• Advances in nano research
• /
• v.1 no.3
• /
• pp.159-169
• /
• 2013

A preparation method for gadolinium compound (GdC) nanoparticles coated with silica ($GdC/SiO_2$) is proposed. GdC nanoparticles were prepared with a homogeneous precipitation method at $80^{\circ}C$ using $1.0{\times}10^{-3}$ M $Gd(NO_3)_3$, 0.5 M urea and $0-3.0{\times}10^{-4}$ M ethylenediarinnetetraacetic acid disodium salt dihydrate (ETDA) in water. As a result of preparation at various EDTA concentrations, GdC nanoparticles with a size as small as $40.5{\pm}6.2$ nm, which were colloidally stable, were prepared at an EDTA concentration of $2.0{\times}10^{-4}$ M. Silica-coating of the GdC nanoparticles was performed by a St$\ddot{o}$ber method at $35^{\circ}C$ using $1.0-10.0{\times}10^{-3}$ M tetraethylorthosilicate (TEOS), 11 M $H_2O$ and $1.5{\times}10^{-3}$ M NaOH in ethanol in the presence of $1.0{\times}10^{-3}$ M GdC nanoparticles. Performance of preparation at various TEOS concentrations resulted in production of $GdC/SiO_2$ particles with an average size of $106.1{\pm}11.2$ nm at a TEOS concentration of $5.0{\times}10^{-3}$ M. The gadolinium (Gd) concentration of $1.0{\times}10^{-3}$ M in the as-prepared $GdC/SiO_2$ particle colloid solution was increased up to a Gd concentration of 0.2 M by concentrating with centrifugation. The core-shell structure of $GdC/SiO_2$ particles was undamaged, and the colloid solution was still colloidally stable, even after the concentrating process. The concentrated $GdC/SiO_2$ colloid solution showed images of X-ray and magnetic resonance with contrast as high as commercial Gd complex contrast agents.

• Applied Chemistry for Engineering
• /
• v.32 no.6
• /
• pp.690-694
• /
• 2021

Carbon spheres (CS) were fabricated using glucose as a precursor in the hydrothermal method. Hollow TiO₂ (H-TiO₂) spheres with 200 nm, 500 nm, and 1,200 nm were synthesized by CS/TiO₂ core-shell particles via a sol-gel and calcination method. H-TiO₂ spheres with nano and micron sizes were characterized using FE-SEM, HR-TEM, and X-ray diffraction. The CIE color coordinate, solar reflectance, and heat shield temperatures of H-TiO₂/polyacrylate (PA) composite film were investigated using a UV-Vis-NIR spectrometer and homemade heat insulation temperature measuring device. H-TiO₂/PA composites exhibit excellent thermal insulation since the hollow structure filled with dry air has low thermal conductivity and near infrared light reflecting performance. The thermal insulation increased with increasing the hollow sphere (HS) size on H-TiO₂/PA composites. The PA composite film mixed with H-TiO₂ filled with 1200 nm HS reduced the heat shield temperature by 26 ℃ compared to that of the transparent glass counterpart.

• Fibers and Polymers
• /
• v.3 no.1
• /
• pp.8-13
• /
• 2002

The effect of block sequence on the self-assembly of ABC-type triblock copolymers in the ordered state is investigated using an isothermal-isobaric molecular dynamics simulation. The block sequence has an important effect ,on the ]norphology of ABC triblock copolymers. Different morphologies are observed depending on the block sequence as well as the block composition. The triblock copolymers with the volume fraction of 1 : 1 : 1 ($f_A$=$f_B$=$f_C$= 0.33) show the three phase and four layered lamellar structures irrespective of the block sequence. The $A_{32}$$B_{16}$$C_{32}$triblock copolymer with $f_B$=0.2 shows a morphology In which cylinders of midblock B are formed at the interface between A and C lamellae, whereas the morphology of triblock copolymer $B_{16}$$C_{32}$ $A_{32}$ and $C_{32}$ $A_{32}$ $B_{16}$ show a cylindrical core-shell structure and a lamellar type morphology, respectively. The $A_{20}$$B_{40}$$C_{20}$the triblock copolymer with the block B as a major component shows a tricontinuous structure, whereas both $B_{40}$$C_{20}$$A_{20}$ and $C_{20}$$A_{20}$$B_{40}$ triblock coolymers exhibit the lamellar structures. When the block B has larger volrome fraction with $f_B$=0.75, the matrix is composed of block B, and other two blocks A and C form spherical domains.

• Korean Journal of Materials Research
• /
• v.19 no.10
• /
• pp.517-521
• /
• 2009

Si-C composite with hollow spherical structure was synthesized using ultrasonic treatment of organosilica powder formed by hydrolysis of phenyltrimethoxysilane. The prepared powder was pyrolyzed at various temperatures ranging from 900 to 1300 $^{\circ}C$ under nitrogen atmosphere to obtain optimum conditions for Li-ion battery anode materials with high capacity and cyclability. The XRD and elemental analysis results show that the pyrolyzed Si/C composite at 1100 $^{\circ}C$ has low oxygen and nitrogen levels, which is desirable for increasing the electrochemical capacity and reducing the irreversible capacity of the first discharge. The solid Si-C composite electrode shows a first charge capacity of $\sim$500 mAhg$^{-1}$ and a capacity fade within 30 cycles of 0.93% per cycle. On the other hand, the electrochemical performance of the hollow Si-C composite electrode exhibits a reversible charge capacity of $\sim$540 mAhg$^{-1}$ with an excellent capacity retention of capacity loss 0.43% per cycle up to 30 cycles. The improved electrochemical properties are attributed to facile diffusion of Li ions into the hollow shell with nanoscale thickness. In addition, the empty core space provides a buffer zone to relieve the mechanical stresses incurred during Li insertion.

• Composites Research
• /
• v.29 no.4
• /
• pp.145-150
• /
• 2016

Polyvinylidene fluoride (PVDF) as a representative polymer with the piezoelectric property has been studied since the 1960s. Crystalline structure of poly(vinylidene fluoride) polymer is composed of five different crystal structure of the polymer as a semi-crystalline. Among the various crystal structures, ${\beta}-type$ crystal exhibits a piezoelectricity because the permanent dipoles are aligned in one direction. Generally ${\beta}-form$ crystal structure can be obtained through the transformation of the ${\alpha}-form$ crystal structure by the stretching and it can increase the amount through the after treatment as poling process after stretching. ${\beta}-form$ crystal structure the PVDF fibers produced by wet spinning is formed through a diffusion mechanism of a polar solvent in the coagulation bath. However, it has a disadvantage that the diffusion path of the solvent remains as pores in the fiber because the fiber solidification occurs simultaneously with the diffusion of the polar solvent. These pores play a role in reducing effect of poling process owing to effect of disturbances acting on the polarization by the electric field. In this work, the drying method using the microwave was introduced to remove more effectively the residual solvent and the pore within PVDF fibers produced through wet-spinning process and piezoelectric PVDF fibers was produced by transformation of the remaining ${\alpha}$ form crystal structure into ${\beta}-crystal$ structure through the stretching process.

• Journal of the Korean Electrochemical Society
• /
• v.12 no.2
• /
• pp.189-195
• /
• 2009

$\beta-Ga_{2}O_{3}$ nanorods were synthesized by chemical vapor deposition method using nickel-oxide nanoparticle as a catalyst and gallium metal powder as a source material. The average diameter of nanorods was around 160 nm and the average length was $4{\mu}m$. Also, we confirmed that the synthesis of nanorods follows the vapor-solid growth mechanism. From the results of X-ray diffraction and HR-TEM observation, it can be found that the synthesized nanorods consisted of a typical core-shell structure with single-crystalline $\beta-Ga_{2}O_{3}$ core with a monoclinic crystal structure and an outer amorphous gallium oxide layer. Li/$\beta-Ga_{2}O_{3}$ nanorods cell delivered capacity of 867 mAh/g-$\beta-Ga_{2}O_{3}$ at first discharge. Although the Li/$\beta-Ga_{2}O_{3}$ nanorods cell showed low coulombic efficiency at first cycle, the cell exhibited stable cycle life property after fifth cycle.

• Journal of the Korea Organic Resources Recycling Association
• /
• v.31 no.1
• /
• pp.5-14
• /
• 2023

In this study, LiDAR-reflective black hollow-structured silica/titania(B-HST) materials are successfully synthesized by employing the NaBH₄ reduction and etching method on silica/titania core/shell(STCS) materials, which also effectively enhance near-infrared(NIR) reflectance. Moreover, core-etched supernatant solutions are collected and recycled for the synthesis of extracted silica(e-SiO₂) process, which successfully applies as filler materials for semiconductor epoxy molding compound(EMC). In detail, B-HST materials, fabricated by the sequential experimental steps of sol-gel, reduction, and sonication-mediated etching method, manifest blackness(L^*) of 13.2 similar to black paint and excellent NIR reflectance(31.1%). Consequently, B-HST materials are successfully prepared as LiDAR-reflective black materials. Additionally, core-etched supernatant solution with silanol precursors are employed for synthesis of homogeneous silica filler materials via sol-gel method. As-synthesized silica fillers are incorporated with epoxy resin and carbon black for the preparation of semiconductor EMC. Experimentally synthesized EMC exhibits comparable mechanical-chemical properties to commercial EMC. Conclusively, this study successfully proposes designing procedure and practical experimental method for simultaneously synthesizing the NIR-reflective black materials for self-driving vehicles and EMC materials for semiconductors, which are materials suitable for the industrial 4.0 era, and presented their applicability in future industries.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.21 no.1
• /
• pp.41-46
• /
• 2011

The artificial aggregates (AAs) composing of 2 wastes, coal bottom ash and dredged soil (7 : 3, weight ratio) were fabricated as a function of red mud contents,0~30 wt% using direct sintering method at $1050{\sim}1250^{\circ}C$ for 10 min, and those physical properties were evaluated. Especially, in order to analyze the red mud addition effect on the bloating phenomenon of AAs manufactured, the specific gravity and water absorption were measured and studied linked with the microstructural observation results. The lightening of AAs was enhanced due to increased bloating with increasing temperature and red mud contents. The AAS sintered at $1050{\sim}1150^{\circ}C$ showed well-developed black-coring structure, but for the specimens containing red mud sintered over $1200^{\circ}C$ generated excessive liquid and gas caused by reduction of $Fe_2O_3$, thus the black-coring part was gradually burst open out of shell of AAs. Particularly, all specimens containing 30 wt% red mud was burst up when sintered over $1100^{\circ}C$. The AAs containing no red mud sintered at $1200^{\circ}C$ had a specific gravity of about 1.2 and those containing 20 wt% had below 1.0 which are characters of lightweight aggregate.

• Journal of the Korean Magnetics Society
• /
• v.27 no.3
• /
• pp.87-91
• /
• 2017

Carbon-encapsulated Ni and metal Ni nanoparticles were synthesized by levitational gas condensation (LGC). Methane ($CH_4$) gas was used to coat the surface of the Ni nanoparticles. The Ni particles had a core diameter of 10 nm, and were covered by 2~3 nm thin carbon layers with multi-shells structure.The low magnetization comparing with the Ni nanoparticles without carbon-shell results in the coexistence of nonmagnetic carbon and a large surface spin percentage with disordered magnetization orientation for the nanoparticles. Biginelli reactions in the presence of L-proline and Ni and carbon encapsulated Ni nanoparticles were carried out to change the ratio between stereoisomers. The obtained S-enantiomers for 3,4-dihydropyrimidine (DHPM) using catalysts of Ni, and Ni@C was an excess of about ${\Delta}{\sim}7.4%$ and ${\Delta}{\sim}19.6%$, respectively. The nanopowders were fully recovered using magnet to reuse as a catalyst. The Ni@C was shown at same yield to formation of 3,4-DHPM, though it was recycled for catalyst in the reaction.

• Korean Chemical Engineering Research
• /
• v.50 no.4
• /
• pp.729-732
• /
• 2012

Herein we report the in-situ synthesis and direct decoration of chalcogenide naoparticles (NPs) onto multiwalled carbon nanotubes (MWCNTs) through an ionic liquid-assisted sonochemical method (ILASM). The as-obtained MWCNT/$BMimBF_4$/CdTe, MWCNT/$BMimBF_4$/ZnTe and MWCNT/$BMimBF_4$/ZnSe nanocomposites were characterized by TEM images and EDS spectra. In particular, the morphologies of nanocomposites such as bump-like, rough, and smooth core-shell structures were strongly influenced by the type of precursors and the interactions with MWCNT. This synthetic strategy opens a new way to directly synthesize and deposit semiconducting NPs (s-NPs) onto CNTs, which consist of binary components obtained from two precursors with different reaction rates.