• Corrosion Science and Technology
• /
• v.3 no.6
• /
• pp.245-250
• /
• 2004

A series of classical G109 type concrete specimens was exposed to cyclic wet and dry ponding with 15 w/o NaCl solution for approximately five years. Mix design variables included 1) three cement alkalinities (EqA of 0.97, 0.52, and 0.36) and 2) three water-cement ratios (0.50, 0.41, and 0.37). To determine the corrosion initiation time, corrosion potential and macro-cell current between top and bottom bars were monitored. Subsequent to corrosion initiation, specimens were autopsied and visually inspected. Concrete powder samples were collected from top rebar trace and chloride concentration was measured. Also, time-to-corrosion, $T_i$, for specimens of the individual mix designs was represented using Weibull analysis. Time-to-corrosion was a distributed parameter; and because of this, corrosion initiation of four identical specimens for each mix varied, often over a relatively wide range. Specimens fabricated using the lowest water cement ratio and the highest alkalinity cement exhibited the longest time-to-corrosion initiation and the highest chloride threshold levels. Time-to-corrosion did not increase monotonically with cement alkalinity, however, presumably as a consequence of relatively high $Cl^-$ binding in the lower pore water pH range. The chloride threshold level, $Cl_{th}$, increased with increasing $T_i$ and, consequently, was greatest for the highest cement alkalinity specimens.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2023.05a
• /
• pp.33-34
• /
• 2023

Corrosion of reinforcement steel is a major cause of deterioration in reinforced concrete (RC) structures. In order to protect these structures from corrosion, corrosion inhibitors are added to the concrete mix. In recent years, zwitterionic compounds have shown promising results as corrosion inhibitors in concrete due to their ability to form a protective layer on the surface of the reinforcement steel. The experimental study involves preparing concrete samples with different concentrations of adding the hybrid corrosion inhibitor at a high concentration of chloride ions. This study aims to determine the chloride threshold value and service life of hybrid corrosion inhibitors in reinforced concrete based on zwitterions. The samples are subjected to accelerated corrosion tests in a chloride environment to determine the threshold value and service life of the corrosion inhibitor. The effect of hybrid inhibitor on mechanical properties is guaranteed in allowable range. The chloride threshold concentration and service life of hybrid inhibitor containing samples perform greater than those of plain RC.

• International Journal of Concrete Structures and Materials
• /
• v.4 no.2
• /
• pp.71-75
• /
• 2010

The chloride ion attack on the passive iron oxide layer of reinforcement steel embedded in concrete under variable temperature environment is influenced by several parameters and some of them still need to be further investigated in more detail. Different school of thoughts exist between past researchers and the data is limited in the high temperature and high chloride concentration range which is necessary with regards to setting boundary conditions for enhancement of tafel diagram model presented in this research. The objective of this paper is to investigate the detrimental coupled effects of chloride and temperature on corrosion of reinforced concrete structures in the high range by incorporating classical Tafel diagram chloride induced corrosion model and laboratory controlled experimental non-linear effect of temperature on corrosion of rebar embedded in concrete.

• Structural Engineering and Mechanics
• /
• v.75 no.4
• /
• pp.455-464
• /
• 2020

Reinforcement corrosion is one of the major problems in the durability of reinforced concrete structures exposed to aggressive environments. Deterioration caused by reinforcement corrosion reduces the durability and the safety margin of concrete structures, causing excessive costs in managing these structures safely. This paper aims to investigate the effects of reinforcement corrosion on the load bearing capacity deterioration of the corroded reinforced concrete structures. A new analytical method is proposed to predict the crack growth of cover concrete and evaluate the residual strength of concrete structures with corroded reinforcement failing in bond. The structural performance indicators, such as concrete crack growth and flexural strength deterioration rate, are assumed to be a stochastic process for lifetime distribution modelling of structural performance deterioration over time during the life cycle. The Weibull life evolution model is employed for analysing lifetime reliability and estimating remaining useful life of the corroded concrete structures. The results for the worked example show that the proposed approach can provide a reliable method for lifetime performance assessment of the corroded reinforced concrete structures.

• Proceedings of the Korea Concrete Institute Conference
• /
• 1998.10c
• /
• pp.217-222
• /
• 1998

In these days, mostof marine structures are constructed by reinforcement concrete due to economic reason. Theoretically, it is widely recognized that rebar in sound concrete is safe against corrosion because of the high alkalinity of concrete. However, corrosion for reinforcement concrete made by marine aggregate and exposed to ocean enviroments has become serious social problem. Especially in Korea, with the rapid economic growth construction activities have been accelerated and needed more natural aggregate. Therefore, inevitably marine aggregate had to be used due to limitation of good quality aggregate. In this study, as a part of efforts to establish the fundamental counterplan on corrosion problems related to marine aggregate, concrete specimens with chloride containing material and inhibitor have been studied. And, in order to analyze corrosion characteristics several electrochemical techniques including half-cell potential survery, linear and cyclic polarization tests were carried out.

• Proceedings of the Korea Concrete Institute Conference
• /
• 1997.10a
• /
• pp.299-302
• /
• 1997

Generally the corrosion expansion of the steel due to outdoor corrosive environmental factor brings about serious problem on the durability of concrete structures. It is the purpose of this study to see whether adapted sacrificial anode method is effective or not. from the experimental results. the potential of steel in concrete in case of adapting the sacrificial anode method satisfies protection standard value (less than -850mV vs CSE).

• Corrosion Science and Technology
• /
• v.21 no.2
• /
• pp.100-110
• /
• 2022

Corrosion of steel reinforcement is the most important mode of concrete structures damages. It strongly depends on the composition and physicochemical properties of the cementitious medium. The use of waste materials as lightweight aggregates in concrete is environmentally recommended in polluted environments such as marine and/or industrial atmospheres in order to reduce its porosity and ensure the requested protection of reinforcing steel. The present study investigated the effect of waste cork addition on corrosion resistance of steel rebar in mortar specimen prepared in the laboratory. The main objective of this study was to improve the corrosion resistance of reinforcing steel. Another objective of this study was to valorize this ecological product and preserve the environment. Results obtained from various electrochemical tests indicated that the presence of a fine cork powder substantially improved the corrosion resistance of steel in the mortar contaminated by chloride ions. This improvement was reflected by a notable decrease in corrosion current density and a shift of corrosion potential of the steel towards more noble values. Moreover, the presence of a fine cork powder in the mortar had no adverse effect on its mechanical properties.

• Journal of the Korea Concrete Institute
• /
• v.26 no.3
• /
• pp.299-306
• /
• 2014

Coating is one of the methods used to solve the problem of corrosion of reinforcement in concrete structures. There are few research reported in the literature regarding the effect of zinc-coating on flexural behavior compared to epoxy coating. The objective of this study was to determine whether zinc-coated rebar adversely affects flexural behavior. Concrete beams reinforced with black or zinc-coated steel were tested in flexure. The test variables included the presence of rebar surface coating with zinc, steel ratio used and cover depth. The study concentrated on comparing crack pattern, crack width, deflection and strain. The ultimate flexural capacity of beams reinforced with zinc-coated bars was not different from that of black steel reinforced beams. The results from deflection and crack width measurements were indicative of no significant variation for the different rebar surface conditions. In addition, it was found that load-strain curve of beam reinforced with zinc-coated steel was similar to that of beam reinforced with zinc-coated steel. Therefore, the test results indicated that the use of zinc-coated rebar had no adverse effect on flexural behavior compared to the use of black rebar.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.14 no.12
• /
• pp.6565-6574
• /
• 2013

Precast concrete blocks are used mainly for score protection, slope protection and riverbed structure protection, etc. Because these concrete blocks are exposed to water or wetting environments, the steel rebar used as reinforcements in concrete blocks can corrode easily. Corrosion of the steel rebar tends to reduce the performance and service life of the concrete blocks. In this study, Glass Fiber Reinforced Polymer(GFRP) rebar, which does not corrode, was applied instead of a steel rebar to prevent performance degradation of the blocks. Recycled concrete aggregate and high early strength cement(HESC) were used in the concrete mix for field applicability. The experiment results showed that the workability and form removal strength of the recycled aggregate concrete using HESC showed comparable results to normal concrete and the compressive strength at 28 days increased by about 18% compared to normal concrete. The load resistance capacity of the recycled aggregate concrete blocks reinforced with a GFRP rebar increased by approximately 10~30% compared to common concrete block.

• Steel and Composite Structures
• /
• v.9 no.1
• /
• pp.77-87
• /
• 2009

This paper reports the results of an experimental investigation of the polyvinylpyrrolidone (PVP) influence on the steel reinforcement corrosion and compressive strength of concretes in sulphate medium. The effect of admixture of PVP in concrete on the corrosion resistance of steel reinforced concrete was assessed by measuring electrochemical test during 60 days immersion in two different external solutions. AC impedance spectrum indicated that the resistance of PVP mixed electrodes were higher than those without PVP. The compressive strength of concrete specimens containing PVP was measured and an increase of 19%~24% was observed.