• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 2006년도 Extended Abstracts of 2006 POWDER METALLURGY World Congress Part2
• /
• pp.1209-1210
• /
• 2006

A novel sintering process is proposed for bonding of $BaTiO_3$ and $Al_2O_3$ layers. Common commercial glass was used and infilterated among filler particles. As the kind of commercial glass, the phenomenon of the infilteration is different. Although Sud-1140 glass forms a glass/filler composite, it is not completely infilterated into the filler particles at $900^{\circ}C$. However as the increase of sintering temperature the infilteration of glass was improved. In this study, GA-1 and GA-12 glasses were infilterated the more than Sud-1140 glass. However, they are reacted by $BaTiO_3$ layer. The results of the experiment show that constrained sintering and the co-firing of the different materials were possible for glass infilteration using Sud-1140 glass at $1000^{\circ}C$.

• 한국세라믹학회지
• /
• 제29권7호
• /
• pp.533-538
• /
• 1992

Effect of Li2O.4B2O frit on the microstructural and thermal expansion behaviour of $\beta$-spodumene ceramics was investigated. With 4.0~8.0 wt.% frit addition, sintering temperature range was enlarged and densification was enhanced through liquid phase sintering. As the amount of frit addition was increased, thermal expansion coefficient was increased to 1.72$\times$10-6$^{\circ}C$-1 of its highest value, which indicated that the increment of thermal expansion coefficient due to the second phase was constrained.

• 한국세라믹학회지
• /
• 제29권8호
• /
• pp.646-650
• /
• 1992

Effect of Li2O.4B2O3 frit addition on microstructural and thermal expansion behaviour of the $\beta$-spodumene ceramics made from kaolinite was investigated. With 2.0~4.0 wt% frit addition, the densification by liquid phase sintering caused low water absorption below 3% and enhancement of beding strength. As the amount of frit addition was increased, thermal expansion coefficient was increased to large scale, but in 2 wt% frit addition, its thermal expansion coefficient was constrained to 1.92$\times$10-6$^{\circ}C$-1.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2003년도 하계학술대회 논문집 Vol.4 No.2
• /
• pp.760-763
• /
• 2003

Low Temperature Cofired Ceramics (LTCC) technology is a promising technology to integrate many devices in a module by embedding passive components. For the module substrate, most LTCC structures have dielectric constants below 10 to reduce signal delay time. Some components, which need high dielectric constants, have not been yet embedded in LTCC module. So, embedding capacitor with high capacitance by applying another dielectrics with high dielectric constants in LTCC is an important issue to maximize circuit density in LTCC module. In this study, electrical properties of embedded capacitor fabricated by dielectric paste of high dielectric constants (K-100) and co-firing behavior with LTCC were investigated. To prevent camber development of co-fired structure, constrained sintering process was tested. Dielectric properties of embedded capacitors were calculated from their capacitance and impedance value. Temperature coefficient of capacitance were also measured.

• 한국전기전자재료학회논문지
• /
• 제36권2호
• /
• pp.151-157
• /
• 2023

Integrating dielectric materials into LTCC is a convenient method to increase the integration density in electronic circuits. To enable co-firing of the high-k and low-k dielectric LTCC materials in a multi-material hetero-laminate, the shrinkage characteristics of both materials should be similar. Moreover, thermal expansion mismatch between materials during co-firing should be minimized. The alternating stacking of an LTCC with silica filler and that with calcium-zirconate filler was observed to examine the use of the same glass in different LTCCs to minimize the difference in shrinkage and thermal expansion coefficient. For the LTCC of silica filler with a low dielectric constant and that of calcium zirconate filler with a high dielectric constant, the amount of shrinkage was examined through a thermomechanical analysis, and the predicted appropriate fraction of each filler was applied to green sheets by tape casting. The green sheets of different fillers were alternatingly laminated to the thickness of 500 ㎛. As a result of examining the junction, it was observed through SEM that a complete bonding was achieved by constrained sintering in the structure of 'calcium zirconate 50 vol%-silica 30 vol%-calcium zirconate 50 vol%'.

• 한국결정성장학회지
• /
• 제25권5호
• /
• pp.199-204
• /
• 2015

본 연구에서는 잔사회와 준설토로 제조된 구형의 인공경량골재 내부에 생성되는 방사형 균열의 원인 및 그 억제 방법에 대하여 연구하였다. 인공경량골재는 잔사회와 준설토를 각각 7 : 3의 무게 비로 혼합하고 직경이 5~20 mm인 구 형태로 성형한 후 $1200^{\circ}C$에서 10분간 직화소성법으로 제조하였다. 골재 내부의 균열은 골재 지름이 작을수록 발생이 억제되었다. 또한 $SiO_2$ 분말을 첨가한 경우, 분말의 크기가 클수록 또는 첨가량이 증가할수록 방사형 균열 발생이 억제되었다. 균열이 억제된 인공경량골재의 비중은 1.3~1.6이고, 흡수율은 5~20 %의 범위를 나타내었다. 따라서 본 논문에서 제조된 인공경량골재는 건설 및 환경소재 등 여러 분야에 적용 가능할 것으로 보이며, 더불어 잔사회 및 준설토의 재활용율을 높이는데 크게 기여할 것으로 기대된다.