• Proceedings of the Korean Magnestics Society Conference
• /
• 2003.06a
• /
• pp.220-221
• /
• 2003

Equiatomic FePt and CoPt alloy thin films have received considerable attention as possible magnetic and magneto-optic recording because of their high magnetic anisotropy energy and high coercivity. The high coercivity in these thin films is due to the presence of finely dispersed ordered FePt phase mixed with disordered FePt phase. However, a high temperature treatment, either substrate heating during deposition or post annealing, is needed to obtain the ordered L1$\_$0/ phase with high value of magneto crystalline anisotropy. Recent microstructural studies on these films suggest that the average grain size ranges from 10-50 nm and the grains are magnetically coupled between each other. On the other hand, the ultrahigh-density magnetic recording media with low media noise imposes the need of a material, which consists of magnetically isolated grains with size below 10 nm. The magnetic grain isolation can be controlled by the amount of additional non-magnetic element in the system which determines the interparticle separation and therefore the interparticle interactions. Recently, much research work has been done on various non-magnetic matrices. Preliminary studies showed that the samples prepared in B$_2$O$_3$ and Carbon matrices have shown strong perpendicular anisotropy and fine grain size down to 4nm, which suggest these nanocomposite films are very promising and may lead to the realization of a magnetic medium capable of recording densities beyond 1 Tb/in$^2$. So, in this work, the effect of Carbon doping on the magnetic properties of FePt nanoparticles were investigated.

• JSTS:Journal of Semiconductor Technology and Science
• /
• v.6 no.2
• /
• pp.61-67
• /
• 2006

We fabricate local damascene FinFET cell array in sub-60nm feature sized DRAM. The local damascene structure can remove passing-gate-effects in FinFET cell array. p+ boron in-situ doped polysilicon is chosen for the gate material, and we obtain a uniform distribution of threshold voltages at around 0.7V. Sub-threshold swing of 75mV/d and extrapolated off-state leakage current of 0.03fA are obtained, which are much suppressed values against those of recessed channel array transistors. We also obtain a few times higher on-state current. Based on the improved on- and off-state current characteristics, we expect that the FinFET cell array could be a new mainstream structure in sub-60nm DRAM devices, satisfying high density, low power, and high-speed device requirements.

• Korean Journal of Materials Research
• /
• v.21 no.8
• /
• pp.450-455
• /
• 2011

[ $Al_2TiO_5$ ]has a high refractive index and good solubility of the chromophore in the $Al_2TiO_5$ lattice, which allows this structure to be a good candidate for the development of new ceramic pigments. However, pure $Al_2TiO_5$ is well known to decompose on firing at $900{\sim}1100^{\circ}C$. However, this process can be inhibited by the incorporation of certain metal cations into its crystalline lattice. In this study, the synthesis of gray ceramic pigment was performed by doping cobalt on the $Al_2TiO_5$ crystal structure. The $Al_2TiO_5$ was synthesized using $Al_2O_3$ and $TiO_2$, and doped with $Co_3O_4$ as a chromophore material. In order to prevent the thermal decomposition during the cooling procedure, MgO was added to samples by 0.05 mole, 0.1 mole, and 0.15 mole as a stabilizer. The samples were fired at $1500^{\circ}C$ for 2 hours and cooled naturally. The crystal structure, solubility limit, and color of the synthesized pigment were analyzed using XRD, Raman spectroscopy, UV, and UV-vis. $Al_2O_3$ was available for the formation of $CoAl_2O_4$, which should also be considered in order to explain the small amount of this phase detected in the sample with the higher $Co^{2+}$ content (${\geq}$ 0.03 mole). It was found that the solubility limit of $Co^{2+}$ in the $Al_2TiO_5$ crystal was 0.02 mole% through an analysis of Raman spectroscopy. Through the addition of a pigment with 0.02 mole% of $Co^{2+}$ to lime-barium glaze, stabilized gray color pigments with 66.54, -2.35, and 4.68 as CIE-$L^*a^*b^*$ were synthesized.

• 한국정보디스플레이학회:학술대회논문집
• /
• 2002.08a
• /
• pp.773-776
• /
• 2002

Efficient organic white light-emitting diodes are fabricated by doping [bis(2-methyl-8-quinolinolato) (tripheny-siloxy)aluminium (III)] (SAlq), a blue-emitting layer, with a red fluorescent dye of 4-dicyanomethylene-2-methyl-6-{2-(2,3,6,7-tetrahydro-1H,5H-benzo[i,j]quinolizin-8-yl)vinyl}-4H-pyran (DCM2). The incomplete energy transfer from blue-emitting SAlq to red-emitting DCM2 enables to obtain a balanced white light-emission. A device with the structure of ITO/TPD (50 nm)/SAlq:DCM2 (30 nm, 0.5 %)/$Alq_3$ (20 nm)/LiF (0.5 nm)/AI shows emission peaks at 456 nm and 482 nm from SAlq and at 570 nm from DCM2. The white light-emitting device shows an external quantum efficiency of about 2.3 %, a luminous efficiency of about 2.4 lm/W, and the CIE chromaticity coordinates of (0.32, 0.37) at 100 cd/m^2. A maximum luminance of about 23,800 cd/m^2. is obtained at 15 V and the current density of 782 mA/cm^2.

• Transactions of the Society of Information Storage Systems
• /
• v.1 no.1
• /
• pp.34-41
• /
• 2005

We report some recent results in the rewritable Blu-ray Disc with enhanced overwrite cyclability by using the growth dominant eutectic based Ge(Sb70Te30)+Sb recording layer, GeN interface layer and write strategy optimization. We have developed phase-change optical media with appropriate write strategy for 36(i.e., 1X)-72Mbps(i.e., 2X) dual speed Blu-ray Disc system and fur the future high speed optical data storage. For recording layer, eutectic-based Ge(Sb70Te30)+Sb material was used and Sb/Te ratio and Ge content were optimized to obtain proper erasability and archival stability of recorded amorphous marks. The recording layer is wrapped up in GeN interface layers to obtain overwrite cyclability and higher crystallization speed. In addition, we designed appropriate write strategy so called Time-Shifted Multipulse (TSMP) write strategy where starting position of multipulse parts are shined from reference clock. With this write strategy, the jitter characteristics of the disc was improved and we found that leading edge jitter was improved much more than trailing edge jitter in 1X-2X speed recording. Finally, we investigated the higher speed feasibility of 144Mbps(i.e., 4X) by adopting some elemental doping to the eutectic based Ag-In-Sb-Te recording layer and structural optimization of constitution layers in Blu-ray Disc. In the paper, we report the effect of Sn addition for the feasibility of higher speed recording. The addition of Sn shows increases of the crystallization speed of phase change recording layer.

• Journal of the Korean Society of Industry Convergence
• /
• v.23 no.1
• /
• pp.25-32
• /
• 2020

Generally, high-temperature, high-pressure, high-priced sintering equipment is used for diamond sintering, and conductivity is a problem for improving the surface modification of the sintered body. In this study, to improve the efficiency of diamond sintering, we identified a new process and material that can be sintered at low temperature, and attempted to develop a composite thin film that can be discharged by doping boron gas to improve the surface modification of the sintered body. Sintered bodies were sintered by mixing Si and two diamonds in different particle sizes based on CIP molding and HIP molding. In CVD deposition, CVD was performed using WC-Co cemented carbide using CH₄ and H₂ gas, and the specimen was made conductive using boron gas. According to the experimental results of the sintered body, as the Si content is increased, the Vickers hardness decreases drastically, and the values of tensile strength, Young's modulus and fracture toughness greatly increase. Conductive CVD deposited diamond was boron deposited and discharged. As the amount of boron added increased, the strength of diamond peaks decreased and crystallinity improved. In addition, considering the release processability, tool life and adhesion of the deposition surface according to the amount of boron added, the appropriate amount of boron can be confirmed. Therefore, by solving the method of low temperature sintering and conductivity problem, the possibility of solving the existing sintering and deposition problem is presented.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2011.02a
• /
• pp.207-207
• /
• 2011

Amorphous transparent oxide semiconductors (a-TOS) have been widely studied for many optoelectronic devices such as AM-OLED (active-matrix organic light emitting diodes). Recently, Nomura et al. demonstrated high performance amorphous IGZO (In-Ga-Zn-O) TFTs.1 Despite the amorphous structure, due to the conduction band minimum (CBM) that made of spherically extended s-orbitals of the constituent metals, an a-IGZO TFT shows high mobility.2,3 But IGZO films contain high cost rare metals. Therefore, we need to investigate the alternatives. Because Aluminum has a high bond enthalpy with oxygen atom and Alumina has a high lattice energy, we try to replace Gallium with Aluminum that is high reserve low cost material. In this study, we focused on the electrical properties of IZO:Al thin films as a channel layer of TFTs. IZO:Al were deposited on unheated non-alkali glass substrates (5 cm ${\times}$ 5 cm) by magnetron co-sputtering system with two cathodes equipped with IZO target and Al target, respectively. The sintered ceramic IZO disc (3 inch ${\phi}$, 5 mm t) and metal Al target (3 inch ${\phi}$, 5 mm t) are used for deposition. The O2 gas was used as the reactive gas to control carrier concentration and mobility. Deposition was carried out under various sputtering conditions to investigate the effect of sputtering process on the characteristics of IZO:Al thin films. Correlation between sputtering factors and electronic properties of the film will be discussed in detail.

• Journal of the Korean Ceramic Society
• /
• v.30 no.5
• /
• pp.397-403
• /
• 1993

Widely used dielectrics, barium titanate was promising material for ceramic capacitor. It was produced by specific formulation with various dopants-La2O3, ZrO2, SnO2, CaZrO3, CaTiO3, CaSnO3, Bi2O3, and etc.-according to demanded properties of capacitor. In this study, we would examinate the study of dielectric properties and temperatuer characteristics (T.C.) with the amount of Bi2O3. The sample was prepared with [BaTiO3]10＋[BaZrO3, SnO2, La2O3, ZrO2]10 and Bi2O3 varied from 1.0, 1.5, 2.0, 2.5 to 3.0wt%. After milling and mixing for 15hrs, each sample was dried and then pressed at 700kg/$\textrm{cm}^2$ into pellets. Pellets were fired at 131$0^{\circ}C$, for 3hrs in air. As the result of measurements, dielectric constant, break down voltage, and insulation resistance were increased with the amount of Bi2O3, and the resonant frequency was shifted from high frequency to low frequency range. In the case of temperature characteristics, capacitance change rate was symmetrically changed at -$25^{\circ}C$ and ＋85$^{\circ}C$ respectively. Therefore, it is recognized that the temperature characteristics can be moderated with doping Bi2O3 in our study.

• Korean Journal of Materials Research
• /
• v.28 no.5
• /
• pp.273-278
• /
• 2018

Lithium-ion batteries have been considered the most important devices to power mobile or small-sized devices due to their high energy density. $LixCoO_2$ has been studied as a cathode material for the Li-ion battery. However, the limitation of its capacity impedes the development of high capacity cathode materials with Ni, Mn, etc. in them. The substitution of Mn and Ni for Co leads to the formation of solid solution phase $LiNi_xMn_yCo_{1-x-y}O_2$ (NMC, both x and y < 1), which shows better battery performance than unsubstituted $LiCoO_2$. However, despite a high discharge capacity in the Ni-rich compound (Ni > 0.8 in the metal site), poor cycle retention capability still remains to be overcome. In this study, aiming to improve the stability of the physical and chemical bonding, we investigate the stabilization effect of Ca in the Ni-rich layered compound $Li(Ni_{0.83}Co_{0.12}Mn_{0.05})O_2$, and then Ca is added to the modified secondary particles to lower the degree of cationic mixing of the final particles. For the optimization of the final grains added with Ca, the Ca content (x = 0, 2.5, 5.0, 10.0 at.%) versus Li is analyzed.

• Clean Technology
• /
• v.21 no.4
• /
• pp.235-240
• /
• 2015

In this study, vanadium dioxide was doped with titanium (0~0.5 at %) to improve thermochromic properties. The titanium doped vanadium dioxide (Ti-VO₂) particles were prepared via thermolysis process using vanadyl sulfate, ammonium bicarbonate and titianium chloride as precursors. The crystal structure, morphology, chemical bonding and thermochromic properties were investigated by using XRD, FE-SEM, XPS, DSC and UV-Vis-NIR spectroscopy. It was found that titanium was successfully doped into the crystal lattice of VO₂ and the obtained Ti-VO₂ particles have monoclinic structure. With increasing Ti concentration, the particle size and phase transition temperature of Ti-VO₂ particles decreased and NIR switching efficiency increased.