• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2013년도 춘계 학술논문 발표대회
• /
• pp.334-336
• /
• 2013

In this study, the temperature history was evaluated for the improved bubble sheets combining hot wires and PE films, which were developed under the extreme environmental condition of -10℃ and applied on the top surface of slab to prevent initial damage by freezing. Results can be summarized as follows. If improved bubble sheets combining hot wires with different capacity on double and quadruple bubble sheets are used, the temperature history for all materials decreased to 2~3℃ below zero but all test materials except Type 1 secured the accumulative temperature of 45° D·D at 7 days of material age, required for the prevention of initial freezing damage. This indicates the bubble sheets can prevent the initial damage by freezing.

• 접착 및 계면
• /
• 제21권3호
• /
• pp.93-100
• /
• 2020

적층제조법 기반의 3D 프린팅 기술은 사용자가 원하는 상품을 출력하여 제공하지만 고온의 사용 환경 및 용융된 필라멘트 수지의 냉각 과정에서 변동적 수축현상이 발생하여 상품의 출력편차를 야기한다. 본 연구에서는 출력물의 들뜸과 뒤틀림을 방지하고 정밀한 형상의 고품질 출력물을 제작하기 위하여 3D 프린터 빌드시트용 아크릴 점착제를 연구하였다. 고온에서 점착특성이 유지되고 점착제로부터 출력물의 안착과 원활한 탈거를 위해 부착성과 강인성이 우수하고 높은 유리전이온도를 갖는 4-acryloylmorpholine (ACMO)를 첨가하여 무용제 타입의 점착제 조성물을 설계하였다. 단량체의 후첨가방식을 사용하여 두 단계를 통해 아크릴 조성물을 합성하였고, 합성된 조성물로 코팅한 점착제 필름을 다각도에서 분석하였다. 그 결과 제조된 점착제는 높은 유리전이온도를 보이고 열처리 전/후에 따른 박리강도 차이가 보이지 않았으며, 유변학적 물성 분석을 통해 점착제의 우수한 접착력 뿐만 아니라 변형 없이 탈착이 가능한 물성을 갖음을 확인하였다. 본 연구에서 제조된 점착제를 3D 프린터의 빌드시트로 활용하였을 때 안착성 및 작업성이 양호하고 출력편차가 적은 출력물을 얻었다. 기존 판매중인 빌드시트와 비교하였을 때 본 연구에서 제조한 점착제 위에서는 출력물이 원활하게 탈거가 가능하기 때문에 FDM 방식 3D프린터의 사용자들에게 작업 편의성을 제공할 수 있을 것으로 기대된다.

• Composites Research
• /
• 제31권4호
• /
• pp.139-144
• /
• 2018

장섬유강화 복합재료는 기존의 연속섬유강화 복합재료에 비해 우수한 생산 효율성과 복잡한 형상의 성형성에 대해 장점을 가지고 있다. 하지만 지나치게 복잡한 복합재료 형상을 제작하거나 서로 다른 재료로 제작된 부품들을 조립/체결해야 하는 경우 다양한 접합 방법들이 필요하다. 일반적으로 LFPS(Long Fiber Prepreg Sheet)는 성형 후 탈형을 쉽게 하기 위해 LFPS안에 이형제가 포함되어 있다. 그러므로 적절한 접합 강도를 위해 접착법과 더불어 기계적인 체결이 요구된다. 본 연구에서 열성형 공정을 통해 LFPS를 경화하고 스테인레스 강 인서트를 접착하는 동시경화 접착을 위한 스테인레스 강 인서트를 제안하였다. 성형공정 동안 펼쳐지는 스테인레스 강 인서트의 날개는 접착력과 기계적인 고정(Mechanical wedging)의 효과를 유발하여 인발력에 저항할 수 있는 갈고리 역할을 한다. 복합재료에 삽입된 인서트 날개들의 펼쳐진 상태를 확인하기 위해 소각 방법을 사용하였다. 그리고 접합 강도를 정량적으로 평가하기 위해 인발시험(Pull-out test)을 수행하였다. 이러한 실험들을 통해 가장 적절한 접합 강도를 보장하는 조건을 도출하였다.

• 접착 및 계면
• /
• 제7권1호
• /
• pp.16-22
• /
• 2006

본 연구에서는 페놀수지 SMC 제조에 사용되는 수용성 레졸형 페놀-포름알데히드 수지의 열안정성과 경화 발열반응 피크의 변화에 미치는 경화온도 및 경화시간의 영향을 열중량분석기와 시차주사열량계를 사용하여 조사하였다. 수용성 페놀-포름알데히드 수지의 중량감소는 주로 $200^{\circ}C,\;400^{\circ}C$ 그리고 $500^{\circ}C$ 부근에서 세 단계로 발생하였다. 경화된 수지의 $750^{\circ}C$에서 탄화수율은 약 62%~65%이었다. 수용성 페놀수지의 열안정성은 경화온도와 경화시간이 증가할수록 증가하였다. 경화시 발열반응은 약 $120^{\circ}C{\sim}190^{\circ}C$ 사이에서 진행되며, 발열피크의 최대점은 약 $165^{\circ}C{\sim}170^{\circ}C$ 사이에서 관찰되었다. 발열반응 곡선의 형태와 발열피크의 최대점은 주어진 경화온도와 경화시간에 의존하였다. 경화되지 않은 수지에 포함되어 있는 $H_2O$ 및 휘발성분을 제거하기 위하여 경화 또는 성형 전에 적어도 $100^{\circ}C$ 이상에서 약 60분 이상의 열처리가 요구되었다. $130^{\circ}C$에서 120분 동안의 경화는 수용성 페놀-포름알데히드 수지의 발열피크를 사라지게 하며, $180^{\circ}C$에서 60분 동안이 후경화는 수지의 열안정성을 더욱 향상시켜 주었다.

• 한국지반공학회논문집
• /
• 제34권3호
• /
• pp.43-56
• /
• 2018

해상처분장의 호안구조물 및 연직차수공으로 강관시트파일이 주로 사용되며, 강관시트파일은 이음부를 연결하여 주열식으로 설치가 되는 만큼 해상 고유의 횡방향 외력에 대한 구조적인 안정성이 확보되어야 한다. 본 연구의 목적은 새로 개발된 연직차수공 이음부의 구조적인 성능을 평가하는 것이다. 먼저 기존 연직차수공 이음부의 문제점을 고찰하고 시공 및 유지보수 측면에서 기존 이음부 형식과의 차별성을 갖도록 새로운 형태의 DHLT(Double H with L-T) 연직차수공 이음부를 개발하였다. 개발된 DHLT 이음부의 실규모 모형을 제작하고 이음부에 그라우트를 채워 양생시킨 후 압축 및 인장강도실험을 수행하고 그 결과를 기존 연구결과와 비교하였다. 실험결과, DHLT 이음부의 압축강도와 인장강도는 그라우트와 강재의 영향으로 인해 기존 이음부 연구결과에 비해 다소 과소평가되었다. 특히 압축강도 실험의 경우 DHLT 이음부의 비대칭 형상으로 인해 그라우트에 균열이 발생하기 전에 강재에서 먼저 항복이 발생하는 결과를 나타내었다. 본 연구를 통해 연직차수공 개발시 이음부 강도발현에 영향을 끼칠 수 있는 요인을 파악할 수 있었으며, 이를 근거로 더 향상된 연직차수공을 개발할 수 있을 것으로 기대된다.

• Corrosion Science and Technology
• /
• 제12권1호
• /
• pp.27-33
• /
• 2013

According to its merits about high curing speed and low emission of volatile organic compounds, UV curable inorganic-organic coating technology has been developed as an alternative for toxic and carcinogenic chromate-based treatments for years. It is consistently observed that ultra-thin films offer excellent corrosion protection as well as paint adhesion to metals. Based on the tetra-ethylorthosilicate(TEOS) and methacryloxypropyl trimethoxysilane(MPTMS), inorganic sol was synthesized and formed hybrid networks with UV curable acrylic monomer, 6-hexanediol diacrylate(HDDA), trimethylolpropane triacrylate(TMPTA), pentaerylthritol triacrylate(PETA). Several methods were used to test their properties such as salt spray test, potentiodynamic measurement, tape peel test, etc. It was shown that anti-corrosive property and stability of storage were affected by the molecular ratios of inorganic and organic compounds. It was not only the stability of storage, but had a excellent anti-corrosive, paint adhesive, and anti-solvent properties in a final molar ratios of 0.6/0.04/0.86/0.005 (TEOS/MPTMS/Acetone/HNO3) and 0.08/0.106/0.081/0.02 (TMPTA/HDDA/PETA/photo initiator).

• 폴리머
• /
• 제24권4호
• /
• pp.529-537
• /
• 2000

본 연구에서는 압출된 PP sheets를 각기 다른 조사량으로 조사 가교시켜, 겔 분율 차이에 따른 세 종류의 샘플을 만든 다음, 회분식 공정을 통해 초임계 유체 (supercritical fluid) 상태의 $CO_2$를 발포제로 사용하여 발포시켰다. 이때, 겔 분율의 차이 및 고압 반응기 내에서 충진 압력과 충진 시간이 셀 구조에 미치는 영향을 관찰하였다. 다음으로, 발포조건에 따른 셀 구조 변화를 알아보기 위해 발포온도와 발포시간을 변화시키면서 실험하였다. 고분자 샘플 내로 침투한 가스의 양은 겔 분율의 차이에 의한 변화가 거의 없었으며, 충진 압력이 2000 psi 이상일 경우 충진 압력의 영향에도 큰 영향을 받지 않았다. 겔 분율이 낮은 샘플은 발포온도나, 발포시간이 증가함에 따라 셀 크기가 불균일하게 증가하였으나, 겔 분율이 높은 샘플은 높은 발포온도와 발포시간에서도 균일하게 셀 크기를 유지하며 안정한 구조를 나타내었다.

• Elastomers and Composites
• /
• 제49권3호
• /
• pp.210-219
• /
• 2014

본 연구에서는 아크릴계 점착제를 합성한 후 이소프렌 액상고무를 블렌드하여 광기능성 시트에 적용될 점착제를 제조하였다. 아크릴 점착제의 모노머로는 butyl acrylate, acrylic acid, 2-ethylhexyl acrylate, 2-hydroxyethyl methacrylate를 사용하였고 용매로는 톨루엔을 사용하였다. 고무계 모노머로는 isoprene 액상고무(LIR-50)를 사용하였고, 아크릴 점착제와의 배합량을 0 ~ 50 wt%로 하여 실험을 진행하였다. 결과에 따르면 LIR-50의 함량이 증가할수록 아크릴계 점착제의 최대 단점이었던 전사현상이 감소하였다. 그 이유는 이소프렌 액상고무의 경우 아크릴 점착제와 달리 극성기가 존재하지 않기 때문에 피착재와 이차결합이 발생하지 않아 경시변화에 따른 전사현상이 감소한 것으로 사료된다. 점착제의 자외선 경화 시 광개시제의 함량이 증가함에 따라, UV에 노출되는 시간이 증가함에 따라 점착제의 경화도가 높아지기 때문에 점착력과 전사현상이 감소하였다. 반면 유지력의 경우는 경화도가 증가하여 분자구조가 망상구조를 이루며 점착제 내부응집력이 증가하기 때문에 유지력은 증가하였다.

• 콘크리트학회논문집
• /
• 제28권5호
• /
• pp.535-544
• /
• 2016

본 연구에서는 디지털 이미지를 사용하여 DIC(Digital Image Correlation) 기법 및 부착파괴면 분석을 통해 부착파괴에너지와 부착강도의 정량적 분석뿐만 아니라 계면의 부착 면 파괴 양상의 정성적 접근을 통해 지속 하중과 온도의 복합 하중에 대한 FRP 부착 실험체의 거동을 분석하였다. 이를 위해 CFRP 쉬트를 부착한 일면전단실험체를 제작하여 사용하였다. 일면전단실험체의 지속 하중 기간의 거동은 에폭시 크리프의 영향을 상당히 받으며 지속 하중 기간 동안에 에폭시의 점탄성 특징으로 인해 응력완화가 발생하였다. 응력완화는 지속 하중 이후 실시한 계면전단실험에서 사용한 DIC 기법을 통해 관찰 하였으며 지속하중 기간 동안의 응력완화로 인해 지속하중 실험체의 최대부착파괴하중 및 계면파괴에너지가 대조실험체보다 증가하였다. 모든 실험체의 부착 파괴 면을 디지털 이미지화하여 파괴 면의 양상을 정성적/정량적으로 분석 하였다. 디지털 이미지 분석 결과 지속 하중 기간 동안 파괴 형태가 콘크리트면내파괴에서 계면부착파괴 형태로 전이가 발생하였으며 이러한 전이로 인해 지속하중 기간이 증가할수록 지속하중의 최대부착파괴하중에 대한 긍정적인 효과 감소하였다.

• 폴리머
• /
• 제35권2호
• /
• pp.157-160
• /
• 2011

본 연구에서는 전자빔을 이용하여 poly(dimethyl siloxane)(PDMS)을 개질하였으며 그 특성 변화를 분석하였다. PDMS 시트를 기존의 열경화법을 통해 제조한 후 20에서 200 kGy의 흡수선량P로 전자빔을 조사하였고, 조사된 시트들의 특성을 팽윤도 및 접촉각 측정, 만능시험분석기(UTM), 열중랑분석기(TGA), X선 광전자 분광기(XPS)들을 이용해 분석하였다. 팽윤도 측정, UTM 및 TGA 결과, 전자빔 조사에 의해 PDMS 시트의 가교 밀도가 증가함에 따라 조사된 PDMS 시트의 팽윤도는 순수한 것에 비해 최대 24%까지 감소하였고 압축강도와 열분해온도는 순수한 것에 대비 각각 최대 2.5 MPa와 $10^{\circ}C$까지 증가함을 확인하였다. 또한, 접촉각 측정과 XPS 분석 결과를 토대로 전자빔 조사에 의한 산화 반응에 의하여 PDMS 표면에 친수성 관능기들이 형성되기 때문에 PDMS 표면의 젖음성은 순수한 것에 비해 최대 24%까지 향상됨을 확인하였다.