• 대한치과기공학회지
• /
• 제21권1호
• /
• pp.123-130
• /
• 1999

I attempted to suggest a better method to separate a refractory cast in order to solve the problems caused by bonding between refractory casts and ceramics in the firing-processing of all ceramic crowns as a part of dental prosthodontics. I emphasize the advantages and effectiveness of easy separation after firing by using the separating materials about the refractory cast dies. 1. We must not usse HF(55%) that is used as the chemical separating methods. 2. We decrease such methods as grinding, blasting, bur, and point 3. We can save time, costs and manual labors by using this methods. 4. This method regulates the expansion and constriction of heat because of the chemical reaction of the separating materials. 5. This method contribute to the breaking down without modification by minimizing the chemical and mechanical damages of the marginal and interior parts.

• The Journal of Advanced Prosthodontics
• /
• 제4권3호
• /
• pp.162-169
• /
• 2012

PURPOSE. Fracture of the veneering material of zirconia restorations frequently occurs in clinical situations. The purpose of this in vitro study was to compare the fracture strengths of zirconia crowns veneered with various ceramic materials by various techniques. MATERIALS AND METHODS. A 1.2 mm, $360^{\circ}$ chamfer preparation and occlusal reduction of 2 mm were performed on a first mandibular molar, and 45 model dies were fabricated in a titanium alloy by CAD/CAM system. Forty-five zirconia copings were fabricated and divided into three groups. In the first group (LT) zirconia copings were veneered with feldspathic porcelain by the layering technique. In the second group (HT) the glass ceramic was heat-pressed on the zirconia coping, and for the third group (ST) a CAD/CAM-fabricated high-strength anatomically shaped veneering cap was sintered onto the zirconia coping. All crowns were cemented onto their titanium dies with Rely $X^{TM}$ Unicem (3M ESPE) and loaded with a universal testing machine (Instron 5583) until failure. The mean fracture values were compared by an one-way ANOVA and a multiple comparison post-hoc test (${\alpha}$= 0.05). Scanning electron microscope was used to investigate the fractured interface. RESULTS. Mean fracture load and standard deviation was $4263.8{\pm}1110.8$ N for Group LT, $5070.8{\pm}1016.4$ for Group HT and $6242.0{\pm}1759.5$ N for Group ST. The values of Group ST were significantly higher than those of the other groups. CONCLUSION. Zirconia crowns veneered with CAD/CAM generated glass ceramics by the sintering technique are superior to those veneered with feldspathic porcelain by the layering technique or veneered with glass ceramics by the heat-pressing technique in terms of fracture strength.

• 대한치과기공학회지
• /
• 제38권3호
• /
• pp.111-117
• /
• 2016

Purpose: The present study was performed to investigate the effect of abutment inclined angle on the marginal fit of zirconia all-ceramic crown. Methods: The Ti abutments with 3 different inclined angle($2^{\circ}$, $4^{\circ}$ and $6^{\circ}$) were fabricated. The zirconia copings were fabricated for each abutment by using dental CAD/CAM system. The manufactured zirconia copings were duplicated through silicone replica technique, and a replicated specimen was sectioned in the center of bucco-lingual and mesio-distal axial to measure the marginal fit by using a stereo microscope. The results were analyzed using a one-way ANOVA with SPSS 22.0 for Windows(${\alpha}=0.05$). Results: On the bucco-lingual axial, marginal fit was the RL3($41.5{\pm}3.4{\mu}m$), RL2($44.3{\pm}4.3{\mu}m$) and RL1($47.5{\pm}5.7{\mu}m$), respectively. On the mesio-distal axial, marginal fit was the RL3($41.1{\pm}3.7{\mu}m$), RL2($45.7{\pm}5.3{\mu}m$) and RL1($46.2{\pm}4.5{\mu}m$), respectively. One-way ANOVA showed statistically significant difference between groups for marginal fit(p<0.05). Conclusion: For marginal fit of the abutments inclined angle, RL3 specimen was superior. The abutment inclined angle had influence on marginal fit of the zirconia copings. The marginal fit of each group were within clinically acceptable range.

• Restorative Dentistry and Endodontics
• /
• 제43권3호
• /
• pp.27.1-27.9
• /
• 2018

Objectives: The aim of this in vitro study was to evaluate the effects of the thickness and shade of 3 types of computer-aided design/computer-aided manufacturing (CAD/CAM) materials. Materials and Methods: A total of 120 specimens of 2 shades (A1 and A3) and 2 thicknesses (1 and 2 mm) were fabricated using VITA Mark II (VM; VITA Zahnfabrik), IPS e.max CAD (IE; IvoclarVivadent), and VITA Suprinity (VS; VITA Zahnfabrik) (n = 10 per subgroup). The amount of light transmission through the ceramic specimens was measured by a radiometer (Optilux, Kerr). Light-cured resin cement samples (Choice 2, Bisco) were fabricated in a Teflon mold and activated through the various ceramics with different shades and thicknesses using an LED unit (Bluephase, IvoclarVivadent). In the control group, the resin cement sample was directly light-cured without any ceramic. Vickers microhardness indentations were made on the resin surfaces (KoopaPazhoohesh) after 24 hours of dark storage in a $37^{\circ}C$ incubator. Data were analyzed using analysis of variance followed by the Tukey post hoc test (${\alpha}=0.05$). Results: Ceramic thickness and shade had significant effects on light transmission and the microhardness of all specimens (p < 0.05). The mean values of light transmittance and microhardness of the resin cement in the VM group were significantly higher than those observed in the IE and VS groups. The lowest microhardness was observed in the VS group, due to the lowest level of light transmission (p < 0.05). Conclusion: Greater thickness and darker shades of the 3 types of CAD/CAM ceramics significantly decreased the microhardness of the underlying resin cement.

• The Journal of Advanced Prosthodontics
• /
• 제14권2호
• /
• pp.96-107
• /
• 2022

PURPOSE. Microstructural and physico-mechanical characterization of highly translucent zirconia, prepared by milling technology (CAD-CAM) and repeated firing cycles, was the main aim of this in vitro study. MATERIALS AND METHODS. Two groups of samples of two commercial highly-translucent yttria-stabilized dental zirconia, VITA YZ-HT^White (Group A) and Zolid HT + White (Group B), with dimensions according to the ISO 6872 "Dentistry - Ceramic materials", were prepared. The specimens of each group were divided into two subgroups. The specimens of the first subgroups (Group A₁ and Group B₁) were merely the sintered specimens. The specimens of the second subgroups (Group A₂ and Group B₂) were subjected to 4 heat treatment cycles. The microstructural features (microstructure, density, grain size, crystalline phases, and crystallite size) and four mechanical properties (flexural strength, modulus of elasticity, Vickers hardness, and fracture toughness) of the subgroups (i.e. before and after heat treatment) were compared. The statistical significance between the subgroups (A₁/A₂, and B₁/B₂) was evaluated by the t-test. In all tests, P values smaller than 5% were considered statistically significant. RESULTS. A homogenous microstructure, with no residual porosity and grains sized between 500 and 450 nm for group A and B, respectively, was observed. Crystalline yttria-stabilized tetragonal zirconia was exclusively registered in the X-ray diffractograms. The mechanical properties decreased after the heat treatment procedure, but the differences were not statistically significant. CONCLUSION. The produced zirconia ceramic materials can be safely (i.e., according to the ISO 6872) used in extensive fixed prosthetic restorations, such as substructure ceramics for three-unit prostheses involving the molar restoration and substructure ceramics for prostheses involving four or more units. Consequently, milling technology is an effective manufacturing technology for producing zirconia substructures for dental fixed all-ceramic prosthetic restorations.

• 치위생과학회지
• /
• 제9권4호
• /
• pp.405-412
• /
• 2009

본 연구는 도재소부용 비귀금속에 Au 코팅 층을 형성하고, Au 코팅 층이 금속-도재의 결합력에 미치는 영향을 알아보고자 2출 굴곡 시험 후에 SEM/EDS 방법으로 조사하여 비교하였다. 1. Ni-Cr ally 군과 Co-Cr alloy 군, 그리고 Ti 군의 절단면 시편의 전자현미경 사진에서 Au 코팅 층은 산화층의 확산을 제어하는 것으로 관찰되었다. 2. 2축 굴곡 시험 후에 EDS 분석 결과 Ni-Cr alloy 군과 Co-Cr alloy 군에서 Si 함량은 Au 코팅 층을 형성한 시편에서 약간 감소하였고, 결합실패의 형태는 cohesive failure와 adhesive failure가 혼재된 양상으로 관찰되었다. 3. Ni-Cr alloy 군과 Co-Cr alloy 군에서 Au 코팅 층은 도재-금속 결합력에 미치는 영향은 미미하였다. 4. Ti 군의 결합실패 형태는 Ni-Cr alloy 군과 Co-Cr alloy 군에 비해서 adhesive failure 양상이 두드러지게 관찰되었고, Au 코팅 층은 도재-금속 결합력에 영향을 미치지 않았다. 이상의 결과 비귀금속에 적용한 Au 코팅은 산화층의 확산을 제어 하는 것으로 관찰 되었으나, 금속-도재 간의 결합력 증징에 미치는 효과는 미미하였다. Au 코팅을 이용하여 금속-도재 간의 결합력 증진을 위해서는 많은 연구가 지속되어야 할 것으로 사료된다.

• 대한치과재료학회지
• /
• 제43권4호
• /
• pp.343-349
• /
• 2016

This experiment was carried out to examine whether the post-firing heat treatment is effective in increasing the hardness of metal-ceramic alloy of the Pd-Au-Ag-Sn system. Precipitation hardening by holding at $600^{\circ}C$ after simulated complete porcelain firing in a metal-ceramic alloy of the Pd-Au-Ag-Sn system was examined by observing the change in hardness, crystal structure, and microstructure using a hardness test, X-ray diffraction (XRD), and field emission scanning electron microscopy (FE-SEM). The hardness of the alloy increased apparently by holding the specimen at $600^{\circ}C$ for 30 min after simulated complete porcelain firing. The formation of fine grain interior precipitates during holding at $600^{\circ}C$ caused the formation of lattice strain in the grain interior, resulting in apparent hardening. The faster cooling rate (stage 0) during simulated complete porcelain firing resulted in more effective precipitation hardening during holding at $600^{\circ}C$. From the above results, an appropriate post-firing heat treatment, such as holding at $600^{\circ}C$ for 30 min after complete porcelain firing may increase the durability of metal-ceramic prostheses composed of Pd-Au-Ag-Sn alloy.

• 한국세라믹학회지
• /
• 제55권2호
• /
• pp.95-107
• /
• 2018

This presentation will give an overview of Ca-aluminate based biomaterials and their proposed use within the field of nanostructured biomaterials. The paper describes typical features of Ca-aluminate materials with regard to technology, chemistry, biocompatibility including hemocompatibility and bioactivity, and developed microstructure. Special focus will be on the developed microstructure, which is in the nanosize range. Application possibilities within odontology, orthopedics, and drug delivery are presented. The nanostructure including pore size below 5 nm in these structures opens up this material for some use in specific dental-related applications in which antibacterial and bacteriostatic aspects are of importance, and as thin coating on implants within dental and orthopaedic applications. Nanosize porosity is essential in drug delivery systems for controlled release of medicaments. The priority field for Ca-aluminate biomaterials is implant materials, which use minimally-invasive techniques to offer in vivo, on-site developed biomaterials.

• 대한치과의사협회지
• /
• 제56권9호
• /
• pp.503-511
• /
• 2018

Outcome of esthetic ceramic restorations are affected by tooth size, gingival contour, occlusal relationship, etc. For this reason, demand of orthodontic treatment before esthetic ceramic restoration is increasing. If a Bolton ratio discrepancy, a problem of the maxillary incisor's vertical position, a problem of inclination of anterior teeth, a pathogenic occlusion is existed, a pre-prosthodontic orthodontics should be accomplished. These problems can be satisfactory only after the prosthetic treatment is performed after orthodontic treatment. When orthodontic treatment is given, it should be treated with the following principle. 1. Treat it in the direction of functioning occlusion. 2. Keep the patient's stable occlusal scheme. 3. Treat the teeth by considering the average tooth size and Bolton ratio. Ortho-Prostho combined treatment with optimal treatment plan can lead a patient's function, esthetics, and long-term stability.

• 구강회복응용과학지
• /
• 제29권4호
• /
• pp.359-365
• /
• 2013

본 연구는 lithium disilicate glass-ceramic과 상아질 간의 결합력에 대한 임시 수복재와 임시 충전재의 효과를 평가하기 위함이 목적이었다. 60개의 발치된 치아를 자가중합형 레진에 포매한 후 교합1/3 부위를 절단하였고, 무작위로 15개씩 4그룹으로 나누었다. 그런 후 lithium disilicate glass-ceramic을 다음과 같이 그룹으로 나누어 상아질에 접착시켰다: 아무 처리도 하지 않은 그룹(그룹A), ALIKETM (GC America Inc.)를 적용한 그룹(그룹 B), Luxatemp$^{(R)}$ Automix plus (DMG, Germany)를 적용한 그룹(그룹 C), Fermit$^{(R)}$ (Ivoclar Vivadent, Leichtenstein)를 적용한 그룹(그룹 D). 모든 시편들을 24시간 증류수에 담가 보관한 후, 1 mm/min의 crosshead speed로 만능시험기(Zwick 1456 41, Zwick, Germany) 상에서 전단 결합 강도를 측정하였다. 모든 그룹 간에 결합력의 통계학적 유의성은 없었으며, 파절양상은 대부분 시편에서 접착성(adhesive)과 응집성(cohesive)이 복합적으로 보이는 혼합형(mixed type)을 보였다. 본 실험의 제한된 조건 하에서는 임상에서 lithium disilicate glass-ceramic을 상아질에 접착시, 임시 수복재나 임시 충전재의 영향이 그리 크지 않을 것으로 판단되었다.