• Architectural research
• /
• v.4 no.1
• /
• pp.39-44
• /
• 2002

Recently, the coal-ash production has been increased by increase of consumption of electric power. So it is important to secure a reclaimed land from pollution and develop practical application of coal ash. This is an experimental study to compare and analyze the properties of concrete using high volume of coal ash (including fly ash and bottom ash) as a part of fine aggregate. For this purpose, the mix proportions of concrete according to replacement ratio of coal ash (10, 20, 35, 50%) were selected. And then air content, slump, setting time, bleeding content, chloride content, compressive strength and carbonation test were performed. According to test results, it was found that the bleeding content of concrete using the coal ash decreased according to increase of replacement ratio. And the chloride content of concrete using the bottom ash as a part of fine aggregate increased as the replacement ratio of bottom ash increased, but it is satisfied with the total chloride content of concrete recommended by KCI - $0.3kg/m^3$ below. Also, the compressive strength of concrete using the bottom ash was similar to that of plain concrete(BA 0) after 28days of curing and the carbonation depth of concrete increased as the replacement ratio increased. However, the carbonation depth of concrete using the fly ash decreased as the replacement ratio of fly ash increased.

• Proceedings of the Korea Concrete Institute Conference
• /
• 1999.04a
• /
• pp.481-486
• /
• 1999

According to results of this research Fly-ash Cement permanent-form production was found to be possible by fly-ash mortal. The compress strength 350kg/$\textrm{cm}^2$, banding strength 120kg/$\textrm{cm}^2$ were possible material separting and bleeding by excessive W/C rate was decreased permanent-form made by polymer solved high price of polymer by fly-ash. Model material was made by result of first research. There were no minute-crack on beam form and out surface of form was very smooth, So filling degree seemed desirable length of form after steaming curing was maintained as expected. with these results production of form seemed possible. In the banding load test, fly-ash showed increase of maxim load 12% than RC. in the case of minute-crack, comparing with RC, fly-ash showed no crack at connect. at the first stage under continuing loading size of crack increased. These phenomena seemed to be based on contribution of stress of inner bars in permanent-form. in the test of defection, fly-ash shower about 10% beam load increase than RC. in the case of beam defection, RC showed sudden decrease of tolerance at maxim load and total breaking, but permanent-form showed breaking of bending maintaining defection with contribution of steel stress ($\Phi$6 wire-mash). There phenomenic seemed to be attributed to increase of surface and steel tolerance of form. According to construction explacemaion, it was guessed that each panel was constructed by conner-steels in form edge. so cohesiveness was small. on these bases. keeping width of horizontal band 30cm, form-panel of 20mm width was found to be of use. Permanent-form was found to be efficient in compressibleness, defection, safety and use of Fly-ash mortal.

• Journal of the Korean Ceramic Society
• /
• v.51 no.2
• /
• pp.57-63
• /
• 2014

Bottom ash can be used as pelletizing seeds in unsintered artificial lightweight aggregates, so it can be called as 'cold-bonded aggregates'. In the present study, the mechanical and chemical characteristics of bottom ash aggregates cold-bonded with fly ash were investigated. The crushing strength and the water transfer characteristic of the aggregates, which may affect the strength gain of the concrete, were evaluated. Moreover, the degree of hydration and the hydration products of the aggregates were analyzed to verify the chemical stability of the aggregates. Compared to commercialized artificial lightweight aggregates manufactured by sintering process, cold-bonded fly/bottom ash aggregates had similar levels of water transfer characteristics, while having lower strengths. The calcium hydroxide in the aggregates was almost completely consumed after 28 days moist curing.

• Journal of the Korea Institute of Building Construction
• /
• v.6 no.3 s.21
• /
• pp.99-105
• /
• 2006

In this paper, the estimation of compressive strength of concrete incorporating fly ash subjected to high temperature is discussed. Ordinary Portland cement and fly ash cement(30% of fly ash) were used, respectively. Water to binder ration ranging from 30% to 60% and curing temperature ranging from $20^{\circ}C{\sim}65^{\circ}C$ were also adopted for the experimental parameters. According to results, at the high temperature, FAC had higher strength development at early age than OPC concrete and it kept its high strength development at later age due to accelerated pozzolanic reaction subjected to high temperature. For strength estimation, Logistic model based on maturity equation and Carino model based on equivalent age were applied to verify the availability of estimation model. It shows that fair agreements between calculated values and measured values were obtained evaluating compressive strength with logistic curve. The application of logistic model at high temperature had remarkable deviations in the same maturity. Whereas, the application of Carino model showed good agreements between calculated values and measured ones regardless of type of cement and W/B. However, some correction factors should be considered to enhance the accuracy of strength estimation of concrete.

• Journal of the Korean Ceramic Society
• /
• v.53 no.3
• /
• pp.354-361
• /
• 2016

The purpose of this study was to prepare lightweight foamed concrete by mixing coal fly ash of circulating fluidized bed combustion(CFBC) with cement, and to develop uses for recycling by analyzing carbonation behavior resulting from a change in conditions for pressurized carbonation. For concrete, CFBC coal fly ash was mixed with Portland cement to the water-binder ratio of 0.5, and aging was applied at room temperature after 3 days of curing at $20^{\circ}C$, RH 60%. For carbonation, temperature was fixed at $60^{\circ}C$ and time at 1 h in the use of autoclave. Pressures were controlled to be $5kgf/cm^2$ and the supercritical condition of $80kgf/cm^2$, and gas compositions were employed as $CO_2$ 100% and $CO_2$ 15%+N2 85%. In the characteristics of produced lightweight concrete, the characteristics of lightweight foamed concrete resulting from carbonation reaction were affirmed through rate of weight change, carbonation depth test, air permeability, and processing analysis for the day 28 specimen. Based on these results, it is concluded that the present approach could provide a viable method for mass production of eco-friendly lightweight foamed concrete from CFBC coal fly ash stabilized by carbonation.

• Geotechnical Engineering
• /
• v.11 no.2
• /
• pp.37-50
• /
• 1995

Recently, the treatment of coal ashes produced from thermal electric power plants have been raised as a serious problem in according to the increasing of electric power demand in Korea. This paper deals with a re -use method of coal ash as a fill material. Two domestic coal ashes are mixed with cement and lime to improve the mechanical properties of coal ash. The mechanical properties such as compressive strength, compressive deformation, permeability and frost heaving property are investigated in according to the change of admixture rate, curing temperature and curing time. In this study, it is found coal ash (fly ash+bottom ash) and fly ash with 2%~3% cement can be used as a fill material, respectively. It is also found the frost heaving properties of coal ash is effectively improved by the mixture of 6%~9% cement.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.7 no.4
• /
• pp.121-127
• /
• 2012

This paper is to present the strength estimation of the cement mortar incorporating 20% of fly ash by equivalent age method. ASTM C 1074 was applied to achieve apparent activation energy($E_a$). Cement mortar was cured at the temperature of $5^{\circ}C$, $20^{\circ}C$ and $35^{\circ}C$ respectively to measure the setting time and compressive strength at designed age. According to test results, it is found that an increase in curing temperature resulted in an acceleration of setting time. $E_a$ was achieved to 34.75 KJ/mol. It was also found that by estimating strength development with Plowman and Gompertz model, good agreement between calculated value and measured one was achieved.

• Advances in concrete construction
• /
• v.5 no.1
• /
• pp.17-29
• /
• 2017

Geopolymer concrete is environmentally friendly and could be considered as a construction material to promote the sustainable development. In this paper fly ash based geopolymer concretes with different percentages of alccofine were made by mixing sodium hydroxide and sodium silicate as an alkaline activator and cured at ambient as well as heat environment in an electric oven at $90^{\circ}C$. Effects of various parameters such as the percentage of alccofine, curing temperature, a period of curing, fly ash content, was studied on compressive strength as well as workability of geopolymer concrete. The study concludes that the presence of alccofine improves the properties of geopolymer concrete during a fresh and hardened state of concrete. Geopolymer concrete in the presence of alccofine can be used for the general purpose of concrete as required compressive strength can be achieved even at ambient temperature. The 28 days compressive strength of 73 MPa, when cured at 90-degree Celsius, confirmed that it is also very suitable for precast concrete components.

• Journal of the Korean Ceramic Society
• /
• v.31 no.12
• /
• pp.1536-1544
• /
• 1994

DSP technique was applied to improve the high strength characteristics of hardened cement paste using pozzolan materials as blending materials, and pozzolan reactivity was investigated. Pozzolanic materials such as diatomaceous earth, fly ash and hydrated silica were used as blending material. And also superplasticizer was added to cement for molding the specimens. After curing for 60 days, the specimens substituted with 10 and 15 wt% of diatomaceous earth showed better strength characteristics than the specimen with fly ash. The specimen substituted 7 wt.% of hydrated silica exhibited excellent strength with above 800 kg/$\textrm{cm}^2$.

• Journal of Korean Society of Environmental Engineers
• /
• v.28 no.6
• /
• pp.661-666
• /
• 2006

The compressive strength of a paste composed of a low-calcium Class F fly ash and alkaline activator solutions was investigated. These activator solutions, made with sodium hydroxide, water glass and water, have a very high $OH^-$ concentration. The composition of alkaline activator solution and temperature have been shown to notably influence the development of the compressive strength of the fly ash-cements paste. Compressive strength of 50 MPa could be achieved by curing of the fly ash at $60^{\circ}C$ for 48 hrs or $85^{\circ}C$ for 24 hrs. This study presented the optimum mixing ratio of Class F fly ash/sodium hydroxide/water glass as 25:8:2 in weight basis, and activator/fly ash as 0.6/1.0 for high strength paste.