• Journal of Sensor Science and Technology
• /
• v.24 no.1
• /
• pp.41-46
• /
• 2015

In this work, pure hierarchical ZnO structure was prepared using a simple hydrothermal method, and Ag nanoparticles doped hierarchical ZnO structure was synthesized uniformly through photochemical route. The reduced graphene oxide (rGO) has been synthesized by typical Hummer's method and reduced by hydrazine. Prepared Ag/ZnO nanostructures are uniformly dispersed on the surface of rGO sheets using ultrasonication process. The synthesized samples were characterized by SEM, TEM, EDS, XRD and PL spectra. The average size of prepared ZnO microspheres was around $2{\sim}3{\mu}m$ and showed highly uniform. The average size of doped-Ag nanoparticles was 50 nm and decorated into ZnO/rGO network. The $C_2H_2$ gas sensing properties of as-prepared products were investigated using resistivity-type gas sensor. Ag/ZnO-rGO based sensors exhibited good performances for $C_2H_2$ gas in comparison with the Ag/ZnO. The $C_2H_2$ sensor based on Ag/ZnO-rGO had linear response property from 3~1000 ppm of $C_2H_2$ concentration at working temperature of $200^{\circ}C$. The response values with 100 ppm $C_2H_2$ at $200^{\circ}C$ were 22% and 78% for Ag/ZnO and Ag/ZnO-rGO, respectively. In additions, the sensor still shows high sensitivity and quick response/recovery to $C_2H_2$ under high relative humidity conditions. Moreover, the device shows excellent selectivity towards to $C_2H_2$ gas at optimal working temperature of $200^{\circ}C$.

• Journal of the Korean institute of surface engineering
• /
• v.40 no.3
• /
• pp.107-112
• /
• 2007

Aluminum doped zinc oxide (AZO) films were deposited on non-alkali glass substrate by DC magnetron sputtering with 3 types of AZO targets (doped with 1.0 wt%, 2.0 wt%, 3.0 wt% $Al_2O_3$). Electrical, optical properties and microstructure of AZO films have been investigated by Hall effect measurements, UV/VIS/NIR spectrophotometer, and XRD, respectively. Crystallinity of AZO films increased with increasing substrate temperature ($T_s$) and doping ratio of Al. Resistivity and optical transmittance in visible light were $8.8{\times}10^{-4}{\Omega}cm$ and above 85%, respectively, for the AZO film deposited using AZO target (doped with 3.0 wt% $Al_2O_3$) at $T_s$ of $300^{\circ}C$. On the other hand, transmittance of AZO films in near-infrared region decreased with increasing $T_s$ and doping ratio of Al, which could be attributed to the increase of carrier density.

• Korean Journal of Materials Research
• /
• v.9 no.2
• /
• pp.173-180
• /
• 1999

Thermally evaporated ZnTe films were investigated as a back contact material for CdS/CdTe solar cells. Two deposition methods, coevaporation and double-layer methods, were used for Cu doping in ZnTe films. ZnTe layers (0.2$\mu\textrm{m}$ thick) were deposited either on glass or on CdS/CdTe substrates without intentional heating of the substrates. Post-deposition annealing was performed at 200,300 and $400^{\circ}C$ for 3,6 and 9 minutes, respectively. Band gap of 2.2eV was measured for both undoped and doped films and a slight change in the shape of absorption spectra was observed in Cu-doped samples after annealing at $400^{\circ}C$. The resistivity of as-deposited ZnTe decreased from 10\ulcorner~10\ulcornerΩcm down to 10\ulcornerΩcm as Cu concentration increased from 0 to 14 at.%. There was not a noticeable change in less of annealing temperature up to $300^{\circ}C$ whereas films annealed at $400^{\circ}C$ revealed hexagonal (101) orientations as well. Some of Cu-doped ZnTe revealed x-ray diffraction (XRD) peaks related with Cu\ulcornerTe(x=1.75~2). Grain growth was observed from about 20nm in as-deposited films to 50nm after annealing at $400^{\circ}C$ by scanning electron microscopy (SEM). Cu distribution in ZnTe films was not uniform according to Auger electron spectroscopy (AES) measurements.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2008.11a
• /
• pp.355-356
• /
• 2008

In this work, ZnO films doped with different contents of Indium (0.1at.%, 0.3at.%, 0.6at.%, respectively) were deposited on Si (111) substrate that has 1~20 $\Omega$cm by pulsed laser deposition (PLD) at $600^{\circ}C$ for 30min. The thickness of the films are about 250 nm. The structural, optical and electrical properties of the films were investigated using X-ray Diffraction (XRD), Atomic force microscope (AFM), Photoluminescence (PL) and Hall measurement. It has been found that RMS of the films is decreased and grain size is increased with increasing the contents of doped Indium. The results of the Photoluminescence properties were indicated that the films have UV emission about 380nm and shows a little red shitf with increasing contents of doped indium. The result of the Hall measurement shows that the concentration and resisitivity in doped ZnO are as changing as one order, respectively ${\sim}10^{18}/cm^2$, ${\sim}10^{-2}cm{\Omega}cm$.

• Journal of Powder Materials
• /
• v.29 no.5
• /
• pp.370-375
• /
• 2022

Cu-doped ZnSe quantum dots were successfully synthesized in an aqueous solution using an internal doping method. The effects of ligand type, CuSe synthesis temperature, and heating time on Cu-doped ZnSe synthesis were systematically investigated. Of MPA, GSH, TGA, and NAC used as ligands, MPA was the optimal ligand as determined by PL spectrum analysis. In addition, the emission wavelength was found to depend on the synthesis temperature of the internal doping core of CuSe. As the temperature increased, the doping of Cu²⁺ was enhanced, and the emission wavelength band was redshifted; accordingly, the emission peaks moved from blue to green (up to 550 nm). Thus, the synthesis of Cu:ZnSe using internal doping in aqueous solutions is a potential method for ecomanufacturing of color-tuned ZnSe quantum dots for display applications.

• Journal of the Korean Vacuum Society
• /
• v.7 no.1
• /
• pp.51-58
• /
• 1998

ZnS and TB-doped ZnS (ZnS:Tb) thin films were grown by traveling wave reactor atomic layer epitaxy (AKE) and characterized using materials and surface analysis techniques. $ZnCl_2$, $H_2$S,and tris(2,26,6-tetramethyl-3,5-heptandionato) terbium ($Tb(TMHD)_3$) were used as the precursors in the growth of ZnS:Tb films. The dependence of Cl content in ZnS films on growth temperature was investigated using Rutherford backscattering spectrometry. The Cl content decreased from approximately 9 at.% to 1 at. % as increasing the growth temperature from 400 to $500^{\circ}C$. The segregation of Cl in near surface region was also observed by depth profiling using Auger electron spectroscopy. Scanning electron microscopic studies showed that the ALE-grown ZnS and ZnS:Tb film during ALE process using $Tb(TMHD)_3$was also investigated. Approximately 1 at.% of O in ZnS:Tb(0.5 at.%) film which showed a good crystallinity of hexagonal 2H structure.

• Journal of Powder Materials
• /
• v.12 no.6 s.53
• /
• pp.399-405
• /
• 2005

Nanopowders of titanium dioxide $(TiO_2)$ incorporating the transition metal element(s) were synthesized by flame synthesis method. Single element among Fe(III), Cr(III), and Zn(II) was doped into the interior of $TiO_2$ crystal; bimetal doping of Fe and Zn was also made. The characteristics of transition-metal-doped $TiO_2$ nanopowders in the particle feature, crystallography and electronic structures were determined with various analytical tools. The chemical bond of Fe-O-Zn was confirmed to exist in the bimetal-doped $TiO_2$ nanopowders incorporating Fe-Zn. The transition element incorporated in the $TiO_2$ was attributed to affect both Ti 3d orbital and O 2p orbital by NEXAFS measurement. The bimetal-doped $TiO_2$ nanopowder showed light absorption over more wide wavelength range than the single-doped $TiO_2$ nanopowders.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1998.06a
• /
• pp.121-124
• /
• 1998

Generally the structure of powder electroluminescent devices (PELDs) on ITO-film was makeup of the ZnS:Cu phosphor layer and BaTiO$_3$ insulating layer. The active layer, which consists of a suitably doped ZnS powder mixed in a dielectric, is sandwiched between two electrodes; one of which are ITO film and the other is aluminum. In this paper, three kinds of powder eleotroluminescent devices (PELDs) : WK-A(ITO/BaTiO$_3$/ZnS:Cu/Silver paste). WK-B(ITO/BaTiO$_3$+ZnS:Cu/Silver paste) and WK-C(ITO/BaTiO$_3$/ZnS:Cu/BaTiO$_3$/Silver paste), fabricated by spin coating method, were investigated. To evaluate the luminescence properties of three kinds of PELDs, EL emission spectroscopy, transferred charge density and time response of EL emission intensity under square wave voltage driving were measured.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.22 no.10
• /
• pp.814-820
• /
• 2009

Antimony (Sb) doped ZnO thin films (0.1 at.%) were deposited on sapphire (0001) substrates at various temperatures (200 - 600$^{\circ}C$) by using pulsed laser deposition technique. All the thin films have been characterized by X-ray diffractometer, atomic force microscopy and spectrophotometer to investigate their structural, morphological and optical properties, respectively. Hall measurements were also carried out to identify the electrical properties of the thin films. These thin films were constituted in wurtzite structure with the preferential orientation of (002) diffraction plane and had as high as 80% optical transmission in the visible range. The bandgap energy also was determined by spectrophotometer which was around 3.28 eV. Hall measurements results revealed that the Sb dope ZnO thin film (0.1 at.%) grown at $500^{\circ}C$ exhibited p-type conduction with a carrier concentration of $8.633\times10^{16}\;cm^{-3}$, a mobility of $1.41\;cm^2/V{\cdot}s$ and a resistivity of $51.8\;\Omega{\cdot}cm$. We have successfully achieved p-type conduction in antimony doped ZnO thin films with low doping level even though the electrical properties are not favorable. This paper suggests the feasibility of p-type doping with large-size-mismatched dopant by using pulsed laser deposition.

• 한국신재생에너지학회:학술대회논문집
• /
• 2005.06a
• /
• pp.154-159
• /
• 2005

Low RF power density was used for preparing transparent conducting AI-doped ZnO (AZO) thin films by RF Magnetron Sputtering on Corning 1737 glass. The dependence of films' structural, optical and electrical properties on sputtering gas, film's thickness and substrate temperature were investigated. Low percent of incorporated H2 in Ar sputtering gas has proven to reduce film's resistivity and sheet resistance as low as $4.1\times10^{-3}{\Omega}.cm$. It also formed new preferred peaks orientation of (101) and (100) which indicated that the c-axis of AZO films was parallel to the substrate. From UN-VIS-NIR Spectrophotometer analysis, it further showed high optical transmittance at about $\~ 90\%$ at visible light spectra (400-700nm).