeration of particles and cross-linked bond. The sodium silicate based silica aerogel by ambient pressure drying were prepared by sol-gel process. Acetonitrile/$Na_2SiO_3$ molar ratio of 0, 0.05, 0.1, 0.15, and 0.2 was added to the sol state. The physical properties of the final product were analyzed using Fourier transform infrared, contact angle measurement, Brunauer-Emmett-Teller and Barrett-Joyner-Halenda measurements and field emission scanning electron microscopy. It was confirmed that the sample with adding 0.15 molar ratio of acetonitrile and sodium silicate showed a high specific surface area ($577m^2/g$), a high pore volume (3.29 cc/g), and a high porosity (93%) comparable to the pore-structural properties of silica alkoxide based silica aerogels.

• Korean Chemical Engineering Research
• /
• v.49 no.5
• /
• pp.594-599
• /
• 2011

$SrAl_2O_4:Eu$ green phosphor was prepared by spray pyrolysis and its luminescence properties were controlled by replacing the Al sites with boron and using organic modifier or drying control chemical additive. It was clear that the substitution of B into the Al sites was helpful to obtain pure monoclinic $SrAl_2O_4$ phase and greatly enhance the emission intensity. In terms of the emission intensity, the optimal content of boron was about 1 at% with respect to the aluminum element. The luminescence intensity of $Sr_{0.9}Al_{1.98}B_{0.02}O_4:Eu_{0.1}$ phosphor could be improved by the use of 0.2 M organic additives in the spray solution. Futhermore, using 0.5 M dimethylformamide(DMF) as a drying control chemical with organic additives made it possible to improve about 172% the emission intensity of $Sr_{0.9}Al_{1.98}B_{0.02}O_4:Eu_{0.1}$ phosphor. According to XRD analysis, the organic additive and DMF used enhanced the crystallinity without any change in the crystal phase. When used only the organic additive without DMF, the surface area of the prepared $Sr_{0.9}Al_{1.98}B_{0.02}O_4:Eu_{0.1}$ phosphor became enlarged. The use of DMF with the organic additive resulted in significant reduction in the surface area. It was concluded that the increase of the crystallinity as well as the reduction of surface area mainly contribute to the improvement in the luminescence intensity of $Sr_{0.9}Al_{1.98}B_{0.02}O_4:Eu_{0.1}$ phosphor prepared using DMF and organic additives.

• Korean Journal of Materials Research
• /
• v.3 no.3
• /
• pp.207-214
• /
• 1993

Glass-ceramic monoliths with an ultra-low thermal expansion coefficient have been synthesized by the sol-gel technique using metal alkoxides as starting materials and dimethyl formamide as a drying control chemical additive. The ternary gels: $Li_2O\cdot Al_2O_3\cdot 2, 4 or $6SiO_2$ were obtained by hydrolysis and polycondensation reactions of metal alkoxides of silicon, aluminum and lithium. To produce cylindrical crack-free gel monoliths, excess water was used to the starting solutions and drying rates were controlled precisely to prevent cracking. In conversion process ,${\beta}$-eucryptite, $Li_2O\cdot Al_2O_3\cdot 3SiO_2$ and P-spodumene with ,${\beta}$-quartz solid solution phase were obtained by heating at the range of 750 ~$1000^{\circ}C$. Above $800^{\circ}C$, the ,${\beta}$-spodumene phase increased while ,${\beta}$-eucryptite phase decreased. The thermal expansion coefficient of the crystallized specimens were -15~ $+5{\times}{10^{-7}}/{\circ}C$ over the temperature range from room temperature to $600^{\circ}C$.

• Journal of the Korean Ceramic Society
• /
• v.47 no.6
• /
• pp.553-559
• /
• 2010

The synthesis behavior of nanoporous silica aerogel in the macroporous ceramic structure was observed using TEOS as a source material and glycerol as a DCCA(dry control chemical additive). Silica aerogel in the macroporous ceramic structure were synthesized through a sono-gel process. The wet gel in the macroporous ceramic structure were aged in ethanol for 72 h at $50^{\circ}C$. The aged wet gel was dried under supercritical drying condition. The addition of glycerol has a role of giving the uniform pore size distribution. The reproducibility of aerogel in the macroporous ceramic was improved in the glycerol(0.05 mol%) added to the silica sol and TEOS : $H_2O$=1 : 12.

• Journal of Powder Materials
• /
• v.18 no.3
• /
• pp.269-276
• /
• 2011

The synthesis behavior of nanoporous silica aerogel in the macroporous ceramic structure was observed using TEOS as a source material and glycerol as a dry control chemical additive (DCCA). Silica aerogel in the macroporous ceramic structure was synthesized via sono-gel process using hexamethyldiazane (HMDS) as a modification agent and n-hexane as a main solvent. The wet gel with a modified surface was dried at $105^{\circ}C$ under ambient pressure. The addition of glycerol appears to give the wet gel a more homogeneous microstructure. However, glycerol also retarded the rate of surface modification and solvent exchange. Silica aerogel completely filled the macroporous ceramic structure without defect in the condition of surface modification (20% HMDS/nhexane at 36hr).

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.5 no.4
• /
• pp.332-342
• /
• 1995

The important factors of reaction conditions in sol-gel transition of silicon alkoxide solution have been reviewed and discussed on the basis of Raman study. Various factors such as type of catalyst, alkoxide, solvent, drying control chemical additive and water content affect the conversion mechanism in sol-gel process.

• The Plant Pathology Journal
• /
• v.33 no.3
• /
• pp.337-344
• /
• 2017

To develop a commercial product using the mycoparasitic fungus Simplicillium lamellicola BCP, the scale-up of conidia production from a 5-l jar to a 5,000-l pilot bioreactor, optimization of the freeze-drying of the fermentation broth, and preparation of a wettable powder-type formulation were performed. Then, its disease control efficacy was evaluated against gray mold diseases of tomato and ginseng plants in field conditions. The final conidial yields of S. lamellicola BCP were $3.3{\times}10^9conidia/ml$ for a 5-l jar, $3.5{\times}10^9conidia/ml$ for a 500-l pilot vessel, and $3.1{\times}10^9conidia/ml$ for a 5,000-l pilot bioreactor. The conidial yield in the 5,000-l pilot bioreactor was comparable to that in the 5-l jar and 500-l pilot vessel. On the other hand, the highest conidial viability of 86% was obtained by the freeze-drying method using an additive combination of lactose, trehalose, soybean meal, and glycerin. Using the freeze-dried sample, a wettable powder-type formulation (active ingredient 10%; BCP-WP10) was prepared. A conidial viability of more than 50% was maintained in BCP-WP10 until 22 weeks for storage at $40^{\circ}C$. BCP-WP10 effectively suppressed the development of gray mold disease on tomato with control efficacies of 64.7% and 82.6% at 500- and 250-fold dilutions, respectively. It also reduced the incidence of gray mold on ginseng by 65.6% and 81.3% at 500- and 250-fold dilutions, respectively. The results indicated that the new microbial fungicide BCP-WP10 can be used widely to control gray mold diseases of various crops including tomato and ginseng.

• Applied Chemistry for Engineering
• /
• v.18 no.6
• /
• pp.568-574
• /
• 2007

Crack-free dried gel monoliths of the composition $Li_2O1{\cdot}7Al_2O_3{\cdot}8.6SiO_2$ have been prepared as a precursor of transparent glass-ceramic by the hydrolysis and polycondensation of mixed metal alkoxides in solutions containing N,N-dimethylformamide as the drying control chemical additive, alcohols, and water. It was investigated that activation energy for gelation according to the variation of water concentration ranged from 13 to 14 kcal/mol. Only when the amount of water for gelation was 3 times higher than the stoichiometric amount, monolithic dry gels were successfully prepared after drying at $70{\sim}75^{\circ}C$ and at a rate of 0.1~0.3%/h. The specific surface area, the pore volume, the average pore diameters of dried gel at $180^{\circ}C$ were about $239.40m^2/g$, 0.001~0.03 mL/g, and $145.62{\AA}$, respectively. It showed that the dried monolithic gel had a porous body. The DTA curve had the first exothermic peak around $800^{\circ}C$ and the 2nd peak around $980^{\circ}C$, which may correspond to crystallization of the gel.