• Progress in Superconductivity and Cryogenics
• /
• v.6 no.3
• /
• pp.16-20
• /
• 2004

YB $a_2$C $u_3$$O_{7-x}$ (YBCO) films were deposited on (100) SrTi $O_3$ single crystal substrates by a metal organic chemical vapor deposition (MOCVD) system of hot-wall type using single liquid source. Under the condition of the mole ratio of Y(tmhd)$_3$:Ba(tmhd)$_2$:Cu(tmhd)$_2$= 1:2.1:2.9. the deposition pressure of 10 Torr. the MO source line speed of 15 cm/min. the Ar/ $O_2$ flow rate of 800/800 sccm. YBCO films were prepared at the deposition temperatures of 780∼89$0^{\circ}C$. In case of the YBCO films with 2.2 ${\mu}{\textrm}{m}$ thickness deposited for 6 minutes at 86$0^{\circ}C$. XRD pattern showed complete c-axis growth and SEM morphology showed dense and crack-free surface. The atomic ratios of Ba/Y and Cu/Ba in the film were 1.92 and 1.56. respectively. The deposition rate of the film was as high as 0.37 ${\mu}{\textrm}{m}$/min. The critical temperature ( $T_{c.zero}$) of the film was 87K. The critical current of the film was 104 A/cm-width. and the critical current density was 0.47 MA/$\textrm{cm}^2$. For the thinner film of 1.3 ${\mu}{\textrm}{m}$ thickness. the critical current density of 0.62 MA/$\textrm{cm}^2$ was obtained.d.

• Progress in Superconductivity and Cryogenics
• /
• v.16 no.1
• /
• pp.9-13
• /
• 2014

Effects of neutron irradiation on the superconducting properties of the undoped $MgB_2$ and the carbon(C)-doped $MgB_2$ bulk superconductors, prepared by an in situ reaction process using Mg and B powder, were investigated. The prepared $MgB_2$ samples were neutron-irradiated at the neutron fluence of $10^{16}-10^{18}n/cm^2$ in a Hanaro nuclear reactor of KAERI involving both fast and thermal neutron. The magnetic moment-temperature (M-T) and magnetization-magnetic field (M-H) curves before/after irradiation were obtained using magnetic property measurement system (MPMS). The superconducting critical temperature ($T_c$) and transition width were estimated from the M-T curves and critical current density ($J_c$) was estimated from the M-H curves using a Bean's critical model. The $T_cs$ of the undoped $MgB_2$ and C-doped $MgB_2$ before irradiation were 36.9-37.0 K and 36.6-36.8 K, respectively. The $T_cs$ decreased to 33.2 K and 31.6 K, respectively after irradiation at neutron fluence of $7.16{\times}10^{17}n/cm^2$, and decreased to 22.6 K and 24.0 K, respectively, at $3.13{\times}10^{18}n/cm^2$. The $J_c$ cross-over was observed at the high magnetic field of 5.2 T for the undoped $MgB_2$ irradiated at $7.16{\times}10^{17}n/cm^2$. The $T_c$ and $J_c$ variation after the neutron irradiation at various neutron fluences were explained in terms of the defect formation in the superconducting matrix by neutron irradiation.

• Progress in Superconductivity
• /
• v.9 no.1
• /
• pp.68-73
• /
• 2007

We fabricated the in-situ $MgB_2$ wires using the powder-in-tube method and investigated the effects of sintering temperature and SiC contents on the microstructure and superconducting properties. Pure $MgB_2$ wires and 5, 10, 20 wt.% SiC doped $MgB_2$ wires were sintered at $600-1000^{\circ}C$ for 30 minutes in Ar atmosphere. We found that $MgB_2$ phase was mostly formed at the sintering temperature of $700^{\circ}C$ and above, and the critical temperature ($T_c$) increased with increasing sintering temperature. For the $MgB_2$ sintered at $850^{\circ}C$, the highest critical current density ($J_c$) was obtained to be $3.7{\times}10^5\;A/cm^2$ at 5 K and 1.6 T by a magnetic properties measurement system (MPMS). The addition of SiC to the $MgB_2$ wires changed microstructure and critical properties. SEM observation showed that the $MgB_2$ core had considerable micro-cracks in undoped wire and the density of micro-cracks decreased with increasing SiC contents. The critical temperature decreased as the SiC contents increased, on the other hand, the critical current density of SiC doped $MgB_2$ wires in high magnetic field was enhanced compared to that of undoped $MgB_2$ wires.

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.15 no.2
• /
• pp.630-643
• /
• 1991

The hydrodynamic stability equations are formulated for buoyancy-induced flows adjacent to a vertical, planar, isothermal surface in cold pure water. The resulting stability equations, when reduced to ordinary differential equation by a similarity transformation, constitute a two-point boundary-value(eigenvalue) problem, which was numerically solved for various values of the density extremum parameter R=( $T_{m}$ - $T_.inf./) / ( $T_{o}$ - $T_.inf./). These stability equations have been solved using a computer code designed to accurately solve two-point boundary-value problems. The present numerical study includes neutral stability results for the region of the flows corresponding to 0.0.leq. R. leq.0.15, where the outside buoyancy force reversals arise. The results show that a small amount of outside buoyancy force reversal causes the critical Grashof number $G^*/ to increase significantly. A further increase of the outside buoyancy force reversal causes the critical Grashof number to decrease. But the dimensionless frequency parameter $B^*/ at $G^*/ is systematically decreased. When the stability results of the present work are compared to the experimental data, the numerical results agree in a qualitative way with the experimental data.erimental data.

• Progress in Superconductivity
• /
• v.13 no.2
• /
• pp.90-96
• /
• 2011

We investigated the properties of artificial pinning centers of YBCO multilayer films in which $Y_2O_3$ and ZnO nanoparticles are uniformly introduced by using the pulsed laser deposition (PLD) technique. $Y_2O_3$ and ZnO nanoparticles were deposited on top of YBCO buffer layer and the density of nanoparticles was controlled by varying the number of nanoparticle layers. YBCO superconducting layers with total thickness of 250 nm were deposited on top of $Y_2O_3$ and ZnO nanoparticles. Based on analyses of the surface morphology, the transition temperature $T_c$, and the critical current density $J_c$, we discussed the difference between the two kinds of nanoparticles as flux pinning centers.

• Progress in Superconductivity and Cryogenics
• /
• v.15 no.2
• /
• pp.12-15
• /
• 2013

The pure and carbon (C)-doped $MgB_2$ thin films were fabricated on $Al_2O_3$ (0001) substrates at a temperature of $650^{\circ}C$ by using hot-filament-assisted hybrid physical-chemical vapor deposition technique. The $T_c$ value for pure $MgB_2$ film is 38.5 K, while it is between 30 and 35 K for carbon-doped $MgB_2$ films. Expansion in c-axis lattice parameter was observed with increase in carbon doping concentration which is in contrast to carbon-doped $MgB_2$ single crystals. Significant enhancement in the critical current density was obtained for C-doped $MgB_2$ films as compared to the undoped $MgB_2$ film. This enhancement is most probably due to the incorporation of C into $MgB_2$ and the high density of grain boundaries, both help in the pinning of vortices and result in improved superconducting performance.

• Progress in Superconductivity and Cryogenics
• /
• v.19 no.3
• /
• pp.18-22
• /
• 2017

Addition of $BaSnO_3$ (BSO) to $GdBa_2Cu_3O_{7-{\delta}}$ (GdBCO) is reported to enhance the flux pinning property of GdBCO thick films. To investigate the effect of growth condition on the pinning properties, 700 nm-thick BSO-added GdBCO films deposited with varying temperatures and growth rates were prepared by using a pulsed laser deposition method. As the deposition temperature increases, the critical current density and the pinning force density show an improved field dependence up to $750^{\circ}C$ due to the increase in the formation of the a-axis growth and the BSO nanostructures. The films deposited at higher temperatures show degraded surfaces and as a result, degraded pinning behaviors. For the change in growth rate, the critical current density and the pinning force increase as the repetition rate increase at low magnetic fields, but this behavior is reversed in high magnetic fields. These results indicate that the film growth conditions significantly affect the formation of BSO nanostructures and the pinning properties of BSO-added GdBCO films.

• Proceedings of the Korean Society of Propulsion Engineers Conference
• /
• 2008.03a
• /
• pp.320-329
• /
• 2008

The influence of thermodynamic transition associated with transcritical nitrogen injection upon the flow structure was investigated to explore numerical simulation of the injectant dynamics of oxygen/hydrogen coaxial jet in liquid rocket engines. Single and coaxial nitrogen jets were treated by comparing the transcritical and perfect-gaseous conditions, wherein the numerical model was accommodative to the real-fluid thermodynamics and transport properties at supercritical pressures. The model was in the first place validated by comparing the results of transcritical nitrogen injection between calculations and available experiments. For a single jet under the transcritical condition, the nitrogen kept a relatively high density up to its pseudo-critical temperature inside the mixing layer, since it remains less expanding until heated up to its pseudo-critical temperature. Numerical analysis revealed that cryogenic jets exhibit strong dependence of specific enthalpy profile upon the associated density profile that are both dominated by turbulent thermal diffusion. In the numerical model, therefore, exact evaluation of turbulent heat fluxes becomes very important for simulating turbulent cryogenic jets under supercritical pressures. Concerning the coaxial jets due to transcritical/gaseous nitrogen injections, the density profile inside the mixing layer was again affected by the thermodynamic transition of nitrogen. However, hydrodynamic instability modes of the inner jet did not show significant differences by this thermodynamic transition, so that further study is needed for the mixing process downstream of the near injection position.

• Geomechanics and Engineering
• /
• v.23 no.5
• /
• pp.493-502
• /
• 2020

The prediction of soil response under repetitive mechanical loadings remains challenging in geotechnical engineering applications. Modeling the cyclic soil response requires a robust model validation with an experimental dataset. This study proposes a unique method adopting linearity of model constant with the number of cycles. The model allows the prediction of the terminal density of sediments when subjected to repetitive changes in pore-fluid pressure based on the two-surface plasticity. Model simulations are analyzed in combination with an experimental dataset of sandy sediments when subjected to repetitive changes in pore fluid pressure under constant deviatoric stress conditions. The results show that the modified plastic moduli in the two-surface plasticity model appear to be critical for determining the terminal density. The methodology introduced in this study is expected to contribute to the prediction of the terminal density and the evolution of shear strain at given repetitive loading conditions.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 1997.10a
• /
• pp.17-23
• /
• 1997

In the two-dimensional Finite Element Method for forming simulation, mesh generation and remeshing process are very significant. In this paper, using the modified splitting mesh generation algorithm, we can overcome the limitation of existing techniques and acquire mesh, which has optimal mesh density. A modified splitting algorithm for automatically generating quadrilateral mesh within a complex domain is described. Unnecessary meshing process for density representation is removed. Especially, during the mesh generation with high gradient density like as shear band representation, the modified mesh density scheme, which will generate quadrilateral mesh with the minimized error, which takes effect on FEM solver, is introduced.