Effects of Flexural Modulus and Fiber Bridging on the Interlaminar Fracture Energy of Multidirectional Composite Laminates under High Rate Loading

고속하중을 받는 다방향복합적층판의 층간파괴에너지에 미치는 굽힘탄성계수와 섬유가교의 효과

  • ;
  • A.J.Kinloch (Mechanical Engineering, Imperial College of Science, Technology and Medicine, U.K.)
  • 최낙삼 (한양대학교 공학대학 기계공학과) ;
  • Published : 1999.10.01
Download PDF
⟨ Previous Next ⟩

Abstract

The interlaminar facture behavior of multidirectional carbon-fiber/epoxy composite laminates under low and high rates of test, up to rate of about 11.4m/s has been investigated using the double cantilever beam specimens. The mode I loasing with rates above 1.0m/s had considerable dynamic effects on the load-time curves and thus revealed higher values of the average crack velocity than thet expected from a simple proportional relationship with the test rate. The modified beam analysis utilizing only the opening displacement and crack length exhibited an effective means for evaluating the dynamic fracture energy $G_{IC}$. Flexural modulus increased gradually with an increase of the test rate, which was utilized in the evaluation of $G_{IC}$. Values of $G_{IC}$ at the crack initiation and arrest were scarcely changed with increasing test rate up to 1.0m/s. However the maximum $G_{IC}$ was much enlarged at 11.4m/s due to the large amount of fiber bridging the crack tip. The larger the initial crack length, the smaller the maximum $G_{IC}$ at high rate.

저속시험 및 약 11.4m/s까지의 고속시험을 받는 다방향 탄소섬유/에폭시 복합적층판의 층간파괴거동에 대해 양외팔보(DCB)시험편을 이용하여 연구했다. 모드I의 하중을 1.0m/s이상으로 가한 결과 하중-시간곡선에 동적효과가 발생하여, 시험속도에 비례하는 단순관게식으로 예상되는 것보다 더 큰 균열속도가 나타났다. 시험편 개구변위와 균열길이만을 사용하는 수정된 선형보해석식은 동적인 층간파괴에너지$G_{IC}$를 평가하기 위해 유효했다. 또한 굽힘탕선계수의 실측값은 시험속도의 증가에 다라 증가했는데, 이를 $G_{IC}$의 평가시에 고려했다. 시험속도가 1.0m/s까지 증가할 때, 균열개시 및 정지시의 $G_{IC}$값은 변화가 없었으나, 11.4m/s의 속도에서 최대 GIC값은 섬유가교효과의 증대로 크게 증가했다. 또한 초기균열길이가 길수록 고속시의 최대GIC값은 저하했다.

Keywords

References

  1. Composites Science and Technology v.35 Effects of fiber bridging on GIC of a unidirectional glass/epoxy composites Huang,X.N.;Hull,D.
  2. Application of Fracture Mechanics to Composite Materials;Composite Materials Series v.6 Imterlaminar mode-Ⅰ fracture testing Davies,P.;Benzeggagh,M.L.;Friedrich,K.(ed.)
  3. Application of Fracture Mechanics to Composite Materials;Composite Materials Series Relationship of matrix toughness to interlaminar fracture toughness Bradley,W.L.
  4. Composites Science and Technology v.39 Measurement of GIC and GIIC in carbon fiber/epoxy composites Davies,P.;Moulin,C.;Kausch,H.H.;Fischer,M.
  5. Journal of Composite Materials v.24 The effect of geometry, rate and temperature on the mode Ⅰ, mode Ⅱ and mixed-mode Ⅰ/Ⅱ interlaminar fracture of carbon-fiber/poly(ether-ether ketone) composites Hashemi,S.;Kinloch,A.J.;Williams,J.G.
  6. Composites Science and Technology v.37 Mechanics and mechanisms of delamination in a poly(ether sulphone)-fiber composites idem
  7. Journal of Composite Materials v.21 Rate Effects on Mode Ⅰ Interlaminar Fracture Toughness in Composite Materials Smiley,A.J.;Pipes, R.B.
  8. Journal of Materials Science v.24 Mechanisms for Rate Effects on Interlaminar Fracture Toughness of Carbon/Epoxy and Carbon/PEEK Composites Friedrich,K.;Walter,R.;Carlsson,L.A.;Smiley,A.J.;Gillespie Jr,J.W.
  9. Journal de Physique Ⅲ Frace Mechanical Characterization of Polymers and Composites with a Servohydraulic High-Speed Tensile Tester Beguelin,Ph.;Barbezat,M.;Kausch,H.H.
  10. Delamination and Debonding of Materials, ASTM STP876 Effects of Strain Rate on Delamination Fracture Toughness of Graphite/Epoxy Aliyu, A.A.;Daniel,I.M.
  11. Journal of Materials Science v.30 The Failure of Fiber Composites and Adhesively Bouded Fiber Composites under High Rates of Test Part Ⅰ: Mode Ⅰ Loading-Experimental Studies Blackman,B.R.K.;Dear,J.P.;Kinolch,A.J.;Macgillivray,H.;Wang,Y.;Williams,J.G.;Yayla,P.
  12. KSME International Journal v.12 A Study on Residual Fatigue Bending Strength and Damage Behavior of CFRP Composites Subjected to Impact Loadings Im,K.-H.;Kim,J.-H.;Yang,I-Y
  13. KSME International Journal v.11 Experiemental Investigation on Low Energy Impact Behavior of Foam Cored Sandwich Composites Yoon,S.H.;Kwon,Y.W.;Clawson Jr.,L.A.
  14. 대한기계학회논문집(A권) v.22 no.3 모드Ⅰ 하중조건하에 있는 다방향적층복합 재료의 층간파괴거동 최낙삼;Kinloch,A.J.
  15. 대한기계학회논문집(A권) 복합적층판의 층간파괴에 미치는 충격하중 속도의 효과 최낙삼;Kinloch,A.J.
  16. ASTM standard E-399 American Society for Testing and Materials
  17. Materials at High Strain Science The Effect of High Strain Rate on Material Properties Harding,J.;Blazynski,T.Z.(ed.)
  18. Journal of Reinforced Plastics and Composites v.2 Delamination of GIC in angle ply composites using a cantilever beam test method Nicholls,D.J.;Gallagher,J.P.
  19. Composites v.15 The characterization of mode Ⅰ delamination failure in non-woven, multidirectional laminates Chai,H
  20. Journal of Composite Materials v.26 A modofied DCB specimens for mode Ⅰ testing of multidirectional laminates Robinson,P.;Song,D.Q.
  21. Composites Science and Technology v.41 Mode Ⅰ interlaminar fracture of symmetrical cross-ply composites Laksimi,A.;Benzeggagh,M.L.;Jing,G.;Hecini,M.;Roelandt,J.M.