• Polymer(Korea)
• /
• v.36 no.1
• /
• pp.29-33
• /
• 2012

Solution type pressure sensitive acrylic adhesives were synthesized from 2-ethylhexyl acrylate (2-EHA) as a base monomer and acrylic acid as a functional monomer. The surface energy and basic physical properties of synthesized PSA (pressure sensitive adhesives) were investigated as a function of contents of acrylic acid and crosslinking agent. The structures of adhesive were identified by FTIR. Viscosities and molecular weights of PSA were measured by a Brookfield viscometer and GPC, respectively. Consequently, molecular weight and viscosity increased as the contents of acrylic acid increased up to 6 wt% and then decreased at higher contents. Surface energy increased as the contents of acrylic acid increased owing to the increase of COOH groups, which yielded the enhancement of polarity of PSA. On the other hands, their peel strengths were inversely proportional to molecular weight and showed tendencies of decreasing as the contents of acrylic acid and crosslinking agent increased.

• Journal of the Korean Wood Science and Technology
• /
• v.41 no.2
• /
• pp.134-140
• /
• 2013

UV curing was introduced via a chemical treatment by adding small amounts of a hexafunctional acrylic monomer and a photoinitiator to improve the mechanical properties of PLA. This study also employed a semi-interpenetrated structured polymer network through the process of UV-curing. The UV curing behaviors were investigated using FTIR-ATR spectroscopy and gel fraction determination. Also, the tensile strength was investigated with different hexafunctional acrylic monomer contents and UV doses. The results showed that the crosslinking of UV-induced chemically treated PLA started at a low content of hexafunctional acrylic monomer, resulting in a significant improvement of the mechanical properties compared to those of neat PLA due to crosslinking.

• Journal of Adhesion and Interface
• /
• v.17 no.2
• /
• pp.56-61
• /
• 2016

This study was to investigate the effect of main monomer, butyl acrylate instead of 2-ethylhexyl acrylate, of acrylic PSAs on adhesive properties. The copolymers of butyl acrylate, acrylic acid and 2-hydroxyethyl acrylate were synthesized and their adhesive properties were investigated after crosslinking with two different agents. Comparing to 2-hydroxyethyl acrylate-based one which has branch-like side groups, butyl acrylate-based PSA with linear side groups show poor adhesive properties. In case of crosslinking agent, epoxy-typed agent than isocyanate-typed one showed better properties than isocyanate-typed one because epoxy-typed agent has more crosslinking sites and produces more flexible bonds, ester and ether, than isocynate-typed one. Most adhesive properties of PSAs were increased with acid content.

• Elastomers and Composites
• /
• v.44 no.3
• /
• pp.308-314
• /
• 2009

The acrylic rubber was synthesized by emulsion polymerization using n-butyl acrylate, n-butyl methacrylate, acrylonitrile, glycidylmethacrylate, and allyl methacrylate. When the contents of acrylonitrile were increased at fixed amount of crosslinking monomers, the Tg of polymers was increased with the contents of acrylonitrile, Mooney viscosity, hardness, and tensile strength also were increased. But the elongation was decreased due to the reduction of chain flexibility. The addition of the monomer for crosslinking, glycidylmethacrylate whose Tg is $56^{\circ}C$ resulted in the increased Tg of the polymer, and increased Mooney viscosity, hardness, and tensile strength, but the elongation at break was decreased with the glycidylmethacrylate contents. It was shown that this phenominon was attributed to the increment of crosslinking density by glycidylmethacrylate through the measurement of rheometer.

• Journal of Adhesion and Interface
• /
• v.14 no.1
• /
• pp.43-48
• /
• 2013

The physical properties of the acrylic pressure sensitive adhesives (PSAs) can be easily controlled by a proper functional monomer which has functional groups for crosslinking. This study was to investigate the effect of crosslinking agents, isocyanate and epoxy types, of acrylic PSAs on adhesive properties. 2-Ethylhexyl acrylate, acrylic acid (AA), and 2-hydroxy ethyl methacrylate as monomer were used. The obtained samples with different AA contents were partially crosslinked with epoxy- or isocyanate-typed agent. Peel strength, balltack, holding power test and contraction percentage of the obtained PSA were evaluated. Most properties of acrylic PSAs were increased with AA content and acrylic PSAs with epoxy-typed crosslinking agent (4 crosslinking sites) which produces flexible link (ether), showed better properties than those of isocyanate-typed one (3 crosslinking sites).

• Journal of the Korean Applied Science and Technology
• /
• v.25 no.4
• /
• pp.525-532
• /
• 2008

To prepare a solution type acrylic pressure-sensitive adhesive, quarter polymers were synthesized from butyl acrylate(BA), 2-ethylhexylacrylate(2-EHA) as a base monomer, methyl methacrylate(MMA) as a comonomer, each of methacrylic acid(MAA), acrylic acid(AA) as a functional monomer. Acrylic solution type pressure-sensitive adhesives(PSA's) of isocyanate derivative crosslinking PSA's were prepared by crosslinking of BEMM, BEMA with toluene-2,4-diisocyanate. The structure of adhesive was identified by FT-IR. The viscosity was measured by using Brookfield DV-III and molecular weight was measured by using gel permeation chromatography. The physical properties of polyethylene film coated with BEMMT, BEMAT were measured as a function of the concentration. As the result, BEMMT(0.6, 0.8), BEMAT(0.6) showed peel adhesion of $160{\sim}180\;g_f$/25 mm width and shear adhesion of more than 24 hours, and tackiness of $4/32{\sim}6/32$ which was relevant to commercial usage.

• Polymer(Korea)
• /
• v.34 no.5
• /
• pp.391-397
• /
• 2010

Poly(amic acid)(PAA) was prepared by reaction of bicyclo(2,2,2)oct-7-ene-2,3,5,6-tetracarboxylicdianhydride(BTDA) containing double bond for crosslinking and bis[4-(3-aminophenoxy) phenyl] sulfone(BAPS) in N,N-dimethylacetamide(DMAc). The cast film of PAA was heat-treated at different temperatures to create polyimide(PI) films. With increasing thermal crosslinking temperatures from 250 to $350^{\circ}C$, the thermo-mechanical properties, degree of crosslinking, and optical transparency of the cross-linked PI were investigated. The maximum enhancement in the thermo-mechanical properties was observed at a heat treatment condition of $350^{\circ}C$. However, the optical transparency was found to be optimal for $250^{\circ}C$ heat treatment. The degree of crosslinking in NMR was determined to be 85% to 93% with increasing annealing temperature conditions from 250 to $350^{\circ}C$.

• Membrane Journal
• /
• v.15 no.1
• /
• pp.8-14
• /
• 2005

The hyaluronic acid (HA) with excellent biocompatibility can be combined with the monomer polylactide with good biodegradability to produce biocompatible materials which can control the period of degradation in a human body. By freeze drying method, HA and the lactic acid, monomer of polylactide, or lactide, the ester dimer of polylactide, were crosslinked with crosslinking agent, l-ethyl-3-(3-dimethyl aminopropyl) carbodiimide. The analysis of infrared spectroscopy showed that the ester linkage was formed and the analysis of nuclear magnetic resonance (NMR) spectroscopy showed that the ester linkage was due to the reaction of lactic acid and HA. The conversion (6∼32%) and degree of crosslinking (4∼19%) increased but the selectivity was almost constant at 62% as the mole ratio of LA to HA increased from 1 to 10 in the crosslinking reaction. The brittleness became more pronounced and the rate of degradation became faster with more addition of lactic acid resulting from the higher ratio of LA to HA, and the swelling ratio was in the range of 500 to 2000%.

• Journal of the Semiconductor & Display Technology
• /
• v.15 no.1
• /
• pp.12-16
• /
• 2016

Toluene-free pressure sensitive adhesives were synthesized by using butyl acrylate (BA), 2-hydroxy ethyl acrylate, methyl methacrylate, acrylic acid (AA) as monomers and ethyl acetate as a solvent. The polymerization recipes were designed by changing 1, 3, 5 part per hundreds monomer (phm) of AA content on the basis of 100 BA parts. Two crosslinking agents, ethyl glycol diglycidyl ether (EDGE) and isophorone diisocyanate (IPDI) were added to the synthesized polymers to increase adhesion due to crosslinking. In the measurement of properties, holding power, peel strength, and initial tackiness increased with AA content due to crosslinking between carboxyl group in AA and epoxy group in EDGE and isocyanate group in IPDI. In the comparison of two crosslinking agents, EDGE showed better in the three properties than IPDI by better reaction of epoxy group of EDGE to carboxyl group of AA.

• Macromolecular Research
• /
• v.12 no.5
• /
• pp.519-527
• /
• 2004

Stable poly(methyl methacrylate-co-divinylbenzene) (poly(MMA-co-DVB)) microspheres were prepared by precipitation polymerization using acetonitrile as the main medium under various polymerization conditions, including modifications of the agitation speed, monomer and initiator concentrations, DVB content in the monomer mixture, and the use of various cosolvents. Gentle agitation was required to obtain smooth spherical particles. The individually stable microspheres were obtained at monomer concentrations of up to 15 vol% in an acetonitrile medium. The number-average diameter increased linearly with respect to increases in the monomer and initiator concentrations. We found, however, that the uniformity of the microspheres was independent of the variation of the polymerization ingredients because nuclei formation was solely influenced by the crosslinking reaction of the monomers. We obtained higher yields for the polymerization at higher concentrations of monomer and initiator. The concentration of DVB in the monomer mixture composition played an important role in determining not only the size of the microspheres but also the yield of the polymerization. In addition, although we employed various cosolvents as the polymerization medium, we found that acetonitrile/2-methoxyethanol was the only system that provided spherical particles without coagulation. This finding indicates that the precipitation polymerization is strongly dependent on the solvent used as the medium.