• Macromolecular Research
• /
• 제10권5호
• /
• pp.259-265
• /
• 2002

The cure kinetics of blends of epoxy (DGEBA, diglycidyl ether of bisphenol A)/anhydride resin with polyamide copolymer, poly(dimmer acid-co-alkyl polyamine), were studied using differential scanning calorimetry (DSC) under isothermal condition. On increasing the amount of polyamide copolymer in the blends, the reaction rate was increased and the final cure conversion was decreased. Lower values of final cure conversions in the epoxy/(polyamide copolymer) blends indicate that polyamide hinders the cure reaction between the epoxy and the curing agent. The value of the reaction order, m, for the initial autocatalytic reaction was not affected by blending polyamide copolymer with epoxy resin, and the value was approximately 1.3, whereas the reaction order, n, for the general n-th order of reaction was increased by increasing the amount of polyamide copolymer in the blends, and the value increased from 1.6 to 4.0. A diffusion-controlled reaction was observed as the cure conversion increased and the rate equation was successfully analyzed by incorporating the diffusion control term for the epoxy/anhydride/(polyamide copolymer) blends. Complete miscibility was observed in the uncured blends of epoxy/(polyamide copolymer) up to 120 $^{\circ}C$, but phase separations occurred in the early stages of the curing process at higher temperatures than 120 "C. During the curing process, the cure reaction involving the functional group in polyamide copolymer was detected on a DSC thermogram.gram.

• 한국정밀공학회:학술대회논문집
• /
• 한국정밀공학회 2011년도 춘계학술대회 논문집
• /
• pp.909-910
• /
• 2011

• 한국복합재료학회:학술대회논문집
• /
• 한국복합재료학회 2004년도 춘계학술발표대회 논문집
• /
• pp.214-217
• /
• 2004

The cure kinetics of blends of epoxy(tetraglycidyl-4,4'-diaminodiphenylmethane ; TGDDM)/curing agent(diaminodiphenyl sulfone ; DDS) resin with amine terminated polyetherimide-CTBN-amine terminated polyetherimide triblock copolymer(ABA) were studied using differential scanning calorimetry under isothermal conditions to determine the reaction parameters such as activation energy and reaction constants. By increasing the amount of ABA in the blends, the final cure conversion was decreased. Lower values of the final cure conversions in the epoxy/ABA blends indicated that ABA hinders the cure reaction between the epoxy and curing agents. 1be value of the reaction order, m, for the initial autocatlytic reaction was not affected by blending ABA with epoxy resin, and the value was approximately 1.0. The value of n for the nth order component in the autocatalytic analysis was increased by increasing the amount of ABA in the blends, and the value increased from 2.0-3.4. A diffusion controlled reaction was observed as the cure conversion increased and the rate equation was successfully analyzed by incorporating the diffusion control term for the epoxy/DDS/ABA blends.

• 한국마이크로전자및패키징학회:학술대회논문집
• /
• 한국마이크로전자및패키징학회 2002년도 춘계 기술심포지움 논문집
• /
• pp.152-157
• /
• 2002

The cure and rheological behavior of Diglycidyl ether of bisphenol F, catalyzed by four kinds of imidazoles and a Nadic methyl anhydride curing agent were studied using a differential scanning calorimeter (DSC) and rheometer. The isothermal traces were employed to analyze cure reaction. The DGEBF/anhydride conversion profiles showed autocatalyzed reaction characterized by maximum conversion rate at 20~40 % of the reaction. The rate constants obtained from isothermal test showed temperature dependance, but reaction order did not. The order of reaction (m+n) was calculated to be close to 3. The measurements of viscosity and relation time in the presence of inorganic fillers were carried out at different isothermal curing temperatures. The viscosity and gelation time increased with filler content at the same isothermal temperature.

• Elastomers and Composites
• /
• 제48권2호
• /
• pp.161-166
• /
• 2013

비등온 TGA 실험방법을 이용하여 가교 사이트가 서로 다른 chlorine cure-site ACM 고무와 carboxylic cure-site ACM 고무 두 종류에 대하여 열분해 거동을 연구하였다. 분해 반응이 최대인 점의 온도는 모든 승온 속도에서 carboxylic cure-site ACM 고무의 열분해 특성이 상대적으로 더 안정함을 보여 주었다. Kissinger의 해석 방법에 의한 활성화에너지는 chlorine cure-site ACM 및 carboxylic cure-site ACM 고무에 대하여 각각 118.6 및 105.5 kJ/mol로 나타났으며, Flynn-Wall-Ozawa의 해석방법에서의 전환율 0.1~0.2 범위의 평균과 유사한 값을 나타내었다. 반응차수 해석으로부터 두 시험편 모두 일반적인 고무와 유사한 다중 복합반응에 의하여 열분해 반응이 진행됨을 알 수 있었다.

• 반도체디스플레이기술학회지
• /
• 제13권4호
• /
• pp.27-32
• /
• 2014

The cure properties of self-extinguishing epoxy resin systems with different charge transfer type latent catalysts were investigated, which are composed of YX4000H as a biphenyl epoxy resin, MEH-7800SS as a hardener, and charge transfer type latent catalysts. We designed and used five kinds of charge transfer type latent catalyst and compared to epoxy resin systems with Triphenylphosphine-Benzoquinone(TPP-BQ) as reference system. The cure kinetics of these systems were analyzed by differential scanning calorimetry with an isothermal approach, the kinetic parameters of all systems were reported in generalized kinetic equations with diffusion effects. The epoxy resin systems with Triphenylphosphine-Quinhydrone(TPP-QH), Triphenylphosphine-Benzanthrone(TPP-BT) and Triphenylphosphine-Anthrone(TPP-AT) as a charge transfer type latent catalyst showed a cure conversion rate of equal or higher rate than those with TPP-BQ. These systems with TPP-QH and Triphenylphosphine-Tetracyanoethylene(TPP-TCE) showed a critical cure reaction conversion of equal or higher conversion than those with TPP-BQ. The increases of cure conversion rates could be explained by the decrease of the activation energy of these epoxy resin systems. It can be considered that the increases of critical cure reaction conversion would be dependent on the crystallinity of the biphenyl epoxy resin systems.

• 한국재료학회지
• /
• 제5권6호
• /
• pp.667-672
• /
• 1995

DGEBA (diglycidyl ether of bisphenol A )/MDA(4,4'-methylene dianiline)/SN(succinonitrile)계와 DGEBA/MDA/SN/HQ(hydroquinone)계의 경화반응 속도론을 Kissinger equation 및 Fractional life 법에 의해 85~15$0^{\circ}C$에서 DSC를 이용하여 연구하였다. 경화반응 온도가 높아짐에 따라 반응속도는 증가하는 반면, 반응차수는 거의 일정하였다. 또한 촉매로 HQ를 첨가한 계가 첨가하지 않은 계보다 반응속도는 크게 증가했으며, 활성화 에너지 값은 약 20% 정도 감소하였다 또한, 경화반응 시작온도는 3$0^{\circ}C$ 정도 낮아졌다.

• Macromolecular Research
• /
• 제11권4호
• /
• pp.267-272
• /
• 2003

The isothermal cure reactions of blends of epoxy (DGEBA, diglycidyl ether of bisphenol A)/anhydride resin with polyamide copolymer (poly(dimmer acid-co-alkyl polyamine)) or PEI were studied using differential scanning calorimetry (DSC). Rheological measurements have been made to investigate the viscosity and mechanical relaxation behavior of the blends. The reaction rate and the final cure conversion were decreased with increasing the amount of thermoplastics in the blends. Lower values of final cure conversions in the epoxy/thermoplastic blends indicate that thermoplastics hinder the cure reaction between the epoxy and the curing agent. Complete miscibility was observed in the uncured blends of epoxy/thermoplastics up to $120^{\circ}C$ but phase separations occurred in the early stages of the curing process at higher temperatures than $120^{\circ}C$. According to the rheological measurement results, a rise of G' and G" at the onset of phase separation is seen. A rise of G' and G" is not observed for neat epoxy system since no phase separation is seen during cure reaction. At the onset of phase separation the rheological behavior was influenced by the amount of thermoplastics in the epoxy/thermoplastic blends, and the onset of phase separation can be detected by rheological measurements.

• 한국윤활학회:학술대회논문집
• /
• 한국윤활학회 1999년도 제30회 추계학술대회
• /
• pp.49-56
• /
• 1999

A material was formulated with Phenol novolac and HEXA only. The cure kinetics and thermal characteristics of phenol novolac with various HEXA contents were peformed by differential scanning calorimetry and thermal gravimetric analysis. All kinetic parameters of the curing reaction including the reaction order, activation energy, and rate constant were calculated and reported. The results indicate that the curing reaction goes through an autocatalytic kinetic mechanism. The friction and wear characteristics of this material were determined using friction material testing machine. The friction coefficient of phenol novolac with various HEXA contents was determined using the PV(pressure & velocity) factor. The most stable and highest friction coefficient with a various pressure and velocity condition was found at HEXA 10 wt.% material. The specific wear rate per unit sliding distance with a various HEXA contents was reported.

• Restorative Dentistry and Endodontics
• /
• 제24권2호
• /
• pp.265-285
• /
• 1999

The purposes of this investigation were to observe the reaction kinetics of five commercial dual cured resin cements (Bistite, Dual, Scotchbond, Duolink and Duo) when cured under varying thicknesses of porcelain inlays by chemical or light activation and to evaluate the effect of the porcelain disc on the rate of polymerization of dual cured resin cement during light exposure by using thermal analysis. Thermogravimetric analysis(TGA) was used to evaluate the weight change as a function of temperature during a thermal program from $25{\sim}800^{\circ}C$ at rate of $10^{\circ}C$/min and to measure inorganic filler weight %. Differential scanning calorimetry(DSC) was used to evaluate the heat of cure(${\Delta}H$), maximum rate of heat output and peak heat flow time in dual cured resin cement systems when the polymerization reaction occured by chemical cure only or by light exposure through 0mm, 1mm, 2mm and 4mm thickness of porcelain discs. In 4mm thickness of porcelain disc, the exposure time was varied from 40s to 60s to investigate the effect of the exposure time on polymerization reaction. To investigate the effect on the setting of dual cured resin cements of absorption of polymerizing light by porcelain materials used as inlays and onlays, the change of the intensity of the light attenuated by 1mm, 2mm and 4mm thickness of porcelain discs was measured using curing radiometer. The results were as follows 1. The heat of cure of resin cements was 34~60J/gm and significant differences were observed between brands (P<0.001). Inverse relationship was present between the heat of reaction and filler weight % the heat of cure decreased with increasing filler content (R=-0.967). The heat of reaction by light cure was greater than by chemical cure in Bistite, Scotchbond and Duolink(P<0.05), but there was no statistically significant difference in Dual and Duo(P>0.05). 2. The polymerization rate of chemical cure and light cure of five commercially available dual cured resin cements was found to vary greatly with brand. Setting time based on peak heat flow time was shortest in Duo during chemical cure, and shortest in Dual during light cure. Cure speed by light exposure was 5~20 times faster than by chemical cure in dual cured resin cements. The dual cured resin cements differed markedly in the ratio of light and chemical activated catalysts. 3. The peak heat flow time increased by 1.51, 1.87, and 3.24 times as light cure was done through 1mm, 2mm and 4mm thick porcelain discs. Exposure times recommended by the manufacturers were insufficient to compensate for the attenuation of light by the 4mm thick porcelain disc. 4. A strong inverse relationship was observed between peak heat flow and peak time in chemical cure(R=0.951), and a strong positive correlations hip was observed between peak heat flow and the heat of cure in light cure(R=0.928). There was no correlationship present between filler weight % or heat of cure and peak time. 5. The thermal decomposition of resin cements occured primarily between $300^{\circ}C$ and $480^{\circ}C$ with maximum decomposition rates at $335^{\circ}C$ and $440^{\circ}C$.