• Magazine of the Korean Society of Agricultural Engineers
• /
• v.26 no.3
• /
• pp.46-58
• /
• 1984

This study was carried out to investigate the compressive strength and the other effects varying to seasons and curing days on the wet curing conditions of the plain concrete. The results obtained are summarized as follows; 1. The longer the wet curing days and the higher the temperature, the greater the compressive strength was expected. 2.。$_2$8, compressive strength of concrete at 28 days under the dry curing conditions showed a range in 64-76% of that under the wet curing conditions. 3. The seasonal variations in the compressive strength under the wet curing showed in order of summer>spring=autumn>winter, and that under the dry curing were in order of spring ≒autumn> summer> winter. 4. In order to obtain 90% of the design compressive strength, 7 days in spring or autumn and 2 weeks of the wet curing in summer were required. 5. The compressive strength of concrete under the wet curing by using wet straw bag cover was almost the same as that of water curing method. 6. Under the wet curing conditions, the higher the temperature, the greater the effect of the curing of concrete was obtained, however, the compressive strength of concrete was decreased under relatively higher (over 15$^{\circ}$ C) and lower temperature (below 4$^{\circ}$C). 7. Freezing damage was occured when temperature was below 0$^{\circ}$ C and humidity was relatively high. 8. A considerable differnce between estimation of $^{\circ}$$_2$8 from $^{\circ}$7 and measured one was appeared in case of the dry curing conditions. Oregon formula was appeared to be acceptable under the wet curing conditions. 9. In relationship between $^{\circ}$$_2$8 and $^{\circ}$7~, $^{\circ}$28=1. 52 $^{\circ}$7 under the wet curing conditions except winter season, and $^{\circ}$$_2$8 =(1.39-1, 48)$^{\circ}$7 under the dry curing conditions were shown.

• Computers and Concrete
• /
• v.19 no.4
• /
• pp.419-427
• /
• 2017

With the rising global environmental awareness on energy saving and carbon reduction, as well as the environmental transition and natural disasters resulted from the greenhouse effect, waste resources should be efficiently used to save environmental space and achieve environmental protection principle of "sustainable development and recycling". This study used recycled cement mortar and adopted the volumetric method for experimental design, which replaced cement (0%, 10%, 20%, 30%) with recycled materials (fly ash, slag, glass powder) to test compressive strength and ultrasonic pulse velocity (UPV). The hyperbolic function for nonlinear multivariate regression analysis was used to build prediction models, in order to study the effect of different recycled material addition levels (the function of $R_m$(F, S, G) was used and be a representative of the content of recycled materials, such as fly ash, slag and glass) on the compressive strength and UPV of cement mortar. The calculated results are in accordance with laboratory-measured data, which are the mortar compressive strength and UPV of various mix proportions. From the comparison between the prediction analysis values and test results, the coefficient of determination $R^2$ and MAPE (mean absolute percentage error) value of compressive strength are 0.970-0.988 and 5.57-8.84%, respectively. Furthermore, the $R^2$ and MAPE values for UPV are 0.960-0.987 and 1.52-1.74%, respectively. All of the $R^2$ and MAPE values are closely to 1.0 and less than 10%, respectively. Thus, the prediction models established in this study have excellent predictive ability of compressive strength and UPV for recycled materials applied in cement mortar.

• Computers and Concrete
• /
• v.32 no.2
• /
• pp.149-163
• /
• 2023

One of the main design parameters traditionally utilized in projects of geotechnical engineering is the uniaxial compressive strength. The present paper employed three artificial intelligence methods, i.e., the stochastic fractal search (SFS), the multi-verse optimization (MVO), and the vortex search algorithm (VSA), in order to determine the compressive strength of concrete (CSC). For the same reason, 1030 concrete specimens were subjected to compressive strength tests. According to the obtained laboratory results, the fly ash, cement, water, slag, coarse aggregates, fine aggregates, and SP were subjected to tests as the input parameters of the model in order to decide the optimum input configuration for the estimation of the compressive strength. The performance was evaluated by employing three criteria, i.e., the root mean square error (RMSE), mean absolute error (MAE), and the determination coefficient (R²). The evaluation of the error criteria and the determination coefficient obtained from the above three techniques indicates that the SFS-MLP technique outperformed the MVO-MLP and VSA-MLP methods. The developed artificial neural network models exhibit higher amounts of errors and lower correlation coefficients in comparison with other models. Nonetheless, the use of the stochastic fractal search algorithm has resulted in considerable enhancement in precision and accuracy of the evaluations conducted through the artificial neural network and has enhanced its performance. According to the results, the utilized SFS-MLP technique showed a better performance in the estimation of the compressive strength of concrete (R²=0.99932 and 0.99942, and RMSE=0.32611 and 0.24922). The novelty of our study is the use of a large dataset composed of 1030 entries and optimization of the learning scheme of the neural prediction model via a data distribution of a 20:80 testing-to-training ratio.

• Journal of the Korea Institute of Building Construction
• /
• v.23 no.1
• /
• pp.35-43
• /
• 2023

In this study, the mechanical properties of concrete mixed with non-sintered hwangto(NHT) as an alternate material for cement were evaluated, and the compressive strength prediction equation of concrete based on ultrasonic pulse velocity analysis was proposed. Cement replacement rates for mixed NHT were set to 0, 15, and 30%, and design compressive strength was set to 30 and 45MPa to evaluate the effect on the amount of cement and NHT powder. The mechanical properties items analyzed were compressive strength, ultrasonic pulse velocity, and elastic modulus, and were measured on days 1, 3, 7, and 28. As the replacement rate of NHT increased, the mechanical properties tended to decrease. In addition, as a result of analyzing the correlation between compressive strength and ultrasonic pulse velocity, the correlation coefficient(R²) showed a high relationship(R²=0.95) on concrete mixed with NHT.

• Geomechanics and Engineering
• /
• v.19 no.4
• /
• pp.307-314
• /
• 2019

Light construction waste (LCW) particles are pieces of light concrete or insulation wall with light quality and certain strength, containing rich isolated and disconnected pores. Mixing LCW particles with soil can be one of the alternative lightweight soils. It can lighten and stabilize the deep-thick soft soil in-situ. In this study, the unconfined compressive strength (UCS) and its mechanism of Construction Waste Stabilized Lightweight Soil (CWSLS) are investigated. According to the prescription design, totally 35 sets of specimens are tested for the index of dry density (DD) and unconfined compressive strength (UCS). The results show that the DD of CWSLS is mainly affected by LCW content, and it decreases obviously with the increase of LCW content, while increases slightly with the increase of cement content. The UCS of CWSLS first increases and then decreases with the increase of LCW content, existing a peak value. The UCS increases linearly with the increase of cement content, while the strength growth rate is dramatically affected by the different LCW contents. The UCS of CWSLS mainly comes from the skeleton impaction of LCW particles and the gelation of soil-cement composite slurry. According to the distribution of LCW particles and soil-cement composite slurry, CWSLS specimens are divided into three structures: "suspend-dense" structure, "framework-dense" structure and "framework-pore" structure.

• Proceedings of the Korea Concrete Institute Conference
• /
• 1998.10b
• /
• pp.706-711
• /
• 1998

Structural tests of the PSC Beam bridge using high strength concrete, concrete compressive strength 700kg/$\textrm{cm}^2$, are conducted for the application including durability and serviceability of the bridge. Current design safety factors with respect to the jacking force and the service design load DB-24 are applied to the design of the bridge. Concrete compressive strength 700kg/$\textrm{cm}^2$, girder depth 2.3m, girder space 3.2m, span length 20m, and slab thickness 27cm are selected for the bridge test. The Bulb-Tee section of the girders is applied instead of I section because it is well known more stable to the longer span(40m). Static load test(4 beams) with composite and non-composite section, and fatigue load test(1 beams) with composite section are conducted. Crack moment, ultimate load, deflections with load steps, and strains of the beam section for those bridges are investigated. The structural test results of the bridges showed a good performance for a safety and a serviceability.

• Journal of the Korean Society for Railway
• /
• v.7 no.4
• /
• pp.319-325
• /
• 2004

In this study, analysis and design programs of bending of RC beams strengthened with fiber sheets are developed by using Visual Basic Language. The program consists two groups, ultimate strength method and nonlinear flexural analysis method. Ultimate strength method regards concrete compressive stress as a rectangular stress block and do not consider tensile stress of concrete and load-deflection curves. On the other hand, nonlinear flexural analysis considers tensile stress of concrete, load-deflection curves, state of stress distribution and failure strain of strengthening material. Also, the analysis method used in this study regards nonlinear flexural stress as compressive stress of concrete. This program can be a good tool for determining the bending strength of strengthened RC beams and estimating the amount of fiber sheets for practical use.

• Proceedings of the Korea Concrete Institute Conference
• /
• 1994.10a
• /
• pp.167-170
• /
• 1994

To reduce the size of structural members, high strength concrete has recently been utilized for structure such as ultra-high-rise buildings and prestressed concrete bridges in North America, and its compressive strength has gone up to 1300kg/$\textrm{cm}^2$. In Japan, research on high-strength concrete has been undertaken on a large scale by the national enterprise so-called New RC Project. And high-strength concrete with a design compressive strength over 450kg/$\textrm{cm}^2$ has recently been employed for high rised reinforced concrete building. As a result of the serious land availability situation of metropolitan areas in the world, buildings will become taller, and even higher strengths will be required. In the future, the utilization of high-strength concrete will spread widely through the development of new structural concepts, application of steels of a higher yield stress, silica fume, and other new materials. Considering these circumstance, the aim of this experimental study is to develop ultra-high-strength concrete with compressive strength over 1800kg/$\textrm{cm}^2$ with domestic current materials. There are so many factors which influence the manufacturing of ultra-high-strength concrete. The experimental factors selected in this study are mixing methods, curing methods, water-binder ratio, maximum size of coarse by silica fume. The results of this experimental study show that it is possible to develop the ultra-high-strength concrete with compressive strength over 1700kg/$\textrm{cm}^2$ at 28days, 1800kg/$\textrm{cm}^2$ at 56 days.

• Proceedings of the Korea Concrete Institute Conference
• /
• 1994.10a
• /
• pp.171-174
• /
• 1994

To reduce the size of structural members, high strength concrete has recently been utilized for structure such as ultra-high-rise buildings and prestressed concrete bridges in North America, and its compressive strength has gone up to 1300kg/$\textrm{cm}^2$. In Japan, research on high-strength concrete has been undertaken on a large scale by the national enterprise so-called New RC Project. And high-strength concrete with a design compressive strength over 450kg/$\textrm{cm}^2$ has recently been employed for high rised reinforced concrete building. As a result of the serious land availability situation of metropolitan areas in the world, buildings will become taller, and even higher strengths will be required. In the future, the utilization of high-strength concrete will spread widely through the development of new structural concepts, application of steels of a higher yield stress, silica fume, and other new materials. Considering these circumstance, the aim of this experimental study is to develop ultra-high-strength concrete with compressive strength over 1800kg/$\textrm{cm}^2$ with domestic current materials. There are so many factors which influence the manufacturing of ultra-high-strength concrete. The experimental factors selected in this study are mixing methods, curing methods, water-binder ratio, maximum size of coarse by silica fume. The results of this experimental study show that it is possible to develop the ultra-high-strength concrete with compressive strength over 1700kg/$\textrm{cm}^2$ at 28days, 1800kg/$\textrm{cm}^2$ at 56 days.

• Journal of the Korea Institute of Building Construction
• /
• v.7 no.4
• /
• pp.145-151
• /
• 2007

In this paper, tests are carried out in order to investigate the strength development of concrete under various binder types, W/B and curing temperature ranged from $5{\sim}20^{\circ}C$. Fly ash and blast furnace slag were incorporated by as much as 30%, respectively. Strength development of concrete are estimated using Logistic model and strength ratio of concrete at 28days to that at early age are also investigated. According to experimental results, it is found that good agreements are obtained between measured values and calculated ones using logistic model below $20^{\circ}C$. Strength ratio of concrete at 28days to that at early age increases in case W/B decreases and curing temperature increases. Tables and graphs for strength ratio of concrete are provided in this paper. It is capable of obtaining and predicting the periods to attain design strength by considering increment factor of strength easily with the table and graphs presented in this paper. This paper presents the reference data to decide removal time of form, time to reach target strength and strength inspection of remicon whether the test specimens meet the specified criteria of compressive strength. Multi regression models with respect to the relationship between 7days compressive strength and 28 days compressive strength depending on W/B and admixture types are presented.