• Structural Engineering and Mechanics
• /
• 제49권2호
• /
• pp.225-235
• /
• 2014

Cold expansion is an efficient way to improve the fatigue life of an open hole. In this paper, three finite element models have been established to bind the crack growth from an expanded hole and simulated. Expansion and its degree influence are studied using a numerical analysis. Stress intensity factors are determined and used to evaluate the fatigue life. Residual stress field is evaluated using a nonlinear analysis and superposed with the applied stresses field in order to estimate fatigue crack growth. Experimental tests are conducted under constant loading. Results of this investigation indicate expansion and its degree are beneficial to fatigue life and a good agreement was observed between FEM simulations and experimental results.

• 대한기계학회논문집A
• /
• 제25권8호
• /
• pp.1269-1276
• /
• 2001

In case of contact fatigue, the accurate calculation of surface tractions and subsurface stress is essential to the predication of crack initiation life. Surface tractions influencing shear stress amplitude have been obtained by contact analysis based on influence function. Subsurface stress has been obtained by using rectangular patch solutions. In this study, to simulate asperity contact under sliding condition, the tip of asperity was simulated by sphere and to calculate crack initiation life in the substrate, dislocation pileup theory was used.

• 한국해양공학회지
• /
• 제15권2호
• /
• pp.94-98
• /
• 2001

fatigue life and nondestructive evaluation were examined experimentally using surface crack specimen and compact tension specimen of 5083 aluminium alloy. Acoustic emission signals emanated during failure of aluminum alloys has been the subject of numerous investigations. Possible sources of AE during deformation have been suggested as the dislocations, fracture of brittle particles and debonding of these particles from the alloy matrix. Fatigue life and penetration behavior of long surface crack can be evaluated quantitatively using K values proposed by authors. The influence of stress ratio on the frequency characteristics of AE signals were investigated.

• Advances in aircraft and spacecraft science
• /
• 제4권1호
• /
• pp.1-19
• /
• 2017

Fatigue life prediction of a multi-row countersunk riveted lap joint was performed numerically. The stress and strain conditions in a highly stressed substructure of the joint were analysed using a global/local finite element (FE) model coupling approach. After validation of the FE models using experimental strain measurements, the stress/strain condition in the local three-dimensional (3D) FE model was simulated under a fatigue loading condition. This local model involved multiple load cases with nonlinearity in material properties, geometric deformation, and contact boundary conditions. The resulting stresses and strains were used in the Smith-Watson-Topper (SWT) strain life equation to assess the fatigue "initiation life", defined as the life to a 0.5 mm deep crack. Effects of the rivet-hole clearance and rivet head deformation on the predicted fatigue life were identified, and good agreement in the fatigue life was obtained between the experimental and the numerical results. Further crack growth from a 0.5 mm crack to the first linkup of two adjacent cracks was evaluated using the NRC in-house tool, CanGROW. Good correlation in the fatigue life was also obtained between the experimental result and the crack growth analysis. The study shows that the selected methodology is promising for assessing the fatigue life for the lap joint, which is expected to improve research efficiency by reducing test quantity and cost.

• 한국공작기계학회논문집
• /
• 제11권2호
• /
• pp.43-49
• /
• 2002

SB41 material is welded automatically and is investigated some effects of the welding residual stress in the growth and propagation of fatigue crack, so as to study the fatigue behaviour in the welding residual stress field. The summarized results are as follows; 1) In case of the load amplitude is constant, as the stress ratio is changing to 0.1, 0.33 and 0.5 the propagation life is constant but the growth life decreases. And than, when maximum load or minimum load is constant as the stress ratio increases the growth life and propagation life. 2) It was shown that fatigue crack propagation ratio da/dN was almost constant regardless of the stress ratio change at constant load amplitude and that the larger stress ratio, the slower was the fatigue crack propagation ratio. 3) The opening ratio U is influenced by $K_max$ but it isn't only the function of $K_max$ because data range is very large. 4) The fatigue life of the specimens on tensile compressive residual stress field was decreased and increased respectably more than that of the base metal.

• 한국안전학회지
• /
• 제17권1호
• /
• pp.33-38
• /
• 2002

SS41 material is welded automatically and is investigated some effects of the welding residual stress on the growth and propagation of fatigue crack, so as to study the fatigue behaviour in the welding residual stress field. The summarized results are as follows; 1) In case of the load amplitude is constant, as the stress ration is changing to 0.1, 0.33 and 0.5 the propagation life is constant but the initiation life decreases. And than, when maximum load or minimum load is constant, s the stress ration increases the initiation life and propagation life. 2) It was shown that the fatigue crack propagation ratio da/dn was almost constant regardless of the stress ratio change at constant load amplitude and that the larger stress ratio, the slower was the fatigue crack propagation ratio. 3) The opening ratio U is influenced by $K_{max}$ but it isn't only the function of $K_{max}$ because data range is very large. 4) The fatigue life of the specimens on tensile compressive residual stress field was decreased and increased respectably more than that of the base metal.

• 대한기계학회논문집
• /
• 제16권8호
• /
• pp.1446-1450
• /
• 1992

본 연구에서는 윤, H. Okamura는 주어진 초기크랙으로부터 관통이전의 한계크 랙까지의 수명을 간단히 평가하는 수법을 제안했으며 또한, 파괴역학적 제인자의 수명 에 미치는 영향을 평가했다. 본 논문은 이러한 연구들의 연장으로서 상기 남등의 응 력 확대 계수 평가식을 이용하여 파단수명의 예측수법을 확립하고 파단수명에 미치는 파괴역학적 제인자의 영향을 밝히는데 그 목적을 두고 있다.

• 한국해양공학회:학술대회논문집
• /
• 한국해양공학회 2002년도 춘계학술대회 논문집
• /
• pp.104-109
• /
• 2002

In this paper, a statistical analysis of fatigue crack growth behavior under constant amplitude loads has been carried out. Fatigue crack growth tests were conducted on sixteen pre-cracked compact tension (CT) specimens of the pressure vessel (SPV50) steel in controlled identical load and environmental conditions. The assessment of the statistical distribution of fatigue crack growth experimental data obtained from SPV50 steel was studied and also the correlation of the parameter C and m in the Paris-Erdogan law was discussed. The probability distribution function of fatigue crack growth life seems to follow the 3-parameter Weibull. The fatigue crack growth rate seems to follow the 3-parameter Weibull and the log-normal distribution. The coefficient of variation (COV) of fatigue crack growth life was observed to decrease as the crack grows. A strong negative linear correlation exists between the coefficient C and the exponent m in Paris model. Fatigue crack growth rate data shows a normal distribution for both m and logC.

• 대한기계학회논문집A
• /
• 제27권6호
• /
• pp.923-929
• /
• 2003

In this paper, an analysis of fatigue crack growth behavior from a statistical point of view has been carried out. Fatigue crack growth tests were conducted on sixteen pre-cracked compact tension (CT) specimens of the pressure vessel (SPV50) steel in controlled identical load and environmental conditions. The assessment of the statistical distribution of fatigue crack growth experimental data obtained from SPV50 steel was studied and also the correlation of the parameter C and m in the Paris-Erdogan law was discussed. The probability distribution function of fatigue crack growth life seems to follow the 3-parameter Weibull. The fatigue crack growth rate seems to follow the 3-parameter Weibull and the log-normal distribution. The coefficient of variation (COV) of fatigue crack growth life was observed to decrease as the crack grows. Fatigue crack growth rate data shows a normal distribution for both m and logC. A strong negative linear correlation exists between the coefficient C and the exponent m.

• 한국해양공학회지
• /
• 제3권2호
• /
• pp.587-587
• /
• 1989