• Journal of the Korea Concrete Institute
• /
• v.17 no.5 s.89
• /
• pp.829-834
• /
• 2005

A series of reinforced G109 type specimens was fabricated and pended with a 15 weight percent NaCl solution. Mix design variables included 1) two cement alkalinities (equivalent alkalinities of 0.32 and 1.08), 2) w/c 0.50 and 3) two rebar surface conditions (as-received and wire-brushed). Potential and macro-cell current between top and bottom bars were monitored to determine corrosion initiation time. Once corrosion was initiated, the specimen was ultimately autopsied to perform visual inspection, and the procedure included determination of the number and size of air voids along the top half of the upper steel surface. This size determination was based upon a diameter measurement assuming the air voids to be half spheres or ellipse. The followings were reached based upon the visual inspection of G109 specimens that were autopsied to date. First, voids at the steel-concrete interface facilitated passive film breakdown and onset of localized corrosion. Based upon this, the initiation mechanism probably involved a concentration cell with contiguous concrete coated and bare steel serving as cathodes and anodes, respectively. Second, the corrosion tended to initiate at relatively large voids. Third, specimens with wire-brushed steel had a lower number of voids at the interface for both cement alkalinities, suggesting that air voids preferentially formed on the rough as-received surface compared to the smooth wire brushed one.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.25 no.5
• /
• pp.149-156
• /
• 2021

FRP has been proposed to replace the steel as a reinforcement in the concrete structures for addressing the corrosion issue. However, FRP-Rebar does not behave in the same manner as steel because the properties of FRP are different. For example, FRP-Rebar has a high tensile strength, low stiffness, and linear elastic behavior which results in a difference bonding mechanism to transfer the load between the reinforcement and the surrounding concrete. Therefore, bonding behavior between FRP-Rebar and concrete has to be investigated using the bonding test. So, Pull-out test has been used to estimate bond behavior because it is simple. However, the results of pull-out test have a difference with flexural-boding behavior of FRP-Rebar concrete member. So, it is needed to evaluate the real fleuxral-bonding behavior. In this study, the evaluation method to flexural-bonding behavior of FRP-Rebar concrete member was reviewed and compared. It was found that the most accurate evaluation method for the fleuxral-bonding behavior of FRP-Rebar concrete member was splice beam test, however, the size and length of specimen have to increase than other test method and the design and analysis of splice beam is complex. Meanwhile, characteristics of concrete could be reflected by using arched beam test, unlike hinged beam test which is based on the ignored change of moment arm length in equilibrium equation. However, the possibility of shear failure exists before the flexural-bonding failure occur.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2020.11a
• /
• pp.192-193
• /
• 2020

In reinforced concrete adhesion studies, the demolition of the specimen is inevitably involved, and the studies conducted are limited to the macro load-displacement analysis. In order to establish an elaborate model for concrete bonding reinforced rebars, it is necessary to observe the rebar bonding behavior in the in-situ state. In this study, specially manufactured reinforcing bars, micro-UTM and 𝝁-computer tomography (𝝁CT) are used to observe reinforcing bars in the in-situ state. As a result of the monotonic pullout test of the processed reinforcing bar, maximum bond stress were shown to be 16.7MPa, which is slightly higher than the existing 10 to 12 MPa, and then the empty space inside the specimen in which the pullout test was conducted using 𝝁CT was confirmed. Through additional research, the fracture phenomenon of concrete excluding voids will be studied.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2008.04a
• /
• pp.1069-1072
• /
• 2008

As embedded reinforcing suffer from corrosion process, the bond strength and stiffness are reduced, and the structure proceed, eventually, to the deterioration of the concrete, shortening the service life of concrete structures rapidly. In order to deal with these problems, a multitude of researches have been carried out up to this date to evaluate the bond characteristics of RC members, i.e. by artificially inducing rapid corrosion of the reinforcing bar. These artificial corrosion methods, however, could not represent the real condition, resulting in the possibility of overestimation for the RC members in real situation. Accordingly, the purpose of this paper is to investigate the difference in the bond characteristics for RC members corroded by different corrosion methods (artificial rapid method, natural method). For the case of natural corrosion, the brittle failure was observedeven for the case of the area ofcorrosion of 50%. And, the bond strength decreased by about 10% or more for the caseofspecimens with the area of corrosion of 80% or above. Especially, the deterioration of concrete starts at the state of low corrosion level for the case of natural corrosion. Thus, the safety of RC members must be assessed and evaluated more carefully for the naturally corroded members than for the RC concrete members corroded rapidly by artificial method.

• Journal of the Korea Institute of Building Construction
• /
• v.19 no.6
• /
• pp.495-501
• /
• 2019

Recently, research has been carried out into the use of carbon fiber reinforced polymer (CFRP), which has good tensile strength and corrosion resistance, as an alternative to rebar. But as of yet, the research into fatigue failure of CFRP is insufficient. In this paper, an analysis was performed of the mechanical behavior and failure patterns of CFRP reinforced concrete beams according to static and cyclic loads, in order to evaluate the safety and validity of CFRP rebar as an alternative material for rebar. The cyclic load ranged from 10 % to 70% of the ultimate load, and was loaded at a speed of 3Hz using a sine wave in the form of a three-point loading method. Through the static load test, the maximum load or stiffness of the beam was found to increase remarkably with the increase of the reinforcement, but the fatigue test showed that the number of repetitions decreased and the amount of deflection increased with the increase of the reinforcement.

• Corrosion Science and Technology
• /
• v.17 no.6
• /
• pp.272-278
• /
• 2018

Reinforced concrete (RC) has been used as a construction material in various environments, such as airports, bridges, and ocean concrete structures, etc. Over time, however, rebar in the concrete is prone to corrosion from environmental forces and structural defects of the concrete. Cathodic protection (CP) was invented to prevent problems with corrosion and is widely used for different applications. Cathodic protection is divided into two types: sacrificial anode cathodic protection (SACP) and impressed current cathodic protection (ICCP). There are several limitations to the use of sacrificial anode cathodic protection in complex reinforced concrete structures, including concrete resistivity, throwing power of the CP, and environmental conditions. These limitations can affect the protection performance of SACP. Therefore, we used impressed current cathodic protection in our study. We tested Ti-Mesh, Ti-Rod, and Ti-Ribbon anodes in slab type reinforced concrete specimens. Electrochemical tests were conducted to confirm the impressed current cathodic protection performance under different environmental conditions.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.12 no.1
• /
• pp.47-52
• /
• 2024

The demand for FRPs that are corrosion-free and have an excellent tensile strength-to-weight ratio. However, there is a lack of research on the mechanical properties of FRP in the form of rebars, especially the changes in performance due to heating. Therefore, in this paper, 60 tensile and compression specimens of CFRP rebars with a diameter of 12 mm were fabricated and subjected to direct tensile and direct compression tests, and their performance was evaluated according to the heating temperature. It was found that as the heating temperature increases above 300 ℃, the performance decrease becomes larger due to the burning of epoxy. The compressive strength was found to be much lower than the tensile strength, but the modulus of elasticity was found to be the same in tension and compression.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2002.10a
• /
• pp.17-22
• /
• 2002

Chloride ions have a tendency to penetrate into concrete and proceed the corrosion by depassivating rebar surface. Thus the deteriorated concrete is subject to experience severe degrading of durability under marine environment. Physical properties of mortar, such as, compressive strength and penetration depth of chloride ion were investigated. And to investigate the effect of containing SG, FA in mortar, the diffusion coefficient of chloride was measured through an electro - migration test. The diffusion coefficient of chloride was decreased with the increase of replacement ratio of SG compared with plain specimen.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2006.11a
• /
• pp.637-640
• /
• 2006

Due to contaminated environment many concrete structures are carbonated. It causes the corrosion of rebar and induces the cracks of concrete, eventually. This study investigates the mechanism and properties of the alkali recovery agents(ARA) which are currently applied for repairing concrete structures on sites. The results indicate that the ARAs are not sufficiently effective to the realkalization of concrete structures.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.22 no.4
• /
• pp.10-18
• /
• 2018

The primary purposes of this study are to understand a fundamental aspect of current uniformity around a reinforcing bar (rebar) in cement mortar, and to develop an accurate monitoring method in a wet-dry cycling process with the alternative current (AC) impedance method. Three cement mortar specimens with two embedded rebars were prepared in the laboratory. As a main variable, the distance between two rebars was designed to be 10, 20 and 30 mm with the same thickness of 20 mm. To simulate the corrosion of rebars in concrete structures in a marine environment, three cement mortar specimens were exposed to 15 wet-drying cycles (24-hour-immersion in seawater and 48-hour-drying in a room temperature) in the laboratory. It was observed that the potential level shifted to a noble value during corrosion potential monitoring, which is attributed to acceleration of dissolved oxygen diffusion at the drying process. AC impedance was measured in a frequency range from 100 kHz to 1 mHz on a wet-drying process. A theoretical model was proposed to explain the interface condition between the rebars and cement mortar by using the equivalent circuit consisting of a solution resistance, a charge transfer resistance and a CPE (constant phase element). It was observed that the diffusion impedance appeared in a low frequency range as corrosion of rebars progresses. At the drying stage of the wet-drying cycles, the currents line for monitoring tended to be non-uniform at the interface of rebar/mortar, being phase shift, ${\theta}$, close to $-45^{\circ}$.