• Journal of Welding and Joining
• /
• v.19 no.2
• /
• pp.182-190
• /
• 2001

A marine structural material was well known to have high tensile strength, good weldability and proper corrosion resistance. Cu-containing high strength low alloy(HSLA) steel was recently developed for their purposes mentioned above. And the steel is free about preheating for welding, therefore it is reported that shipbuilding cost by using it can be saved more or less. However the marine structural materials like Cu-containing HSLA steel are being generally adopted with cathodic protection method in severe corrosive environment like natural sea water but the high strength steel may give rise to Hydrogen Embrittlement due to over protection at high cathodic current density for cathodic protection. In this study Cu-containing HSLA steel using well for marine atructure was investigated about the susceptibility of Hydrogen Embrittlement as functions of tensile strength, strain ratio, fracture time, and fracture mode, etc. and an optimum cathodic protection potential by slow strain rate test(SSRT) method as well as corrosion properties in natural sea water. And its corrosion resistance was superior to SS400 steel, but Hydrogen Embrittlement susceptibility of Cu-containing HSLA steel was higer than that of SS400 steel. However Hydrogen Embrittlement of its steel by SSRT method was showed with pheonomena such as decreasing of fracture time, strain ratio and fracture mode of QC(quasi-cleavage). Eventually it is suggested that an optimum cathodic protection potential not presenting Hydrogen Embrittlement of Cu-containing of HSLA steel by SSRT method was from-770mv(SCE) to - 900mV(SCE)under natural sea water.

• Journal of the Korean Society of Safety
• /
• v.28 no.5
• /
• pp.21-26
• /
• 2013

Delamination of cover concrete due to re-bar corrosion is a critical damage reducing structural safety of reinforced concrete structures. Therefore, it should be detected and evaluated to provide appropriate maintenance to recover structural integrity. Impact-echo method, which utilizes thickness vibration characteristics of delaminated concrete section, is effective for detection and evaluation of small areal size delamination. However, it may not be applicable for large areal size delamination in which flexural vibration modes are dominated. In this study, applicability of vibration mode shapes of delaminated concrete section is investigated for visualization of delamination region in concrete structures. Numerical and experimental modal tests are performed to estimate mode shapes of delaminated concrete section and linear absolute summation technique is proposed for effective visualization of delamination region based on estimated mode shapes.

• Journal of Ocean Engineering and Technology
• /
• v.11 no.1
• /
• pp.16-23
• /
• 1997

Stainless steel are widely applicable in various engineering fields for its exellent corrosion and impact ressistance. Austenitic weld metal has some ferrite for preventing solidification cracking by ASME specification. Several family of austenic stainless steel contains varying ferrite contents. But ferrite in austenic stainless steels is adversely affect weld metal toughness and since fully austenic grades are known to have good toughness. Austenic stainless steel has various alloying addition for improving corrosion resistance, impact toughness and solidification crack resistance. The effect of various alloying elements are not found to be clear in present. From this view of point, this study tried to establish the criteria of alloy design for austenic stainless steel by controlling primary solidification mode and clarifying the effect of several alloying elements.

• Journal of the Korean institute of surface engineering
• /
• v.50 no.6
• /
• pp.432-438
• /
• 2017

AZ91D casting alloy requires an advanced plasma anodizing processing because large amount of defects are liable to generate during anodization. In this study, plasma electrolytic oxidation (PEO) of AZ91D Mg alloy was conducted by the application of either constant voltage or current using a pulse mode and its effects on pore formation, surface roughness and corrosion resistance were investigated. The PEO films showed a three-layer structure. The PEO film thickness was found to increase linearly with voltage. The surface roughness, Ra, ranged between $0.2{\mu}m$ and $0.3{\mu}m$. The corrosion resistance increased from RN 3.5 to 9.5 by the PEO treatment when evaluated according to the 72 hour salt spray test. The PEO-treated surface exhibited higher pitting potential than the raw material.

• Journal of the Korean institute of surface engineering
• /
• v.55 no.6
• /
• pp.417-424
• /
• 2022

This research develops an easy-to-use, environmentally friendly method for fabricating functional 1050 aluminum alloy surfaces with excellent corrosion resistance. Functional aluminum surfaces with various nanostructures are fabricated by controlling the experimental conditions of anodizing process. The experiment used a multi-step anodizing process that alternates between two different anodizing modes, mild anodizing (MA) and hard anodizing (HA), together with a pore-widening (PW) process. Among them, the nanostructured surface with a small solid fraction shows superhydrophobicity with a contact angle of more than 170° after water-repellent coating. In addition, the surface with superhydrophobicity is difficult for corrosive substances to penetrate, so the corrosion resistance is greatly improved.

• Bulletin of the Korean Chemical Society
• /
• v.9 no.4
• /
• pp.191-195
• /
• 1988

The effect of some thiosemicarbazide derivatives on corrosion of aluminium in 2M sodium hydroxide has been studied using thermometric, weight loss and hydrogen evolution techniques. The rate of the corrosion depends on the nature of the inhibitor and its concentration, heated of hydrogenation, mode of interaction with the metal surface and formation of metallic complexes. The compounds are weakly adsorbed on the surface of aluminium and form a monolayer of the adsorbate. Values of the Arrhenius activation energies indicate agreement with those obtained for an activation controlled process.

• Corrosion Science and Technology
• /
• v.12 no.6
• /
• pp.274-279
• /
• 2013

Flow accelerated corrosion (FAC) of the carbon steel piping in nuclear power plants (NPPs) has been major issue in nuclear industry. During the FAC, a protective oxide layer on carbon steel dissolves into flowing water leading to a thinning of the oxide layer and accelerating corrosion of base material. As a result, severe failures may occur in the piping and equipment of NPPs. Effect of alloying elements on FAC of pipe materials was studied with rotating cylinder FAC test facility at $150^{\circ}C$ and at flow velocity of 4m/s. The facility is equipped with on line monitoring of pH, conductivity, dissolved oxygen(DO) and temperature. Test solution was the demineralized water, and DO concentration was less than 1 ppb. Surface appearance of A 106 Gr. B which is used widely in secondary pipe in NPPs showed orange peel appearance, typical appearance of FAC. The materials with Cr content higher than 0.17wt.% showed pit. The pit is thought to early degradation mode of FAC. The corrosion product within the pit was enriched with Cr, Mo, Cu, Ni and S. But S was not detected in SA336 F22V with 2.25wt.% Cr. The enrichment of Cr and Mo seemed to be related with low, solubility of Cr and Mo compared to Fe. Measured FAC rate was compared with Ducreaux's relationship and showed slightly lower FAC rate than Ducreaux's relationship.

• Journal of the Korean Society of Combustion
• /
• v.16 no.3
• /
• pp.12-20
• /
• 2011

Oxy-coal combustion for $CO_2$ capture in coal power plants entails a mode switching from air-firing to oxyfiring. In this study, procedure of the mode switching was investigated and discussed through experiments in pilot scale facilities: (1) a 0.3 $MW_{th}$ furnace with a vertical single burner and a FGR(Flue Gas Recirculation) system (2) a 1 $MW_{th}$ furnace with horizontal 4 burners and a FGR system. Principle of the mode switching was established and performed with control of FD fan, FGR fan, ID fan and oxygen flow rates. We have found that equivalence ratio in the oxy-firing mode should be increased more than that in the air-firing to achieve stable mode switching. Control of FD, ID and FGR fans should be performed carefully in the mode switching, in the sense of complete combustion and flame attachment. Moisture contents in the ash and the flue gas recycled to the primary oxidizer stream should be removed to prevent condensation, corrosion and duct clogging.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.24 no.1 s.173
• /
• pp.156-162
• /
• 2000

Sensitized STS 304 stainless steel crack growth rate(CGR) in high temperature water was investigated under trapezoidal wave loading test using fracture mechanics techniques. The CGR, due to stress corrosion cracking(SCC), were systematically measured as a function of the stress intensity factor and stress. holding time under trapezoidal wave loading. In high temperature water, CGR was enhanced by a synergistic effects in combination with an aggressive environment and mechanical damage. The CGR, $(da/dN)_{env}$ was basically described as a summation of the environmentally assisted crack growth rate $(da/dN)_{SCC}$, $(da/dN)_{CF}$ and fatigue crack growth rate in air $(da/dN)air,. The CGR, $(da/dN)_{env}$, increased linearly with increasing stress holding time. The CGR, $(da/dN)_{SCC}$ decreased linearly with increasing stress holding time. Fracture surface mode varied from trans-granular cracking to inter-granular cracking with increasing stress holding time.

• Journal of Korea Foundry Society
• /
• v.12 no.2
• /
• pp.131-138
• /
• 1992

The effects of B additions, alone or in combination with Si, on the microstructure, $DO_3{\rightleftharpoons}B2$ transition temperature($T_c$) and corrosion behavior of Fe-25at%Al alloys were investigated. The raw materials were arc-melted in vacuum and then subjected to the following heat treatments to maximize the $DO_3$ order : homogenized at $1000^{\circ}C$ for 48hrs, slowly cooled to $500^{\circ}C$, and held at that temperature for 24hours. Results showed that the B addition to Fe-25at%Al alloys does indeed refine the grain and change from intergranular to transgranular fracture mode at room temperature, indicating a strengthening of grain boundaries. The Fe-25at% Al-1at% B-3at% Si alloy showed the highest $T_c$(${\Delta}T_c=150^{\circ}C$) in this work. However, the effectiveness of Si in raising $T_c$ decreased with more than 5at% Si additions combined with B. Since the preferential corrosion occurs at the precipitates, the corrosion resistance decreased due to the increased amount of precipitates with alloying additions.