• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.23 no.11 s.170
• /
• pp.1886-1895
• /
• 1999

The delamination behavior of multidirectional carbon-fiber/epoxy composite laminates under 10NA intermediate and high rates of test, up to rate of about 11.4m s has been investigated using the double cantilever beam specimens. The mode I loading under rates above l.0m/s showed considerable dynamic effects on the load-time curves and thus higher values of the average crack velocity than that expected from a simple proportional relationship with the test rate. The modified beam analysis utilizing only the opening displacement and crack length exhibited an effective means for evaluating the dynamic fracture energy $G_{IC}$. Based on the assumption of constant flexural modulus, values of $G_{IC}$ at the crack initiation and arrest were decreased with an increase of the test rate up to 5.7m/s, but the maximum $G_{IC}$ was increased at 11.4m/s.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.21 no.7
• /
• pp.1089-1096
• /
• 1997

In this paper, Rancho Seco transient which is reported as a typical pressurized thermal shock event is postulated to be occuring in the Kori unit 1 plant, the oldest nuclear power plant in Korea. For the given material properties, transient history such as temperature and pressure, and postulated flaw, the stress distribution is obtained to calculate stress intensities for a wide range of assumed crack sizes. The stress intensities are compared with the fracture toughness, which is determined using the material properties and the distribution of the nil ductility transition temperature, to determine if cracking is expected to occur during the transient. The allowable operating year for the transient is determined and the evaluation results are discussed.

• Proceedings of the Korea Concrete Institute Conference
• /
• 1990.04a
• /
• pp.51-56
• /
• 1990

Investigations on the behavior of steel fiber reinforced high strength concrete beams subjected to predominant shear are accomplished to determine their diagonal shear strength including ultimate shear strength. The parameters varied were the volume fraction(Vf) of the fibers, shear span depth ratio(a/d). The test result show that diagonal shear strength and ultimate shear strength are increased siginificantly due to crack arrest mechanism. Predictive equations are suggested for evaluating the diagonal cracking strength and ultimate shear strength of the fiber reinforced high strength concrete beams.

• Journal of the KSME
• /
• v.24 no.6
• /
• pp.452-458
• /
• 1984

동적 파괴역학 연구의 필요성과 응용분야를 설명하였다. 다음 2장에 동적 파괴역학 연구의 역 사적인 발전과정을 간단히 살펴보면서 현재 이 분야의 문제점과 논쟁대상이 되고 있는 점들을 지적해 보고자 한다. 3장에는 탄성 동적 파괴역학 문제, 4장에는 탄소성 동적 파괴역학 문제에 대해서 각각 실험적연구, 수치 해석적 연구, 이론적인 연구의 측면으로 나누어서 이 강좌를 전개 할려고 한다. 5장에서는 Crack Arrest에 관한 이론 및 실제응용 예를 간단히 설명하고 6장에서 고찰 및 결론을 맺음으로서 이 강좌를 마무리 지울려고 한다.

• Proceedings of the Korea Concrete Institute Conference
• /
• 1992.10a
• /
• pp.76-81
• /
• 1992

Short, randomly disturbed steel fibers in concrete increase tensile strength and ductility of concrete under direct tension. These improvements are results form crack arrest mechanisms of steel fibers in concrete. These mechanisms are theoretically considered in this study and verification on the adequancy of different spacing for predicting tensile strength of SFRC are assessed. Results indicate that better correlation exists between experimental result and the spacing concept which take into account the effect of boundaries as well as vibration on reorientation of steel fibers inside concrete. Also considered is the modeling of stress-crack opening relationships in post-peak region of SFRC under tension which bass its deviation on micromechanics of fiber pull-out. Satisfactoring results are observed between tests results and the prediction of the model.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 1996.04a
• /
• pp.697-703
• /
• 1996

Fatigue strength of high strengthsteels are variable with many different surface treatment. It is well known that residual compressive stress retard fatigue crack growth rate(or arrest crack). High strngth steels are manufactured by following process. Heat treatment, shot peening and chromium plating process. High strength steel(HRC40 or above) which are subjected to fatigue load and dynamic load, chromium plated parts shall be peened in accordance with requirements and baked after plating. The purpose of this paper is to compare and discuss the influence of surface treatment and hydrogen embrittlement on fatigue strength of high strength steel. Therefore, fatigue test was performed to investigate influence of surface treatment. The results shows that shot peening is very effect method in creasing fatigue life and after plating, baking process is essential to prevent hydogen failure. In this paper, the experimental investigation is made to clarify the influence of shot peening conditions and baking process on fatigue strength of high strength steel.

• Composites Research
• /
• v.12 no.5
• /
• pp.40-53
• /
• 1999

The interlaminar facture behavior of multidirectional carbon-fiber/epoxy composite laminates under low and high rates of test, up to rate of about 11.4m/s has been investigated using the double cantilever beam specimens. The mode I loasing with rates above 1.0m/s had considerable dynamic effects on the load-time curves and thus revealed higher values of the average crack velocity than thet expected from a simple proportional relationship with the test rate. The modified beam analysis utilizing only the opening displacement and crack length exhibited an effective means for evaluating the dynamic fracture energy $G_{IC}$. Flexural modulus increased gradually with an increase of the test rate, which was utilized in the evaluation of $G_{IC}$. Values of $G_{IC}$ at the crack initiation and arrest were scarcely changed with increasing test rate up to 1.0m/s. However the maximum $G_{IC}$ was much enlarged at 11.4m/s due to the large amount of fiber bridging the crack tip. The larger the initial crack length, the smaller the maximum $G_{IC}$ at high rate.

• Nuclear Engineering and Technology
• /
• v.50 no.7
• /
• pp.1138-1147
• /
• 2018

Delayed hydride cracking (DHC) is an important failure mechanism for Zircaloy tubes in the demanding environment of nuclear reactors. The threshold stress intensity factor, $K_{IH}$, and critical hydride length, $l_C$, are important parameters to evaluate DHC. Theoretical models of them are developed for Zircaloy tubes undergoing non-homogenous temperature loading, with new stress distributions ahead of the crack tip and thermal stresses involved. A new stress distribution in the plastic zone ahead of the crack tip is proposed according to the fracture mechanics theory of second-order estimate of plastic zone size. The developed models with fewer fitting parameters are validated with the experimental results for $K_{IH}$ and $l_C$. The research results for radial cracking cases indicate that a better agreement for $K_{IH}$ can be achieved; the negative axial thermal stresses can lessen $K_{IH}$ and enlarge the critical hydride length, so its effect should be considered in the safety evaluation and constraint design for fuel rods; the critical hydride length $l_C$ changes slightly in a certain range of stress intensity factors, which interprets the phenomenon that the DHC velocity varies slowly in the steady crack growth stage. Besides, the sensitivity analysis of model parameters demonstrates that an increase in yield strength of zircaloy will result in a decrease in the critical hydride length $l_C$, and $K_{IH}$ will firstly decrease and then have a trend to increase with the yield strength of Zircaloy; higher fracture strength of hydrided zircaloy will lead to very high values of threshold stress intensity factor and critical hydride length at higher temperatures, which might be the main mechanism of crack arrest for some Zircaloy materials.

• KSCE Journal of Civil and Environmental Engineering Research
• /
• v.28 no.4A
• /
• pp.529-536
• /
• 2008

The failure behavior of structures is changed under different loading rates, which might arise from the rate dependency of materials. This phenomenon has been focused in the engineering fields. However, the failure mechanism is not fully understood yet, so that it is hard to be implemented in numerical simulations. In this study, the numerical experiments to a brittle material are simulated by the Molecular Dynamics (MD) for understanding the rate dependent failure behavior. The material specimen with a notch is modeled for the compact tension test simulation. Lennard-Jones potential is used to describe the properties of a brittle material. Several dynamic failure features under 6 different loading rates are achieved from the numerical experiments, where remarkable characteristics such as crack roughness, crack recession/arrest, and crack branching are observed during the crack propagation. These observations are interpreted by the energy inflow-consumption rates. This study will provides insight about the dynamic failure mechanism under different loading rates. In addition, the applicability of the MD to the macroscopic mechanics is estimated by simulating the previous experimental research.

• Proceedings of the KWS Conference
• /
• 2009.11a
• /
• pp.92-92
• /
• 2009

조선업을 포함한 다양한 산업 분야에서 후판 강재의 수요량 증가와 함께 사용 범위 또한 폭넓게 되고 있다. 특히, 선박의 수송효율의 극대화를 위하여 컨테이너선의 대형화가 급속하게 진행되고 있으며, 2009년 현재1,300TEU 이상의 초대형 컨테이너선이 건조되고 이다. 이처럼 용접구조물의 초대형화에 따른 사용강재 또한 고강도 극후물화 되고 있다. 현재 선박에 적용중인 고강도 강재는 EH47 강재로 YP 460MPa 급의 강재가 Hatch Coamming부에 적용중에 있으며, 강재의 두께 또한 70mm 이상이다. 이러한 고강도 극후물재의 강구조물에 적용에 따른 선급협회에서는 용접부에서의 취성균열 전파에 의한 취성파괴의 위험성이 있으므로 강재의 두께를 제한하고 더욱 엄격한 파괴인성값을 요구하고 있다. 일본선급협회(NK)를 중심으로 취성균열의 정지를 위한 모재의 요구 성능등에 관한 연구들이 진행되고 있다. 이 연구의 대부분의 전제 조건은 선박의 블럭과 블럭의 조립시에 용접부가 직선형이 아닌 계단형(Butt shift)를 하는 것으로 하고 있으므로, 국내의 조선건조 공법의 현실과는 거리감이 있다. 본 연구에서는 국내 조선사에서 수행중인 직선 이음부에 대한 시공 공법에서 취성균열이 발생하여 진전 되더라도 균열을 정지 시킬 수 있는 기술에 관한 연구를 수행하였다. 균열의 진전은 대부부의 연속면에서는 정지를 시키지 못하고 직진 전파 하여서 파괴에 도달하게 된다. 따라서 뭔가의 불연속적인 면을 임의로 생성하여야 균열을 정지 시킬 수 있다. 본 연구에서는 이러한 균열의 정지 방법으로 형상적인 측면과 재료적인 측면에서 검토를 수행하였다. 형상적인 측면에서는 균열을 정지 시키고자 하는 위치에 불연속적인 면을 만들기 위하여 일정 크기의 hole을 만들어서 균열을 정지시켰으며, 재료적인 측면에서는 고인성의 용접재료를 사용하여서 취성균열이 진행하는 경로에 인성을 높은 재료를 적용하여 불연속적인 면의 생성과 함께 인성을 높여서 균열을 정지 시키는 기술을 개발하였다. 이러한 기술의 개발을 통하여 취성균열의 전파에 의한 파괴를 방지 할 수 있으며, 용접구조물의 안전성 확보를 가능하게 하였다.